CN108839192A - A kind of casting method of high adhesion force pencil timber - Google Patents
A kind of casting method of high adhesion force pencil timber Download PDFInfo
- Publication number
- CN108839192A CN108839192A CN201810634408.2A CN201810634408A CN108839192A CN 108839192 A CN108839192 A CN 108839192A CN 201810634408 A CN201810634408 A CN 201810634408A CN 108839192 A CN108839192 A CN 108839192A
- Authority
- CN
- China
- Prior art keywords
- parts
- wax
- wood surface
- timber
- high adhesion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses a kind of casting method of high adhesion force pencil timber, including following operating procedure：（1）After the wood surface of excision forming is removed grieshoch, grinding process, in the spraying modified liquid in its surface；（2）Samarium trichloride, lanthanum chloride are added into water, after being mixed evenly, odium stearate is then added thereto, continues stir process, isothermal holding obtains stearic acid mischmetal；（3）After mixing by beeswax, insect wax, paraffin, stearic acid mischmetal, hydrogenation ester gum, tricalcium phosphate, blended wax is made using the method for melt blending；（4）Behind heat gun heat wood surface, then by the blended wax brushing of melting in wood surface, after blended wax surface cure, after having carried out wax, having wiped Lasaxing Oilfield, timber casting is completed.The technical issues of present invention solves pencil obtained blade sticky wax and wax layer fall off during the cutting process, greatly improves the quality of pencil.
Description
Technical field
The invention belongs to pencil timber treatment technology fields, and in particular to a kind of casting of high adhesion force pencil timber
Method.
Background technique
Paraffin is had very long phase of history using oneself in pencil production, and the wax developed on this basis boils work
Skill can improve the dimensional stability of processing material.It in the prior art, is to be placed on paraffin in iron pan to be heated to 80 DEG C or so, so
Timber sequence is placed in pot afterwards, immersion is boiled, and heating temperature gradually rises up to 120 DEG C, and the processing time is generally 24-48h.
Paraffin is impregnated into wood internal during processing, and at the same time, the moisture of wood internal discharges, 120 DEG C for the treatment of conditions
Under, wood internal moisture drains, while wax infiltration is completed, and the whole process that timber seeps wax heat treatment terminates, but after handling
Pencil made from timber, for pencil in cutting, wax is easy viscous knife, and the adhesive force of wax is poor, is also easy to produce the de- of large area
It falls, has seriously affected the quality of pencil.
Summary of the invention
In order to solve the above technical problem, the present invention provides a kind of casting methods of high adhesion force pencil timber.
The present invention is achieved by the following technical solutions.
A kind of casting method of high adhesion force pencil timber, including following operating procedure：
（1）After the wood surface of excision forming is removed grieshoch, grinding process, in the spraying modified liquid in its surface, wherein modification liquid
It is made of the component of following parts by weight：10-14 parts of sodium phytate, 7-12 parts of ammonium pentaborate, 1-3 parts of dipotassium glycyrrhizinate, water 160-200
Part；
（2）By weight, 19-24 parts of samarium trichlorides, 10-15 parts of lanthanum chlorides are added into 105-115 parts of water, are mixed equal
After even, 31-38 parts of odium stearate are then added thereto, after continuing stir process 10-15min, the temperature of mixture is risen to
It after 150-160 DEG C, isothermal holding 3-4 hours, then cools to room temperature, after going upper aqueous layer, obtains stearic acid mischmetal；
（3）By weight, by 36-44 parts of beeswaxs, 10-15 parts of insect waxes, 24-30 parts of paraffin, 8-13 parts of stearic acid mischmetals,
Blended wax is made after mixing, using the method for melt blending in 1-3 parts of hydrogenation ester gums, 0.6-0.9 parts of tricalcium phosphates；
（4）Behind heat gun heat wood surface, the blended wax brushing of melting is then waited until into blended wax table in wood surface
After the solidification of face, after having carried out wax, having wiped Lasaxing Oilfield, timber casting is completed.
Specifically, above-mentioned steps（3）In, the temperature of melt blending is 85-90 DEG C.
Specifically, above-mentioned steps（4）In, wood surface is heated to 91-95 DEG C using heat gun.
Specifically, above-mentioned steps（4）In, the floating wax of wood surface is scalped when playing wax with perching knife, the direction of perching knife shovel wax is
Along Wood surface texture.
Specifically, above-mentioned steps（4）In, wiping wax is carried out to wood surface using byssus, along the suitable of timber when wiping wax
Line direction.
