CN107558066A - The preparation of far infrared Composite Double functional fibre and its application method - Google Patents
The preparation of far infrared Composite Double functional fibre and its application method Download PDFInfo
- Publication number
- CN107558066A CN107558066A CN201710781337.4A CN201710781337A CN107558066A CN 107558066 A CN107558066 A CN 107558066A CN 201710781337 A CN201710781337 A CN 201710781337A CN 107558066 A CN107558066 A CN 107558066A
- Authority
- CN
- China
- Prior art keywords
- weaving
- fiber
- far infrared
- functional fibre
- endless apron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the preparation of far infrared Composite Double functional fibre and its application method, belong to functional fibre technical field.The present invention relates to far infrared Composite Double functional fibre preparation and its application method, the new mite Composite Double functional fibre passes through during final finishing, weaving is combined with each other with far infrared auxiliary agent, weaving with function additive and basic polyester fiber, formation has far infrared and functional terylene composite fibre, this method technique is simple, it is easy to streamline large-scale operation, easy control of process conditions in production process, production cost is low；A process for preparing the functional fibre come, can pass through repeatedly washing, also with good composite functional, be worth of widely use.
Description
Technical field
The present invention relates to the preparation of far infrared Composite Double functional fibre and its application method, belongs to functional fibre technology neck
Domain.
Background technology
At present, as textile technology and life taste, the raising of quality, the garment material of simple function can not expire
The life requirement of sufficient people.Multifunction is the inexorable trend of costume fabric development.
The development of functional fibre is the symbol of modern fiber science progress.Functional fibre, fibre in differentiation and high-performance are fine
The technological innovation for developing into traditional textile industry of dimension, the conversion to high-tech industry creates advantage, is human lives
Horizontal raising contributes.Functional fibre refers in addition to physical and mechanical properties possessed by general fiber, also have
The tencel of certain specific function.Such as:Fiber has health care function (antibacterial, mite killing, physiotherapy and eliminate the unusual smell)
；Safeguard function (radiation proof, antistatic, uvioresistant etc.)；The wet comfortable function (heat absorption, heat release, moisture absorption, moisture releasing etc.) of heat；Doctor
Treat and environment-friendly function (biocompatibility and biological degradability).Common functional fibre, complex manufacturing technology, cost of manufacture
It is higher, and function is not firm enough possessed by fiber, and by washing twice, the function of fiber will have a greatly reduced quality, and be unfavorable for
The manufacture of functional fibre and promote the use of.
Object of the present invention is to provide the preparation of far infrared Composite Double functional fibre and its application method, the new mite is answered
Difunctional fiber is closed by during final finishing, weaving far infrared auxiliary agent, weaving function additive and basic terylene is fine
Dimension is combined with each other, and formation has far infrared and functional terylene composite fibre, and this method technique is simple, is easy to streamline
Large-scale operation, easy control of process conditions in production process, production cost are low；, can a process for preparing the functional fibre come
By repeatedly washing, also with good composite functional, to be worth of widely use.
The content of the invention
The technical solution adopted for the present invention to solve the technical problems is：The preparation side of far infrared Composite Double functional fibre
Method, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is sent on first circulation conveyer belt；
（2）, it is fluffy after polyester fiber by first circulation conveyer belt enter fiber soak casing one, fiber immersion casing one in
Provided with second circulation conveyer belt and the 3rd endless apron, second circulation conveyer belt is located at the top of the 3rd endless apron, the
One endless apron will be fluffy after polyester fiber be sent between second circulation conveyer belt and the 3rd endless apron, second circulation
Conveyer belt and the 3rd endless apron are immersed in weaving in fiber immersion casing one with function compounding agent solution, weaving function
Weaving is 1-5 with the weight of far-infrared functional auxiliary agent and water ratio in compounding agent solution:102, the temperature of weaving function compounding agent solution
For 50-112 degrees Celsius, soaked when weaving of the polyester fiber in fiber immersion casing one is with function compounding agent solution in motion,
Soak time is 3-8 minutes；
（3）, the polyester fiber that soaked enters the 4th endless apron out of fiber immersion casing one, in the 4th endless apron
On the fiber soaked is extruded with squeezing roller, the pressure of squeezing roller is 5 kilograms, after being extruded through squeezing roller
The weight of polyester fiber and solution ratio is 5 in polyester fiber:0.1-1；
（4）, the polyester fiber for preparing step 3 be put into steam drying box and bakeed, stoving temperature is that 80-124 is Celsius
Degree, the baking time is 10-20 minutes；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into far infrared functional fibre.
