CN107512037A - 一种安全高韧性家用多层防滑垫 - Google Patents
一种安全高韧性家用多层防滑垫 Download PDFInfo
- Publication number
- CN107512037A CN107512037A CN201710764216.9A CN201710764216A CN107512037A CN 107512037 A CN107512037 A CN 107512037A CN 201710764216 A CN201710764216 A CN 201710764216A CN 107512037 A CN107512037 A CN 107512037A
- Authority
- CN
- China
- Prior art keywords
- parts
- slipmat
- multilayer
- warp
- family expenses
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种安全高韧性家用多层防滑垫,其特征在于:该防滑垫包括三层结构,顶层为PVC发泡材料构成的防滑层,中层为特斯林网布,底层为植物胶垫。三层结构,其层为PVC发泡材料构成的防滑层,中层为特斯林网布,底层为植物胶垫,这种设计结构,使得本发明不仅可当做家居的防滑垫使用,还可作为睡觉用的席子、沙发垫或者出游用垫等,其用途广泛,给人们带来了方便;本发明的顶层为特斯林网布,特斯林具有耐水耐油、耐磨损、色彩鲜艳、抗紫外线、无毒等优点,已经被人们所接受,并且其造价并不昂贵,经济实用,在人们选择防滑垫时,多出了一种选择。
Description
技术领域:
本发明涉及一种防滑垫,具体涉及一种安全高韧性家用多层防滑垫。
背景技术:
随着人们生活水平的日益提高,人们对家庭中或其他场合使用的楼梯或地板的外观、品质等要求也越来越高,很多楼梯或地面采用表面油漆、光滑打磨或贴上瓷砖、大理石质、玻璃材质等材料来进行装置,表面光彩靓丽、平滑照人,改善了人们的视觉体验,但是问题也同时产生,由于楼梯或地板表面光滑,给使用者带来了潜在的危险,比如滑倒,而且楼梯在使用中具有一定的高度,不安全因素更是不容忽视,除安全原因外,完美的装饰经踩踏后极易损坏,使用寿命大大缩短。为了解决上述问题,目前采用的方法即铺设防滑垫来增加楼梯或地板表面的摩擦力,以降低潜在危险发生的几率,并且对楼梯或者地板表面起到一定的保护作用,然而,现有防滑垫一般均为单纯的PVC发泡材料做成,其主要功能是防滑,但现代人们生活水平的提高使人们对各类产品的功能要求多元化,现有防滑垫单一的防滑功能便不能满足消费者的需求。
发明内容:
本发明所要解决的技术问题在于份服现有技术的缺陷,提供一种安全高韧性家用多层防滑垫。
本发明所要解决的技术问题采用以下技术方案来实现。
一种安全高韧性家用多层防滑垫,其特征在于:该防滑垫包括三层结构,顶层为PVC发泡材料构成的防滑层,中层为特斯林网布,底层为植物胶垫。
进一步技术:所述斯特林网布包括纵横交错编织的经线与纬线,该纬线与经线均选用特斯林线,该经线与纬线间均无间隙。
进一步技术:所述经线与纬线纵横交错编织重叠位置利用熔接的方式将两者相互固定。
进一步技术:所述底层下表面上设置有若干防滑点,上表面设有若干方形凸块,方形凸块与斯特林网的经线与纬线组成的方格配合。
进一步技术:所述底层与中层通过增韧剂与胶黏剂按1:1混合剂进行粘合。
