CN107447395A - A kind of preparation of antibacterial Composite Double functional fibre and its application method - Google Patents
A kind of preparation of antibacterial Composite Double functional fibre and its application method Download PDFInfo
- Publication number
- CN107447395A CN107447395A CN201710765680.XA CN201710765680A CN107447395A CN 107447395 A CN107447395 A CN 107447395A CN 201710765680 A CN201710765680 A CN 201710765680A CN 107447395 A CN107447395 A CN 107447395A
- Authority
- CN
- China
- Prior art keywords
- weaving
- fiber
- polyester fiber
- functional fibre
- composite double
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of preparation of antibacterial Composite Double functional fibre and its application method, belong to functional fibre technical field.A kind of preparation of antibacterial Composite Double functional fibre of the present invention and its application method, the antibacterial Composite Double functional fibre passes through during final finishing, weaving is combined with each other with Antibacterial accessory ingredient, weaving with function additive and basic polyester fiber, formation has antibiotic property and functional terylene composite fibre, this method technique is simple, it is easy to streamline large-scale operation, easy control of process conditions in production process, production cost is low；A process for preparing the functional fibre come, can pass through repeatedly washing, also with good composite functional, be worth of widely use.
Description
Technical field
The present invention relates to a kind of preparation of antibacterial Composite Double functional fibre and its application method, belong to functional fibre technology
Field.
Background technology
At present, as textile technology and life taste, the raising of quality, the garment material of simple function can not expire
The life requirement of sufficient people.Multifunction is the inexorable trend of costume fabric development.
The development of functional fibre is the symbol of modern fiber science progress.Functional fibre, fibre in differentiation and high-performance are fine
The technological innovation for developing into traditional textile industry of dimension, the conversion to high-tech industry creates advantage, is human lives
Horizontal raising contributes.Functional fibre refers in addition to physical and mechanical properties possessed by general fiber, also have
The tencel of certain specific function.Such as:Fiber has health care function (antibacterial, mite killing, physiotherapy and eliminate the unusual smell)
；Safeguard function (radiation proof, antistatic, uvioresistant etc.)；The wet comfortable function (heat absorption, heat release, moisture absorption, moisture releasing etc.) of heat；Doctor
Treat and environment-friendly function (biocompatibility and biological degradability).Common functional fibre, complex manufacturing technology, cost of manufacture
It is higher, and function is not firm enough possessed by fiber, and by washing twice, the function of fiber will have a greatly reduced quality, and be unfavorable for
The manufacture of functional fibre and promote the use of.
It is an object of the invention to provide a kind of preparation of antibacterial Composite Double functional fibre and its application method, the antibacterial is answered
Difunctional fiber is closed by during final finishing, by weaving Antibacterial accessory ingredient, weaving function additive and basic polyester fiber
It is combined with each other, formation has antibiotic property and functional terylene composite fibre, and this method technique is simple, is easy to the big rule of streamline
Modulo operation, easy control of process conditions in production process, production cost are low；A process for preparing the functional fibre come, Ke Yijing
Repeatedly washing is crossed, also with good composite functional, is worth of widely use.
The content of the invention
The technical solution adopted for the present invention to solve the technical problems is：A kind of preparation side of antibacterial Composite Double functional fibre
Method, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is sent on first circulation conveyer belt；
（2）, it is fluffy after polyester fiber fiber entered by first circulation conveyer belt soak casing, be provided with fiber soaking box body
Second circulation conveyer belt and the 3rd endless apron, second circulation conveyer belt are located at the top of the 3rd endless apron, and first follows
Endless conveying belt will be fluffy after polyester fiber be sent between second circulation conveyer belt and the 3rd endless apron, second circulation conveying
Band and the 3rd endless apron are immersed in weaving in fiber soaking box body with function compounding agent solution, and weaving function additive is molten
Weaving is 1-5 with antibacterial functions auxiliary agent, weaving with the weight of function additive and water ratio in liquid:1-5:102, weaving function additive
The temperature of solution is 50-112 degrees Celsius, and weaving of the polyester fiber in fiber soaking box body is moved with side in function compounding agent solution
Side is soaked, and soak time is 3-8 minutes；
（3）, the polyester fiber that soaked out of fiber soaking box body enter the 4th endless apron, on the 4th circulation conveying band
The fiber soaked is extruded with squeezing roller, the pressure of squeezing roller is 5 kilograms, washing after being extruded through squeezing roller
The weight of polyester fiber and solution ratio is 5 in synthetic fibre fiber:0.1-1；
（4）, the polyester fiber for preparing step 3 be put into steam drying box and bakeed, stoving temperature is that 80-123 is Celsius
Degree, the baking time is 10-20 minutes；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into antibacterial Composite Double functional fibre.