（6）, by step（5）The far infrared functional fibre prepared enters fiber by the 5th endless apron and soaks casing
Two, fiber immersion casing two is interior to be provided with the 6th endless apron and the 7th endless apron, and the 6th endless apron is located at the 7th
The far infrared functional fibre prepared is sent into the 6th endless apron and the by the top of endless apron, the 5th endless apron
Between seven endless aprons, the weaving that the 6th endless apron and the 7th endless apron are immersed in fiber immersion casing two is used
In function additive solution, weaving is 1-5 with weaving in function compounding agent solution with the weight of function additive and water ratio:102, weaving is used
The temperature of function additive solution is 50-112 degrees Celsius, weaving function of the far infrared functional fibre in fiber immersion casing two
Soaked in compounding agent solution in motion, soak time is 3-8 minutes；
（7）, the far infrared functional fibre that soaked enters the 8th endless apron out of fiber immersion casing two, circulated the 8th
The fiber soaked is extruded with squeezing roller on conveyer belt, the pressure of squeezing roller is 5 kilograms, is extruded through squeezing roller
Later fiber mid and far infrared functional fibre and the weight ratio of solution is 5:0.1-1；
（8）, the polyester fiber for preparing step 7 be put into steam drying box and bakeed, stoving temperature is that 80-124 is Celsius
Degree, the baking time is 10-20 minutes；
（9）, the fiber after baking carry out packing encapsulation, that is, be prepared into far infrared Composite Double functional fibre.
The preparation method of preferable described far infrared Composite Double functional fibre, it is characterised in that the step（6）Middle spinning
It is weaving anti-bacteria and mite-proof functional auxiliary agent, weaving antibacterial functions auxiliary agent, weaving anion function auxiliary agent, weaving to knit with function additive
With function of driving mosquitoes auxiliary agent, weaving with deodorization functions auxiliary agent, weaving with formaldehyde-removing antibiotic deodorization functions auxiliary agent, weaving moisture absorbing and sweat releasing
Function additive, weaving are helped with cool feeling function additive, weaving with accumulation of heat temperature storage heat-preserving function auxiliary agent or weaving with phase-change constant-temperature function
Agent.
The application method of described far infrared Composite Double functional fibre, its step are：
（1）, the far infrared Composite Double functional fibre for preparing claim 1 and polyester fiber, eutectic polyester fiber be according to weight
Measure ratio 1：1-2：0.1-0.5 carries out uniformly mixing and unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15-40 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180-197 it is Celsius
Degree so that eutectic polyester fiber melts, and the baking time is the 50-60 seconds；
（5）, it is baked after, roll coiled, that is, be prepared into far infrared Composite Double functional fibre flocculus.
The application method of described far infrared Composite Double functional fibre, it is characterised in that compound difunctional using far infrared
The fabric that fiber is prepared.
It is an object of the invention to the preparation of far infrared Composite Double functional fibre and its application method, the new mite Composite Double
Functional fibre is by the way that during final finishing, weaving is answered with far infrared auxiliary agent, weaving with function additive and basic polyester fiber
It is combined, formation has far infrared and functional terylene composite fibre, and this method technique is simple, is easy to the big rule of streamline
Modulo operation, easy control of process conditions in production process, production cost are low；A process for preparing the functional fibre come, Ke Yijing
Repeatedly washing is crossed, also with good composite functional, is worth of widely use.