进一步技术:所述的增韧剂包括纳米碳纤维5-15份,引发剂5-12份,粘度1000~20000mPa·s的二甲基乙烯基甲硅氧基封端的聚二甲基硅氧烷100-110份,六甲基二硅氮烷2-3份,甘油3-5份,气相法白炭黑5-10份,粘度为1000~20000mPa·s的二甲基乙烯基甲硅氧基封端的聚二甲基硅氧烷兑稀60-70份,抗氧剂0.1-0.5份,润滑剂0.1-1份,复合纳米弹性体18-50份,FL-1复合润滑分散剂1-5份,FL-2活性表面处理剂5-10份,消泡剂1-5份,海因环氧树脂30-75份,水30-50份。
进一步技术:所述的胶黏剂包括括聚乳酸50-60份,低分子量聚己二酸二甘醇酯10-12份,高分子量聚己二酸二甘醇酯5-20份,羧甲基纤维素10-15份,烷基丙磺酸钠2-5份,十二烷基丙环酸钠6-10份,水1000-1300份,环氧树脂60-70份。
进一步技术:所述的按重量配比称取干燥的纳米碳纤维、引发剂和海因环氧树脂,分别加入料筒温度为60℃~90℃的高速混合机中,搅拌2~6小时,再加入按重量配比称取的粘度1000~20000mPa·s的二甲基乙烯基甲硅氧基封端的聚二甲基硅氧烷,六甲基二硅氮烷,甘油,气相法白炭黑,粘度为1000~20000mPa·s的二甲基乙烯基甲硅氧基封端的聚二甲基硅氧烷兑稀,使一起搅拌10~40分钟和达到混合均匀后,出料,得到混合物;
将抗氧剂,润滑剂,复合纳米弹性体,FL-1复合润滑分散剂,FL-2活性表面处理剂,消泡剂,与水混合,加热,蒸馏,收集蒸汽,将蒸汽瞬间喷射到混合物中,使混合物迅速升温至130-140℃,时间3~5秒,再通过真空罐瞬间冷却至78~85℃,得到增韧剂;
取干燥过的聚乳酸,重均分子量为3096g/mol的低分子量聚己二酸二甘醇酯,重均分子量为50000~180000g/mol的高分子量聚己二酸二醇酯,将聚乳 酸同时与低分子量聚己二酸二甘醇酯和高分子量聚己二酸二甘醇酯放入密炼机内熔融共混,温度180~190℃,转矩50转/分,时间5~8分钟,得到辅料;
取羧甲基纤维素10-15份,烷基丙磺酸钠2-5份,十二烷基丙环酸钠6-10份,水1000-1300份混合均匀,得到混料;其次,辅料,加入到混料中混合均匀,先由室温升温到40℃后保温1小时,再升温到80℃并保温1.5小时,加入环氧树脂,混合,然后升温到110℃,保温2个小时,最后升高至139-146℃并保温27-36小时,断电并自然冷却至60℃以下,出炉冷却至常温,得到胶黏剂;
分别将增韧剂与胶黏剂进行真空浓缩,按1:1混合进行,得到混合剂。
进一步技术:在防滑层表面涂抹一层无毒植物胶,冷却后,即可使用,更换时,微加热即可撕掉;
所述的无毒植物胶包括,辣椒素5-20份,大蒜素2-15份,甲基烯丙基硫醚5-10份,黄酮苷5-10份,菊酯5-10份,薄荷精油1-10份,扩散剂10-12份,润湿剂5-10份,乙醇5-10份,丙二醇丙二醇10-25份,E-42环氧树脂89-99份,酚醛-丁晴橡胶共聚物89-99份,丙酮66-75份,乙二胺10-15份,改性氢化蓖麻油5-6份、膨润土6-10份。
进一步技术:所述菊酯的制备是菊花中萃取得3,3-二甲基-4-戊烯酸乙酯用环丁酮法合成二氯菊酸,经转位及碱作用下环缩小而得二氯菊酸。丙烯腈与四氯化碳进行加成反应、水解、用氯化亚砜进行酰氯化,得四氯丁酰氯,在三乙胺作用下,与异丁烯进行环加成反应,得2-氯代环丁酮,加热进行Cine分子重排,得4-氯代环丁酮,再在强碱作用下,进行Favorskii反应,得菊酯。
进一步技术:所述大蒜素的制备是大蒜粉碎在萃取压力18MPa,萃取温度为25℃,萃取剂流量2.0L/分钟,萃取时间3小时,得大蒜素制剂。
