A kind of preparation of new anti-mite Composite Double functional fibre and its application method
Technical field
The present invention relates to a kind of preparation of new anti-mite Composite Double functional fibre and its application method, belong to functional fibre
Technical field.
Background technology
At present, as textile technology and life taste, the raising of quality, the garment material of simple function can not expire
The life requirement of sufficient people.Multifunction is the inexorable trend of costume fabric development.
The development of functional fibre is the symbol of modern fiber science progress.Functional fibre, fibre in differentiation and high-performance are fine
The technological innovation for developing into traditional textile industry of dimension, the conversion to high-tech industry creates advantage, is human lives
Horizontal raising contributes.Functional fibre refers in addition to physical and mechanical properties possessed by general fiber, also have
The tencel of certain specific function.Such as:Fiber has health care function (antibacterial, mite killing, physiotherapy and eliminate the unusual smell)
;Safeguard function (radiation proof, antistatic, uvioresistant etc.);The wet comfortable function (heat absorption, heat release, moisture absorption, moisture releasing etc.) of heat;Doctor
Treat and environment-friendly function (biocompatibility and biological degradability).Common functional fibre, complex manufacturing technology, cost of manufacture
It is higher, and function is not firm enough possessed by fiber, and by washing twice, the function of fiber will have a greatly reduced quality, and be unfavorable for
The manufacture of functional fibre and promote the use of.
It is an object of the invention to provide a kind of preparation of new anti-mite Composite Double functional fibre and its application method, this is new
The anti-mite Composite Double functional fibre of type is by during final finishing, will weave with anti-mite auxiliary agent, weaving function additive and basis
Polyester fiber is combined with each other, and formation has anti-mite property and functional terylene composite fibre, and this method technique is simple, is easy to flow
Waterline large-scale operation, easy control of process conditions in production process, production cost are low;It is fine a process for preparing the function of coming
Dimension, repeatedly washing can be passed through, also with good composite functional, be worth of widely use.
The content of the invention
The technical solution adopted for the present invention to solve the technical problems is:A kind of system of new anti-mite Composite Double functional fibre
Preparation Method, its step are:
(1), will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 4-6.4 kilograms, and terylene mesh bag is placed into conveyer belt
On;
(2), terylene mesh bag entered by conveyer belt in circulation solution case, circulate in solution case that weaving is helped with anti-bacteria and mite-proof functional in solution
Agent, weaving are 1-5 with the weight of function additive and water ratio:1-5:104, the temperature for circulating solution in solution case is Celsius for 50-114
Degree, soak time of the polyester fiber in circulation solution case is 3-8 minutes;
(3), the polyester fiber that soaked is rolled 5 times repeatedly with Pneumatic pressure bar in circulation solution case, roll every time 1 minute,
The pressure of press rods is 5 kilograms, it is adjacent roll twice between be spaced 1-2 minutes so that the weight of polyester fiber and solution ratio
For 5:0.1-1;
(4), the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is that 80-124 is Celsius
Degree, the baking time is 100-138 minutes;
(5), the polyester fiber after baking carry out packing encapsulation, that is, be prepared into new anti-mite Composite Double functional fibre.
A kind of preparation method of new anti-mite Composite Double functional fibre, it is characterised in that the step(2)Middle weaving is diligent
Energy auxiliary agent is weaving antibacterial functions auxiliary agent, weaving far-infrared functional auxiliary agent, weaving anion function auxiliary agent, weaving drive
Mosquito function additive, weaving are with deodorization functions auxiliary agent, weaving with formaldehyde-removing antibiotic deodorization functions auxiliary agent, weaving moisture absorption sweat discharging functions
Auxiliary agent, weaving cool feeling function additive, weaving use phase-change constant-temperature function additive with accumulation of heat temperature storage heat-preserving function auxiliary agent or weaving.
A kind of application method of new anti-mite Composite Double functional fibre, its step are:
(1), claim 1 prepared new anti-mite Composite Double functional fibre and polyester fiber, eutectic polyester fiber according to
Weight is than 1:1-2:0.1-0.5 carries out uniformly mixing and unclamps combing;
(2), according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15-40 grams;
(3), then in step(2)The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing;
(4), then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180-188 it is Celsius
Degree so that eutectic polyester fiber melts, and the baking time is the 50-60 seconds;
(5), it is baked after, roll coiled, that is, be prepared into new anti-mite Composite Double functional fibre flocculus.
The application method of described a kind of new anti-mite Composite Double functional fibre, it is characterised in that using new anti-mite multiple
Close the fabric that difunctional fiber is prepared.
It is an object of the invention to provide a kind of preparation of new anti-mite Composite Double functional fibre and its application method, this is new
The anti-mite Composite Double functional fibre of type is by during final finishing, will weave with anti-mite auxiliary agent, weaving function additive and basis
Polyester fiber is combined with each other, and formation has anti-mite property and functional terylene composite fibre, and this method technique is simple, is easy to flow
Waterline large-scale operation, easy control of process conditions in production process, production cost are low;It is fine a process for preparing the function of coming
Dimension, repeatedly washing can be passed through, also with good composite functional, be worth of widely use.
Embodiment
Specific embodiment one:A kind of preparation method of new anti-mite Composite Double functional fibre, its step are:
(1), will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 4 kilograms, and terylene mesh bag is placed on conveyer belt;
(2), terylene mesh bag entered by conveyer belt in circulation solution case, circulate in solution case that weaving is helped with anti-bacteria and mite-proof functional in solution
The weight ratio of agent, weaving antibacterial functions auxiliary agent and water is 1:1:104, the temperature for circulating solution in solution case is 50 degrees Celsius,
Soak time of the polyester fiber in circulation solution case is 3 minutes;
(3), the polyester fiber that soaked is rolled 5 times repeatedly with Pneumatic pressure bar in circulation solution case, roll every time 1 minute,
The pressure of press rods is 5 kilograms, it is adjacent roll twice between be spaced 1 minute so that the weight of polyester fiber and solution ratio is
5:0.1;
(4), the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is 80 degrees Celsius, is dried
It is 100 minutes to roast the time;
(5), the polyester fiber after baking carry out packing encapsulation, that is, be prepared into new anti-mite Composite Double functional fibre.
