CN104559555A - Method for preparing boiling-resistant waterborne acrylic paint - Google Patents
Method for preparing boiling-resistant waterborne acrylic paint Download PDFInfo
- Publication number
- CN104559555A CN104559555A CN201410702331.XA CN201410702331A CN104559555A CN 104559555 A CN104559555 A CN 104559555A CN 201410702331 A CN201410702331 A CN 201410702331A CN 104559555 A CN104559555 A CN 104559555A
- Authority
- CN
- China
- Prior art keywords
- water
- acrylic paint
- paint
- caused
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a method for preparing boiling-resistant waterborne acrylic paint. The method comprises the following steps of selecting 36% of waterborne acrylic resin, 12% of waterborne amino resin, 2% of modified epoxy resin, 15% of 99% ethanol, 10% of isopropanol, 3% of a silane coupling agent and 22% of water; sequentially mixing the above materials, spraying the mixture on a glass bottle and at a constant temperature of 180 DEG C, baking for 20 minutes. The acrylic paint has the beneficial effects that the boiling resistance is achieved and after the acrylic paint can be continuously boiled in water of 100 DEG C for 2-3 hours, no any change in appearance is caused; the ethanol resistance is achieved and after the acrylic paint is soaked in white wine of which the alcohol content is 52% for 8 hours, no any change in appearance of the paint is caused; the advantage of high gloss is achieved; and no effect is caused when the acrylic paint is washed with a detergent.
Description
Technical field
The present invention relates to acrylic paint compounding process, particularly relate to a kind of water soluble acrylic acid paint compound method of water boiling resistance.
Background technology
Water soluble acrylic acid paint is formulated primarily of water-borne acrylic resin, water-compatible amino resin, pigment, auxiliary agent, solubility promoter etc., water soluble acrylic acid paint paint film adhesion is good, thermotolerance and weather resistance good.When carrying out japanning use, substrate surface will reach clean, without greasy dirt, dust etc., water soluble acrylic acid paint of the present invention is mainly used in surface treatment and the decorations such as glass, pottery, stainless steel, alloy, five metals metallic substance.
General water soluble acrylic acid paint not water boiling resistance.Although ceramic glaze is smoked by high temperature, inherently high temperature resistant, boiling water poach can be stood, but the manufacture craft of ceramic bottle mouth does not reach accurate standard, bottle sealing is bad, and easily cause wine body seepage to volatilize, therefore ceramic wine bottle day by day declines in the application of wine industry.In addition, when for bottle, makeup body, industry specifies, before dispatching from the factory, bottle all can through soaking 2-4 hour in ethanol (99% concentration) solution.
In addition, during filling yellow wine, the temperature of yellow rice wine is 80 DEG C, and existing spraying yellow rice wine bottle can not steep in the hot water, for a long time because top coat easily comes off on the market.
Therefore, for above situation, need effectively to innovate prior art.
Summary of the invention
For above defect, the invention provides a kind of water boiling resistance, resistance to ethanol, high gloss, washing composition cleaning without the water soluble acrylic acid paint compound method of water boiling resistance of impact, thus solve the deficiencies in the prior art.
For achieving the above object, the present invention is by the following technical solutions:
A water soluble acrylic acid paint compound method for water boiling resistance, setting material requested gross weight is 100%, prepares according to following steps:
(1) choose water-borne acrylic resin 36%;
Water-compatible amino resin 12%;
Modified epoxy 2%;
99% concentration ethanol 15%;
Virahol 10%;
Silane coupling agent 3%;
Water 22%;
(2), to glass wine bottle spraying after above material being mixed successively, under 180 ° of C constant temperatures, toast 20 minutes.
The beneficial effect of the water soluble acrylic acid paint compound method of water boiling resistance of the present invention is:
(1) water boiling resistance, can in 100 ° of C water continuous poach 2-3 hour, appearance is not any change;
(2) resistance to ethanol, unchanged soaking in Chinese liquor 8 hours paint appearances of 52 degree;
(3) there is the advantage of high gloss;
(4) adopt washing composition cleaning without impact.
Embodiment
embodiment 1
The water soluble acrylic acid paint compound method of the water boiling resistance described in the embodiment of the present invention, forms primarily of following steps:
(1) setting material gross weight is 100%, according to following per-cent chosen material:
Water-borne acrylic resin 36%;
Water-compatible amino resin 12%;
Modified epoxy 2%;
99% concentration ethanol 15%;
Virahol 10%;
Silane coupling agent 3%;
Water 22%;
(2), to glass wine bottle spraying after above material being mixed successively, under 180 ° of C constant temperatures, toast 20 minutes.
embodiment 2
The water soluble acrylic acid paint compound method of the water boiling resistance described in the embodiment of the present invention, forms primarily of following steps:
(1) setting material gross weight is 100%, according to following per-cent chosen material:
Water-borne acrylic resin 40%;
Water-compatible amino resin 10%;
Modified epoxy 2%;
99% concentration ethanol 15%;
Virahol 10%;
Silane coupling agent 3%;
Water 20%;
(2), to glass wine bottle spraying after above material being mixed successively, under 180 ° of C constant temperatures, toast 20 minutes.
Above embodiment is the several of the present invention's more preferably embodiment, and the usual change that those skilled in the art carry out within the scope of the technical program and replacing should be included in protection scope of the present invention.
Claims (1)
1. a water soluble acrylic acid paint compound method for water boiling resistance, setting material requested gross weight is 100%, it is characterized in that, prepares according to following steps:
(1) choose water-borne acrylic resin 36%;
Water-compatible amino resin 12%;
Modified epoxy 2%;
99% concentration ethanol 15%;
Virahol 10%;
Silane coupling agent 3%;
Water 22%;
(2), to glass wine bottle spraying after above material being mixed successively, under 180 ° of C constant temperatures, toast 20 minutes.