CN107401009A - A kind of preparation of novel aromatic fiber type and its application method - Google Patents
A kind of preparation of novel aromatic fiber type and its application method Download PDFInfo
- Publication number
- CN107401009A CN107401009A CN201710766239.3A CN201710766239A CN107401009A CN 107401009 A CN107401009 A CN 107401009A CN 201710766239 A CN201710766239 A CN 201710766239A CN 107401009 A CN107401009 A CN 107401009A
- Authority
- CN
- China
- Prior art keywords
- type
- fiber
- novel aromatic
- polyester fiber
- weaving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of preparation of novel aromatic fiber type and its application method, belong to functional fibre technical field.A kind of preparation of novel aromatic fiber type of the present invention and its application method, the novel aromatic fiber type passes through during final finishing, weaving is combined with each other with aroma type auxiliary agent and basic polyester fiber, formation has the functional polyester fiber of aroma type, this method technique is simple, it is easy to streamline large-scale operation, easy control of process conditions in production process, production cost is low；A process for preparing the functional fibre come, can pass through repeatedly washing, also with good aroma type feature, be worth of widely use.
Description
Technical field
The present invention relates to a kind of preparation of novel aromatic fiber type and its application method, belongs to functional fibre technology neck
Domain.
Background technology
At present, as textile technology and life taste, the raising of quality, the garment material of simple function can not expire
The life requirement of sufficient people.Multifunction is the inexorable trend of costume fabric development.
The development of functional fibre is the symbol of modern fiber science progress.Functional fibre, fibre in differentiation and high-performance are fine
The technological innovation for developing into traditional textile industry of dimension, the conversion to high-tech industry creates advantage, is human lives
Horizontal raising contributes.Functional fibre refers in addition to physical and mechanical properties possessed by general fiber, also have
The tencel of certain specific function.Such as:Fiber has health care function (antibacterial, mite killing, physiotherapy and eliminate the unusual smell)
；Safeguard function (radiation proof, antistatic, uvioresistant etc.)；The wet comfortable function (heat absorption, heat release, moisture absorption, moisture releasing etc.) of heat；Doctor
Treat and environment-friendly function (biocompatibility and biological degradability).Common functional fibre, complex manufacturing technology, cost of manufacture
It is higher, and function is not firm enough possessed by fiber, and by washing twice, the function of fiber will have a greatly reduced quality, and be unfavorable for
The manufacture of functional fibre and promote the use of.
It is an object of the invention to provide a kind of preparation of novel aromatic fiber type and its application method, the novel aromatic type
For fiber by the way that during final finishing, weaving is combined with each other with aroma type auxiliary agent and basic polyester fiber, being formed has virtue
The functional polyester fiber of odor type, this method technique is simple, is easy to streamline large-scale operation, and process conditions are held in production process
Easy to control, production cost is low；A process for preparing the functional fibre come, can pass through repeatedly washing, also with good fragrance
Type feature, is worth of widely use.
The content of the invention
The technical solution adopted for the present invention to solve the technical problems is：A kind of preparation method of novel aromatic fiber type,
It is characterized in that its step is：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 4.5-6.8 kilograms, and terylene mesh bag is placed into conveyer belt
On；
（2）, terylene mesh bag entered by conveyer belt in circulation solution case, circulate the weaving in solution case in solution and helped with aroma type
The weight of agent and water ratio is 1-5:101, the temperature for circulating solution in solution case is 51-111 degrees Celsius, and polyester fiber is molten in circulation
Soak time in body case is 3-8 minutes；
（3）, the polyester fiber that soaked is rolled 5 times repeatedly with Pneumatic pressure bar in circulation solution case, roll every time 1 minute,
The pressure of press rods is 5 kilograms, it is adjacent roll twice between be spaced 1-2 minutes so that the weight of polyester fiber and solution ratio
For 5:0.1-1；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is that 82-121 is Celsius
Degree, the baking time is 105-135 minutes；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into novel aromatic fiber type.
The preferable step（2）Middle weaving is to weave with plant microcapsules auxiliary agent, weaving fruity with aroma type auxiliary agent
Microcapsules auxiliary agent, weaving use nature microcapsules auxiliary agent with lovers' microcapsules auxiliary agent or weaving.