进一步技术:所述无毒植物胶的制备工艺是将菊酯大蒜素素辣椒素素混合经过复分解反应得混合液1,薄荷经过亚临界生物技术低温萃取液的薄荷精华,薄荷精华与混合液1混合得混合液2,再将甲基烯丙基硫醚C4H8S、黄酮苷、丙二醇丙二醇与混合液2混合经过隔绝空气浸取工艺手段溶剂回收,得到香液;
将香液至于高速搅拌机内,转速1000转/分钟,加入扩散剂,搅拌3分钟;
转速2000转/分钟,加入润湿剂,搅拌3分钟;
转速800转/分钟,加入乙醇,搅拌5分钟;取出泡沫,得到混合液;
将E-42环氧树脂、酚醛-丁晴橡胶共聚物加入反应釜中采用速度大于15000rmp分散机分散30-60分钟,将改性氢化蓖麻油加入反应釜中采用速度大于19000rmp分散机分散30分钟,再添加膨润土,分散机速度5000rmp分散15分钟,加入混合液,后抽真空30分钟,分散速度为100rmp,反应釜中的真空度为0.8-0.9Mpa,得到混合物,将混合物研磨30分钟,过滤500目筛网,得到无毒植物胶。
进一步技术:在上述配方中增加防裂添加剂,包括,对氨基苯甲酸25-100份,氢氧化钠4-16份、甘露醇2-8份,硝酸钙3-12份,水50-60份,氧化锌10-12份,抗静电剂6-9份。
进一步技术:所述的防裂添加剂制备方法为,在搅拌器中依次加入水、对氨基苯甲酸、氢氧化钠、甘露醇、搅拌至完全溶解;然后加入硝酸钙、氧化锌,搅拌混合溶解后静置、过滤,所得滤液加入抗静电剂混合均匀,即得成品。
进一步技术:所述的份为重量份。
有益效果:三层结构,其层为PVC发泡材料构成的防滑层,中层为特斯林网布,底层为植物胶垫,这种设计结构,使得本发明不仅可当做家居的防滑垫使用,还可作为睡觉用的席子、沙发垫或者出游用垫等,其用途广泛,给人们带来了方便;本发明的顶层为特斯林网布,特斯林具有耐水耐油、耐磨损、色彩鲜艳、抗紫外线、无毒等优点,已经被人们所接受,并且其造价并不昂贵,经济实用,在人们选择防滑垫时,多出了一种选择;
底层与中层通过增韧剂与胶黏剂按1:1混合剂进行粘合,在粘合的同时,利用复合纳米弹性体,增加黏胶的韧性,从而提高防滑垫整体的中段韧性,增强横向抗拉伸能力;
在防滑垫表面,涂上一层特制的无毒植物胶,一方面,增加表面摩擦力,另一方面,可有效去除表面残留灰尘等杂质,同时,含有的香液有效祛除了胶体原本的气味,更重要的是香液中含有的辣椒素和大蒜素有效驱除蚊虫, 避免细菌的滋生;
防裂添加剂中含有的氨基苯甲酸能够使防滑垫在极端温度下保持一点的柔软度,避免变硬,导致的韧性降低。
附图说明:
图1为本发明的结构示意图;
图2为本发明的斯特林网布结构示意图。
具体实施方式:
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合附图及具体实施例,进一步阐述本发明。
具体实施例1:如图1和图2一种安全高韧性家用多层防滑垫,该防滑垫包括三层结构,顶层为PVC发泡材料构成的防滑层1,中层为特斯林网布2,底层为植物胶垫3。
斯特林网布包括纵横交错编织的经线6与纬线7,该纬线与经线均选用特斯林线,该经线与纬线间均无间隙。
经线与纬线纵横交错编织重叠位置利用熔接的方式将两者相互固定。
底层下表面上设置有若干防滑点4,上表面设有若干方形凸块5,方形凸块与斯特林网的经线与纬线组成的方格配合。
底层与中层通过增韧剂与胶黏剂按1:1混合剂进行粘合。
