CN107558163A - A kind of preparation of novel and multifunctional composite fibre and its application method - Google Patents
A kind of preparation of novel and multifunctional composite fibre and its application method Download PDFInfo
- Publication number
- CN107558163A CN107558163A CN201710781945.5A CN201710781945A CN107558163A CN 107558163 A CN107558163 A CN 107558163A CN 201710781945 A CN201710781945 A CN 201710781945A CN 107558163 A CN107558163 A CN 107558163A
- Authority
- CN
- China
- Prior art keywords
- weaving
- novel
- polyester fiber
- multifunctional composite
- composite fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of preparation of novel and multifunctional composite fibre and its application method, belong to functional fibre technical field.The preparation of novel and multifunctional composite fibre of the present invention and its application method, the novel and multifunctional composite fibre passes through during final finishing, weaving is combined with each other with anti-mite auxiliary agent, weaving with function additive and basic polyester fiber, formation has anti-mite property and functional terylene composite fibre, this method technique is simple, it is easy to streamline large-scale operation, easy control of process conditions in production process, production cost is low；A process for preparing the functional fibre come, can pass through repeatedly washing, also with good composite functional, be worth of widely use.
Description
Technical field
The present invention relates to a kind of preparation of novel and multifunctional composite fibre and its application method, belong to functional fibre technology
Field.
Background technology
At present, as textile technology and life taste, the raising of quality, the garment material of simple function can not expire
The life requirement of sufficient people.Multifunction is the inexorable trend of costume fabric development.
The development of functional fibre is the symbol of modern fiber science progress.Functional fibre, fibre in differentiation and high-performance are fine
The technological innovation for developing into traditional textile industry of dimension, the conversion to high-tech industry creates advantage, is human lives
Horizontal raising contributes.Functional fibre refers in addition to physical and mechanical properties possessed by general fiber, also have
The tencel of certain specific function.Such as:Fiber has health care function (antibacterial, mite killing, physiotherapy and eliminate the unusual smell)
；Safeguard function (radiation proof, antistatic, uvioresistant etc.)；The wet comfortable function (heat absorption, heat release, moisture absorption, moisture releasing etc.) of heat；Doctor
Treat and environment-friendly function (biocompatibility and biological degradability).Common functional fibre, complex manufacturing technology, cost of manufacture
It is higher, and function is not firm enough possessed by fiber, and by washing twice, the function of fiber will have a greatly reduced quality, and be unfavorable for
The manufacture of functional fibre and promote the use of.
It is an object of the invention to provide a kind of preparation of novel and multifunctional composite fibre and its application method, and this is new more
Function and service fiber is by during final finishing, will weave with anti-mite auxiliary agent, weaving function additive and basic polyester fiber
It is combined with each other, formation has anti-mite property and functional terylene composite fibre, and this method technique is simple, is easy to the big rule of streamline
Modulo operation, easy control of process conditions in production process, production cost are low；A process for preparing the functional fibre come, Ke Yijing
Repeatedly washing is crossed, also with good composite functional, is worth of widely use.
The content of the invention
The technical solution adopted for the present invention to solve the technical problems is：A kind of preparation side of novel and multifunctional composite fibre
Method, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 4-6.4 kilograms, and terylene mesh bag is placed into conveyer belt
On；
（2）, terylene mesh bag entered by conveyer belt in circulation solution case, circulate in solution case that weaving is helped with anti-bacteria and mite-proof functional in solution
Agent, weaving are 1-5 with anti-bacteria and mite-proof functional auxiliary agent, weaving with the weight of function additive and water ratio:1-5: 1-5:104, circulate solution case
The temperature of interior solution is 50-114 degrees Celsius, and soak time of the polyester fiber in circulation solution case is 3-8 minutes；
（3）, the polyester fiber that soaked is rolled 5 times repeatedly with Pneumatic pressure bar in circulation solution case, roll every time 1 minute,
The pressure of press rods is 5 kilograms, it is adjacent roll twice between be spaced 1-2 minutes so that the weight of polyester fiber and solution ratio
For 5:0.1-1；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is that 80-124 is Celsius
Degree, the baking time is 100-138 minutes；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into novel and multifunctional composite fibre.
A kind of preparation method of novel and multifunctional composite fibre, it is characterised in that the step（2）Middle weaving is helped with function
Agent is weaving far-infrared functional auxiliary agent, weaving anion function auxiliary agent, weaving function of driving mosquitoes auxiliary agent, weaving deodorization work(
Energy auxiliary agent, weaving are helped with formaldehyde-removing antibiotic deodorization functions auxiliary agent, weaving with moisture absorption sweat discharging functions auxiliary agent, weaving with cool feeling function
Agent, weaving use phase-change constant-temperature function additive with accumulation of heat temperature storage heat-preserving function auxiliary agent or weaving.
