CN106733559A - A kind of oak furniture is waxed method - Google Patents

A kind of oak furniture is waxed method Download PDF

Info

Publication number
CN106733559A
CN106733559A CN201611106966.9A CN201611106966A CN106733559A CN 106733559 A CN106733559 A CN 106733559A CN 201611106966 A CN201611106966 A CN 201611106966A CN 106733559 A CN106733559 A CN 106733559A
Authority
CN
China
Prior art keywords
parts
waxing
furniture
wax
oak
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611106966.9A
Other languages
Chinese (zh)
Inventor
刘伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FUYANG WEIYE FURNITURE Co Ltd
Original Assignee
FUYANG WEIYE FURNITURE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FUYANG WEIYE FURNITURE Co Ltd filed Critical FUYANG WEIYE FURNITURE Co Ltd
Priority to CN201611106966.9A priority Critical patent/CN106733559A/en
Publication of CN106733559A publication Critical patent/CN106733559A/en
Pending legal-status Critical Current

Abstract

The present invention discloses a kind of oak furniture and waxes method, including following operating procedure：（1）Liquid before waxing uniformly is sprayed to the furniture surface after polishing, usage amount is 150 180ml/m；（2）Beeswax is melted, 0.06 0.08 times of additives of weight of its weight are added thereto to, stirred；（3）Mixing beeswax is coated in oak furniture surface, the amount of waxing is 30 50g/m2, the wax time is played for 4 5min；（4）Surface is toasted using 60 65 DEG C of baking temperatures 20 30 seconds, and wax is smeared uniform, cooled down afterwards, then again wipe only the floating wax in furniture top layer, constantly smear wiping polishing, completion of waxing.The technology of waxing provided using the present invention, clearly substantially, hardness is good, and water resistance is superior for the bright clean, grain of wood in furniture top layer after causing to process.

