CN107541876A - A kind of preparation of new skin care fiber type and its application method - Google Patents
A kind of preparation of new skin care fiber type and its application method Download PDFInfo
- Publication number
- CN107541876A CN107541876A CN201710766402.6A CN201710766402A CN107541876A CN 107541876 A CN107541876 A CN 107541876A CN 201710766402 A CN201710766402 A CN 201710766402A CN 107541876 A CN107541876 A CN 107541876A
- Authority
- CN
- China
- Prior art keywords
- polyester fiber
- weaving
- fiber
- skin care
- new skin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of preparation of new skin care fiber type and its application method, belong to functional fibre technical field.A kind of preparation of new skin care fiber type of the present invention and its application method, the new skin care fiber type passes through during final finishing, weaving is combined with each other with skin-protection type auxiliary agent and basic polyester fiber, formation has the functional polyester fiber of skin-protection type, this method technique is simple, it is easy to streamline large-scale operation, easy control of process conditions in production process, production cost is low；A process for preparing the functional fibre come, can pass through repeatedly washing, also with good skin-protection type feature, be worth of widely use.
Description
Technical field
The present invention relates to a kind of preparation of new skin care fiber type and its application method, belongs to functional fibre technology neck
Domain.
Background technology
At present, as textile technology and life taste, the raising of quality, the garment material of simple function can not expire
The life requirement of sufficient people.Multifunction is the inexorable trend of costume fabric development.
The development of functional fibre is the symbol of modern fiber science progress.Functional fibre, fibre in differentiation and high-performance are fine
The technological innovation for developing into traditional textile industry of dimension, the conversion to high-tech industry creates advantage, is human lives
Horizontal raising contributes.Functional fibre refers in addition to physical and mechanical properties possessed by general fiber, also have
The tencel of certain specific function.Such as:Fiber has health care function (antibacterial, mite killing, physiotherapy and eliminate the unusual smell)
；Safeguard function (radiation proof, antistatic, uvioresistant etc.)；The wet comfortable function (heat absorption, heat release, moisture absorption, moisture releasing etc.) of heat；Doctor
Treat and environment-friendly function (biocompatibility and biological degradability).Common functional fibre, complex manufacturing technology, cost of manufacture
It is higher, and function is not firm enough possessed by fiber, and by washing twice, the function of fiber will have a greatly reduced quality, and be unfavorable for
The manufacture of functional fibre and promote the use of.
It is an object of the invention to provide a kind of preparation of new skin care fiber type and its application method, the new skin-protection type
For fiber by the way that during final finishing, weaving is combined with each other with skin-protection type auxiliary agent and basic polyester fiber, being formed has shield
The functional polyester fiber of skin type, this method technique is simple, is easy to streamline large-scale operation, and process conditions are held in production process
Easy to control, production cost is low；A process for preparing the functional fibre come, can pass through repeatedly washing, also with good skin care
Type feature, is worth of widely use.
The content of the invention
The technical solution adopted for the present invention to solve the technical problems is：A kind of preparation method of new skin care fiber type,
Its step is：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 5-6 kilograms, and terylene mesh bag is placed on conveyer belt；
（2）, terylene mesh bag entered by conveyer belt in circulation solution case, circulate the weaving in solution case in solution and helped with skin-protection type
The weight of agent and water ratio is 2-5:95, the temperature for circulating solution in solution case is 50-105 degrees Celsius, and polyester fiber is molten in circulation
Soak time in body case is 3-8 minutes；
（3）, the polyester fiber that soaked in solution case rolled repeatedly 5 times with Pneumatic pressure bar, roll 1 minute every time, pressure
The pressure of bar is 5 kilograms, it is adjacent roll twice between be spaced 1-2 minutes so that the weight of polyester fiber and solution ratio is 5:
0.1-1；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is that 90-115 is Celsius
Degree, the baking time is 110-120 minutes；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into new skin care fiber type.
