CN107604640A - A kind of preparation of novel negative ion Composite Double functional fibre and its application method - Google Patents
A kind of preparation of novel negative ion Composite Double functional fibre and its application method Download PDFInfo
- Publication number
- CN107604640A CN107604640A CN201710781255.XA CN201710781255A CN107604640A CN 107604640 A CN107604640 A CN 107604640A CN 201710781255 A CN201710781255 A CN 201710781255A CN 107604640 A CN107604640 A CN 107604640A
- Authority
- CN
- China
- Prior art keywords
- negative ion
- weaving
- functional fibre
- polyester fiber
- composite double
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of preparation of novel negative ion Composite Double functional fibre and its application method, belong to functional fibre technical field.A kind of preparation of novel negative ion Composite Double functional fibre of the present invention and its application method, the novel negative ion Composite Double functional fibre passes through during final finishing, weaving is combined with each other with negative-ion auxiliary agent, weaving with function additive and basic polyester fiber, formation has anion and functional terylene composite fibre, this method technique is simple, it is easy to streamline large-scale operation, easy control of process conditions in production process, production cost is low；A process for preparing the functional fibre come, can pass through repeatedly washing, also with good composite functional, be worth of widely use.
Description
Technical field
The present invention relates to a kind of preparation of novel negative ion Composite Double functional fibre and its application method, belongs to function fibre
Tie up technical field.
Background technology
At present, as textile technology and life taste, the raising of quality, the garment material of simple function can not expire
The life requirement of sufficient people.Multifunction is the inexorable trend of costume fabric development.
The development of functional fibre is the symbol of modern fiber science progress.Functional fibre, fibre in differentiation and high-performance are fine
The technological innovation for developing into traditional textile industry of dimension, the conversion to high-tech industry creates advantage, is human lives
Horizontal raising contributes.Functional fibre refers in addition to physical and mechanical properties possessed by general fiber, also have
The tencel of certain specific function.Such as:Fiber has health care function (antibacterial, mite killing, physiotherapy and eliminate the unusual smell)
；Safeguard function (radiation proof, antistatic, uvioresistant etc.)；The wet comfortable function (heat absorption, heat release, moisture absorption, moisture releasing etc.) of heat；Doctor
Treat and environment-friendly function (biocompatibility and biological degradability).Common functional fibre, complex manufacturing technology, cost of manufacture
It is higher, and function is not firm enough possessed by fiber, and by washing twice, the function of fiber will have a greatly reduced quality, and be unfavorable for
The manufacture of functional fibre and promote the use of.
, should it is an object of the invention to provide a kind of preparation of novel negative ion Composite Double functional fibre and its application method
Novel negative ion Composite Double functional fibre is by during final finishing, by weaving with negative-ion auxiliary agent, weaving function additive
It is combined with each other with basic polyester fiber, formation has anion and functional terylene composite fibre, the letter of this method technique
It is single, it is easy to streamline large-scale operation, easy control of process conditions in production process, production cost is low；A process for preparing come
Functional fibre, can pass through repeatedly washing, also with good composite functional, be worth of widely use.
The content of the invention
The technical solution adopted for the present invention to solve the technical problems is：A kind of novel negative ion Composite Double functional fibre
Preparation method, it is characterised in that its step is：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 4-6 kilograms, and terylene mesh bag is placed on conveyer belt；
（2）, terylene mesh bag entered by conveyer belt in circulation solution case, circulate in solution case weaving anion function in solution
Auxiliary agent, weaving are 1-5 with the weight of function additive and water ratio:1-5:104, the temperature for circulating solution in solution case is taken the photograph for 50-114
Family name's degree, soak time of the polyester fiber in solution case are 3-8 minutes；
（3）, the polyester fiber that soaked in solution case rolled repeatedly 5 times with Pneumatic pressure bar, roll 1 minute every time, pressure
The pressure of bar is 5 kilograms, it is adjacent roll twice between be spaced 1-2 minutes so that the weight of polyester fiber and solution ratio is 5:
0.1-1；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is that 80-124 is Celsius
Degree, the baking time is 100-144 minutes；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into novel negative ion Composite Double functional fibre.
The preferable step（2）Middle weaving is weaving with function of driving mosquitoes auxiliary agent, weaving deodorization functions with function additive
Auxiliary agent, weaving with formaldehyde-removing antibiotic deodorization functions auxiliary agent, weaving with moisture absorption sweat discharging functions auxiliary agent, weaving with cool feeling function additive,
Weaving uses phase-change constant-temperature function additive with accumulation of heat temperature storage heat-preserving function auxiliary agent or weaving.