A kind of preparation method of preferable described antibacterial Composite Double functional fibre, it is characterised in that the step（2）In
Weaving with function additive be weaving far-infrared functional auxiliary agent, weaving anion function auxiliary agent, weaving function of driving mosquitoes auxiliary agent,
Weaving deodorization functions auxiliary agent, weaving formaldehyde-removing antibiotic deodorization functions auxiliary agent, weaving moisture absorption sweat discharging functions auxiliary agent, weaving are used
Cool feeling function additive, weaving use phase-change constant-temperature function additive with accumulation of heat temperature storage heat-preserving function auxiliary agent or weaving.
A kind of application method of described antibacterial Composite Double functional fibre, its step are：
（1）, the antibacterial Composite Double functional fibre for preparing claim 1 and polyester fiber, eutectic polyester fiber be according to weight
Than 1：1-2：0.1-0.5 carries out uniformly mixing and unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15-44 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180-194 it is Celsius
Degree so that eutectic polyester fiber melts, and the baking time is the 50-60 seconds；
（5）, it is baked after, roll coiled, that is, be prepared into antibacterial Composite Double functional fibre flocculus.
A kind of application method of antibacterial Composite Double functional fibre, it is characterised in that use antibacterial Composite Double functional fibre system
For the fabric gone out.
It is an object of the invention to provide a kind of preparation of antibacterial Composite Double functional fibre and its application method, the antibacterial is answered
Difunctional fiber is closed by during final finishing, by weaving Antibacterial accessory ingredient, weaving function additive and basic polyester fiber
It is combined with each other, formation has antibiotic property and functional terylene composite fibre, and this method technique is simple, is easy to the big rule of streamline
Modulo operation, easy control of process conditions in production process, production cost are low；A process for preparing the functional fibre come, Ke Yijing
Repeatedly washing is crossed, also with good composite functional, is worth of widely use.
Embodiment
Specific embodiment one：A kind of preparation method of antibacterial Composite Double functional fibre, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is sent on first circulation conveyer belt；
（2）, it is fluffy after polyester fiber fiber entered by first circulation conveyer belt soak casing, be provided with fiber soaking box body
Second circulation conveyer belt and the 3rd endless apron, second circulation conveyer belt are located at the top of the 3rd endless apron, and first follows
Endless conveying belt will be fluffy after polyester fiber be sent between second circulation conveyer belt and the 3rd endless apron, second circulation conveying
Band and the 3rd endless apron are immersed in weaving in fiber soaking box body with function compounding agent solution, and weaving function additive is molten
The weight ratio of weaving antibacterial functions auxiliary agent, weaving far-infrared functional auxiliary agent and water is 1 in liquid:1:102, weaving is helped with function
The temperature of agent solution be 50 degrees Celsius, weaving of the polyester fiber in fiber soaking box body with function compounding agent solution while motion while
Immersion, soak time are 3 minutes；
（3）, the polyester fiber that soaked out of fiber soaking box body enter the 4th endless apron, on the 4th circulation conveying band
The fiber soaked is extruded with squeezing roller, the pressure of squeezing roller is 5 kilograms, washing after being extruded through squeezing roller
The weight of polyester fiber and solution ratio is 5 in synthetic fibre fiber:0.1；
（4）, the polyester fiber for preparing step 3 be put into steam drying box and bakeed, stoving temperature is 80 degrees Celsius, is dried
It is 10 minutes to roast the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into antibacterial Composite Double functional fibre.
