CN107603222A - 一种中高密度含氢硅油及其制备方法 - Google Patents
一种中高密度含氢硅油及其制备方法 Download PDFInfo
- Publication number
- CN107603222A CN107603222A CN201710653018.5A CN201710653018A CN107603222A CN 107603222 A CN107603222 A CN 107603222A CN 201710653018 A CN201710653018 A CN 201710653018A CN 107603222 A CN107603222 A CN 107603222A
- Authority
- CN
- China
- Prior art keywords
- silicone oil
- containing hydrogen
- hydrogen silicone
- high density
- density containing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种中高密度含氢硅油,包括如下重量百分比的原料:D4 50‑70%,环氧树脂20‑35%,助剂8‑12%。该产品活性高,质量稳定,抗氧化性强,无损耗,无异味,催化效果好,成本低。
Description
技术领域
本发明属于化工领域,尤其涉及一种中高密度含氢硅油及其制备方法。
背景技术
现有的硅油生产所需原材料多,工艺流程复杂多变,损耗大,产品的活性低,催化效果不好,不稳定,易氧化变质,所生产的海绵孔径粗,不均匀,手感差,压缩变形,伸长率低,成本高,气味重,VOC检测不符合规定。
发明内容
鉴于上述现有技术存在的缺陷,本发明的目的是提出一种中高密度含氢硅油,活性高,质量稳定,抗氧化性强,无损耗,无异味,催化效果好,成本低。
本发明的目的将通过以下技术方案得以实现:
一种中高密度含氢硅油,包括如下重量百分比的原料:D4 50-70%,环氧树脂20-35%,助剂8-12%。
上述的一种中高密度含氢硅油,其中,所述助剂包括4500分子量聚醚、2000分子量聚醚、高含氢硅油。
上述的一种中高密度含氢硅油,其中,所述4500分子量聚醚:所述2000分子量聚醚:所述高含氢硅油的重量百分比为30-40%:40-45%:20-25%。
本发明的另一个目的是提出一种中高密度含氢硅油的制备方法,Si、O、C非水解流程短,简单易操作,可控性强,采取纯天然催化剂环氧树脂在生产过程中规避了污染、氧化、化学成分流失、废渣、废液、废气、催化效果减弱等风险、安全、环保。
一种中高密度含氢硅油的制备方法,包括如下步骤:将D4、环氧树脂、助剂混合,搅拌,加热,通氮气,反应11-13h,至反应后的混合液体澄清,即得。
上述的中高密度含氢硅油的制备方法,其中,所述搅拌的时间为50-60分钟,所述搅拌的转速为40-50转/分钟。
上述的中高密度含氢硅油的制备方法,其中,所述加热的温度为90-100℃。
上述的中高密度含氢硅油的制备方法,其中,所述混合液体的含氢量为0.01-0.03%,含氢黏度为70-75CST。
与现有技术相比,本发明提供的一种中高密度含氢硅油及其制备方法,达到的技术效果是:本发明的制备方法中,Si、O、C非水解流程短,简单易操作,原材料少,价格低,易采购,环保,无污染,可控性强,采取纯天然催化剂环氧树脂在生产过程中规避了污染、氧化、化学成分流失、废渣、废液、废气、催化效果减弱等风险、安全、环保;本发明的中高密度硅油活性高,质量稳定,抗氧化性强,无损耗,无异味,催化效果好,成本低;保质期长,所生产的产品手感佳,不变形,泡孔细腻,均匀。
以下便结合实施例,对本发明的具体实施方式作进一步的详述,以使技术方案更易于理解、掌握。
具体实施方式
下面通过具体实施例对本发明进行说明,但本发明并不局限于此。下述实施例中所述实验方法,如无特殊说明,均为常规方法;所述试剂和材料,如无特殊说明,均可从商业途径获得,下面实施例并非用以限制本发明的专利范围,凡未脱离本发明所为的等效实施或变更,均应包含于本专利保护范围中。
实施例1
一种中高密度含氢硅油:D4 55kg,环氧树脂25kg,4500分子量聚醚3.5kg、2000分子量聚醚4kg、高含氢硅油2.5kg。