A kind of application method of new anti-mite Composite Double functional fibre, it is characterised in that its step is:
(1), claim 1 prepared new anti-mite Composite Double functional fibre and polyester fiber, eutectic polyester fiber according to
Weight is than 1:1:0.1, which carries out uniformly mixing, unclamps combing;
(2), according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15 grams;
(3), then in step(2)The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing;
(4), then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 50 seconds to bakee the time;
(5), it is baked after, roll coiled, that is, be prepared into new anti-mite Composite Double functional fibre flocculus.
The application method of described a kind of new anti-mite Composite Double functional fibre, it is characterised in that using new anti-mite multiple
Close the fabric that difunctional fiber is prepared.
Specific embodiment two:A kind of preparation method of new anti-mite Composite Double functional fibre, its step are:
(1), will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 5.8 kilograms, and terylene mesh bag is placed on conveyer belt;
(2), terylene mesh bag entered by conveyer belt in circulation solution case, circulate in solution case that weaving is helped with anti-bacteria and mite-proof functional in solution
The weight ratio of agent, weaving formaldehyde-removing antibiotic deodorization functions auxiliary agent and water is 2:3:104, circulating the temperature of solution in solution case is
86 degrees Celsius, soak time of the polyester fiber in circulation solution case is 6 minutes;
(3), the polyester fiber that soaked is rolled 5 times repeatedly with Pneumatic pressure bar in circulation solution case, roll every time 1 minute,
The pressure of press rods is 5 kilograms, it is adjacent roll twice between be spaced 1.7 minutes so that the weight of polyester fiber and solution ratio
For 5:0.35;
(4), the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is 89 degrees Celsius, is dried
It is 128 minutes to roast the time;
(5), the polyester fiber after baking carry out packing encapsulation, that is, be prepared into new anti-mite Composite Double functional fibre.
The application method of described a kind of new anti-mite Composite Double functional fibre, it is characterised in that its step is:
(1), claim 1 prepared new anti-mite Composite Double functional fibre and polyester fiber, eutectic polyester fiber according to
Weight is than 1:1.3:0.35, which carries out uniformly mixing, unclamps combing;
(2), according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 18 grams;
(3), then in step(2)The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing;
(4), then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 184 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 53 seconds to bakee the time;
(5), it is baked after, roll coiled, that is, be prepared into new anti-mite Composite Double functional fibre flocculus.
The application method of described a kind of new anti-mite Composite Double functional fibre, it is characterised in that using new anti-mite multiple
Close the fabric that difunctional fiber is prepared.
Specific embodiment three:A kind of preparation method of new anti-mite Composite Double functional fibre, its step are:
(1), will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 6.4 kilograms, and terylene mesh bag is placed on conveyer belt;
(2), terylene mesh bag entered by conveyer belt in circulation solution case, circulate in solution case that weaving is helped with anti-bacteria and mite-proof functional in solution
The weight ratio of agent, weaving accumulation of heat temperature storage heat-preserving function auxiliary agent and water is 5: 5:104, circulating the temperature of solution in solution case is
114 degrees Celsius, soak time of the polyester fiber in circulation solution case is 8 minutes;
(3), the polyester fiber that soaked is rolled 5 times repeatedly with Pneumatic pressure bar in circulation solution case, roll every time 1 minute,
The pressure of press rods is 5 kilograms, it is adjacent roll twice between be spaced 2 minutes so that the weight of polyester fiber and solution ratio is
5: 1;
(4), the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is 124 degrees Celsius,
It is 138 minutes to bakee the time;
(5), the polyester fiber after baking carry out packing encapsulation, that is, be prepared into new anti-mite Composite Double functional fibre.
The application method of described a kind of new anti-mite Composite Double functional fibre, it is characterised in that its step is:
(1), claim 1 prepared new anti-mite Composite Double functional fibre and polyester fiber, eutectic polyester fiber according to
Weight is than 1: 2:0.5, which carries out uniformly mixing, unclamps combing;
(2), according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 40 grams;
(3), then in step(2)The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing;
(4), then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 188 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 60 seconds to bakee the time;
(5), it is baked after, roll coiled, that is, be prepared into new anti-mite Composite Double functional fibre flocculus.
The application method of described a kind of new anti-mite Composite Double functional fibre, it is characterised in that using new anti-mite multiple
Close the fabric that difunctional fiber is prepared.
It is an object of the invention to provide a kind of preparation of new anti-mite Composite Double functional fibre and its application method, this is new
The anti-mite Composite Double functional fibre of type is by during final finishing, will weave with anti-mite auxiliary agent, weaving function additive and basis
Polyester fiber is combined with each other, and formation has anti-mite property and functional terylene composite fibre, and this method technique is simple, is easy to flow
Waterline large-scale operation, easy control of process conditions in production process, production cost are low;It is fine a process for preparing the function of coming
Dimension, repeatedly washing can be passed through, also with good composite functional, be worth of widely use.
Obviously, above-described embodiment is only intended to clearly illustrate example, and is not the restriction to embodiment.It is right
For those of ordinary skill in the art, can also make on the basis of the above description it is other it is various forms of change or
Change.There is no necessity and possibility to exhaust all the enbodiments.And the obvious change thus extended out or
Among changing still in the protection domain of the invention.