CN107476046A - A kind of preparation of formaldehyde-removing antibiotic deodorization functions fiber and its application method - Google Patents
A kind of preparation of formaldehyde-removing antibiotic deodorization functions fiber and its application method Download PDFInfo
- Publication number
- CN107476046A CN107476046A CN201710782077.2A CN201710782077A CN107476046A CN 107476046 A CN107476046 A CN 107476046A CN 201710782077 A CN201710782077 A CN 201710782077A CN 107476046 A CN107476046 A CN 107476046A
- Authority
- CN
- China
- Prior art keywords
- formaldehyde
- fiber
- polyester fiber
- deodorization functions
- antibiotic deodorization
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of preparation of formaldehyde-removing antibiotic deodorization functions fiber and its application method, belong to functional fibre technical field.A kind of preparation of formaldehyde-removing antibiotic deodorization functions fiber of the present invention and its application method, the formaldehyde-removing antibiotic deodorization functions fiber passes through during final finishing, weaving is combined with each other with formaldehyde-removing antibiotic deodorization functions auxiliary agent and basic polyester fiber, form the polyester fiber with formaldehyde-removing antibiotic deodorization functions, this method technique is simple, it is easy to streamline large-scale operation, easy control of process conditions in production process, production cost is low；A process for preparing the functional fibre come, can pass through repeatedly washing, also with good feature, be worth of widely use.
Description
Technical field
The present invention relates to a kind of preparation of formaldehyde-removing antibiotic deodorization functions fiber and its application method, belong to functional fibre
Technical field.
Background technology
At present, as textile technology and life taste, the raising of quality, the garment material of simple function can not expire
The life requirement of sufficient people.Multifunction is the inexorable trend of costume fabric development.
The development of functional fibre is the symbol of modern fiber science progress.Functional fibre, fibre in differentiation and high-performance are fine
The technological innovation for developing into traditional textile industry of dimension, the conversion to high-tech industry creates advantage, is human lives
Horizontal raising contributes.Functional fibre refers in addition to physical and mechanical properties possessed by general fiber, also have
The tencel of certain specific function.Such as:Fiber has health care function (antibacterial, mite killing, physiotherapy and eliminate the unusual smell)
；Safeguard function (radiation proof, antistatic, uvioresistant etc.)；The wet comfortable function (heat absorption, heat release, moisture absorption, moisture releasing etc.) of heat；Doctor
Treat and environment-friendly function (biocompatibility and biological degradability).Common functional fibre, complex manufacturing technology, cost of manufacture
It is higher, and function is not firm enough possessed by fiber, and by washing twice, the function of fiber will have a greatly reduced quality, and be unfavorable for
The manufacture of functional fibre and promote the use of.
It is an object of the invention to provide a kind of preparation of formaldehyde-removing antibiotic deodorization functions fiber and its application method, this is removed
Formaldehyde antibacterial and deodouring function fiber is by the way that during final finishing, weaving is washed with formaldehyde-removing antibiotic deodorization functions auxiliary agent with basis
Synthetic fibre fiber composite together, forms the polyester fiber with formaldehyde-removing antibiotic deodorization functions, this method technique is simple, is easy to flowing water
Line large-scale operation, easy control of process conditions in production process, production cost are low；A process for preparing come functional fibre,
Repeatedly washing can be passed through, also with good feature, be worth of widely use.
The content of the invention
The technical solution adopted for the present invention to solve the technical problems is：A kind of system of formaldehyde-removing antibiotic deodorization functions fiber
Preparation Method, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 4-6.5 kilograms, and terylene mesh bag is placed into conveyer belt
On；
（2）, terylene mesh bag by conveyer belt enter circulation solution case in, circulate solution case in weaving use formaldehyde-removing antibiotic deodorization work(
The weight ratio of energy auxiliary agent and water is 1-5:105, the temperature for circulating solution in solution case is 50-115 degrees Celsius, and polyester fiber is following
Soak time in ring solution case is 3-8 minutes；
（3）, the polyester fiber that soaked is rolled 5 times repeatedly with Pneumatic pressure bar in circulation solution case, roll every time 1 minute,
The pressure of press rods is 5 kilograms, it is adjacent roll twice between be spaced 1-2 minutes so that the weight of polyester fiber and solution ratio
For 5:0.1-1；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is that 80-125 is Celsius
Degree, the baking time is 100-140 minutes；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into formaldehyde-removing antibiotic deodorization functions fiber.