增韧剂包括纳米碳纤维5份,引发剂5份,粘度1000~20000mPa·s的二甲基乙烯基甲硅氧基封端的聚二甲基硅氧烷100份,六甲基二硅氮烷2份,甘油3份,气相法白炭黑5份,粘度为1000~20000mPa·s的二甲基乙烯基甲硅氧基封端的聚二甲基硅氧烷兑稀60份,抗氧剂0.1份,润滑剂0.1份,复合纳米弹性体18份,FL-1复合润滑分散剂1份,FL-2活性表面处理剂5份,消泡剂1份,海因环氧树脂30份,水30份。
胶黏剂包括括聚乳酸50份,低分子量聚己二酸二甘醇酯10份,高分子量聚己二酸二甘醇酯5份,羧甲基纤维素10份,烷基丙磺酸钠2份,十二烷基丙环酸钠6份,水1000份,环氧树脂60份。
按重量配比称取干燥的纳米碳纤维、引发剂和海因环氧树脂,分别加入料筒温度为60℃~90℃的高速混合机中,搅拌2~6小时,再加入按重量配比称取的粘度1000~20000mPa·s的二甲基乙烯基甲硅氧基封端的聚二甲基硅氧烷,六甲基二硅氮烷,甘油,气相法白炭黑,粘度为1000~20000mPa·s的二甲基乙烯基甲硅氧基封端的聚二甲基硅氧烷兑稀,使一起搅拌10~40分钟和达到混合均匀后,出料,得到混合物;
将抗氧剂,润滑剂,复合纳米弹性体,FL-1复合润滑分散剂,FL-2活性表面处理剂,消泡剂,与水混合,加热,蒸馏,收集蒸汽,将蒸汽瞬间喷射到混合物中,使混合物迅速升温至130-140℃,时间3~5秒,再通过真空罐瞬间冷却至78~85℃,得到增韧剂;
取干燥过的聚乳酸,重均分子量为3096g/mol的低分子量聚己二酸二甘醇酯,重均分子量为50000~180000g/mol的高分子量聚己二酸二醇酯,将聚乳酸同时与低分子量聚己二酸二甘醇酯和高分子量聚己二酸二甘醇酯放入密炼机内熔融共混,温度180~190℃,转矩50转/分,时间5~8分钟,得到辅料;
取羧甲基纤维素10份,烷基丙磺酸钠2份,十二烷基丙环酸钠6份,水1000份混合均匀,得到混料;其次,辅料,加入到混料中混合均匀,先由室温升温到40℃后保温1小时,再升温到80℃并保温1.5小时,加入环氧树脂,混合,然后升温到110℃,保温2个小时,最后升高至139-146℃并保温27-36小时,断电并自然冷却至60℃以下,出炉冷却至常温,得到胶黏剂;
分别将增韧剂与胶黏剂进行真空浓缩,按1:1混合进行,得到混合剂。
在防滑层表面涂抹一层无毒植物胶,冷却后,即可使用,更换时,微加热即可撕掉;
无毒植物胶包括,辣椒素5份,大蒜素2份,甲基烯丙基硫醚5份,黄酮苷5份,菊酯5份,薄荷精油1份,扩散剂10份,润湿剂5份,乙醇5份,丙二醇丙二醇10份,E-42环氧树脂89-份,酚醛-丁晴橡胶共聚物89份,丙酮66份,乙二胺10份,改性氢化蓖麻油5份、膨润土6份。
菊酯的制备是菊花中萃取得3,3-二甲基-4-戊烯酸乙酯用环丁酮法合成二氯菊酸,经转位及碱作用下环缩小而得二氯菊酸。丙烯腈与四氯化碳进行加成反应、水解、用氯化亚砜进行酰氯化,得四氯丁酰氯,在三乙胺作用 下,与异丁烯进行环加成反应,得2-氯代环丁酮,加热进行Cine分子重排,得4-氯代环丁酮,再在强碱作用下,进行Favorskii反应,得菊酯。
大蒜素的制备是大蒜粉碎在萃取压力18MPa,萃取温度为25℃,萃取剂流量2.0L/分钟,萃取时间3小时,得大蒜素制剂。
无毒植物胶的制备工艺是将菊酯大蒜素素辣椒素素混合经过复分解反应得混合液1,薄荷经过亚临界生物技术低温萃取液的薄荷精华,薄荷精华与混合液1混合得混合液2,再将甲基烯丙基硫醚C4H8S、黄酮苷、丙二醇丙二醇与混合液2混合经过隔绝空气浸取工艺手段溶剂回收,得到香液;
将香液至于高速搅拌机内,转速1000转/分钟,加入扩散剂,搅拌3分钟;
转速2000转/分钟,加入润湿剂,搅拌3分钟;
