CN107216595A - 一种环保保鲜膜及其生产工艺 - Google Patents

一种环保保鲜膜及其生产工艺 Download PDF

Info

Publication number
CN107216595A
CN107216595A CN201710583960.9A CN201710583960A CN107216595A CN 107216595 A CN107216595 A CN 107216595A CN 201710583960 A CN201710583960 A CN 201710583960A CN 107216595 A CN107216595 A CN 107216595A
Authority
CN
China
Prior art keywords
parts
environment
preservative film
friendlypreservative
friendlypreservative preservative
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201710583960.9A
Other languages
English (en)
Inventor
吴旭
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Peak Energy Saving Technology Co Ltd
Original Assignee
Hefei Peak Energy Saving Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Peak Energy Saving Technology Co Ltd filed Critical Hefei Peak Energy Saving Technology Co Ltd
Priority to CN201710583960.9A priority Critical patent/CN107216595A/zh
Publication of CN107216595A publication Critical patent/CN107216595A/zh
Withdrawn legal-status Critical Current

Abstract

本发明提供了一种环保保鲜膜及其生产工艺，所述环保保鲜膜包括以下按重量份计的原料：SEBS树脂80‑120份，聚乳酸20‑40份，抗氧化剂0.5‑1.5份，抗菌剂0.6‑1.2份，增韧剂0.5‑1.5份，敏化剂1.5‑2.5份。采用本发明的环保保鲜膜，可以在大大降低生产成本的同时保持薄膜本身的高强度，其拉伸强度、断裂伸长率、摩擦系数、透光率均符合国家标准，同时还具有良好的食品包装抗菌保鲜性能。