Description

A kind of oak furniture is waxed method
Technical field
The invention belongs to oak furniture manufacture field, and in particular to a kind of oak furniture is waxed method.
Background technology
The technology of waxing is a kind of trailing that Chinese Ming-style furniture of hardwood carries out wood surface treatment, can not only be represented well The graceful texture of timber, and layer protecting film is formd in wood surface, to prevent external environment to the detrimental effect of timber. As time goes by, this layer of diaphragm due to constantly being aoxidized by air, stroke and the rag of staff the factor such as wipe Influence, occur in that surface, corner angle and sideline of furniture etc. a kind of natural, bright, gentle such as beautiful configuration of surface, I.e. " bag slurry ", produces the aesthetic feeling of " naturally going carve, Graceful lotus ".Oak sapwood is soft, therefore its water proofing property is poor, uses Conventional method of waxing, cannot still change the oak furniture poor problem of water proofing property in use.
The content of the invention
In order to solve the deficiencies in the prior art, the present invention provides a kind of method of waxing for improving oak furniture water resistance.
The present invention is achieved by the following technical solutions.
A kind of oak furniture is waxed method, including following operating procedure：
（1）Liquid before waxing uniformly is sprayed to the furniture surface after polishing, usage amount is 150-180ml/m2, wherein liquid before waxing It is made up of the component of following weight portion：19-21 parts of citric acid disodium salt times semihydrate, sodium trifluoroacetate 10-15 parts, water 100- 120 parts；
（2）Beeswax is melted, the additive that 0.06-0.08 times of its weight is weighed is added thereto to, stirred, wherein additive by The component of following weight portion is made：Absolute ethyl alcohol 20-30 parts, rosin acid 8-10 parts, 12-16 parts of quinoline -5- alcohol, N- acyl group paddy 13-15 parts, fanesol 6-9 parts, potassium stearate 8-10 parts of propylhomoserin sodium；
（3）Mixing beeswax is coated in oak furniture surface, the amount of waxing is 30-50g/m2, the wax time is played for 4-5min；
（4）Toasted surface 20-30 seconds using 60-65 DEG C of baking temperature, and wax is smeared uniform, cooled down afterwards, then again will The floating wax in furniture top layer is wiped only, constantly smears wiping polishing, completion of waxing.
Specifically, above-mentioned steps（1）In wax before liquid temperature for 40-45 DEG C, spray before waxing after liquid 30-40min, Waxed again.
Specifically, above-mentioned steps（2）In fanesol effective content be 99%, density is 0.89g/cm3。
Technical scheme more than, the beneficial effects of the invention are as follows：
Using the technology of waxing of present invention offer, can cause that the bright clean, grain of wood in the furniture top layer after processing is clearly obvious, Hardness is good, and water resistance is superior.Wherein, citric acid disodium salt times semihydrate, the sodium trifluoroacetate collaboration before waxing in liquid are made With the pest-resistant performance of anti-corrosion of oak can be improved, moreover it is possible to increase adsorption capacity of the oak to beeswax, and then improve the wear-resisting of furniture Property and water resistance；Rosin acid, potassium stearate and N- acyl glutamic acids sodium synergy, can improve the wooden structures of oak, carry The hardness of oak is risen, and then increases the water resistance of oak；Fanesol and quinoline -5- alcohol act synergistically, and can effectively be lifted The glossiness of furniture surface, greatly improves the degree of viewing and admiring of furniture after waxing.
Specific embodiment
Following examples are used to illustrate the present invention, but can not be used for limiting the scope of the present invention.The reality used in embodiment The condition of applying can be for further adjustments according to the condition of producer, and unaccounted implementation condition is usually conventional laboratory conditions.
Embodiment 1
A kind of oak furniture is waxed method, including following operating procedure：
（1）Liquid before waxing uniformly is sprayed to the furniture surface after polishing, usage amount is 150ml/m2, wherein before waxing liquid by with The component of lower weight portion is made：19 parts of citric acid disodium salt times semihydrate, 10 parts of sodium trifluoroacetate, 100 parts of water；
（2）Beeswax is melted, 0.06 times of additive of weight of its weight is added thereto to, stirred, wherein additive is by following The component of weight portion is made：20 parts of absolute ethyl alcohol, 8 parts of rosin acid, 12 parts of quinoline -5- alcohol, 13 parts of N- acyl glutamic acids sodium, gold 6 parts of silk tree alcohol, 8 parts of potassium stearate；
（3）Mixing beeswax is coated in oak furniture surface, the amount of waxing is 30g/m2, the wax time is played for 4min；
（4）Surface is toasted using 60 DEG C of baking temperatures 20 seconds, and wax is smeared uniform, cool down afterwards, then again by furniture table The floating wax of layer is wiped only, constantly smears wiping polishing, completion of waxing.
Specifically, above-mentioned steps（1）In wax before liquid temperature for 40 DEG C, spray before waxing after liquid 30min, then carry out Waxing.
Specifically, above-mentioned steps（2）In fanesol effective content be 99%, density is 0.89g/cm3。
Embodiment 2
A kind of oak furniture is waxed method, including following operating procedure：
（1）Liquid before waxing uniformly is sprayed to the furniture surface after polishing, usage amount is 170ml/m2, wherein before waxing liquid by with The component of lower weight portion is made：20 parts of citric acid disodium salt times semihydrate, 13 parts of sodium trifluoroacetate, 110 parts of water；
（2）Beeswax is melted, 0.07 times of additive of weight of its weight is added thereto to, stirred, wherein additive is by following The component of weight portion is made：25 parts of absolute ethyl alcohol, 9 parts of rosin acid, 14 parts of quinoline -5- alcohol, 14 parts of N- acyl glutamic acids sodium, gold 8 parts of silk tree alcohol, 9 parts of potassium stearate；
（3）Mixing beeswax is coated in oak furniture surface, the amount of waxing is 40g/m2, the wax time is played for 4min；
（4）Surface is toasted using 63 DEG C of baking temperatures 25 seconds, and wax is smeared uniform, cool down afterwards, then again by furniture table The floating wax of layer is wiped only, constantly smears wiping polishing, completion of waxing.
Specifically, above-mentioned steps（1）In wax before liquid temperature for 43 DEG C, spray before waxing after liquid 35min, then carry out Waxing.
Specifically, above-mentioned steps（2）In fanesol effective content be 99%, density is 0.89g/cm3。
Embodiment 3
A kind of oak furniture is waxed method, including following operating procedure：
（1）Liquid before waxing uniformly is sprayed to the furniture surface after polishing, usage amount is 180ml/m2, wherein before waxing liquid by with The component of lower weight portion is made：21 parts of citric acid disodium salt times semihydrate, 15 parts of sodium trifluoroacetate, 120 parts of water；
（2）Beeswax is melted, 0.08 times of additive of weight of its weight is added thereto to, stirred, wherein additive is by following The component of weight portion is made：30 parts of absolute ethyl alcohol, 10 parts of rosin acid, 16 parts of quinoline -5- alcohol, 15 parts of N- acyl glutamic acids sodium, gold 9 parts of silk tree alcohol, 10 parts of potassium stearate；
（3）Mixing beeswax is coated in oak furniture surface, the amount of waxing is 50g/m2, the wax time is played for 4-5min；
（4）Surface is toasted using 65 DEG C of baking temperatures 30 seconds, and wax is smeared uniform, cool down afterwards, then again by furniture table The floating wax of layer is wiped only, constantly smears wiping polishing, completion of waxing.
Specifically, above-mentioned steps（1）In wax before liquid temperature for 45 DEG C, spray before waxing after liquid 40min, then carry out Waxing.
Specifically, above-mentioned steps（2）In fanesol effective content be 99%, density is 0.89g/cm3。
Oak furniture after being waxed in embodiment and the oak furniture after being waxed using conventional method carry out rough surface Degree, glossiness, wearability, water repellency detection, detection method are as follows：Glossiness detecting instrument selection Tianjin section device new and high technology The KGZ-1B type Portable vancometers of company's production；Wearability detecting instrument is from the production of Shanghai coatings industry mechanical repair plant JM-1 type paint film abrasion instruments, balance yard 1000g that dispels, 2000 turns of revolution of abrasion；Water repellency detection is put into using the test specimen after waxing Hour is soaked in clear water, the thickness difference before and after immersion is measured with electronic digital indicator, difference is smaller to show that deformation is smaller, then water repellent Property is higher.The result of detection is as shown in table 1：
A kind of oak furniture of table 1 is waxed method effect detection
Project Rift grain glossiness/% Abrasion decline thickness/μm Immersion thickness difference/μm
Embodiment 1 48 15 90.12
Embodiment 2 45 10 86.25
Embodiment 3 49 12 85.69
Comparative example 31 80 200.35
As shown in Table 1, the method for waxing for being provided using the present invention, compared with conventional method, glossiness, wear resistance after waxing Energy, water repellency have risen, and are greatly improved the quality of oak furniture.
Certainly, described above is not limitation of the present invention, and the present invention is also not limited to the example above, the art Those of ordinary skill, in essential scope of the invention, the change made, change, addition or replace, should all belong to the present invention Protection domain.