A kind of application method of described formaldehyde-removing antibiotic deodorization functions fiber, its step are：
（1）, the formaldehyde-removing antibiotic deodorization functions fiber for preparing claim 1 and polyester fiber, eutectic polyester fiber according to
Weight is than 1：1-2：0.1-0.5 carries out uniformly mixing and unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15-40 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180-195 it is Celsius
Degree so that eutectic polyester fiber melts, and the baking time is the 50-60 seconds；
（5）, it is baked after, roll coiled, that is, be prepared into formaldehyde-removing antibiotic deodorization functions fibrefill.
Described a kind of formaldehyde-removing antibiotic deodorization functions fiber application method, it is characterised in that removed using formaldehyde-removing antibiotic
The fabric that smelly functional fibre is prepared.
A kind of preparation of formaldehyde-removing antibiotic deodorization functions fiber of the purpose of the present invention and its application method, the formaldehyde-removing antibiotic
Deodorization functions fiber is by the way that during final finishing, weaving is answered with formaldehyde-removing antibiotic deodorization functions auxiliary agent and basic polyester fiber
It is combined, forms the polyester fiber with formaldehyde-removing antibiotic deodorization functions, this method technique is simple, is easy to streamline extensive
Operate, easy control of process conditions in production process, production cost is low；A process for preparing the functional fibre come, can pass through
Repeatedly washing, also with good feature, is worth of widely use.
Embodiment
Specific embodiment one：A kind of preparation method of formaldehyde-removing antibiotic deodorization functions fiber, it is characterised in that its step is：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 4 kilograms, and terylene mesh bag is placed on conveyer belt；
（2）, terylene mesh bag by conveyer belt enter circulation solution case in, circulate solution case in weaving use formaldehyde-removing antibiotic deodorization work(
The weight ratio of energy auxiliary agent and water is 1:105, the temperature for circulating solution in solution case is 50 degrees Celsius, and polyester fiber is in circulation solution
Soak time in case is 3 minutes；
（3）, the polyester fiber that soaked is rolled 5 times repeatedly with Pneumatic pressure bar in circulation solution case, roll every time 1 minute,
The pressure of press rods is 5 kilograms, it is adjacent roll twice between be spaced 1-2 minutes so that the weight of polyester fiber and solution ratio
For 5:0.1-1；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is 80 degrees Celsius, is dried
It is 100 minutes to roast the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into formaldehyde-removing antibiotic deodorization functions fiber.
A kind of 1. application method of formaldehyde-removing antibiotic deodorization functions fiber according to claim 1, it is characterised in that
Its step is：
（1）, the formaldehyde-removing antibiotic deodorization functions fiber for preparing claim 1 and polyester fiber, eutectic polyester fiber according to
Weight is than 1：1：0.1, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15-40 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 50 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into formaldehyde-removing antibiotic deodorization functions fibrefill.
Described a kind of formaldehyde-removing antibiotic deodorization functions fiber application method, it is characterised in that removed using formaldehyde-removing antibiotic
The fabric that smelly functional fibre is prepared.
Specific embodiment two：A kind of preparation method of formaldehyde-removing antibiotic deodorization functions fiber, it is characterised in that its step is：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 5 kilograms, and terylene mesh bag is placed on conveyer belt；
（2）, terylene mesh bag by conveyer belt enter circulation solution case in, circulate solution case in weaving use formaldehyde-removing antibiotic deodorization work(
The weight ratio of energy auxiliary agent and water is 3:105, the temperature for circulating solution in solution case is 85 degrees Celsius, and polyester fiber is in circulation solution
Soak time in case is 6 minutes；
（3）, the polyester fiber that soaked is rolled 5 times repeatedly with Pneumatic pressure bar in circulation solution case, roll every time 1 minute,
The pressure of press rods is 5 kilograms, it is adjacent roll twice between be spaced 1-2 minutes so that the weight of polyester fiber and solution ratio
For 5:0.1-1；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is 95 degrees Celsius, is dried
It is 120 minutes to roast the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into formaldehyde-removing antibiotic deodorization functions fiber.
A kind of application method of described formaldehyde-removing antibiotic deodorization functions fiber, its step are：
（1）, the formaldehyde-removing antibiotic deodorization functions fiber for preparing claim 1 and polyester fiber, eutectic polyester fiber according to
Weight is than 1：1-2：0.3, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 30 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 185 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 55 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into formaldehyde-removing antibiotic deodorization functions fibrefill.
Described a kind of formaldehyde-removing antibiotic deodorization functions fiber application method, it is characterised in that removed using formaldehyde-removing antibiotic
The fabric that smelly functional fibre is prepared.