A kind of application method of novel and multifunctional composite fibre, its step are：
（1）, claim 1 prepared novel and multifunctional composite fibre and polyester fiber, eutectic polyester fiber is according to weight
Than 1：1-2：0.1-0.5 carries out uniformly mixing and unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15-40 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180-188 it is Celsius
Degree so that eutectic polyester fiber melts, and the baking time is the 50-60 seconds；
（5）, it is baked after, roll coiled, that is, be prepared into novel and multifunctional composite fiber flocculus.
The application method of described a kind of novel and multifunctional composite fibre, it is characterised in that using novel and multifunctional compound
The fabric that fiber is prepared.
It is an object of the invention to provide a kind of preparation of novel and multifunctional composite fibre and its application method, and this is new more
Function and service fiber is by during final finishing, will weave with anti-mite auxiliary agent, weaving function additive and basic polyester fiber
It is combined with each other, formation has anti-mite property and functional terylene composite fibre, and this method technique is simple, is easy to the big rule of streamline
Modulo operation, easy control of process conditions in production process, production cost are low；A process for preparing the functional fibre come, Ke Yijing
Repeatedly washing is crossed, also with good composite functional, is worth of widely use.
Embodiment
Specific embodiment one：A kind of preparation method of novel and multifunctional composite fibre, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 4 kilograms, and terylene mesh bag is placed on conveyer belt；
（2）, terylene mesh bag entered by conveyer belt in circulation solution case, circulate in solution case that weaving is helped with anti-bacteria and mite-proof functional in solution
Agent, weaving antibacterial functions auxiliary agent, the weight ratio of weaving far-infrared functional auxiliary agent and water are 1:1:1:104, circulate solution case
The temperature of interior solution is 50 degrees Celsius, and soak time of the polyester fiber in circulation solution case is 3 minutes；
（3）, the polyester fiber that soaked is rolled 5 times repeatedly with Pneumatic pressure bar in circulation solution case, roll every time 1 minute,
The pressure of press rods is 5 kilograms, it is adjacent roll twice between be spaced 1 minute so that the weight of polyester fiber and solution ratio is
5:0.1；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is 80 degrees Celsius, is dried
It is 100 minutes to roast the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into novel and multifunctional composite fibre.
A kind of application method of novel and multifunctional composite fibre, it is characterised in that its step is：
（1）, claim 1 prepared novel and multifunctional composite fibre and polyester fiber, eutectic polyester fiber is according to weight
Than 1：1：0.1, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 50 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into novel and multifunctional composite fiber flocculus.
The application method of described a kind of novel and multifunctional composite fibre, it is characterised in that using novel and multifunctional compound
The fabric that fiber is prepared.
Specific embodiment two：A kind of preparation method of novel and multifunctional composite fibre, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 5.8 kilograms, and terylene mesh bag is placed on conveyer belt；
（2）, terylene mesh bag entered by conveyer belt in circulation solution case, circulate in solution case that weaving is helped with anti-bacteria and mite-proof functional in solution
The weight ratio of agent, weaving antibacterial functions auxiliary agent weaving formaldehyde-removing antibiotic deodorization functions auxiliary agent and water is 2:2:3:104, circulation
The temperature of solution is 86 degrees Celsius in solution case, and soak time of the polyester fiber in circulation solution case is 6 minutes；
（3）, the polyester fiber that soaked is rolled 5 times repeatedly with Pneumatic pressure bar in circulation solution case, roll every time 1 minute,
The pressure of press rods is 5 kilograms, it is adjacent roll twice between be spaced 1.7 minutes so that the weight of polyester fiber and solution ratio
For 5:0.35；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is 89 degrees Celsius, is dried
It is 128 minutes to roast the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into novel and multifunctional composite fibre.
The application method of described a kind of novel and multifunctional composite fibre, it is characterised in that its step is：
（1）, claim 1 prepared novel and multifunctional composite fibre and polyester fiber, eutectic polyester fiber is according to weight
Than 1：1.3：0.35, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 18 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 184 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 53 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into novel and multifunctional composite fiber flocculus.
The application method of described a kind of novel and multifunctional composite fibre, it is characterised in that using novel and multifunctional compound
The fabric that fiber is prepared.