The preferable step（2）Middle weaving is that weaving is helped with barbaloin auxiliary agent, weaving with vitamin with skin-protection type auxiliary agent
Agent, weaving silk-fibroin auxiliary agent, weaving camellia oil assistant, weaving newborn fruit tree auxiliary agent, weaving deep sea fish oil auxiliary agent, weaving
With chitin adjuvant or weaving collagen auxiliary agent.
A kind of application method of new skin care fiber type, its step are：
（1）, claim 1 prepared new skin care fiber type and polyester fiber, eutectic polyester fiber according to weight than 1：
1-2：0.1-0.5 carries out uniformly mixing and unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15-40 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180-185 it is Celsius
Degree so that eutectic polyester fiber melts, and the baking time is the 50-60 seconds；
（5）, it is baked after, roll coiled, that is, be prepared into new skin-protection type fibrefill.
A kind of new functional fiber application method, it is characterised in that the fabric prepared using new skin care fiber type.
It is an object of the invention to provide a kind of preparation of new skin care fiber type and its application method, the new skin-protection type
For fiber by the way that during final finishing, weaving is combined with each other with skin-protection type auxiliary agent and basic polyester fiber, being formed has shield
The functional polyester fiber of skin type, this method technique is simple, is easy to streamline large-scale operation, and process conditions are held in production process
Easy to control, production cost is low；A process for preparing the functional fibre come, can pass through repeatedly washing, also with good skin care
Type feature, is worth of widely use.
Embodiment
Specific embodiment one：A kind of preparation method of new skin care fiber type, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 5 kilograms, and terylene mesh bag is placed on conveyer belt；
（2）, terylene mesh bag entered by conveyer belt in circulation solution case, circulate the weaving in solution case in solution and helped with barbaloin
The weight of agent and water ratio is 2:95, the temperature for circulating solution in solution case is 50 degrees Celsius, and polyester fiber is in circulation solution case
Soak time be 3 minutes；
（3）, the polyester fiber that soaked in solution case rolled repeatedly 5 times with Pneumatic pressure bar, roll 1 minute every time, pressure
The pressure of bar is 5 kilograms, it is adjacent roll twice between be spaced 1 minute so that the weight of polyester fiber and solution ratio is 5:
0.1；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is 90 degrees Celsius, is dried
It is 110 minutes to roast the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into new skin care fiber type.
A kind of application method of described new skin care fiber type, its step are：
（1）, claim 1 prepared new skin care fiber type and polyester fiber, eutectic polyester fiber according to weight than 1：
1：0.1, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 50 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into new skin-protection type fibrefill.
A kind of new functional fiber application method, it is characterised in that the fabric prepared using new skin care fiber type.
Specific embodiment two：A kind of preparation method of new skin care fiber type, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 5.3 kilograms, and terylene mesh bag is placed on conveyer belt；
（2）, terylene mesh bag entered by conveyer belt in circulation solution case, circulate the weaving in solution case in solution and helped with camellia oil
The weight of agent and water ratio is 4:95, the temperature for circulating solution in solution case is 85 degrees Celsius, and polyester fiber is in circulation solution case
Soak time be 7 minutes；
（3）, the polyester fiber that soaked in solution case rolled repeatedly 5 times with Pneumatic pressure bar, roll 1 minute every time, pressure
The pressure of bar is 5 kilograms, it is adjacent roll twice between be spaced 1.4 minutes so that the weight of polyester fiber and solution ratio is 5:
0.4；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is 99 degrees Celsius, is dried
It is 115 minutes to roast the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into new skin care fiber type.
A kind of application method of new skin care fiber type, it is characterised in that its step is：
（1）, claim 1 prepared new skin care fiber type and polyester fiber, eutectic polyester fiber according to weight than 1：
1.5：0.4, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 23 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 184 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 54 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into new skin-protection type fibrefill.
A kind of new functional fiber application method, it is characterised in that the fabric prepared using new skin care fiber type.