The application method of described a kind of antibacterial Composite Double functional fibre, it is characterised in that its step is：
（1）, the antibacterial Composite Double functional fibre for preparing claim 1 and polyester fiber, eutectic polyester fiber be according to weight
Than 1：1：0.1, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 50 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into antibacterial Composite Double functional fibre flocculus.
The application method of described a kind of antibacterial Composite Double functional fibre, it is characterised in that compound difunctional using antibacterial
The fabric that fiber is prepared.
Specific embodiment two：A kind of preparation method of antibacterial Composite Double functional fibre, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is sent on first circulation conveyer belt；
（2）, it is fluffy after polyester fiber fiber entered by first circulation conveyer belt soak casing, be provided with fiber soaking box body
Second circulation conveyer belt and the 3rd endless apron, second circulation conveyer belt are located at the top of the 3rd endless apron, and first follows
Endless conveying belt will be fluffy after polyester fiber be sent between second circulation conveyer belt and the 3rd endless apron, second circulation conveying
Band and the 3rd endless apron are immersed in weaving in fiber soaking box body with function compounding agent solution, and weaving function additive is molten
The weight ratio of weaving antibacterial functions auxiliary agent, weaving deodorization functions auxiliary agent and water is 3 in liquid:2:102, weaving function additive
The temperature of solution be 94 degrees Celsius, weaving of the polyester fiber in fiber soaking box body with function compounding agent solution while motion while soak
Bubble, soak time are 4 minutes；
（3）, the polyester fiber that soaked out of fiber soaking box body enter the 4th endless apron, on the 4th circulation conveying band
The fiber soaked is extruded with squeezing roller, the pressure of squeezing roller is 5 kilograms, washing after being extruded through squeezing roller
The weight of polyester fiber and solution ratio is 5 in synthetic fibre fiber:0.44；
（4）, the polyester fiber for preparing step 3 be put into steam drying box and bakeed, stoving temperature is 102 degrees Celsius,
It is 13 minutes to bakee the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into antibacterial Composite Double functional fibre.
A kind of application method of described antibacterial Composite Double functional fibre, its step are：
（1）, the antibacterial Composite Double functional fibre for preparing claim 1 and polyester fiber, eutectic polyester fiber be according to weight
Than 1：1.4：0.4, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 34 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 182 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 54 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into antibacterial Composite Double functional fibre flocculus.
The application method of described a kind of antibacterial Composite Double functional fibre, it is characterised in that compound difunctional using antibacterial
The fabric that fiber is prepared.
Specific embodiment three：A kind of preparation method of antibacterial Composite Double functional fibre, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is sent on first circulation conveyer belt；
（2）, it is fluffy after polyester fiber fiber entered by first circulation conveyer belt soak casing, be provided with fiber soaking box body
Second circulation conveyer belt and the 3rd endless apron, second circulation conveyer belt are located at the top of the 3rd endless apron, and first follows
Endless conveying belt will be fluffy after polyester fiber be sent between second circulation conveyer belt and the 3rd endless apron, second circulation conveying
Band and the 3rd endless apron are immersed in weaving in fiber soaking box body with function compounding agent solution, and weaving function additive is molten
The weight ratio of weaving antibacterial functions auxiliary agent, weaving phase-change constant-temperature function additive and water is 5 in liquid: 5:102, weaving is diligent
The temperature of energy compounding agent solution is 112 degrees Celsius, weaving of the polyester fiber in fiber soaking box body side in function compounding agent solution
Side immersion is moved, soak time is 8 minutes；
（3）, the polyester fiber that soaked out of fiber soaking box body enter the 4th endless apron, on the 4th circulation conveying band
The fiber soaked is extruded with squeezing roller, the pressure of squeezing roller is 5 kilograms, washing after being extruded through squeezing roller
The weight of polyester fiber and solution ratio is 5 in synthetic fibre fiber: 1；
（4）, the polyester fiber for preparing step 3 be put into steam drying box and bakeed, stoving temperature is 123 degrees Celsius,
It is 20 minutes to bakee the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into antibacterial Composite Double functional fibre.
The application method of described a kind of antibacterial Composite Double functional fibre, it is characterised in that its step is：
（1）, the antibacterial Composite Double functional fibre for preparing claim 1 and polyester fiber, eutectic polyester fiber be according to weight
Than 1： 2：0.5, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 44 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 194 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 60 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into antibacterial Composite Double functional fibre flocculus.
