CN105583131A - Coating surface treatment process for frosted color-changing mug - Google Patents
Coating surface treatment process for frosted color-changing mug Download PDFInfo
- Publication number
- CN105583131A CN105583131A CN201511034304.0A CN201511034304A CN105583131A CN 105583131 A CN105583131 A CN 105583131A CN 201511034304 A CN201511034304 A CN 201511034304A CN 105583131 A CN105583131 A CN 105583131A
- Authority
- CN
- China
- Prior art keywords
- cup
- coating
- treatment process
- surface treatment
- frosted
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a coating surface treatment process for a frosted color-changing mug. The coating surface treatment process specifically comprises the following steps of 1, cleaning; 2, baking; 3, inspecting; 4, feeding; 5 coating blending; 6, dust removing; 7, spraying; and 8, baking. According to the coating surface treatment process for the frosted color-changing mug, conditions of the coating treatment process, coating formulas and the coating thickness are adjusted, so that a frosted coating of the frosted mug has excellent bonding capacity and adhesive capacity.
Description
Technical field
The present invention relates to glassware manufacture field, more particularly, relate to a kind of frosted variable colorThe coating surface treatment process of cup.
Background technology
Ground glass cup is again frosted glass, dark glass, sprays one deck coating on common cupObtain, due to its rough surface, make light produce diffuse reflection, printing opacity and not having an X-rayed, canMake cup light soft, not dazzling, and common cup can seem especially dazzling through shining upon.The bottom of frosted material can increase the roughness of contact area, and increasing friction force can ensure millStablizing of sand cup, can avoid the effect of sliding.
But traditional coating surface frosted finish effect is not obvious, feel is coarse, has particle to appear in one's mindSense, baking is that coating easily comes off, because the degree of adhesion of coating and poor adhesive force.
Summary of the invention
The technical problem to be solved in the present invention is, for the above-mentioned defect of prior art, providesA kind of coating surface treatment process of frosted color-changeable cup.
The technical solution adopted for the present invention to solve the technical problems is: a kind of frosted variable color is providedThe coating surface treatment process of cup, specifically comprises the steps:
(1) clean: adopt ultrasonic cleaning instrument to carry out ultrasonic cleaning by selecting qualified cup;
(2) baking: the cup that step (1) is cleaned up is put into oven, by cup tableFace moisture is dried;
(3) inspection: the cleannes of the cup that checking procedure (2) obtains, ensure cup's surfaceSmooth, there is no impurity, meet the standard of coating;
(4) upper part: the cup that step (3) is up to the standards hangs on fixture, waits to be sprayed;
(5) adjust coating: the coating configuring is mixed, then add dimethylbenzene to adjust rare,Obtain spray coating liquor;
(6) dedusting: the spray coating liquor mixing up in step (5) is stirred, pour oil injecting groove intoIn; Then oil spout room temperature is adjusted into 20-28 DEG C, humidity 35-50%, uses electrostatic gunCup's surface in step (4) and paint spray booth are carried out to dust removal process;
(7) spraying: the spray coating liquor mixing up is evenly sprayed to cup's surface, there is frosted and be coated withThe cup of layer;
(8) baking: the qualified cup of spraying in step (7) is put into tunnel oven and dryRoasting, guarantee that coating is completely curing.
The coating surface treatment process of frosted color-changeable cup of the present invention, wherein, described step(1) cup is glass or ceramic cup.
The coating surface treatment process of frosted color-changeable cup of the present invention, wherein, step (1)The condition of middle ultrasonic cleaning is 1000W Ultrasonic Cleaning 3-5 minute.
The coating surface treatment process of frosted color-changeable cup of the present invention, wherein, step (2)In the condition of drying be 150-180 DEG C, baking 10-20 minute.
The coating surface treatment process of frosted color-changeable cup of the present invention, wherein, step (5)Described in coating formed by the component of following percetage by weight: acrylate 25-65%, variable colorPowder 3-5%, flatting silica 6-10%, frosting powder 5-25%, curing agent 3-6%; Described acrylateWith the weight ratio of dimethylbenzene be (2-4): 1.
The coating surface treatment process of frosted color-changeable cup of the present invention, wherein, step (5)In also comprise that the spray coating liquor to mixing up carries out the step of viscosity test, this viscosity test adopts examines graceCup test, selects and examines grace cup No. 2, and the spray coating liquor mixing up is from examining the time of flowing out completely in grace cupFor 15-17 second.
The coating surface treatment process of frosted color-changeable cup of the present invention, wherein, step (7)Middle spraying condition is 8 of spray guns, and spray gun translational speed is 1.8-2.2m/min, spray gun pressureFor 0.4-0.6MPa, coating layer thickness is 30-35 μ m.