Specific embodiment three：A kind of preparation method of new skin care fiber type, it is characterised in that its step is：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 6 kilograms, and terylene mesh bag is placed on conveyer belt；
（2）, terylene mesh bag entered by conveyer belt in circulation solution case, circulate the weaving collagen in solution in solution case
The weight of auxiliary agent and water ratio is 1:19, the temperature for circulating solution in solution case is 105 degrees Celsius, and polyester fiber is in circulation solution case
Interior soak time is 8 minutes；
（3）, the polyester fiber that soaked in solution case rolled repeatedly 5 times with Pneumatic pressure bar, roll 1 minute every time, pressure
The pressure of bar is 5 kilograms, it is adjacent roll twice between be spaced 2 minutes so that the weight of polyester fiber and solution ratio is 5: 1；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is 115 degrees Celsius,
It is 120 minutes to bakee the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into new skin care fiber type.
A kind of application method of new skin care fiber type, its step are：
（1）, claim 1 prepared new skin care fiber type and polyester fiber, eutectic polyester fiber according to weight than 1：
2：0.5, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 40 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 185 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 60 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into new skin-protection type fibrefill.
Described a kind of new functional fiber application method, it is characterised in that prepared using new skin care fiber type
Fabric.
It is an object of the invention to provide a kind of preparation of new skin care fiber type and its application method, the new skin-protection type
For fiber by the way that during final finishing, weaving is combined with each other with skin-protection type auxiliary agent and basic polyester fiber, being formed has shield
The functional polyester fiber of skin type, this method technique is simple, is easy to streamline large-scale operation, and process conditions are held in production process
Easy to control, production cost is low；A process for preparing the functional fibre come, can pass through repeatedly washing, also with good skin care
Type feature, is worth of widely use.
Obviously, above-described embodiment is only intended to clearly illustrate example, and is not the restriction to embodiment.It is right
For those of ordinary skill in the art, can also make on the basis of the above description it is other it is various forms of change or
Change.There is no necessity and possibility to exhaust all the enbodiments.And the obvious change thus extended out or
Among changing still in the protection domain of the invention.
Claims (4)
1. a kind of preparation method of new skin care fiber type, it is characterised in that its step is：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 5-6 kilograms, and terylene mesh bag is placed on conveyer belt；
（2）, terylene mesh bag entered by conveyer belt in circulation solution case, circulate the weaving in solution case in solution and helped with skin-protection type
The weight of agent and water ratio is 2-5:95, the temperature for circulating solution in solution case is 50-105 degrees Celsius, and polyester fiber is molten in circulation
Soak time in body case is 3-8 minutes；
（3）, the polyester fiber that soaked in solution case rolled repeatedly 5 times with Pneumatic pressure bar, roll 1 minute every time, pressure
The pressure of bar is 5 kilograms, it is adjacent roll twice between be spaced 1-2 minutes so that the weight of polyester fiber and solution ratio is 5:
0.1-1；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is that 90-115 is Celsius
Degree, the baking time is 110-120 minutes；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into new skin care fiber type.
A kind of 2. preparation method of new skin care fiber type according to claim 1, it is characterised in that the step（2）
Middle weaving is weaving barbaloin auxiliary agent, weaving vitamin auxiliary agent, weaving silk-fibroin auxiliary agent, weaving use with skin-protection type auxiliary agent
Camellia oil assistant, weaving use collagen egg with newborn fruit tree auxiliary agent, weaving deep sea fish oil auxiliary agent, weaving chitin adjuvant or weaving
White auxiliary agent.
3. the application method of a kind of new skin care fiber type according to claim 1, it is characterised in that its step is：
（1）, claim 1 prepared new skin care fiber type and polyester fiber, eutectic polyester fiber according to weight than 1：
1-2：0.1-0.5 carries out uniformly mixing and unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15-40 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180-185 it is Celsius
Degree so that eutectic polyester fiber melts, and the baking time is the 50-60 seconds；
（5）, it is baked after, roll coiled, that is, be prepared into new skin-protection type fibrefill.
4. a kind of new functional fiber application method according to claim 1, it is characterised in that fine using new skin-protection type
Tie up the fabric prepared.