From the above technical scheme, it can be seen that the beneficial effects of the invention are as follows：
A kind of casting method of high adhesion force pencil timber provided by the invention, it is easy to operate, it is environmentally protective, it can effectively mention
The stability of litre material, and timber can be made to keep preferable texture and water resistance, especially overcome pencil obtained
The technical issues of blade sticky wax and wax layer fall off during the cutting process greatly improves the quality of pencil.Wherein, step（1）
In modification liquid, can effectively promote the permeability of timber, and contact of the blended wax in wood surface of molten state can be reduced
Angle promotes blended wax in the permeability of wood internal；The present invention can have by the way that stearic acid mischmetal is added in blended wax
The promotion blended wax of effect promotes the adhesive force after blended wax solidifies in the wettability of wood surface, and it can promote difference
Compatibility between wax stock, so that cere interface is uniform after solidification.
Specific embodiment
The following examples are intended to illustrate the invention but are not intended to limit the scope of the invention.Reality used in the examples
The condition of applying can be for further adjustments according to the condition of producer, and unaccounted implementation condition is usually conventional laboratory conditions.
Embodiment 1
A kind of casting method of high adhesion force pencil timber, including following operating procedure：
（1）After the wood surface of excision forming is removed grieshoch, grinding process, in the spraying modified liquid in its surface, wherein modification liquid
It is made of the component of following parts by weight：10 parts of sodium phytate, 7 parts of ammonium pentaborate, 1 part of dipotassium glycyrrhizinate, 160 parts of water；
（2）By weight, 19 parts of samarium trichlorides, 10 parts of lanthanum chlorides are added into 105 parts of water, after being mixed evenly, then
31 parts of odium stearate are added thereto, after continuing stir process 10min, after the temperature of mixture is risen to 150 DEG C, isothermal holding
It 3 hours, then cools to room temperature, after going upper aqueous layer, obtains stearic acid mischmetal；
（3）By weight, by 36 parts of beeswaxs, 10 parts of insect waxes, 24 parts of paraffin, 8 parts of stearic acid mischmetals, 1 part of hydrogenation ester gum,
Blended wax is made after mixing, using the method for melt blending in 0.6 part of tricalcium phosphate；
（4）Behind heat gun heat wood surface, the blended wax brushing of melting is then waited until into blended wax table in wood surface
After the solidification of face, after having carried out wax, having wiped Lasaxing Oilfield, timber casting is completed.
Specifically, above-mentioned steps（3）In, the temperature of melt blending is 85 DEG C.
Specifically, above-mentioned steps（4）In, wood surface is heated to 91 DEG C using heat gun.
Specifically, above-mentioned steps（4）In, the floating wax of wood surface is scalped when playing wax with perching knife, the direction of perching knife shovel wax is
Along Wood surface texture.
Specifically, above-mentioned steps（4）In, wiping wax is carried out to wood surface using byssus, along the suitable of timber when wiping wax
Line direction.
Embodiment 2
A kind of casting method of high adhesion force pencil timber, including following operating procedure：
（1）After the wood surface of excision forming is removed grieshoch, grinding process, in the spraying modified liquid in its surface, wherein modification liquid
It is made of the component of following parts by weight：12 parts of sodium phytate, 10 parts of ammonium pentaborate, 2 parts of dipotassium glycyrrhizinate, 180 parts of water；
（2）By weight, 21 parts of samarium trichlorides, 13 parts of lanthanum chlorides are added into 110 parts of water, after being mixed evenly, then
33 parts of odium stearate are added thereto, after continuing stir process 13min, after the temperature of mixture is risen to 155 DEG C, isothermal holding
It 3.5 hours, then cools to room temperature, after going upper aqueous layer, obtains stearic acid mischmetal；
（3）By weight, by 40 parts of beeswaxs, 13 parts of insect waxes, 26 parts of paraffin, 10 parts of stearic acid mischmetals, 2 parts of hydrogenated esters
Blended wax is made after mixing, using the method for melt blending in glue, 0.8 part of tricalcium phosphate；
（4）Behind heat gun heat wood surface, the blended wax brushing of melting is then waited until into blended wax table in wood surface
After the solidification of face, after having carried out wax, having wiped Lasaxing Oilfield, timber casting is completed.
Specifically, above-mentioned steps（3）In, the temperature of melt blending is 88 DEG C.
Specifically, above-mentioned steps（4）In, wood surface is heated to 93 DEG C using heat gun.
Specifically, above-mentioned steps（4）In, the floating wax of wood surface is scalped when playing wax with perching knife, the direction of perching knife shovel wax is
Along Wood surface texture.
Specifically, above-mentioned steps（4）In, wiping wax is carried out to wood surface using byssus, along the suitable of timber when wiping wax
Line direction.