Description

一种环保保鲜膜及其生产工艺
技术领域
本发明涉及环保材料技术领域，具体涉及一种环保保鲜膜及其生产工艺。
背景技术
目前，市售保鲜膜按原材料不同可分为三大类：第一类是聚偏二氯乙烯(PVDC)，主要用于熟食、火腿肠等保质期长、大规模工业化产品的包装；第二类是聚乙烯(PE)，主要用于普通水果、蔬菜等的包装；第三类即是人们使用较多的聚氯乙烯(PVC)。其中，聚乙烯、聚氯乙烯保鲜膜在日常生活中使用相当广泛，从蔬菜、水果到家庭食品的临时保鲜，以及防止食品存放时串味，都要使用保鲜膜。保鲜膜的自粘性主要依靠塑料自身特性实现，不能使粘合剂。
然而，PE保鲜膜透明度一般，延伸性能不够，很容易破裂；而且在自粘性方面存在严重不足，自粘性不强，在塑料盒上很难使用，包装速度慢，不利于机械化包装。
相反，PVC保鲜膜透明度高，延伸性好，不容易破裂，粘合性能好，包装速度快，适合于机械化包装；所以超市、商场出售的食品，特别是分隔鱼、肉等所使用的保鲜膜基本是PVC保鲜膜。但PVC保鲜膜存在如下问题：
1.单体问题，聚氯乙烯不可避免地存在聚合时残留的氯乙烯单体(VCM)，浓度超标将对人体造成严重危害(损害神经系统、肝脏和胚胎)；
2.添加剂问题，聚氯乙烯保鲜膜在生产时，需要加入各种添加剂(稳定剂、增塑剂等)，它们长期接触含油食品，尤其夏季温度较高时，很容易从保鲜膜中迁移析出，渗入并残留在食物中，对人类健康造成危害；
3.环保问题，PVC自身不能生物降解，在光/热作用下，降解也很缓慢，若采用焚烧处理，将产生大量刺激性、腐蚀性气体，燃烧不彻底时还会产生严重致癌物质。
发明内容
本发明的目的是针对现有技术的问题，提供一种环保保鲜膜及其生产工艺。
为了达到上述目的，本发明通过以下技术方案来实现：
一种环保保鲜膜，所述环保保鲜膜包括以下按重量份计的原料：
SEBS树脂80-120份，
聚乳酸20-40份，
抗氧化剂0.5-1.5份，
抗菌剂0.6-1.2份，
增韧剂0.5-1.5份，
敏化剂1.5-2.5份。
进一步地，所述环保保鲜膜包括以下按重量份计的原料：
SEBS树脂102份，
聚乳酸30份，
抗氧化剂1份，
抗菌剂0.9份，
增韧剂1份，
敏化剂2份。
进一步地，所述SEBS树脂选自高分子量SEBS、和低分子量SEBS中的一种或两种。
进一步地，所述抗氧化剂为丁基羟基茴香醚。
进一步地，所述增韧剂为丙烯酸酯类聚合物。
进一步地，所述敏化剂为安息香二甲醚。
进一步地，所述抗菌剂选自氧化银、载银磷酸锆、亚甲基双硫氰酸酯和甲壳素中的一种或几种。
一种环保保鲜膜的生产工艺，包括以下步骤：
（1）按所需重量份准备好各项原料：SEBS树脂80-120份，聚乳酸20-40份，抗氧化剂0.5-1.5份，抗菌剂0.6-1.2份，增韧剂0.5-1.5份和敏化剂1.5-2.5份；
（2）将所述各项原料混合后加热熔化挤出，在塑料挤出吹膜机中挤出成型的保鲜薄膜；
（3）将步骤（2）中得到的薄膜按照不同尺寸的产品规格进行卷膜切割，检查合格后即得到所述环保保鲜膜。
本发明与现有技术相比，具有如下的有益效果：
本发明采用SEBS树脂、聚乳酸、抗氧化剂、抗菌剂、增韧剂和敏化剂为原料，在生产过程中不使用二辛酯等增塑剂，不含卤素元素，是一种卫生、安全环保的新型包装材料，使用敏化剂可以使产品更加的容易分解，且分解后的产物无污染，具有绿色环保的性能。在聚乳酸中加入增韧剂，二者可保持材料的强度和延展性能；抗菌剂中的抗菌因子溶于聚乳酸和SEBS树脂中，使乳酸链球菌肽和抗菌因子牢固镶嵌于保鲜膜表面，增加了保鲜膜的抑菌性能。此外本发明还具有优异的透明性、自粘性，以及优良的机械性能。采用本发明的环保保鲜膜，可以在大大降低生产成本的同时保持薄膜本身的高强度，其拉伸强度、断裂伸长率、摩擦系数、透光率均符合国家标准，同时还具有良好的食品包装抗菌保鲜性能。
具体实施方式
下面结合实施例对本发明作进一步说明。
实施例1
一种环保保鲜膜，所述环保保鲜膜包括以下按重量份计的原料：
SEBS树脂80份，
聚乳酸20份，
抗氧化剂0.5份，
抗菌剂0.6份，
增韧剂0.5份，
敏化剂1.5份。
所述SEBS树脂选自高分子量SEBS、和低分子量SEBS中的一种或两种。
所述抗氧化剂为丁基羟基茴香醚。
所述增韧剂为丙烯酸酯类聚合物。
所述敏化剂为安息香二甲醚。
所述抗菌剂选自氧化银、载银磷酸锆、亚甲基双硫氰酸酯和甲壳素中的一种或几种。
一种环保保鲜膜的生产工艺，包括以下步骤：
（1）按所需重量份准备好各项原料：SEBS树脂80份，聚乳酸20份，抗氧化剂0.5份，抗菌剂0.6份，增韧剂0.5份和敏化剂1.5份；
（2）将所述各项原料混合后加热熔化挤出，在塑料挤出吹膜机中挤出成型的保鲜薄膜；
（3）将步骤（2）中得到的薄膜按照不同尺寸的产品规格进行卷膜切割，检查合格后即得到所述环保保鲜膜。
本发明采用SEBS树脂、聚乳酸、抗氧化剂、抗菌剂、增韧剂和敏化剂为原料，在生产过程中不使用二辛酯等增塑剂，不含卤素元素，是一种卫生、安全环保的新型包装材料，使用敏化剂可以使产品更加的容易分解，且分解后的产物无污染，具有绿色环保的性能。在聚乳酸中加入增韧剂，二者可保持材料的强度和延展性能；抗菌剂中的抗菌因子溶于聚乳酸和SEBS树脂中，使乳酸链球菌肽和抗菌因子牢固镶嵌于保鲜膜表面，增加了保鲜膜的抑菌性能。此外本发明还具有优异的透明性、自粘性，以及优良的机械性能。采用本发明的环保保鲜膜，可以在大大降低生产成本的同时保持薄膜本身的高强度，其拉伸强度、断裂伸长率、摩擦系数、透光率均符合国家标准，同时还具有良好的食品包装抗菌保鲜性能。
实施例2
一种环保保鲜膜，所述环保保鲜膜包括以下按重量份计的原料：
SEBS树脂120份，
聚乳酸40份，
抗氧化剂1.5份，
抗菌剂1.2份，
增韧剂1.5份，
敏化剂2.5份。
所述SEBS树脂选自高分子量SEBS、和低分子量SEBS中的一种或两种。
所述抗氧化剂为丁基羟基茴香醚。
所述增韧剂为丙烯酸酯类聚合物。
所述敏化剂为安息香二甲醚。
所述抗菌剂选自氧化银、载银磷酸锆、亚甲基双硫氰酸酯和甲壳素中的一种或几种。
一种环保保鲜膜的生产工艺，包括以下步骤：
（1）按所需重量份准备好各项原料：SEBS树脂120份，聚乳酸40份，抗氧化剂1.5份，抗菌剂1.2份，增韧剂1.5份和敏化剂2.5份；
（2）将所述各项原料混合后加热熔化挤出，在塑料挤出吹膜机中挤出成型的保鲜薄膜；
（3）将步骤（2）中得到的薄膜按照不同尺寸的产品规格进行卷膜切割，检查合格后即得到所述环保保鲜膜。
本发明采用SEBS树脂、聚乳酸、抗氧化剂、抗菌剂、增韧剂和敏化剂为原料，在生产过程中不使用二辛酯等增塑剂，不含卤素元素，是一种卫生、安全环保的新型包装材料，使用敏化剂可以使产品更加的容易分解，且分解后的产物无污染，具有绿色环保的性能。在聚乳酸中加入增韧剂，二者可保持材料的强度和延展性能；抗菌剂中的抗菌因子溶于聚乳酸和SEBS树脂中，使乳酸链球菌肽和抗菌因子牢固镶嵌于保鲜膜表面，增加了保鲜膜的抑菌性能。此外本发明还具有优异的透明性、自粘性，以及优良的机械性能。采用本发明的环保保鲜膜，可以在大大降低生产成本的同时保持薄膜本身的高强度，其拉伸强度、断裂伸长率、摩擦系数、透光率均符合国家标准，同时还具有良好的食品包装抗菌保鲜性能。
实施例3
一种环保保鲜膜，所述环保保鲜膜包括以下按重量份计的原料：
SEBS树脂102份，
聚乳酸30份，
抗氧化剂1份，
抗菌剂0.9份，
增韧剂1份，
敏化剂2份。
所述SEBS树脂选自高分子量SEBS、和低分子量SEBS中的一种或两种。
所述抗氧化剂为丁基羟基茴香醚。
所述增韧剂为丙烯酸酯类聚合物。
所述敏化剂为安息香二甲醚。
所述抗菌剂选自氧化银、载银磷酸锆、亚甲基双硫氰酸酯和甲壳素中的一种或几种。
一种环保保鲜膜的生产工艺，包括以下步骤：
（1）按所需重量份准备好各项原料：SEBS树脂102份，聚乳酸30份，抗氧化剂1份，抗菌剂0.9份，增韧剂1份，敏化剂2份；
（2）将所述各项原料混合后加热熔化挤出，在塑料挤出吹膜机中挤出成型的保鲜薄膜；
（3）将步骤（2）中得到的薄膜按照不同尺寸的产品规格进行卷膜切割，检查合格后即得到所述环保保鲜膜。
本发明采用SEBS树脂、聚乳酸、抗氧化剂、抗菌剂、增韧剂和敏化剂为原料，在生产过程中不使用二辛酯等增塑剂，不含卤素元素，是一种卫生、安全环保的新型包装材料，使用敏化剂可以使产品更加的容易分解，且分解后的产物无污染，具有绿色环保的性能。在聚乳酸中加入增韧剂，二者可保持材料的强度和延展性能；抗菌剂中的抗菌因子溶于聚乳酸和SEBS树脂中，使乳酸链球菌肽和抗菌因子牢固镶嵌于保鲜膜表面，增加了保鲜膜的抑菌性能。此外本发明还具有优异的透明性、自粘性，以及优良的机械性能。采用本发明的环保保鲜膜，可以在大大降低生产成本的同时保持薄膜本身的高强度，其拉伸强度、断裂伸长率、摩擦系数、透光率均符合国家标准，同时还具有良好的食品包装抗菌保鲜性能。
以上仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (8)