Specific embodiment three：A kind of preparation method of formaldehyde-removing antibiotic deodorization functions fiber, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 6.5 kilograms, and terylene mesh bag is placed on conveyer belt；
（2）, terylene mesh bag by conveyer belt enter circulation solution case in, circulate solution case in weaving use formaldehyde-removing antibiotic deodorization work(
The weight ratio of energy auxiliary agent and water is 5:105, the temperature for circulating solution in solution case is 115 degrees Celsius, and polyester fiber is molten in circulation
Soak time in body case is 8 minutes；
（3）, the polyester fiber that soaked is rolled 5 times repeatedly with Pneumatic pressure bar in circulation solution case, roll every time 1 minute,
The pressure of press rods is 5 kilograms, it is adjacent roll twice between be spaced 2 minutes so that the weight of polyester fiber and solution ratio is
5: 1；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is 125 degrees Celsius,
It is 140 minutes to bakee the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into formaldehyde-removing antibiotic deodorization functions fiber.
A kind of application method of described formaldehyde-removing antibiotic deodorization functions fiber, its step are：
（1）, the formaldehyde-removing antibiotic deodorization functions fiber for preparing claim 1 and polyester fiber, eutectic polyester fiber according to
Weight is than 1： 2：0.5, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15-40 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 195 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 60 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into formaldehyde-removing antibiotic deodorization functions fibrefill.
Described a kind of formaldehyde-removing antibiotic deodorization functions fiber application method, it is characterised in that removed using formaldehyde-removing antibiotic
The fabric that smelly functional fibre is prepared.
It is an object of the invention to provide a kind of preparation of formaldehyde-removing antibiotic deodorization functions fiber and its application method, this is removed
Formaldehyde antibacterial and deodouring function fiber is by the way that during final finishing, weaving is washed with formaldehyde-removing antibiotic deodorization functions auxiliary agent with basis
Synthetic fibre fiber composite together, forms the polyester fiber with formaldehyde-removing antibiotic deodorization functions, this method technique is simple, is easy to flowing water
Line large-scale operation, easy control of process conditions in production process, production cost are low；A process for preparing come functional fibre,
Repeatedly washing can be passed through, also with good feature, be worth of widely use.
Obviously, above-described embodiment is only intended to clearly illustrate example, and is not the restriction to embodiment.It is right
For those of ordinary skill in the art, can also make on the basis of the above description it is other it is various forms of change or
Change.There is no necessity and possibility to exhaust all the enbodiments.And the obvious change thus extended out or
Among changing still in the protection domain of the invention.
Claims (3)
1. a kind of preparation method of formaldehyde-removing antibiotic deodorization functions fiber, it is characterised in that its step is：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 4-6.5 kilograms, and terylene mesh bag is placed into conveyer belt
On；
（2）, terylene mesh bag by conveyer belt enter circulation solution case in, circulate solution case in weaving use formaldehyde-removing antibiotic deodorization work(
The weight ratio of energy auxiliary agent and water is 1-5:105, the temperature for circulating solution in solution case is 50-115 degrees Celsius, and polyester fiber is following
Soak time in ring solution case is 3-8 minutes；
（3）, the polyester fiber that soaked is rolled 5 times repeatedly with Pneumatic pressure bar in circulation solution case, roll every time 1 minute,
The pressure of press rods is 5 kilograms, it is adjacent roll twice between be spaced 1-2 minutes so that the weight of polyester fiber and solution ratio
For 5:0.1-1；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is that 80-125 is Celsius
Degree, the baking time is 100-140 minutes；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into formaldehyde-removing antibiotic deodorization functions fiber.
2. the application method of a kind of formaldehyde-removing antibiotic deodorization functions fiber according to claim 1, it is characterised in that it is walked
Suddenly it is：
（1）, the formaldehyde-removing antibiotic deodorization functions fiber for preparing claim 1 and polyester fiber, eutectic polyester fiber according to
Weight is than 1：1-2：0.1-0.5 carries out uniformly mixing and unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15-40 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180-195 it is Celsius
Degree so that eutectic polyester fiber melts, and the baking time is the 50-60 seconds；
（5）, it is baked after, roll coiled, that is, be prepared into formaldehyde-removing antibiotic deodorization functions fibrefill.
3. a kind of formaldehyde-removing antibiotic deodorization functions fiber application method according to claim 1, it is characterised in that using removing
The fabric that formaldehyde antibacterial and deodouring function fiber is prepared.