转速800转/分钟,加入乙醇,搅拌5分钟;取出泡沫,得到混合液;
将E-42环氧树脂、酚醛-丁晴橡胶共聚物加入反应釜中采用速度大于15000rmp分散机分散30-60分钟,将改性氢化蓖麻油加入反应釜中采用速度大于19000rmp分散机分散30分钟,再添加膨润土,分散机速度5000rmp分散15分钟,加入混合液,后抽真空30分钟,分散速度为100rmp,反应釜中的真空度为0.8-0.9Mpa,得到混合物,将混合物研磨30分钟,过滤500目筛网,得到无毒植物胶。
在上述配方中增加防裂添加剂,包括,对氨基苯甲酸25份,氢氧化钠4份、甘露醇2份,硝酸钙3份,水50份,氧化锌10份,抗静电剂6份。
所述的防裂添加剂制备方法为,在搅拌器中依次加入水、对氨基苯甲酸、氢氧化钠、甘露醇、搅拌至完全溶解;然后加入硝酸钙、氧化锌,搅拌混合溶解后静置、过滤,所得滤液加入抗静电剂混合均匀,即得成品。
份为重量份。
对比现有的橡胶防滑垫,本法的橡胶垫性能得到提升,具体如下:
底层与中层通过增韧剂与胶黏剂按1:1混合剂进行粘合,在粘合的同时,利用复合纳米弹性体,增加黏胶的韧性,从而提高防滑垫整体的中段韧性,增强横向抗拉伸能力;
在防滑垫表面,涂上一层特制的无毒植物胶,一方面,增加表面摩擦力,另一方面,可有效去除表面残留灰尘等杂质,同时,含有的香液有效祛除了胶体原本的气味,更重要的是香液中含有的辣椒素和大蒜素有效驱除蚊虫,避免细菌的滋生;
防裂添加剂中含有的氨基苯甲酸能够使防滑垫在极端温度下保持一点的柔软度,避免变硬,导致的韧性降低。
具体实施例2:如图1和图2一种安全高韧性家用多层防滑垫,该防滑垫包括三层结构,顶层为PVC发泡材料构成的防滑层1,中层为特斯林网布2,底层为植物胶垫3。
斯特林网布包括纵横交错编织的经线6与纬线7,该纬线与经线均选用特斯林线,该经线与纬线间均无间隙。
经线与纬线纵横交错编织重叠位置利用熔接的方式将两者相互固定。
底层下表面上设置有若干防滑点4,上表面设有若干方形凸块5,方形凸块与斯特林网的经线与纬线组成的方格配合。
底层与中层通过增韧剂与胶黏剂按1:1混合剂进行粘合。
增韧剂包括纳米碳纤维10份,引发剂10份,粘度1000~20000mPa·s的二甲基乙烯基甲硅氧基封端的聚二甲基硅氧烷105份,六甲基二硅氮烷2份,甘油4份,气相法白炭黑7份,粘度为1000~20000mPa·s的二甲基乙烯基甲硅氧基封端的聚二甲基硅氧烷兑稀65份,抗氧剂0.3份,润滑剂0.5份,复合纳米弹性体30份,FL-1复合润滑分散剂3份,FL-2活性表面处理剂7份,消泡剂3 份,海因环氧树脂50份,水40份。
胶黏剂包括括聚乳酸55份,低分子量聚己二酸二甘醇酯11份,高分子量聚己二酸二甘醇酯15份,羧甲基纤维素12份,烷基丙磺酸钠4份,十二烷基丙环酸钠8份,水1100份,环氧树脂65份。
按重量配比称取干燥的纳米碳纤维、引发剂和海因环氧树脂,分别加入料筒温度为60℃~90℃的高速混合机中,搅拌2~6小时,再加入按重量配比称取的粘度1000~20000mPa·s的二甲基乙烯基甲硅氧基封端的聚二甲基硅氧烷,六甲基二硅氮烷,甘油,气相法白炭黑,粘度为1000~20000mPa·s的二甲基乙烯基甲硅氧基封端的聚二甲基硅氧烷兑稀,使一起搅拌10~40分钟和达到混合均匀后,出料,得到混合物;
将抗氧剂,润滑剂,复合纳米弹性体,FL-1复合润滑分散剂,FL-2活性表面处理剂,消泡剂,与水混合,加热,蒸馏,收集蒸汽,将蒸汽瞬间喷射到混合物中,使混合物迅速升温至130-140℃,时间3~5秒,再通过真空罐瞬间冷却至78~85℃,得到增韧剂;