A kind of application method of described novel aromatic fiber type, its step are：
（1）, the novel aromatic fiber type for preparing claim 1 and polyester fiber, eutectic polyester fiber according to weight than 1：
1-2：0.1-0.5 carries out uniformly mixing and unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15-40 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180-188 it is Celsius
Degree so that eutectic polyester fiber melts, and the baking time is the 50-60 seconds；
（5）, it is baked after, roll coiled, that is, be prepared into novel aromatic fiber type flocculus.
Described a kind of new functional fiber application method, it is characterised in that prepared using novel aromatic fiber type
Fabric.
The preferable weaving odor type of plant microcapsules auxiliary agent include santal odor type, agalloch eaglewood odor type, lavender flavor type,
Jasmine fragrance, rose fragrance type and cordate telosma odor type；The weaving odor type of fruity microcapsules auxiliary agent include lemon flavor,
Orange odor type, banana-aroma-type, strawberry odor type and apple fragrance type.
It is an object of the invention to provide a kind of preparation of novel aromatic fiber type and its application method, the novel aromatic type
For fiber by the way that during final finishing, weaving is combined with each other with aroma type auxiliary agent and basic polyester fiber, being formed has virtue
The functional polyester fiber of odor type, this method technique is simple, is easy to streamline large-scale operation, and process conditions are held in production process
Easy to control, production cost is low；A process for preparing the functional fibre come, can pass through repeatedly washing, also with good fragrance
Type feature, is worth of widely use.
Embodiment
Specific embodiment one：A kind of preparation method of novel aromatic fiber type, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 4.5 kilograms, and terylene mesh bag is placed on conveyer belt；
（2）, terylene mesh bag entered by conveyer belt in circulation solution case, circulate the weaving micro- glue of plant in solution in solution case
The weight of capsule auxiliary agent and water ratio is 1:101, the temperature for circulating solution in solution case is 51 degrees Celsius, and polyester fiber is in circulation solution
Soak time in case is 3 minutes；
（3）, the polyester fiber that soaked is rolled 5 times repeatedly with Pneumatic pressure bar in circulation solution case, roll every time 1 minute,
The pressure of press rods is 5 kilograms, it is adjacent roll twice between be spaced 1 minute so that the weight of polyester fiber and solution ratio is
5:0.1；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is 82 degrees Celsius, is dried
It is 105 minutes to roast the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into novel aromatic fiber type.
A kind of application method of described novel aromatic fiber type, its step are：
（1）, the novel aromatic fiber type for preparing claim 1 and polyester fiber, eutectic polyester fiber according to weight than 1：
1：0.1, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 50 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into novel aromatic fiber type flocculus.
A kind of new functional fiber application method, it is characterised in that the fabric prepared using novel aromatic fiber type.
The preferable weaving is jasmine fragrance with the odor type of plant microcapsules auxiliary agent.
Specific embodiment two：A kind of preparation method of novel aromatic fiber type, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 5 kilograms, and terylene mesh bag is placed on conveyer belt；
（2）, terylene mesh bag entered by conveyer belt in circulation solution case, circulate the micro- glue of weaving fruity in solution in solution case
The weight of capsule auxiliary agent and water ratio is 3:101, the temperature for circulating solution in solution case is 71 degrees Celsius, and polyester fiber is in circulation solution
Soak time in case is 6 minutes；
（3）, the polyester fiber that soaked is rolled 5 times repeatedly with Pneumatic pressure bar in circulation solution case, roll every time 1 minute,
The pressure of press rods is 5 kilograms, it is adjacent roll twice between be spaced 1.4 minutes so that the weight of polyester fiber and solution ratio
For 5:0.4；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is 95 degrees Celsius, is dried
It is 125 minutes to roast the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into novel aromatic fiber type.
A kind of application method of novel aromatic fiber type, its step are：
（1）, the novel aromatic fiber type for preparing claim 1 and polyester fiber, eutectic polyester fiber according to weight than 1：
1.5：0.3, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 30 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 184 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 55 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into novel aromatic fiber type flocculus.
A kind of new functional fiber application method, it is characterised in that the fabric prepared using novel aromatic fiber type.
