CN103289202A - 一种抑菌阻燃聚丙烯双向拉伸薄膜 - Google Patents
一种抑菌阻燃聚丙烯双向拉伸薄膜 Download PDFInfo
- Publication number
- CN103289202A CN103289202A CN2013102504395A CN201310250439A CN103289202A CN 103289202 A CN103289202 A CN 103289202A CN 2013102504395 A CN2013102504395 A CN 2013102504395A CN 201310250439 A CN201310250439 A CN 201310250439A CN 103289202 A CN103289202 A CN 103289202A
- Authority
- CN
- China
- Prior art keywords
- parts
- polypropylene
- fire retardation
- antibacterial
- biaxial tension
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明涉及一种抑菌阻燃聚丙烯双向拉伸薄膜，属于高分子材料技术领域，其特征在于包括按照重量份数计的如下原料：聚丙烯100~120份、氮系阻燃剂10~15份、乙氧基化烷基酸胺1~2份、抗氧剂10760.2~0.5份、茶树油0.1~0.5份、抗粘连剂2~6份、紫外线吸收剂UV-5310.5~1份、六甲基磷酰三胺0.2~0.5份。本发明产品在保持传统BOPP薄膜优点的基础上，不仅具有良好的阻燃、抑菌功效，还具有抗紫外线功能，可防止内包装物因紫外线照射而降解、褪色。
Description
技术领域
本发明属于高分子材料技术领域，具体涉及一种抑菌阻燃聚丙烯双向拉伸薄膜。
背景技术
双向拉伸聚丙烯薄膜（BOPP）一般为多层共济薄膜，是由聚丙烯颗粒经共挤形成片材后，再经纵横两个方向的拉伸而制得的。由于拉伸分子定向，所以这种薄膜的物理稳定性、机械强度、气密性较好，透明度和光泽度较高，坚韧耐磨，是目前应用最广泛的印刷薄膜，广泛应用于食品、糖果、香烟、茶叶、果汁、牛奶、纺织品等的包装，有“包装皇后”的美称。
但是，市场上传统的双向拉伸聚丙烯薄膜阻燃性能差，且功能较为单一，不具有抑菌、抗紫外线等功能，虽然有些添加因此如何克服现有技术的不足是目前亟需解决的问题。
发明内容
本发明的目的是为了解决现有技术的不足，提供一种抑菌阻燃聚丙烯双向拉伸薄膜，本发明产品不仅具有良好的抑菌、阻燃功能，且可防止内包装物因紫外线照射而降解、褪色。
本发明采用的技术方案如下：
一种抑菌阻燃聚丙烯双向拉伸薄膜，其特征在于包括按照重量份数计的如下原料：聚丙烯100~120份、氮系阻燃剂10~15份、乙氧基化烷基酸胺1~2份、抗氧剂1076 0.2~0.5份、茶树油0.1~0.5份、抗粘连剂2~6份、紫外线吸收剂UV-531 0.5~1份、六甲基磷酰三胺0.2~0.5份。
进一步，其优化方案为所述的氮系阻燃剂为氰尿酸三聚氰胺盐。
进一步，其优化方案为所述的抗粘连剂为聚甲基丙烯酸甲酯或二氧化硅。
本发明的制备方法：按照上述重量份数称取各原料，将其放入低速搅拌机中搅拌均匀，然后将混合物料通过双螺杆挤出机熔融共混，挤出造粒，干燥，然后流延成片材，最后利用双向拉伸设备将片材拉伸成BOPP薄膜，即本发明产品。
本发明与现有技术相比，其有益效果为：（1）本发明产品在保持传统BOPP薄膜优点的基础上，具有抗紫外线功能，可防止内包装物因紫外线照射而降解、褪色；（2）采用无卤阻燃剂，使得本发明产品拥有较好的阻燃效果，同时对环境友好，无污染；（3）添加了天然抑菌剂——茶树油，使得本发明产品具有一定的抑菌性能，能有效地抑制金黄色葡萄球菌、大肠杆菌等的生长。
具体实施例
下面结合实施例对本发明作进一步的详细描述。
实施例1
一种抑菌阻燃聚丙烯双向拉伸薄膜，包括按照重量份数计的如下原料：聚丙烯100份、氰尿酸三聚氰胺盐10份、乙氧基化烷基酸胺1份、抗氧剂1076 0.2、茶树油0.1份、聚甲基丙烯酸甲酯2份、紫外线吸收剂UV-531 0.5份、六甲基磷酰三胺0.2份。
实施例2
一种抑菌阻燃聚丙烯双向拉伸薄膜，包括按照重量份数计的如下原料：聚丙烯120份、氰尿酸三聚氰胺盐15份、乙氧基化烷基酸胺2份、抗氧剂1076 0.5份、茶树油0.5份、二氧化硅6份、紫外线吸收剂UV-531 1份、六甲基磷酰三胺0.5份。
实施例3
一种抑菌阻燃聚丙烯双向拉伸薄膜，包括按照重量份数计的如下原料：聚丙烯110份、氰尿酸三聚氰胺盐13份、乙氧基化烷基酸胺1.5份、抗氧剂1076 0.3份、茶树油0.3份、聚甲基丙烯酸甲酯4份、紫外线吸收剂UV-531 0.75份、六甲基磷酰三胺0.44份。
对本实施例产品的抗菌性能进行测试：
采用常规微生物杀菌效果检测，其杀菌力结果为：金黄色葡萄球菌97%，大肠杆菌96%，白色念珠菌96%。
并对本实施例进行性能测试，其结果如表1所示。
表1 实施例3产品性能测试
| 项目 | 数据结果 |
| 拉伸强度（MPa） | 16.56 |
| 撕裂强度（kN/m） | 29.24 |
| 断裂伸长率（%） | 232.5 |
| 氧指数（%） | 28.3 |
| 垂直燃烧（厚度0.2mm） | VTM-2 |
Claims (3)
1.一种抑菌阻燃聚丙烯双向拉伸薄膜，其特征在于包括按照重量份数计的如下原料：聚丙烯100~120份、氮系阻燃剂10~15份、乙氧基化烷基酸胺1~2份、抗氧剂1076 0.2~0.5份、茶树油0.1~0.5份、抗粘连剂2~6份、紫外线吸收剂UV-531 0.5~1份、六甲基磷酰三胺0.2~0.5份。
2.根据权利要求1所述的抑菌阻燃聚丙烯双向拉伸薄膜，其特征在于所述的氮系阻燃剂为氰尿酸三聚氰胺盐。
3.根据权利要求1所述的抑菌阻燃聚丙烯双向拉伸薄膜，其特征在于所述的抗粘连剂为聚甲基丙烯酸甲酯或二氧化硅。