CN102864911A - Solvent-free epoxy colorful artistic floor and preparation method thereof - Google Patents
Solvent-free epoxy colorful artistic floor and preparation method thereof Download PDFInfo
- Publication number
- CN102864911A CN102864911A CN2012103915380A CN201210391538A CN102864911A CN 102864911 A CN102864911 A CN 102864911A CN 2012103915380 A CN2012103915380 A CN 2012103915380A CN 201210391538 A CN201210391538 A CN 201210391538A CN 102864911 A CN102864911 A CN 102864911A
- Authority
- CN
- China
- Prior art keywords
- solvent
- preparation
- terrace
- free epoxy
- artistic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the floor field, and particularly relates to a solvent-free epoxy colorful artistic floor and a preparation method thereof. According to the provided aqueous solvent-free epoxy colorful artistic floor, a colorful artistic effect of natural flowers and grasses is added in floor materials, so that the harmony of human and nature is achieved, and defects of a single color and no artistry of prior epoxy floors are overcome. The solvent-free epoxy colorful artistic floor is simple in technology, convenient to construct, capable of being solidified rapidly in moist environments and not affected by vapor, and has good cohesiveness to moist base material surfaces.
Description
Technical field
The present invention relates to the terrace field, relate in particular to a kind of non-solvent epoxy color floor and preparation method thereof.
Background technology
Traditional solvent based coating and epoxide terrace contain about 50% organic solvent, and namely volatile organic matter (being called for short VOC) is one of important environmental contaminants.Many statistics show that coating industry has become the VOC second row and amplified the family.At present, the industry ground slab material of China mainly adopts the solvent type epoxy floor material, and contains a large amount of volatile organic solvents in the solvent type epoxy floor material, and dicyandiamide solution adopts reactive diluent, and certain toxicity is not only arranged, and cost is also very high; And the solvent type epoxy floor material is constructional difficulties under wet environment, the problems such as aliquation occur easily.In recent years, along with improving constantly of people's environmental consciousness, many countries have promulgated the environmental regulation of restriction VOC (VOC) in succession, such as 66 rules of the U.S., the Law on Environmental Protection that the Chinese government promulgates etc.
Epoxide terrace is a kind of high strength, floor wear-resistant, attractive in appearance, has without seam, and quality is solid, and resistance to chemical reagents is good, and is anticorrosion, and waterproof is dustproof, easy maintenance, the advantage such as maintenance cost is cheap.It is for functional terrace that epoxide terrace begins: wear-resisting as anticorrosion, anti-skidding, develop into general general industry terrace; Except having functional requirement, also has ornamental effect.Obtain at industry ground slab along with improving constantly of people's living standard, now in house decoration, to be applied on the basis of extensive use.People increase the color of epoxide terrace by add color stuffing in the epoxy flooring coating layer, but the defective that still exists of epoxide terrace is at present, and color is single, and pattern is dull, lacks artistry, breaks away from the aesthetic feeling of the Nature.Therefore the Water-borne modification of floor coatings, solvent free and become the inexorable trend of paint industry development near the aesthetic feeling demand of the Nature.
Summary of the invention
In view of above-mentioned the deficiencies in the prior art, the invention provides a kind of water-based non-solvent epoxy color artistic terrace, in floor material, increase the color artistic effect of natural flowers and plants, realized the harmony of man and nature, solved the defective that original epoxide terrace color is single, do not have artistry.
The present invention also provides a kind of preparation method of water-based non-solvent epoxy color artistic terrace, can be under the environment of humidity rapid curing, be not subjected to influence of moisture, by determining rational hardening time, even the substrate surface of humidity is had good caking property equally.
Technical scheme of the present invention is as follows:
A kind of preparation method of water-based non-solvent epoxy color artistic terrace mainly may further comprise the steps
1, base treatment:
Remove ground laitance, earth, laitance and other pollutant, guarantee that ground and end oil adhere to solid.
2, priming paint construction:
With the earth's surface sealing, allow priming paint fully permeate ground, strengthen adhesive power, it is smooth smooth to impel face to be coated with.
In priming paint when construction, stir material in proportion, with roller coating or with the scraping blade blade coating in element, evenly glossy, the coating second time is carried out in inhomogeneous processing.
3, artistic material layer construction:
After prime coat solidified, natural flowers, grass and blade that the drying of some is processed were arranged according to certain pattern and are formed artistic material layer.Used flower, grass and blade etc. have all passed through drying and processing, and water content at utmost keeps original complexion of flower, grass and blade about 10%, can be applied in the epoxy floor material layer again.Its abundance on priming paint is 500g/m
2
4, face is coated with construction:
With deployed solvent-free epoxy self-leveling material on the ground, cover submergence art material layer fully, evenly spread out cloth with trowel, stand cloth number of times must not be too many, in order to avoid a large amount of bubbles and scratch occur.
5, water white transparency varnish construction:
After top coat layer solidifies, deployed water white transparency varnish is coated on the top coat layer.
Wherein said solidification temperature is more than 10 ℃, if environment temperature is higher than 10 degrees centigrade during construction, then constructing at ambient temperature gets final product.