Specific embodiment three：A kind of preparation method of novel and multifunctional composite fibre, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 6.4 kilograms, and terylene mesh bag is placed on conveyer belt；
（2）, terylene mesh bag entered by conveyer belt in circulation solution case, circulate in solution case that weaving is helped with anti-bacteria and mite-proof functional in solution
Agent, weaving antibacterial functions auxiliary agent, the weight ratio of weaving accumulation of heat temperature storage heat-preserving function auxiliary agent and water are 5:5: 5:104, circulation
The temperature of solution is 114 degrees Celsius in solution case, and soak time of the polyester fiber in circulation solution case is 8 minutes；
（3）, the polyester fiber that soaked is rolled 5 times repeatedly with Pneumatic pressure bar in circulation solution case, roll every time 1 minute,
The pressure of press rods is 5 kilograms, it is adjacent roll twice between be spaced 2 minutes so that the weight of polyester fiber and solution ratio is
5: 1；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is 124 degrees Celsius,
It is 138 minutes to bakee the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into novel and multifunctional composite fibre.
The application method of described a kind of novel and multifunctional composite fibre, it is characterised in that its step is：
（1）, claim 1 prepared novel and multifunctional composite fibre and polyester fiber, eutectic polyester fiber is according to weight
Than 1： 2：0.5, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 40 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 188 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 60 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into novel and multifunctional composite fiber flocculus.
The application method of described a kind of novel and multifunctional composite fibre, it is characterised in that using novel and multifunctional compound
The fabric that fiber is prepared.
It is an object of the invention to provide a kind of preparation of novel and multifunctional composite fibre and its application method, and this is new more
Function and service fiber is by during final finishing, will weave with anti-mite auxiliary agent, weaving function additive and basic polyester fiber
It is combined with each other, formation has anti-mite property and functional terylene composite fibre, and this method technique is simple, is easy to the big rule of streamline
Modulo operation, easy control of process conditions in production process, production cost are low；A process for preparing the functional fibre come, Ke Yijing
Repeatedly washing is crossed, also with good composite functional, is worth of widely use.
Obviously, above-described embodiment is only intended to clearly illustrate example, and is not the restriction to embodiment.It is right
For those of ordinary skill in the art, can also make on the basis of the above description it is other it is various forms of change or
Change.There is no necessity and possibility to exhaust all the enbodiments.And the obvious change thus extended out or
Among changing still in the protection domain of the invention.
Claims (4)
1. a kind of preparation method of novel and multifunctional composite fibre, it is characterised in that its step is：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 4-6.4 kilograms, and terylene mesh bag is placed into conveyer belt
On；
（2）, terylene mesh bag entered by conveyer belt in circulation solution case, circulate in solution case that weaving is helped with anti-bacteria and mite-proof functional in solution
Agent, weaving are 1-5 with antibacterial functions auxiliary agent, weaving with the weight of function additive and water ratio:1-5: 1-5:104, circulate solution case
The temperature of interior solution is 50-114 degrees Celsius, and soak time of the polyester fiber in circulation solution case is 3-8 minutes；
（3）, the polyester fiber that soaked is rolled 5 times repeatedly with Pneumatic pressure bar in circulation solution case, roll every time 1 minute,
The pressure of press rods is 5 kilograms, it is adjacent roll twice between be spaced 1-2 minutes so that the weight of polyester fiber and solution ratio
For 5:0.1-1；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is that 80-124 is Celsius
Degree, the baking time is 100-138 minutes；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into novel and multifunctional composite fibre.
A kind of 2. preparation method of novel and multifunctional composite fibre according to claim 1, it is characterised in that the step
（2）Middle weaving is weaving with far-infrared functional auxiliary agent, weaving with anion function auxiliary agent, weaving function of driving mosquitoes with function additive
Auxiliary agent, weaving with deodorization functions auxiliary agent, weaving with formaldehyde-removing antibiotic deodorization functions auxiliary agent, weaving with moisture absorption sweat discharging functions auxiliary agent,
Weaving cool feeling function additive, weaving use phase-change constant-temperature function additive with accumulation of heat temperature storage heat-preserving function auxiliary agent or weaving.
3. the application method of a kind of novel and multifunctional composite fibre according to claim 1, it is characterised in that its step is：
（1）, claim 1 prepared novel and multifunctional composite fibre and polyester fiber, eutectic polyester fiber is according to weight
Than 1：1-2：0.1-0.5 carries out uniformly mixing and unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15-40 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180-188 it is Celsius
Degree so that eutectic polyester fiber melts, and the baking time is the 50-60 seconds；
（5）, it is baked after, roll coiled, that is, be prepared into novel and multifunctional composite fiber flocculus.
4. the application method of a kind of novel and multifunctional composite fibre according to claim 1, it is characterised in that using new
The fabric that multifunctional composite fiber is prepared.