Specific embodiment three：A kind of preparation method of novel aromatic fiber type, its step are：
（1）、（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, washing after fluffy processing
Synthetic fibre fiber is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 6.8 kilograms, and terylene mesh bag is placed into conveyer belt
On；
（2）, terylene mesh bag entered by conveyer belt in circulation solution case, circulate the naturally micro- glue of weaving in solution in solution case
The weight of capsule auxiliary agent and water ratio is 5:101, the temperature for circulating solution in solution case is 111 degrees Celsius, and polyester fiber is molten in circulation
Soak time in body case is 8 minutes；
（3）, the polyester fiber that soaked is rolled 5 times repeatedly with Pneumatic pressure bar in circulation solution case, roll every time 1 minute,
The pressure of press rods is 5 kilograms, it is adjacent roll twice between be spaced 2 minutes so that the weight of polyester fiber and solution ratio is
5: 1；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is 121 degrees Celsius,
It is 135 minutes to bakee the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into novel aromatic fiber type.
A kind of application method of described novel aromatic fiber type, its step are：
（1）, the novel aromatic fiber type for preparing claim 1 and polyester fiber, eutectic polyester fiber according to weight than 1：
2：0.5, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 40 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 188 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 60 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into novel aromatic fiber type flocculus.
Described a kind of new functional fiber application method, it is characterised in that prepared using novel aromatic fiber type
Fabric.
It is an object of the invention to provide a kind of preparation of novel aromatic fiber type and its application method, the novel aromatic type
For fiber by the way that during final finishing, weaving is combined with each other with aroma type auxiliary agent and basic polyester fiber, being formed has virtue
The functional polyester fiber of odor type, this method technique is simple, is easy to streamline large-scale operation, and process conditions are held in production process
Easy to control, production cost is low；A process for preparing the functional fibre come, can pass through repeatedly washing, also with good fragrance
Type feature, is worth of widely use.
Obviously, above-described embodiment is only intended to clearly illustrate example, and is not the restriction to embodiment.It is right
For those of ordinary skill in the art, can also make on the basis of the above description it is other it is various forms of change or
Change.There is no necessity and possibility to exhaust all the enbodiments.And the obvious change thus extended out or
Among changing still in the protection domain of the invention.
Claims (5)
1. a kind of preparation method of novel aromatic fiber type, it is characterised in that its step is：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is put into terylene mesh bag, and every bag of weight for being put into polyester fiber is 4.5-6.8 kilograms, and terylene mesh bag is placed into conveyer belt
On；
（2）, terylene mesh bag entered by conveyer belt in circulation solution case, circulate the weaving in solution case in solution and helped with aroma type
The weight of agent and water ratio is 1-5:101, the temperature for circulating solution in solution case is 51-111 degrees Celsius, and polyester fiber is molten in circulation
Soak time in body case is 3-8 minutes；
（3）, the polyester fiber that soaked is rolled 5 times repeatedly with Pneumatic pressure bar in circulation solution case, roll every time 1 minute,
The pressure of press rods is 5 kilograms, it is adjacent roll twice between be spaced 1-2 minutes so that the weight of polyester fiber and solution ratio
For 5:0.1-1；
（4）, the terylene mesh bag that step 3 prepares be put into steam drying box bakeed, stoving temperature is that 82-121 is Celsius
Degree, the baking time is 105-135 minutes；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into novel aromatic fiber type.
A kind of 2. preparation method of novel aromatic fiber type according to claim 1, it is characterised in that the step（2）
Middle weaving is to weave to use the micro- glue of lovers with plant microcapsules auxiliary agent, weaving fruity microcapsules auxiliary agent, weaving with aroma type auxiliary agent
Nature microcapsules auxiliary agent is used in capsule auxiliary agent or weaving.
3. the application method of a kind of novel aromatic fiber type according to claim 1, it is characterised in that its step is：
（1）, the novel aromatic fiber type for preparing claim 1 and polyester fiber, eutectic polyester fiber according to weight than 1：
1-2：0.1-0.5 carries out uniformly mixing and unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15-40 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180-188 it is Celsius
Degree so that eutectic polyester fiber melts, and the baking time is the 50-60 seconds；
（5）, it is baked after, roll coiled, that is, be prepared into novel aromatic fiber type flocculus.
4. a kind of new functional fiber application method according to claim 1, it is characterised in that fine using novel aromatic type
Tie up the fabric prepared.
5. the preparation method of a kind of novel aromatic fiber type according to claim 2, it is characterised in that the weaving is planted
The odor type of thing microcapsules auxiliary agent includes santal odor type, agalloch eaglewood odor type, lavender flavor type, jasmine fragrance, rose fragrance type and night
Carry out odor type；The weaving odor type of fruity microcapsules auxiliary agent includes lemon flavor, orange odor type, banana-aroma-type, strawberry perfume
Type and apple fragrance type.