取干燥过的聚乳酸,重均分子量为3096g/mol的低分子量聚己二酸二甘醇酯,重均分子量为50000~180000g/mol的高分子量聚己二酸二醇酯,将聚乳酸同时与低分子量聚己二酸二甘醇酯和高分子量聚己二酸二甘醇酯放入密炼机内熔融共混,温度180~190℃,转矩50转/分,时间5~8分钟,得到辅料;
取羧甲基纤维素12份,烷基丙磺酸钠4份,十二烷基丙环酸钠8份,水1100份混合均匀,得到混料;其次,辅料,加入到混料中混合均匀,先由室温升温到40℃后保温1小时,再升温到80℃并保温1.5小时,加入环氧树脂,混合,然后升温到110℃,保温2个小时,最后升高至139-146℃并保温27-36小时,断电并自然冷却至60℃以下,出炉冷却至常温,得到胶黏剂;
分别将增韧剂与胶黏剂进行真空浓缩,按1:1混合进行,得到混合剂。
在防滑层表面涂抹一层无毒植物胶,冷却后,即可使用,更换时,微加热即可撕掉;
无毒植物胶包括,辣椒素15份,大蒜素10份,甲基烯丙基硫醚7份,黄酮苷7份,菊酯7份,薄荷精油5份,扩散剂11份,润湿剂7份,乙醇7份,丙二醇丙二醇20份,E-42环氧树脂95份,酚醛-丁晴橡胶共聚物90份,丙酮70份, 乙二胺12份,改性氢化蓖麻油5份、膨润土8份。
菊酯的制备是菊花中萃取得3,3-二甲基-4-戊烯酸乙酯用环丁酮法合成二氯菊酸,经转位及碱作用下环缩小而得二氯菊酸。丙烯腈与四氯化碳进行加成反应、水解、用氯化亚砜进行酰氯化,得四氯丁酰氯,在三乙胺作用下,与异丁烯进行环加成反应,得2-氯代环丁酮,加热进行Cine分子重排,得4-氯代环丁酮,再在强碱作用下,进行Favorskii反应,得菊酯。
大蒜素的制备是大蒜粉碎在萃取压力18MPa,萃取温度为25℃,萃取剂流量2.0L/分钟,萃取时间3小时,得大蒜素制剂。
无毒植物胶的制备工艺是将菊酯大蒜素素辣椒素素混合经过复分解反应得混合液1,薄荷经过亚临界生物技术低温萃取液的薄荷精华,薄荷精华与混合液1混合得混合液2,再将甲基烯丙基硫醚C4H8S、黄酮苷、丙二醇丙二醇与混合液2混合经过隔绝空气浸取工艺手段溶剂回收,得到香液;
将香液至于高速搅拌机内,转速1000转/分钟,加入扩散剂,搅拌3分钟;
转速2000转/分钟,加入润湿剂,搅拌3分钟;
转速800转/分钟,加入乙醇,搅拌5分钟;取出泡沫,得到混合液;
将E-42环氧树脂、酚醛-丁晴橡胶共聚物加入反应釜中采用速度大于15000rmp分散机分散30-60分钟,将改性氢化蓖麻油加入反应釜中采用速度大于19000rmp分散机分散30分钟,再添加膨润土,分散机速度5000rmp分散15分钟,加入混合液,后抽真空30分钟,分散速度为100rmp,反应釜中的真空度为0.8-0.9Mpa,得到混合物,将混合物研磨30分钟,过滤500目筛网,得到无毒植物胶。
在上述配方中增加防裂添加剂,包括,对氨基苯甲酸50份,氢氧化钠10份、甘露醇5份,硝酸钙8份,水55份,氧化锌11份,抗静电剂7份。
所述的防裂添加剂制备方法为,在搅拌器中依次加入水、对氨基苯甲酸、氢氧化钠、甘露醇、搅拌至完全溶解;然后加入硝酸钙、氧化锌,搅拌混合溶解后静置、过滤,所得滤液加入抗静电剂混合均匀,即得成品。
份为重量份。
对比现有的橡胶防滑垫,本法的橡胶垫性能得到提升,具体如下:
底层与中层通过增韧剂与胶黏剂按1:1混合剂进行粘合,在粘合的同时,利用复合纳米弹性体,增加黏胶的韧性,从而提高防滑垫整体的中段韧性,增强横向抗拉伸能力;