A kind of application method of described novel negative ion Composite Double functional fibre, its step are：
（1）, the novel negative ion Composite Double functional fibre for preparing claim 1 and polyester fiber, eutectic polyester fiber by
According to weight than 1：1-2：0.1-0.5 carries out uniformly mixing and unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15-40 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180-190 it is Celsius
Degree so that eutectic polyester fiber melts, and the baking time is the 50-60 seconds；
（5）, it is baked after, roll coiled, that is, be prepared into novel negative ion Composite Double functional fibre flocculus.
A kind of application method of described novel negative ion Composite Double functional fibre, it is characterised in that using novel negative from
The fabric that sub- Composite Double functional fibre is prepared.
, should it is an object of the invention to provide a kind of preparation of novel negative ion Composite Double functional fibre and its application method
Novel negative ion Composite Double functional fibre is by during final finishing, by weaving with negative-ion auxiliary agent, weaving function additive
It is combined with each other with basic polyester fiber, formation has anion and functional terylene composite fibre, the letter of this method technique
It is single, it is easy to streamline large-scale operation, easy control of process conditions in production process, production cost is low；A process for preparing come
Functional fibre, can pass through repeatedly washing, also with good composite functional, be worth of widely use.
Embodiment
Specific embodiment one：A kind of preparation method of novel negative ion Composite Double functional fibre, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 4 kilograms, and terylene mesh bag is placed on conveyer belt；
（2）, terylene mesh bag cross conveyer belt and enter in circulation solution case, circulate in solution case that weaving is helped with anion function in solution
The weight ratio of agent, weaving function of driving mosquitoes auxiliary agent and water is 1:1:104, the temperature for circulating solution in solution case is 50 degrees Celsius,
Soak time of the polyester fiber in solution case is 3 minutes；
（3）, the polyester fiber that soaked in solution case rolled repeatedly 5 times with Pneumatic pressure bar, roll 1 minute every time, pressure
The pressure of bar is 5 kilograms, it is adjacent roll twice between be spaced 1 minute so that the weight of polyester fiber and solution ratio is 5:
0.1；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is 80 degrees Celsius, is dried
It is 100 minutes to roast the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into novel negative ion Composite Double functional fibre.
A kind of application method of described novel negative ion Composite Double functional fibre, its step are：
（1）, the novel negative ion Composite Double functional fibre for preparing claim 1 and polyester fiber, eutectic polyester fiber by
According to weight than 1：1：0.1, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 50 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into novel negative ion Composite Double functional fibre flocculus.
A kind of application method of described novel negative ion Composite Double functional fibre, it is characterised in that using novel negative from
The fabric that sub- Composite Double functional fibre is prepared.
Specific embodiment two：A kind of preparation method of novel negative ion Composite Double functional fibre, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 4.85 kilograms, and terylene mesh bag is placed on conveyer belt；
（2）, terylene mesh bag entered by conveyer belt in circulation solution case, circulate in solution case weaving anion function in solution
The weight ratio of auxiliary agent, weaving moisture absorption sweat discharging functions auxiliary agent and water is 3:2:104, the temperature for circulating solution in solution case is taken the photograph for 88
Family name's degree, soak time of the polyester fiber in solution case are 6.3 minutes；
（3）, the polyester fiber that soaked in solution case rolled repeatedly 5 times with Pneumatic pressure bar, roll 1 minute every time, pressure
The pressure of bar is 5 kilograms, it is adjacent roll twice between be spaced 1.27 minutes so that the weight of polyester fiber and solution ratio is 5:
0.41；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is 95 degrees Celsius, is dried
It is 127 minutes to roast the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into novel negative ion Composite Double functional fibre.
A kind of application method of described novel negative ion Composite Double functional fibre, its step are：
（1）, the novel negative ion Composite Double functional fibre for preparing claim 1 and polyester fiber, eutectic polyester fiber by
According to weight than 1：1.3：0.45, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 32 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 184 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 57 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into novel negative ion Composite Double functional fibre flocculus.
A kind of application method of described novel negative ion Composite Double functional fibre, it is characterised in that using novel negative from
The fabric that sub- Composite Double functional fibre is prepared.