The coating surface treatment process of frosted color-changeable cup of the present invention, wherein, step (8)Middle baking condition is 170-190 DEG C, baking 40-50 minute.
Implement the coating surface treatment process of frosted color-changeable cup of the present invention, there is the following beneficial effect that hasReally:
The present invention passes through to adjust condition, formulation for coating material and the coating layer thickness of coating treatment process,Make frosted cup frosted coating there is excellent adhesive power and adhesive ability. Concrete passing through at coatingMiddle interpolation frosting powder, the applicable ratio of adjustment frosting powder and coating, solidified coating degree of adhesion and attachedPut forth effort, make coating difficult drop-off. Add a certain proportion of flatting silica simultaneously, promote frosted finish effect,Comfortable feel and attractive in appearance; In addition, by adjust and grope spraying condition and coating layer thickness (thickDegree for 30-35 μ m), can ensure coating difficult drop-off more.
Detailed description of the invention
Below, in conjunction with detailed description of the invention, the present invention is described further:
A coating surface treatment process for frosted color-changeable cup, specifically comprises the steps:
(1) clean: adopt ultrasonic cleaning instrument to carry out ultrasonic cleaning by selecting qualified cup;The condition of ultrasonic cleaning is 1000W Ultrasonic Cleaning 3-5 minute. This cup is glass or potteryPorcelain cup.
(2) baking: the cup that step (1) is cleaned up is put into oven, by cup tableFace moisture is dried; The condition of drying is 150-180 DEG C, baking 10-20 minute.
(3) inspection: the cleannes of the cup that checking procedure (2) obtains, ensure cup's surfaceSmooth, there is no impurity, meet the standard of coating;
(4) upper part: the cup that step (3) is up to the standards hangs on fixture, waits to be sprayed;
(5) adjust coating: the coating configuring is mixed, then add dimethylbenzene to adjust rare,Obtain spray coating liquor, and spray coating liquor is carried out to viscosity test; Described coating is by following percetage by weightComponent composition: acrylate 25-65%, variable color powder 3-5%, flatting silica 6-10%, frostedPowder 5-25%, curing agent 3-6%; It is conventional that raw material involved in the present invention is this area, all fromThe raw material of buying in raw materials market. The weight ratio of described acrylate and dimethylbenzene is (2-4):1. Viscosity test adopts examines the test of grace cup, selects and examines grace cup No. 2, and the spray coating liquor mixing up is from examiningThe time of flowing out completely in grace cup is 15-17 second, is preferably 16 seconds. Viscosity test methodStep: adopt measuring cup instrument to examine grace cup, the coating of fixed amount by measuring cup at a fixed time inFlow out completely, degree of adhesion is up to standard.
(6) dedusting: the spray coating liquor mixing up in step (5) is stirred, pour oil injecting groove intoIn; Then oil spout room temperature is adjusted into 20-28 DEG C, humidity 35-50%, uses electrostatic gunCup's surface in step (4) and paint spray booth are carried out to dust removal process;
(7) spraying: the spray coating liquor mixing up is evenly sprayed to cup's surface, there is frosted and be coated withThe cup of layer; Spraying condition is 8 of spray guns, and spray gun translational speed is 1.8-2.2m/min,Spray gun pressure is 0.4-0.6MPa, and coating layer thickness is 30-35 μ m.
(8) baking: the qualified cup of spraying in step (7) is put into tunnel oven and dryRoasting, guarantee that coating is completely curing. Baking condition is 170-190 DEG C, baking 40-50 minute.
Embodiment 1
A coating surface treatment process for frosted color-changeable cup, specifically comprises the steps:
(1) clean: adopt ultrasonic cleaning instrument to carry out ultrasonic cleaning by selecting qualified glass;The condition of ultrasonic cleaning is 1000W Ultrasonic Cleaning 3-5 minute.
(2) baking: the glass that step (1) is cleaned up is put into oven, by glassCup surface moisture is dried; The condition of drying is 150-180 DEG C, baking 10-20 minute.
(3) inspection: the cleannes of the glass that checking procedure (2) obtains, ensure glassSmooth surface, there is no impurity, meet the standard of coating;
(4) upper part: the glass that step (3) is up to the standards hangs on fixture, waits to be paintedBe coated with;
(5) adjust coating: the coating configuring is mixed, then add dimethylbenzene to adjust rare,Obtain spray coating liquor, and spray coating liquor is carried out to viscosity test; Described coating is by following percetage by weightComponent composition: acrylate 55%, variable color powder 5%, flatting silica 10%, frosting powder 25%,Curing agent 5%; The weight ratio of described acrylate and dimethylbenzene is 2:1. Viscosity test adoptsExamine grace cup test, select and examine grace cup No. 2, the spray coating liquor mixing up flows out in grace cup completely from examiningTime is 15 seconds.