Embodiment
Specific embodiment one：The preparation method of far infrared Composite Double functional fibre, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is sent on first circulation conveyer belt；
（2）, it is fluffy after polyester fiber by first circulation conveyer belt enter fiber soak casing one, fiber immersion casing one in
Provided with second circulation conveyer belt and the 3rd endless apron, second circulation conveyer belt is located at the top of the 3rd endless apron, the
One endless apron will be fluffy after polyester fiber be sent between second circulation conveyer belt and the 3rd endless apron, second circulation
Conveyer belt and the 3rd endless apron are immersed in weaving in fiber immersion casing one with function compounding agent solution, weaving function
The weight of weaving far-infrared functional auxiliary agent and water ratio is 1 in compounding agent solution:102, weaving is with the temperature of function compounding agent solution
50 degrees Celsius, soaked when weaving of the polyester fiber in fiber immersion casing one is with function compounding agent solution in motion, during immersion
Between be 3 minutes；
（3）, the polyester fiber that soaked enters the 4th endless apron out of fiber immersion casing one, in the 4th endless apron
On the fiber soaked is extruded with squeezing roller, the pressure of squeezing roller is 5 kilograms, after being extruded through squeezing roller
The weight of polyester fiber and solution ratio is 5 in polyester fiber:0.1；
（4）, the polyester fiber for preparing step 3 be put into steam drying box and bakeed, stoving temperature is 80 degrees Celsius, is dried
It is 10 minutes to roast the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into far infrared functional fibre.
（6）, by step（5）The far infrared functional fibre prepared enters fiber by the 5th endless apron and soaks casing
Two, fiber immersion casing two is interior to be provided with the 6th endless apron and the 7th endless apron, and the 6th endless apron is located at the 7th
The far infrared functional fibre prepared is sent into the 6th endless apron and the by the top of endless apron, the 5th endless apron
Between seven endless aprons, the weaving that the 6th endless apron and the 7th endless apron are immersed in fiber immersion casing two is used
In function additive solution, the weight of weaving antibacterial functions auxiliary agent and water ratio is 1 in weaving function compounding agent solution:102, weaving
It it is 50 degrees Celsius with the temperature of function compounding agent solution, weaving of the far infrared functional fibre in fiber immersion casing two is helped with function
Soaked in agent solution in motion, soak time is 3 minutes；
（7）, the far infrared functional fibre that soaked enters the 8th endless apron out of fiber immersion casing two, circulated the 8th
The fiber soaked is extruded with squeezing roller on conveyer belt, the pressure of squeezing roller is 5 kilograms, is extruded through squeezing roller
Later fiber mid and far infrared functional fibre and the weight ratio of solution is 5:0.1；
（8）, the polyester fiber for preparing step 7 be put into steam drying box and bakeed, stoving temperature is 80 degrees Celsius, is dried
It is 10 minutes to roast the time；
（9）, the fiber after baking carry out packing encapsulation, that is, be prepared into far infrared Composite Double functional fibre.
The application method of described far infrared Composite Double functional fibre, its step are：
（1）, the far infrared Composite Double functional fibre for preparing claim 1 and polyester fiber, eutectic polyester fiber be according to weight
Measure ratio 1：1：0.1, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 50 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into far infrared Composite Double functional fibre flocculus.
The application method of described far infrared Composite Double functional fibre, it is characterised in that compound difunctional using far infrared
The fabric that fiber is prepared.