The application method of a kind of antibacterial Composite Double functional fibre according to claim 1, it is characterised in that using anti-
The fabric that bacterium Composite Double functional fibre is prepared.
It is an object of the invention to provide a kind of preparation of antibacterial Composite Double functional fibre and its application method, the antibacterial is answered
Difunctional fiber is closed by during final finishing, by weaving Antibacterial accessory ingredient, weaving function additive and basic polyester fiber
It is combined with each other, formation has antibiotic property and functional terylene composite fibre, and this method technique is simple, is easy to the big rule of streamline
Modulo operation, easy control of process conditions in production process, production cost are low；A process for preparing the functional fibre come, Ke Yijing
Repeatedly washing is crossed, also with good composite functional, is worth of widely use.
Obviously, above-described embodiment is only intended to clearly illustrate example, and is not the restriction to embodiment.It is right
For those of ordinary skill in the art, can also make on the basis of the above description it is other it is various forms of change or
Change.There is no necessity and possibility to exhaust all the enbodiments.And the obvious change thus extended out or
Among changing still in the protection domain of the invention.
Claims (4)
1. a kind of preparation method of antibacterial Composite Double functional fibre, it is characterised in that its step is：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is sent on first circulation conveyer belt；
（2）, it is fluffy after polyester fiber fiber entered by first circulation conveyer belt soak casing, be provided with fiber soaking box body
Second circulation conveyer belt and the 3rd endless apron, second circulation conveyer belt are located at the top of the 3rd endless apron, and first follows
Endless conveying belt will be fluffy after polyester fiber be sent between second circulation conveyer belt and the 3rd endless apron, second circulation conveying
Band and the 3rd endless apron are immersed in weaving in fiber soaking box body with function compounding agent solution, and weaving function additive is molten
Weaving is 1-5 with antibacterial functions auxiliary agent, weaving with the weight of function additive and water ratio in liquid:1-5:102, weaving function additive
The temperature of solution is 50-112 degrees Celsius, and weaving of the polyester fiber in fiber soaking box body is moved with side in function compounding agent solution
Side is soaked, and soak time is 3-8 minutes；
（3）, the polyester fiber that soaked out of fiber soaking box body enter the 4th endless apron, on the 4th circulation conveying band
The fiber soaked is extruded with squeezing roller, the pressure of squeezing roller is 5 kilograms, washing after being extruded through squeezing roller
The weight of polyester fiber and solution ratio is 5 in synthetic fibre fiber:0.1-1；
（4）, the polyester fiber for preparing step 3 be put into steam drying box and bakeed, stoving temperature is that 80-123 is Celsius
Degree, the baking time is 10-20 minutes；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into antibacterial Composite Double functional fibre.
A kind of 2. preparation method of antibacterial Composite Double functional fibre according to claim 1, it is characterised in that the step
（2）Middle weaving is weaving with far-infrared functional auxiliary agent, weaving with anion function auxiliary agent, weaving function of driving mosquitoes with function additive
Auxiliary agent, weaving with deodorization functions auxiliary agent, weaving with formaldehyde-removing antibiotic deodorization functions auxiliary agent, weaving with moisture absorption sweat discharging functions auxiliary agent,
Weaving cool feeling function additive, weaving use phase-change constant-temperature function additive with accumulation of heat temperature storage heat-preserving function auxiliary agent or weaving.
3. the application method of a kind of antibacterial Composite Double functional fibre according to claim 1, it is characterised in that its step is：
（1）, the antibacterial Composite Double functional fibre for preparing claim 1 and polyester fiber, eutectic polyester fiber be according to weight
Than 1：1-2：0.1-0.5 carries out uniformly mixing and unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15-44 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180-194 it is Celsius
Degree so that eutectic polyester fiber melts, and the baking time is the 50-60 seconds；
（5）, it is baked after, roll coiled, that is, be prepared into antibacterial Composite Double functional fibre flocculus.
4. the application method of a kind of antibacterial Composite Double functional fibre according to claim 1, it is characterised in that use antibacterial
The fabric that Composite Double functional fibre is prepared.