在防滑垫表面,涂上一层特制的无毒植物胶,一方面,增加表面摩擦力,另一方面,可有效去除表面残留灰尘等杂质,同时,含有的香液有效祛除了胶体原本的气味,更重要的是香液中含有的辣椒素和大蒜素有效驱除蚊虫,避免细菌的滋生;
防裂添加剂中含有的氨基苯甲酸能够使防滑垫在极端温度下保持一点的柔软度,避免变硬,导致的韧性降低。
具体实施例3:如图1和图2一种安全高韧性家用多层防滑垫,该防滑垫包括三层结构,顶层为PVC发泡材料构成的防滑层1,中层为特斯林网布2,底层为植物胶垫3。
斯特林网布包括纵横交错编织的经线6与纬线7,该纬线与经线均选用特斯林线,该经线与纬线间均无间隙。
经线与纬线纵横交错编织重叠位置利用熔接的方式将两者相互固定。
底层下表面上设置有若干防滑点4,上表面设有若干方形凸块5,方形凸块与斯特林网的经线与纬线组成的方格配合。
底层与中层通过增韧剂与胶黏剂按1:1混合剂进行粘合。
增韧剂包括纳米碳纤维15份,引发剂12份,粘度1000~20000mPa·s的二 甲基乙烯基甲硅氧基封端的聚二甲基硅氧烷110份,六甲基二硅氮烷3份,甘油5份,气相法白炭黑10份,粘度为1000~20000mPa·s的二甲基乙烯基甲硅氧基封端的聚二甲基硅氧烷兑稀70份,抗氧剂0.5份,润滑剂1份,复合纳米弹性体50份,FL-1复合润滑分散剂5份,FL-2活性表面处理剂10份,消泡剂15份,海因环氧树75份,水50份。
胶黏剂包括括聚乳酸60份,低分子量聚己二酸二甘醇酯12份,高分子量聚己二酸二甘醇酯20份,羧甲基纤维素15份,烷基丙磺酸钠5份,十二烷基丙环酸钠10份,水1300份,环氧树脂70份。
按重量配比称取干燥的纳米碳纤维、引发剂和海因环氧树脂,分别加入料筒温度为60℃~90℃的高速混合机中,搅拌2~6小时,再加入按重量配比称取的粘度1000~20000mPa·s的二甲基乙烯基甲硅氧基封端的聚二甲基硅氧烷,六甲基二硅氮烷,甘油,气相法白炭黑,粘度为1000~20000mPa·s的二甲基乙烯基甲硅氧基封端的聚二甲基硅氧烷兑稀,使一起搅拌10~40分钟和达到混合均匀后,出料,得到混合物;
将抗氧剂,润滑剂,复合纳米弹性体,FL-1复合润滑分散剂,FL-2活性表面处理剂,消泡剂,与水混合,加热,蒸馏,收集蒸汽,将蒸汽瞬间喷射到混合物中,使混合物迅速升温至130-140℃,时间3~5秒,再通过真空罐瞬间冷却至78~85℃,得到增韧剂;
取干燥过的聚乳酸,重均分子量为3096g/mol的低分子量聚己二酸二甘醇酯,重均分子量为50000~180000g/mol的高分子量聚己二酸二醇酯,将聚乳酸同时与低分子量聚己二酸二甘醇酯和高分子量聚己二酸二甘醇酯放入密炼机内熔融共混,温度180~190℃,转矩50转/分,时间5~8分钟,得到辅料;
取羧甲基纤维素15份,烷基丙磺酸钠5份,十二烷基丙环酸钠10份,水1300份混合均匀,得到混料;其次,辅料,加入到混料中混合均匀,先由室温升温到40℃后保温1小时,再升温到80℃并保温1.5小时,加入环氧树脂,混合,然后升温到110℃,保温2个小时,最后升高至139-146℃并保温27-36小时,断电并自然冷却至60℃以下,出炉冷却至常温,得到胶黏剂;
分别将增韧剂与胶黏剂进行真空浓缩,按1:1混合进行,得到混合剂。
在防滑层表面涂抹一层无毒植物胶,冷却后,即可使用,更换时,微加 热即可撕掉;
无毒植物胶包括,辣椒素20份,大蒜素15份,甲基烯丙基硫醚10份,黄酮苷10份,菊酯10份,薄荷精油10份,扩散剂12份,润湿剂10份,乙醇10份,丙二醇丙二醇25份,E-42环氧树脂99份,酚醛-丁晴橡胶共聚物99份,丙酮75份,乙二胺15份,改性氢化蓖麻油6份、膨润土10份。