制备方法:将D4 55kg、环氧树脂25kg、500分子量聚醚3.5kg、2000分子量聚醚4kg、高含氢硅油2.5kg混合,搅拌速度为45转/分钟,搅拌时间55分钟,加热至90℃,通氮气,反应12h,至混合液体变澄清后,直至检测混合液的含氢量符合0.95-1.2%,含氢黏度为70-75CST,即得。本实施例的含氢量为0.02%,含氢黏度为73CST。
实施例2
一种中高密度含氢硅油:D4 60kg,环氧树脂30kg,4500分子量聚醚3.5kg、2000分子量聚醚4.5kg、高含氢硅油2kg。
制备方法:将D4 60kg,环氧树脂30kg,4500分子量聚醚3.5kg、2000分子量聚醚4.5kg、高含氢硅油2kg混合,搅拌速度为40转/分钟,搅拌时间52分钟,加热至95℃,通氮气,反应11h,至混合液体变澄清后,直至检测混合液的含氢量符合0.95-1.2%,含氢黏度为70-75CST,即得。本实施例的含氢量为0.03%,含氢黏度为72CST。
实施例3
一种中高密度含氢硅油:D4 65kg,环氧树脂35kg,4500分子量聚醚3kg、2000分子量聚醚4.8kg、高含氢硅油2.2kg。
制备方法:将D4 65kg,环氧树脂35kg,4500分子量聚醚3kg、2000分子量聚醚4.8kg、高含氢硅油2.2kg混合,搅拌速度为45转/分钟,搅拌时间55分钟,加热至100℃,通氮气,反应13h,至混合液体变澄清后,直至检测混合液的含氢量符合0.95--1.2%,含氢黏度为70-75CST,即得。本实施例的含氢量为0.02%,含氢黏度为73CST。
将实施例1-3制备的中高密度含氢硅油进行检测,检测结果见表1。
表1实施例1-3制备的中高密度含氢硅油的检测结果
测试项目 | 标准 | 实施例1 | 实施例2 | 实施例3 |
外观 | 澄清液体 | 符合 | 符合 | 符合 |
颜色(GVS) | 0-2 | 0.5 | 0.6 | 0.5 |
发泡测试 | >38cm | 符合 | 符合 | 符合 |
泡孔结构 | 5-8 | 5 | 5.2 | 5.2 |
哈希数(NTU) | 0-4.5 | 1 | 1 | 0.9 |
黏度(CST) | 70-75 | 73 | 72 | 73 |
比重,25℃ | 1.025-1.035 | 1.03 | 1.028 | 1.032 |
pH值 | 5-8 | 7.1 | 7.1 | 7.1 |
含水量 | <0.1% | 0.05% | 0.04% | 0.06% |
由表1可知,本发明的中高度密度含氢硅油活性高,质量稳定,抗氧化性强,无损耗,无异味,催化效果好,成本低;保质期长,所生产的产品手感佳,不变形,泡孔细腻,均匀。
上述说明示出并描述了本发明的若干优选实施例,但如前所述,应当理解本发明并非局限于本文所披露的形式,不应看作是对其他实施例的排除,而可用于各种其他组合、修改和环境,并能够在本文所述发明构想范围内,通过上述教导或相关领域的技术或知识进行改动。而本领域人员所进行的改动和变化不脱离本发明的精神和范围,则都应在本发明所附权利要求的保护范围内。
Claims (7)
1.一种中高密度含氢硅油,其特征在于,包括如下重量百分比的原料:D4 50-70%,环氧树脂20-35%,助剂8-12%。
2.根据权利要求1所述的一种中高密度含氢硅油,其特征在于,所述助剂包括4500分子量聚醚、2000分子量聚醚、高含氢硅油。
3.根据权利要求2所述的一种中高密度含氢硅油,其特征在于,所述4500分子量聚醚:所述2000分子量聚醚:所述高含氢硅油的重量百分比为30-40%:40-45%:20-25%。
4.一种根据权利要求1-3所述的中高密度含氢硅油的制备方法,其特征在于,包括如下步骤:将D4、环氧树脂、助剂混合,搅拌,加热,通氮气,反应11-13h,至反应后的混合液体澄清,即得。
5.根据权利要求4所述的中高密度含氢硅油的制备方法,其特征在于,所述搅拌的时间为50-60分钟,所述搅拌的转速为40-50转/分钟。
6.根据权利要求4所述的中高密度含氢硅油的制备方法,其特征在于,所述加热的温度为90-100℃。
7.根据权利要求4所述的中高密度含氢硅油的制备方法,其特征在于,所述混合液体的含氢量为0.01-0.03%,含氢黏度为70-75CTS。