(6) dedusting: the spray coating liquor mixing up in step (5) is stirred, pour oil injecting groove intoIn; Then oil spout room temperature is adjusted into 20-28 DEG C, humidity 35-50%, uses electrostatic gunGlass surface and paint spray booth in step (4) are carried out to dust removal process;
(7) spraying: the spray coating liquor mixing up is evenly sprayed to glass surface, there is frostedThe glass of coating; Spraying condition is 8 of spray guns, and spray gun translational speed is 1.8-2.2m/min,Spray gun pressure is 0.4-0.6MPa, and coating layer thickness is 30 μ m.
(8) baking: the qualified glass of spraying in step (7) is put into tunnel ovenBaking, guarantees that coating is completely curing. Baking condition is 170 DEG C, toasts 40 minutes.
Embodiment 2
A coating surface treatment process for frosted color-changeable cup, specifically comprises the steps:
(1) clean: adopt ultrasonic cleaning instrument to carry out ultrasonic cleaning by selecting qualified ceramic cup;The condition of ultrasonic cleaning is 1000W Ultrasonic Cleaning 3-5 minute.
(2) baking: the ceramic cup that step (1) is cleaned up is put into oven, by potteryCup surface moisture is dried; The condition of drying is 150-180 DEG C, baking 10-20 minute.
(3) inspection: the cleannes of the ceramic cup that checking procedure (2) obtains, ensure ceramic cupSmooth surface, there is no impurity, meet the standard of coating;
(4) upper part: the ceramic cup that step (3) is up to the standards hangs on fixture, waits to be paintedBe coated with;
(5) adjust coating: the coating configuring is mixed, then add dimethylbenzene to adjust rare,Obtain spray coating liquor, and spray coating liquor is carried out to viscosity test; Described coating is by following percetage by weightComponent composition: acrylate 65%, variable color powder 3%, flatting silica 6%, frosting powder 20%, solidAgent 6%; The weight ratio of described acrylate and dimethylbenzene is 3:1. Viscosity test adopts and examinesGrace cup test, selects and examines grace cup No. 2, the spray coating liquor mixing up from examine in grace cup, flow out completely timeBetween be 16 seconds.
(6) dedusting: the spray coating liquor mixing up in step (5) is stirred, pour oil injecting groove intoIn; Then oil spout room temperature is adjusted into 20-28 DEG C, humidity 35-50%, uses electrostatic gunCeramic cup surface and paint spray booth in step (4) are carried out to dust removal process;
(7) spraying: the spray coating liquor mixing up is evenly sprayed to ceramic cup surface, there is frostedThe ceramic cup of coating; Spraying condition is 8 of spray guns, and spray gun translational speed is 1.8-2.2m/min,Spray gun pressure is 0.4-0.6MPa, and coating layer thickness is 30 μ m.
(8) baking: the qualified ceramic cup of spraying in step (7) is put into tunnel ovenBaking, guarantees that coating is completely curing. Baking condition is 180 DEG C, toasts 45 minutes.
Embodiment 3
A coating surface treatment process for frosted color-changeable cup, specifically comprises the steps:
(1) clean: adopt ultrasonic cleaning instrument to carry out ultrasonic cleaning by selecting qualified ceramic cup;The condition of ultrasonic cleaning is 1000W Ultrasonic Cleaning 3-5 minute.
(2) baking: the ceramic cup that step (1) is cleaned up is put into oven, by potteryCup surface moisture is dried; The condition of drying is 150-180 DEG C, baking 10-20 minute.
(3) inspection: the cleannes of the ceramic cup that checking procedure (2) obtains, ensure ceramic cupSmooth surface, there is no impurity, meet the standard of coating;
(4) upper part: the ceramic cup that step (3) is up to the standards hangs on fixture, waits to be paintedBe coated with;
(5) adjust coating: the coating configuring is mixed, then add dimethylbenzene to adjust rare,Obtain spray coating liquor, and spray coating liquor is carried out to viscosity test; Described coating is by following parts by weightComponent composition: acrylate 54%, variable color powder 5%, flatting silica 10%, frosting powder 25%, solidAgent 6%; The weight ratio of described acrylate and dimethylbenzene is 4:1. Viscosity test adopts and examinesGrace cup test, selects and examines grace cup No. 2, the spray coating liquor mixing up from examine in grace cup, flow out completely timeBetween be 17 seconds.