菊酯的制备是菊花中萃取得3,3-二甲基-4-戊烯酸乙酯用环丁酮法合成二氯菊酸,经转位及碱作用下环缩小而得二氯菊酸。丙烯腈与四氯化碳进行加成反应、水解、用氯化亚砜进行酰氯化,得四氯丁酰氯,在三乙胺作用下,与异丁烯进行环加成反应,得2-氯代环丁酮,加热进行Cine分子重排,得4-氯代环丁酮,再在强碱作用下,进行Favorskii反应,得菊酯。
大蒜素的制备是大蒜粉碎在萃取压力18MPa,萃取温度为25℃,萃取剂流量2.0L/分钟,萃取时间3小时,得大蒜素制剂。
无毒植物胶的制备工艺是将菊酯大蒜素素辣椒素素混合经过复分解反应得混合液1,薄荷经过亚临界生物技术低温萃取液的薄荷精华,薄荷精华与混合液1混合得混合液2,再将甲基烯丙基硫醚C4H8S、黄酮苷、丙二醇丙二醇与混合液2混合经过隔绝空气浸取工艺手段溶剂回收,得到香液;
将香液至于高速搅拌机内,转速1000转/分钟,加入扩散剂,搅拌3分钟;
转速2000转/分钟,加入润湿剂,搅拌3分钟;
转速800转/分钟,加入乙醇,搅拌5分钟;取出泡沫,得到混合液;
将E-42环氧树脂、酚醛-丁晴橡胶共聚物加入反应釜中采用速度大于15000rmp分散机分散30-60分钟,将改性氢化蓖麻油加入反应釜中采用速度大于19000rmp分散机分散30分钟,再添加膨润土,分散机速度5000rmp分散15分钟,加入混合液,后抽真空30分钟,分散速度为100rmp,反应釜中的真空度为0.8-0.9Mpa,得到混合物,将混合物研磨30分钟,过滤500目筛网,得到无毒植物胶。
在上述配方中增加防裂添加剂,包括,对氨基苯甲酸100份,氢氧化钠16份、甘露醇8份,硝酸钙12份,水60份,氧化锌12份,抗静电剂9份。
所述的防裂添加剂制备方法为,在搅拌器中依次加入水、对氨基苯甲酸、氢氧化钠、甘露醇、搅拌至完全溶解;然后加入硝酸钙、氧化锌,搅拌混合 溶解后静置、过滤,所得滤液加入抗静电剂混合均匀,即得成品。
份为重量份。
对比现有的橡胶防滑垫,本法的橡胶垫性能得到提升,具体如下:
底层与中层通过增韧剂与胶黏剂按1:1混合剂进行粘合,在粘合的同时,利用复合纳米弹性体,增加黏胶的韧性,从而提高防滑垫整体的中段韧性,增强横向抗拉伸能力;
在防滑垫表面,涂上一层特制的无毒植物胶,一方面,增加表面摩擦力,另一方面,可有效去除表面残留灰尘等杂质,同时,含有的香液有效祛除了胶体原本的气味,更重要的是香液中含有的辣椒素和大蒜素有效驱除蚊虫,避免细菌的滋生;
防裂添加剂中含有的氨基苯甲酸能够使防滑垫在极端温度下保持一点的柔软度,避免变硬,导致的韧性降低。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (5)
1.一种安全高韧性家用多层防滑垫,其特征在于:该防滑垫包括三层结构,顶层为PVC发泡材料构成的防滑层,中层为特斯林网布,底层为植物胶垫。
2.根据权利要求1中所述的一种安全高韧性家用多层防滑垫,其特征在于:所述斯特林网布包括纵横交错编织的经线与纬线,该纬线与经线均选用特斯林线,该经线与纬线间均无间隙。
3.根据权利要求1中所述的一种安全高韧性家用多层防滑垫,其特征在于:所述经线与纬线纵横交错编织重叠位置利用熔接的方式将两者相互固定。
4.根据权利要求1中所述的一种安全高韧性家用多层防滑垫,其特征在于:所述底层下表面上设置有若干防滑点,上表面设有若干方形凸块,方形凸块与斯特林网的经线与纬线组成的方格配合。
5.根据权利要求1中所述的一种安全高韧性家用多层防滑垫,其特征在于:所述底层与中层通过增韧剂与胶黏剂按1:1混合剂进行粘合。