Claims (3)

1. a kind of oak furniture is waxed method, it is characterised in that including following operating procedure：
（1）Liquid before waxing uniformly is sprayed to the furniture surface after polishing, usage amount is 150-180ml/m2, wherein liquid before waxing It is made up of the component of following weight portion：19-21 parts of citric acid disodium salt times semihydrate, sodium trifluoroacetate 10-15 parts, water 100- 120 parts；
（2）Beeswax is melted, the additive that 0.06-0.08 times of its weight is weighed is added thereto to, stirred, wherein additive by The component of following weight portion is made：Absolute ethyl alcohol 20-30 parts, rosin acid 8-10 parts, 12-16 parts of quinoline -5- alcohol, N- acyl group paddy 13-15 parts, fanesol 6-9 parts, potassium stearate 8-10 parts of propylhomoserin sodium；
（3）Mixing beeswax is coated in oak furniture surface, the amount of waxing is 30-50g/m2, the wax time is played for 4-5min；
（4）Toasted surface 20-30 seconds using 60-65 DEG C of baking temperature, and wax is smeared uniform, cooled down afterwards, then again will The floating wax in furniture top layer is wiped only, constantly smears wiping polishing, completion of waxing.
2. a kind of oak furniture according to claim 1 is waxed method, it is characterised in that step（1）In wax before The temperature of liquid is 40-45 DEG C, is sprayed before waxing after liquid 30-40min, then waxed.
3. a kind of oak furniture according to claim 1 is waxed method, it is characterised in that step（2）In Acacia The effective content of alcohol is 99%, and density is 0.89g/cm3。
CN201611106966.9A 2016-12-06 2016-12-06 A kind of oak furniture is waxed method Pending CN106733559A (en)