Embodiment 3
A kind of casting method of high adhesion force pencil timber, including following operating procedure：
（1）After the wood surface of excision forming is removed grieshoch, grinding process, in the spraying modified liquid in its surface, wherein modification liquid
It is made of the component of following parts by weight：14 parts of sodium phytate, 12 parts of ammonium pentaborate, 3 parts of dipotassium glycyrrhizinate, 200 parts of water；
（2）By weight, 24 parts of samarium trichlorides, 15 parts of lanthanum chlorides are added into 115 parts of water, after being mixed evenly, then
38 parts of odium stearate are added thereto, after continuing stir process 15min, after the temperature of mixture is risen to 160 DEG C, isothermal holding
It 4 hours, then cools to room temperature, after going upper aqueous layer, obtains stearic acid mischmetal；
（3）By weight, by 44 parts of beeswaxs, 15 parts of insect waxes, 30 parts of paraffin, 13 parts of stearic acid mischmetals, 3 parts of hydrogenated esters
Blended wax is made after mixing, using the method for melt blending in glue, 0.9 part of tricalcium phosphate；
（4）Behind heat gun heat wood surface, the blended wax brushing of melting is then waited until into blended wax table in wood surface
After the solidification of face, after having carried out wax, having wiped Lasaxing Oilfield, timber casting is completed.
Specifically, above-mentioned steps（3）In, the temperature of melt blending is 90 DEG C.
Specifically, above-mentioned steps（4）In, wood surface is heated to 95 DEG C using heat gun.
Specifically, above-mentioned steps（4）In, the floating wax of wood surface is scalped when playing wax with perching knife, the direction of perching knife shovel wax is
Along Wood surface texture.
Specifically, above-mentioned steps（4）In, wiping wax is carried out to wood surface using byssus, along the suitable of timber when wiping wax
Line direction.
Comparative example 1
Step（3）In do not add stearic acid mischmetal, remaining operating procedure is identical with embodiment 1.
Casting processing is carried out to lime tree timber with the method for each embodiment and comparative example respectively, then according to national standard
GB/T 9286-1998《The cross cut test of paint and varnish paint film》, copy paint film adhesion to draw lattice measuring method and carry out test material of waxing
Cere adhesive force cross cut test, the resistance being detached from from substrate to measure wax layer, provides according to standard, is existed using Checker marking knife tool
Parallel lines are cut in square crossing in test material of waxing, and using tape-stripping, removing, utilize magnifying glass close-ups cutting tool
To the destruction situation of test material surface wax layer, test result is 0-5 grades, and 5 grades of representatives damage most serious, and wax layer adhesive force is worst, examination
Test that the results are shown in Table 1：
A kind of casting method measure of merit of the high adhesion force pencil timber of table 1
As shown in Table 1, cere made from the present embodiment, adhesive force is strong, is not susceptible to the phenomenon that falling off.
It should be noted that the above examples are only used to illustrate the technical scheme of the present invention and are not limiting.Although referring to compared with
Good embodiment describes the invention in detail, those skilled in the art should understand that, it can be to the technology of invention
Scheme is modified or replaced equivalently, and without departing from the range of technical solution of the present invention, should all be covered in power of the invention
In sharp claimed range.
Claims (5)
1. a kind of casting method of high adhesion force pencil timber, which is characterized in that including following operating procedure：
（1）After the wood surface of excision forming is removed grieshoch, grinding process, in the spraying modified liquid in its surface, wherein modification liquid
It is made of the component of following parts by weight：10-14 parts of sodium phytate, 7-12 parts of ammonium pentaborate, 1-3 parts of dipotassium glycyrrhizinate, water 160-200
Part；
（2）By weight, 19-24 parts of samarium trichlorides, 10-15 parts of lanthanum chlorides are added into 105-115 parts of water, are mixed equal
After even, 31-38 parts of odium stearate are then added thereto, after continuing stir process 10-15min, the temperature of mixture is risen to
It after 150-160 DEG C, isothermal holding 3-4 hours, then cools to room temperature, after going upper aqueous layer, obtains stearic acid mischmetal；
（3）By weight, by 36-44 parts of beeswaxs, 10-15 parts of insect waxes, 24-30 parts of paraffin, 8-13 parts of stearic acid mischmetals,
Blended wax is made after mixing, using the method for melt blending in 1-3 parts of hydrogenation ester gums, 0.6-0.9 parts of tricalcium phosphates；
（4）Behind heat gun heat wood surface, the blended wax brushing of melting is then waited until into blended wax table in wood surface
After the solidification of face, after having carried out wax, having wiped Lasaxing Oilfield, timber casting is completed.
2. a kind of casting method of high adhesion force pencil timber according to claim 1, which is characterized in that above-mentioned steps
（3）In, the temperature of melt blending is 85-90 DEG C.
3. a kind of casting method of high adhesion force pencil timber according to claim 1, which is characterized in that above-mentioned steps
（4）In, wood surface is heated to 91-95 DEG C using heat gun.
4. a kind of casting method of high adhesion force pencil timber according to claim 1, which is characterized in that above-mentioned steps
（4）In, the floating wax of wood surface is scalped when playing wax with perching knife, the direction that perching knife shovels wax is along Wood surface texture.
5. a kind of casting method of high adhesion force pencil timber according to claim 1, which is characterized in that above-mentioned steps
（4）In, wiping wax is carried out to wood surface using byssus, along the rift grain direction of timber when wiping wax.