Wherein the component of priming paint is, by weight percentage, and solvent-free epoxy resin 50%, reactive diluent 15%, curing compound 35%.
Wherein the component of finish paint is, by weight percentage, and solvent-free epoxy resin 50%, reactive diluent 5%, color stuffing 19%, auxiliary agent 1%, curing compound 25%.
Wherein the component of water white transparency varnish is, by weight percentage, and solvent-free epoxy resin 50%, reactive diluent 14%, auxiliary agent 1%, curing compound 35%.
Above-mentioned auxiliary agent is defoamer, dispersing agent, levelling agent.
Described no-solvent type epoxy resin can be terrace field aqueous epoxy resins commonly used.
Water-based non-solvent epoxy color artistic terrace of the present invention and preparation method thereof has following useful technique effect:
1) with in the distribution of natural seasoning flowers and plants and the floor material layer, solved the defective that original terrace color is single, do not have artistry.
2) take aqueous epoxy resins as base-material, have the breathing performance, avoided greatly the layer part bubble that produces because of moisture and peeled off.
3) volatile organic solvent of containing benezene does not fire, not quick-fried, can not cause environment pollution, does not have disaster hidden-trouble, and is safe and convenient to use, satisfied current environmental requirement, is conducive to health.
4) technique is simple, easy construction, can be under the environment of humidity rapid curing, not affected by aqueous vapor, even the substrate surface of humidity is had good caking property equally.
The specific embodiment
At first terrace basic unit is polished, with solvent-free epoxy resin 50% by weight percentage, the priming paint that reactive diluent 15% and curing compound 35% is mixed with evenly is coated in the basic unit, after prime coat solidifies, be about 10% natural seasoning flowers and plants in distribution 500g drying water content on every square metre the priming paint, requirement according to the client can be carried out permutation and combination according to certain mode with the natural flowers and plants of drying, form riotous with colour, the artistic pattern of tool, to again solvent-free epoxy resin 50% by weight percentage, reactive diluent 5%, color stuffing 19%, the finish paint of the self-leveling material that auxiliary agent 1% and curing compound 25% is mixed with evenly applies thereon, after finish paint solidifies, to at last solvent-free epoxy resin 50% by weight percentage, reactive diluent 14%, the water white transparency varnish that auxiliary agent 1% and curing compound 35% is mixed with is coated on the finish paint, namely makes water-based non-solvent epoxy color artistic terrace after the curing.
After tested, the key technical indexes of prepared non-solvent epoxy color artistic terrace is as follows:
The key technical indexes of table 1 non-solvent epoxy color artistic terrace
| Surface drying (25 ℃ of h) | ≤4 |
| Do solid work (25 ℃ of h) | ≤24 |
| Adhesion strength (Mpa) | ≥2 |
| Resistance to impact (the 1kg steel ball freely falls from 1 meter eminence) | Paint film is without cracking |
| Compressive strength (Mpa) | ≥70 |
| Rupture strength (Mpa) | ≥6 |
| Abrasion resistance (1000g/1000r) g | ≤0.02 |
| Shore hardness (Mpa) | ≥80 |
| Petrol-resistance (120# gasoline) 30d | Paint film is without significant change |
| Alkali resistance (10%NaOH) 30d | Paint film is without significant change |
| Resistance to salt water (3%NaCl) | Paint film is without significant change |
| Acid resistance (10%HCl) | Paint film is without significant change |
As can be seen from Table 1, the technical indicator of the prepared non-solvent epoxy color artistic terrace of the present invention has all reached acceptance criteria.
Claims (7)
1. the preparation method of a water-based non-solvent epoxy color artistic terrace, it is characterized in that, mainly may further comprise the steps: at first terrace basic unit is polished and apply priming paint, after prime coat solidifies, natural flowers, grass and the blade of on priming paint drying being processed arranged according to certain pattern and formed artistic material layer, again the solvent-free epoxy self-leveling material is coated on the natural flowers and plants and formed finish paint, after top coat layer solidifies, water white transparency varnish on finish paint is coated with treats that varnish solidifies the preparation of namely finishing epoxide terrace at last.
2. preparation method as claimed in claim 1 is characterized in that, described solidification temperature is more than 10 ℃.
3. preparation method as claimed in claim 1 is characterized in that, wherein the component of priming paint is, by weight percentage, and solvent-free epoxy resin 50%, reactive diluent 15%, curing compound 35%.
4. preparation method as claimed in claim 1 is characterized in that, wherein the component of finish paint is, by weight percentage, and solvent-free epoxy resin 50%, reactive diluent 5%, color stuffing 19%, auxiliary agent 1%, curing compound 25%.
5. preparation method as claimed in claim 1 is characterized in that, wherein the component of water white transparency varnish is, by weight percentage, and solvent-free epoxy resin 50%, reactive diluent 14%, auxiliary agent 1%, curing compound 35%.
6. preparation method as claimed in claim 1 is characterized in that, wherein artistic material is natural flowers, grass and the blade after drying is processed, and water content is about 10%, and its abundance on priming paint is 500g/m
2
7. prepared epoxide terrace of preparation method such as the described water-based non-solvent epoxy of claim 1-6 color artistic terrace.