Specific embodiment two：The preparation method of far infrared Composite Double functional fibre, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is sent on first circulation conveyer belt；
（2）, it is fluffy after polyester fiber by first circulation conveyer belt enter fiber soak casing one, fiber immersion casing one in
Provided with second circulation conveyer belt and the 3rd endless apron, second circulation conveyer belt is located at the top of the 3rd endless apron, the
One endless apron will be fluffy after polyester fiber be sent between second circulation conveyer belt and the 3rd endless apron, second circulation
Conveyer belt and the 3rd endless apron are immersed in weaving in fiber immersion casing one with function compounding agent solution, weaving function
The weight of weaving far-infrared functional auxiliary agent and water ratio is 3 in compounding agent solution:102, weaving is with the temperature of function compounding agent solution
86 degrees Celsius, soaked when weaving of the polyester fiber in fiber immersion casing one is with function compounding agent solution in motion, during immersion
Between be 5 minutes；
（3）, the polyester fiber that soaked enters the 4th endless apron out of fiber immersion casing one, in the 4th endless apron
On the fiber soaked is extruded with squeezing roller, the pressure of squeezing roller is 5 kilograms, after being extruded through squeezing roller
The weight of polyester fiber and solution ratio is 5 in polyester fiber:0.35；
（4）, the polyester fiber for preparing step 3 be put into steam drying box and bakeed, stoving temperature is 111 degrees Celsius,
It is 16 minutes to bakee the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into far infrared functional fibre.
（6）, by step（5）The far infrared functional fibre prepared enters fiber by the 5th endless apron and soaks casing
Two, fiber immersion casing two is interior to be provided with the 6th endless apron and the 7th endless apron, and the 6th endless apron is located at the 7th
The far infrared functional fibre prepared is sent into the 6th endless apron and the by the top of endless apron, the 5th endless apron
Between seven endless aprons, the weaving that the 6th endless apron and the 7th endless apron are immersed in fiber immersion casing two is used
In function additive solution, the weight of weaving deodorization functions auxiliary agent and water ratio is 2 in weaving function compounding agent solution:102, weaving
It it is 92 degrees Celsius with the temperature of function compounding agent solution, weaving of the far infrared functional fibre in fiber immersion casing two is helped with function
Soaked in agent solution in motion, soak time is 7 minutes；
（7）, the far infrared functional fibre that soaked enters the 8th endless apron out of fiber immersion casing two, circulated the 8th
The fiber soaked is extruded with squeezing roller on conveyer belt, the pressure of squeezing roller is 5 kilograms, is extruded through squeezing roller
Later fiber mid and far infrared functional fibre and the weight ratio of solution is 5:0.35；
（8）, the polyester fiber for preparing step 7 be put into steam drying box and bakeed, stoving temperature is 110 degrees Celsius,
It is 16 minutes to bakee the time；
（9）, the fiber after baking carry out packing encapsulation, that is, be prepared into far infrared Composite Double functional fibre.
The application method of described far infrared Composite Double functional fibre, its step are：
（1）, the far infrared Composite Double functional fibre for preparing claim 1 and polyester fiber, eutectic polyester fiber be according to weight
Measure ratio 1：1.6：0.35, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 28 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 188 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 58 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into far infrared Composite Double functional fibre flocculus.
The application method of described far infrared Composite Double functional fibre, it is characterised in that compound difunctional using far infrared
The fabric that fiber is prepared.
Specific embodiment three：The preparation method of far infrared Composite Double functional fibre, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is sent on first circulation conveyer belt；
（2）, it is fluffy after polyester fiber by first circulation conveyer belt enter fiber soak casing one, fiber immersion casing one in
Provided with second circulation conveyer belt and the 3rd endless apron, second circulation conveyer belt is located at the top of the 3rd endless apron, the
One endless apron will be fluffy after polyester fiber be sent between second circulation conveyer belt and the 3rd endless apron, second circulation
Conveyer belt and the 3rd endless apron are immersed in weaving in fiber immersion casing one with function compounding agent solution, weaving function
The weight of weaving far-infrared functional auxiliary agent and water ratio is 5 in compounding agent solution:102, weaving is with the temperature of function compounding agent solution
112 degrees Celsius, soaked when weaving of the polyester fiber in fiber immersion casing one is with function compounding agent solution in motion, during immersion
Between be 8 minutes；
（3）, the polyester fiber that soaked enters the 4th endless apron out of fiber immersion casing one, in the 4th endless apron
On the fiber soaked is extruded with squeezing roller, the pressure of squeezing roller is 5 kilograms, after being extruded through squeezing roller
The weight of polyester fiber and solution ratio is 5 in polyester fiber: 1；
（4）, the polyester fiber for preparing step 3 be put into steam drying box and bakeed, stoving temperature is 124 degrees Celsius,
It is 20 minutes to bakee the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into far infrared functional fibre.