1.一种环保保鲜膜，其特征在于，所述环保保鲜膜包括以下按重量份计的原料：
SEBS树脂80-120份，
聚乳酸20-40份，
抗氧化剂0.5-1.5份，
抗菌剂0.6-1.2份，
增韧剂0.5-1.5份，
敏化剂1.5-2.5份。
2.根据权利要求1所述的一种环保保鲜膜，其特征在于，所述环保保鲜膜包括以下按重量份计的原料：
SEBS树脂102份，
聚乳酸30份，
抗氧化剂1份，
抗菌剂0.9份，
增韧剂1份，
敏化剂2份。
3.根据权利要求1所述的一种环保保鲜膜，其特征在于，所述SEBS树脂选自高分子量SEBS、和低分子量SEBS中的一种或两种。
4.根据权利要求1所述的一种环保保鲜膜，其特征在于，所述抗氧化剂为丁基羟基茴香醚。
5.根据权利要求1所述的一种环保保鲜膜，其特征在于，所述增韧剂为丙烯酸酯类聚合物。
6.根据权利要求1所述的一种环保保鲜膜，其特征在于，所述敏化剂为安息香二甲醚。
7.根据权利要求1所述的一种环保保鲜膜，其特征在于，所述抗菌剂选自氧化银、载银磷酸锆、亚甲基双硫氰酸酯和甲壳素中的一种或几种。
8.一种如权利要求1-7任意一项所述的环保保鲜膜的生产工艺，其特征在于，包括以下步骤：
（1）按所需重量份准备好各项原料：SEBS树脂80-120份，聚乳酸20-40份，抗氧化剂0.5-1.5份，抗菌剂0.6-1.2份，增韧剂0.5-1.5份和敏化剂1.5-2.5份；
（2）将所述各项原料混合后加热熔化挤出，在塑料挤出吹膜机中挤出成型的保鲜薄膜；
（3）将步骤（2）中得到的薄膜按照不同尺寸的产品规格进行卷膜切割，检查合格后即得到所述环保保鲜膜。
CN201710583960.9A 2017-07-18 2017-07-18 一种环保保鲜膜及其生产工艺 Withdrawn CN107216595A (zh)