Specific embodiment three：A kind of preparation method of novel negative ion Composite Double functional fibre, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 6 kilograms, and terylene mesh bag is placed on conveyer belt；
（2）, terylene mesh bag entered by conveyer belt in circulation solution case, circulate in solution case weaving anion function in solution
The weight ratio of auxiliary agent, weaving phase-change constant-temperature function additive and water is 5: 5:104, the temperature for circulating solution in solution case is 114
Degree Celsius, soak time of the polyester fiber in solution case is 8 minutes；
（3）, the polyester fiber that soaked in solution case rolled repeatedly 5 times with Pneumatic pressure bar, roll 1 minute every time, pressure
The pressure of bar is 5 kilograms, it is adjacent roll twice between be spaced 2 minutes so that the weight of polyester fiber and solution ratio is 5: 1；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is 124 degrees Celsius,
It is 144 minutes to bakee the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into novel negative ion Composite Double functional fibre.
A kind of application method of described novel negative ion Composite Double functional fibre, its step are：
（1）, the novel negative ion Composite Double functional fibre for preparing claim 1 and polyester fiber, eutectic polyester fiber by
According to weight than 1： 2：0.5, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 40 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 190 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 60 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into novel negative ion Composite Double functional fibre flocculus.
A kind of application method of described novel negative ion Composite Double functional fibre, it is characterised in that using novel negative from
The fabric that sub- Composite Double functional fibre is prepared.
, should it is an object of the invention to provide a kind of preparation of novel negative ion Composite Double functional fibre and its application method
Novel negative ion Composite Double functional fibre is by during final finishing, by weaving with negative-ion auxiliary agent, weaving function additive
It is combined with each other with basic polyester fiber, formation has anion and functional terylene composite fibre, the letter of this method technique
It is single, it is easy to streamline large-scale operation, easy control of process conditions in production process, production cost is low；A process for preparing come
Functional fibre, can pass through repeatedly washing, also with good composite functional, be worth of widely use.
Obviously, above-described embodiment is only intended to clearly illustrate example, and is not the restriction to embodiment.It is right
For those of ordinary skill in the art, can also make on the basis of the above description it is other it is various forms of change or
Change.There is no necessity and possibility to exhaust all the enbodiments.And the obvious change thus extended out or
Among changing still in the protection domain of the invention.
Claims (4)
1. a kind of preparation method of novel negative ion Composite Double functional fibre, it is characterised in that its step is：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 4-6 kilograms, and terylene mesh bag is placed on conveyer belt；
（2）, terylene mesh bag entered by conveyer belt in circulation solution case, circulate in solution case weaving anion function in solution
Auxiliary agent, weaving are 1-5 with the weight of function additive and water ratio:1-5:104, the temperature for circulating solution in solution case is taken the photograph for 50-114
Family name's degree, soak time of the polyester fiber in solution case are 3-8 minutes；
（3）, the polyester fiber that soaked in solution case rolled repeatedly 5 times with Pneumatic pressure bar, roll 1 minute every time, pressure
The pressure of bar is 5 kilograms, it is adjacent roll twice between be spaced 1-2 minutes so that the weight of polyester fiber and solution ratio is 5:
0.1-1；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is that 80-124 is Celsius
Degree, the baking time is 100-144 minutes；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into novel negative ion Composite Double functional fibre.
A kind of 2. preparation method of novel negative ion Composite Double functional fibre according to claim 1, it is characterised in that institute
State step（2）Middle weaving is weaving function of driving mosquitoes auxiliary agent, weaving deodorization functions auxiliary agent, weaving with removing formaldehyde with function additive
Antibacterial and deodouring function auxiliary agent, weaving moisture absorption sweat discharging functions auxiliary agent, weaving cool feeling function additive, weaving are warming with accumulation of heat temperature storage
Phase-change constant-temperature function additive is used in function additive or weaving.
A kind of 3. application method of novel negative ion Composite Double functional fibre according to claim 1, it is characterised in that its
Step is：
（1）, the novel negative ion Composite Double functional fibre for preparing claim 1 and polyester fiber, eutectic polyester fiber by
According to weight than 1：1-2：0.1-0.5 carries out uniformly mixing and unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15-40 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180-190 it is Celsius
Degree so that eutectic polyester fiber melts, and the baking time is the 50-60 seconds；
（5）, it is baked after, roll coiled, that is, be prepared into novel negative ion Composite Double functional fibre flocculus.
4. the application method of a kind of novel negative ion Composite Double functional fibre according to claim 1, it is characterised in that make
The fabric prepared with novel negative ion Composite Double functional fibre.