（6）, by step（5）The far infrared functional fibre prepared enters fiber by the 5th endless apron and soaks casing
Two, fiber immersion casing two is interior to be provided with the 6th endless apron and the 7th endless apron, and the 6th endless apron is located at the 7th
The far infrared functional fibre prepared is sent into the 6th endless apron and the by the top of endless apron, the 5th endless apron
Between seven endless aprons, the weaving that the 6th endless apron and the 7th endless apron are immersed in fiber immersion casing two is used
In function additive solution, the weight of weaving moisture absorption sweat discharging functions auxiliary agent and water ratio is 5 in weaving function compounding agent solution:102,
The temperature of weaving function compounding agent solution is 112 degrees Celsius, and weaving of the far infrared functional fibre in fiber immersion casing two is used
Soaked in function additive solution in motion, soak time is 8 minutes；
（7）, the far infrared functional fibre that soaked enters the 8th endless apron out of fiber immersion casing two, circulated the 8th
The fiber soaked is extruded with squeezing roller on conveyer belt, the pressure of squeezing roller is 5 kilograms, is extruded through squeezing roller
Later fiber mid and far infrared functional fibre and the weight ratio of solution is 5: 1；
（8）, the polyester fiber for preparing step 7 be put into steam drying box and bakeed, stoving temperature is 124 degrees Celsius,
It is 20 minutes to bakee the time；
（9）, the fiber after baking carry out packing encapsulation, that is, be prepared into far infrared Composite Double functional fibre.
The application method of described far infrared Composite Double functional fibre, its step are：
（1）, the far infrared Composite Double functional fibre for preparing claim 1 and polyester fiber, eutectic polyester fiber be according to weight
Measure ratio 1： 2：0.5, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 40 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 197 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 60 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into far infrared Composite Double functional fibre flocculus.
The application method of described far infrared Composite Double functional fibre, it is characterised in that compound difunctional using far infrared
The fabric that fiber is prepared.
Object of the present invention is to provide the preparation of far infrared Composite Double functional fibre and its application method, the new mite is answered
Difunctional fiber is closed by during final finishing, weaving far infrared auxiliary agent, weaving function additive and basic terylene is fine
Dimension is combined with each other, and formation has far infrared and functional terylene composite fibre, and this method technique is simple, is easy to streamline
Large-scale operation, easy control of process conditions in production process, production cost are low；, can a process for preparing the functional fibre come
By repeatedly washing, also with good composite functional, to be worth of widely use.
Obviously, above-described embodiment is only intended to clearly illustrate example, and is not the restriction to embodiment.It is right
For those of ordinary skill in the art, can also make on the basis of the above description it is other it is various forms of change or
Change.There is no necessity and possibility to exhaust all the enbodiments.And the obvious change thus extended out or
Among changing still in the protection domain of the invention.