(6) dedusting: the spray coating liquor mixing up in step (5) is stirred, pour oil injecting groove intoIn; Then oil spout room temperature is adjusted into 20-28 DEG C, humidity 35-50%, uses electrostatic gunCeramic cup surface and paint spray booth in step (4) are carried out to dust removal process;
(7) spraying: the spray coating liquor mixing up is evenly sprayed to ceramic cup surface, there is frostedThe ceramic cup of coating; Spraying condition is 8 of spray guns, and spray gun translational speed is 1.8-2.2m/min,Spray gun pressure is 0.4-0.6MPa, and coating layer thickness is 35 μ m.
(8) baking: the qualified ceramic cup of spraying in step (7) is put into tunnel ovenBaking, guarantees that coating is completely curing. Baking condition is 190 DEG C, toasts 50 minutes.
Firmness, the adhesive force of the frosted color-changeable cup of below, being prepared by embodiment 1-3 are examinedSurvey:
To spraying the product surface inspection after qualified, to the cup being up to the standards with every halfImpression processing is carried out in hour one of selective examination, and the effect of impression is to detect the thickness of coating, firmlyDegree, whether adhesive force up to standard, and whether E Wendu is up to standard in baking, and whether coating is completely curing. FalseAs, cup's surface has impression, and overweight coating, if fade in surface, is exactly that coating surface is firmDegree not.
Test shows, the equal energy of firmness, adhesive force of frosted color-changeable cup prepared by embodiment 1-3Reach requirement, preparation technology's of the present invention condition, formulation for coating material and coating layer thickness control are describedSystem is appropriate, makes frosted cup frosted coating have excellent adhesive power and adhesive ability.
To one skilled in the art, can be according to technical scheme described above and structureThink, make other various corresponding changes and deformation, and all these changes and deformationWithin all should belonging to the protection domain of the claims in the present invention.
Claims (8)
1. a coating surface treatment process for frosted color-changeable cup, is characterized in that, specifically bagDraw together following steps:
(1) clean: adopt ultrasonic cleaning instrument to carry out ultrasonic cleaning by selecting qualified cup;
(2) baking: the cup that step (1) is cleaned up is put into oven, by cup tableFace moisture is dried;
(3) inspection: the cleannes of the cup that checking procedure (2) obtains, ensure cup's surfaceSmooth, there is no impurity, meet the standard of coating;
(4) upper part: the cup that step (3) is up to the standards hangs on fixture, waits to be sprayed;
(5) adjust coating: the coating configuring is mixed, then add dimethylbenzene to adjust rare,Obtain spray coating liquor;
(6) dedusting: the spray coating liquor mixing up in step (5) is stirred, pour oil injecting groove intoIn; Then oil spout room temperature is adjusted into 20-28 DEG C, humidity 35-50%, uses electrostatic gunCup's surface in step (4) and paint spray booth are carried out to dust removal process;
(7) spraying: the spray coating liquor mixing up is evenly sprayed to cup's surface, there is frosted and be coated withThe cup of layer;
(8) baking: the qualified cup of spraying in step (7) is put into tunnel oven and dryRoasting, guarantee that coating is completely curing.
2. the coating surface treatment process of frosted color-changeable cup according to claim 1, itsBe characterised in that, described step (1) cup is glass or ceramic cup.
3. the coating surface treatment process of frosted color-changeable cup according to claim 1, itsBe characterised in that, in step (1), the condition of ultrasonic cleaning is that 1000W Ultrasonic Cleaning 3-5 dividesClock.
4. the coating surface treatment process of frosted color-changeable cup according to claim 1, itsBe characterised in that, the condition of drying in step (2) is 150-180 DEG C, baking 10-20 minute.
5. the coating surface treatment process of frosted color-changeable cup according to claim 1, itsBe characterised in that, described in step (5), coating is made up of the component of following percetage by weight: thirdOlefin(e) acid ester 25-65%, variable color powder 3-5%, flatting silica 6-10%, frosting powder 5-25%, curing agent3-6%; The weight ratio of described acrylate and dimethylbenzene is (2-4): 1.
6. the coating surface treatment process of frosted color-changeable cup according to claim 4, itsBe characterised in that, in step (5), also comprise that the spray coating liquor to mixing up carries out the step of viscosity test,This viscosity test adopts examines the test of grace cup, selects and examines grace cup No. 2, and the spray coating liquor mixing up is from examining graceThe time of flowing out completely in cup is 15-17 second.
7. the coating surface treatment process of frosted color-changeable cup according to claim 1, itsBe characterised in that, in step (7), spraying condition is 8 of spray guns, and spray gun translational speed is1.8-2.2m/min, spray gun pressure is 0.4-0.6MPa, coating layer thickness is 30-35 μ m.
8. the coating surface treatment process of frosted color-changeable cup according to claim 1, itsBe characterised in that, in step (8), baking condition is 170-190 DEG C, baking 40-50 minute.