Claims (4)
1. the preparation method of far infrared Composite Double functional fibre, it is characterised in that its step is：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is sent on first circulation conveyer belt；
（2）, it is fluffy after polyester fiber by first circulation conveyer belt enter fiber soak casing one, fiber immersion casing one in
Provided with second circulation conveyer belt and the 3rd endless apron, second circulation conveyer belt is located at the top of the 3rd endless apron, the
One endless apron will be fluffy after polyester fiber be sent between second circulation conveyer belt and the 3rd endless apron, second circulation
Conveyer belt and the 3rd endless apron are immersed in weaving in fiber immersion casing one with function compounding agent solution, weaving function
Weaving is 1-5 with the weight of far-infrared functional auxiliary agent and water ratio in compounding agent solution:102, the temperature of weaving function compounding agent solution
For 50-112 degrees Celsius, soaked when weaving of the polyester fiber in fiber immersion casing one is with function compounding agent solution in motion,
Soak time is 3-8 minutes；
（3）, the polyester fiber that soaked enters the 4th endless apron out of fiber immersion casing one, in the 4th endless apron
On the fiber soaked is extruded with squeezing roller, the pressure of squeezing roller is 5 kilograms, after being extruded through squeezing roller
The weight of polyester fiber and solution ratio is 5 in polyester fiber:0.1-1；
（4）, the polyester fiber for preparing step 3 be put into steam drying box and bakeed, stoving temperature is that 80-124 is Celsius
Degree, the baking time is 10-20 minutes；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into far infrared functional fibre；
（6）, by step（5）The far infrared functional fibre prepared enters fiber by the 5th endless apron and soaks casing two,
The 6th endless apron and the 7th endless apron are provided with fiber immersion casing two, the 6th endless apron is positioned at the 7th circulation
The top of conveyer belt, the 5th endless apron follow the far infrared functional fibre prepared feeding the 6th endless apron and the 7th
Between endless conveying belt, the 6th endless apron and the 7th endless apron are immersed in the weaving function in fiber immersion casing two
In compounding agent solution, weaving is 1-5 with weaving in function compounding agent solution with the weight of function additive and water ratio:102, weaving function
The temperature of compounding agent solution is 50-112 degrees Celsius, weaving function additive of the far infrared functional fibre in fiber immersion casing two
Soaked in solution in motion, soak time is 3-8 minutes；
（7）, the far infrared functional fibre that soaked enters the 8th endless apron out of fiber immersion casing two, circulated the 8th
The fiber soaked is extruded with squeezing roller on conveyer belt, the pressure of squeezing roller is 5 kilograms, is extruded through squeezing roller
Later fiber mid and far infrared functional fibre and the weight ratio of solution is 5:0.1-1；
（8）, the polyester fiber for preparing step 7 be put into steam drying box and bakeed, stoving temperature is that 80-124 is Celsius
Degree, the baking time is 10-20 minutes；
（9）, the fiber after baking carry out packing encapsulation, that is, be prepared into far infrared Composite Double functional fibre.
2. the preparation method of far infrared Composite Double functional fibre according to claim 1, it is characterised in that the step
（6）Middle weaving is that weaving is helped with anti-bacteria and mite-proof functional auxiliary agent, weaving with antibacterial functions auxiliary agent, weaving with anion function with function additive
Agent, weaving function of driving mosquitoes auxiliary agent, weaving deodorization functions auxiliary agent, weaving formaldehyde-removing antibiotic deodorization functions auxiliary agent, weaving are used
Moisture absorption sweat discharging functions auxiliary agent, weaving cool feeling function additive, weaving are permanent with accumulation of heat temperature storage heat-preserving function auxiliary agent or weaving phase transformation
Temperature function auxiliary agent.
3. the application method of far infrared Composite Double functional fibre according to claim 1, it is characterised in that its step is：
（1）, the far infrared Composite Double functional fibre for preparing claim 1 and polyester fiber, eutectic polyester fiber be according to weight
Measure ratio 1：1-2：0.1-0.5 carries out uniformly mixing and unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15-40 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180-197 it is Celsius
Degree so that eutectic polyester fiber melts, and the baking time is the 50-60 seconds；
（5）, it is baked after, roll coiled, that is, be prepared into far infrared Composite Double functional fibre flocculus.
4. the application method of far infrared Composite Double functional fibre according to claim 1, it is characterised in that use far infrared
The fabric that Composite Double functional fibre is prepared.