CN106669640A - 一种聚苯胺修饰膨润土纳米微球吸附材料及其制备方法 - Google Patents
一种聚苯胺修饰膨润土纳米微球吸附材料及其制备方法 Download PDFInfo
- Publication number
- CN106669640A CN106669640A CN201611009392.3A CN201611009392A CN106669640A CN 106669640 A CN106669640 A CN 106669640A CN 201611009392 A CN201611009392 A CN 201611009392A CN 106669640 A CN106669640 A CN 106669640A
- Authority
- CN
- China
- Prior art keywords
- polyaniline
- bentonite
- modified bentonite
- absorption material
- nano micro
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种聚苯胺修饰膨润土纳米微球吸附材料，该材料由下述重量百分比的原料制备而成：苯胺单体插层有机化膨润土10—20％，蒸馏水60—80％，氢氧化钠9—15％，引发剂0.02％—0.06％，乳化剂0.3％—0.5％。本发明还提供了一种制造聚苯胺修饰膨润土纳米微球吸附材料的方法，通过特定的配方设计和工艺参数选择，制备合成出一种成本低廉、有良好的兼容性、环境友好、易于固液分离和纳米尺寸效应的聚苯胺修饰膨润土纳米微球吸附材料，该吸附材料具有较大的比表面积、较小的纳米尺度和具有协同吸附污水中金属离子与有机物双污染成分的功能特性。
Description
技术领域
本发明涉及一种新型膨润土吸附材料及其制备工艺，特别是一种聚苯胺修饰膨润土纳米微球吸附材料及其制备方法。
背景技术
吸附是脱除污染水体中可溶性重金属离子和有机物的通用方法，该法是通过吸附材料来实现。当前，常用的无机吸附材料主要有活性炭和粘土矿。
活性炭材料因其具有良好的孔态分布和巨大的比表面积，已被广泛应用于特种污水或含有难于用一般方法处理的有毒有机物的污水处理中，但改吸附材料在使用中存在两种局限性：一是成本过高，即升高了水处理污染的成本；二是其对水体中重金属离子的除效率较低。这两个缺点限制了活性炭材料的在污水处理领域的应用与推广。
粘土类矿物贮量大、低廉环保并兼具优良的吸附性能而备受关注，已成为近年来研究与应用的优选材料之一，特别是该类材料的具有较多的改性功能，可根据不同的吸附处理对象进行针对性改性，使其具有更加优良的吸附性能。主要的粘土矿物有膨润土、高岭石、沸石和硅藻土等。其中研究最广、最为大家青睐且有望市场化应的当属膨润土矿物材料。
如中国专利ZL200410018109所述的一种有机-无机符合膨润土废水处理材料的制备方法。在膨润土层间与表面形成羟基金属，有效的吸附了磷酸根与有机物，并提高了固液分离能力。
如美国专利US6093241所述的一种从废水中除油的颗粒状有机粘土混合物，配方涉及海泡石、绿坡石、四元化合物及水泥胶黏剂等，该吸附材料具有高温稳定性的特质。
膨润土矿物材料经提纯与改性后是一种具有高活性和高吸附性能的优质吸附材料，其在污水处理工业中具有广泛的应用价值和应用前景。但是，该材料在改性研究和应用推广中主要存在如下问题：1)固-液分离困难。由相关研究可知，膨润土的颗粒粒径越小，比表面积和表面张力越大，其水处理吸附效率越高；但是颗粒粒径越小，颗粒在液体中的沉降速率越慢，其颗粒的相对溶胀性越大(10％左右)，两者均加大了沉降、浓缩和脱水等工艺的成本。现在解决该问题的办法主要有两种，一是向固-液体系中加入絮凝剂；二是提高过滤压力，前者引入了二次污染物，后者提高了投资成本。2)深加工研究不足。当前，大多研究者集中于表面改性剂对膨润土处理不同污水时的吸附效果及行业等方面的研究，所用的膨润土原料均为传统的粉状颗粒，没有结合原料深加工与膨润土改性两者相关性的研究。3)引入二次污染。由于膨润土吸附材料吸水膨胀后，其呈絮凝态，材料强度极低，在搅拌和脱失工艺中将会破裂，裂化的膨润土粒度下，沉降极其缓慢，在水处理中，不得不采用絮凝剂去除这些颗粒；无论是有机絮凝剂，还是无机絮凝剂均会溶解在水体当中，这样，造成水处理成本的上升，并引入了二次污染。4)吸附兼容性差。吸附材料处理水体中的污染物大致可分为两类，即金属离子和有害有机物。金属离子和有害有机物各自种类繁多，具相关报道，采用膨润土改性吸附金属离子或有害有机物时，有一种改性及改性的膨润土仅能有效吸附水中的1～2种有害物质，所以，针对受多种有害物质污染的水体，将使用多种被改性后的膨润土，这样，造成了水处理工艺的复杂化，提高了成本；这也是膨润土一直未曾取代活性炭用于水体治理的原因之一。
发明内容
针对膨润土吸附材料在污水吸附研究与应用中存在的科技问题，本发明的目的是制备一种新型污水吸附材料，本发明通过特定的配方设计和工艺参数选择，制备合成出一种成本低廉、有良好的兼容性、环境友好、易于固液分离和纳米尺寸效应的聚苯胺修饰膨润土纳米微球吸附材料，该吸附材料具有较大的比表面积、较小的纳米尺度和具有协同吸附污水中金属离子与有机物双污染成分的功能特性。
本发明的目的是通过下述技术方案来实现的。
一种聚苯胺修饰膨润土纳米微球吸附材料，该材料由下述重量百分比的原料制备而成：
苯胺单体插层有机化膨润土10—20％；蒸馏水60—80％；引发剂0.02％—0.06％；氢氧化钠9—15％；乳化剂0.3％—0.5％。
进一步的，所述材料中：
所述引发剂为三氯化铁。
所述乳化剂为Span60。
进一步的，所述苯胺单体插层有机化膨润土由下述重量百分比的原料制备而成：
膨润土10—20％；苯胺3％—8％；蒸馏水60—75％；氢氧化钠9—15％；表面活性剂0.01％—0.06％。
进一步的，所述材料中：
所述表面活性剂为十六烷基三甲基溴化铵。
相应地，本发明还给出了一种聚苯胺修饰膨润土纳米微球吸附材料的制备方法，包括下述两个步骤：
第一步、膨润土的有机化及苯胺单体插层制备：
选取重量百分比为10—20％的膨润土，60—75％的蒸馏水，9—15％的氢氧化钠，0.01—0.06％的表面活性剂，于容器中混合；在40—50℃水浴中热搅拌1—2h，使膨润土有机化制得有机化膨润土，然后继续滴加3—8％的苯胺，于容器中混合；在60—70℃水浴中热搅拌2—4h，制备得苯胺单体插层有机化膨润土。
第二步、聚苯胺修饰膨润土纳米微球吸附材料的制备；
选取重量百分比为10—20％的步骤一制取的苯胺单体插层有机化膨润土，60—80％的蒸馏水，0.02—0.06％的引发剂，0.3—0.5％的乳化剂，9—15％的氢氧化钠，于容器中混合；在70—80℃水浴中热搅拌2—4h，然后离心洗涤、真空抽提后，制备得聚苯胺修饰膨润土纳米微球吸附材料。
本发明相对于现有的膨润土复合材料的制备工艺、配方设计和应用推广等具有下述有益效果：
1)、协同兼容吸附
聚苯胺修饰膨润土纳米微球吸附材料充分利用了膨润土的亲水性能和聚苯胺的亲油性能，使其同时吸收水中的有机物和金属离子，达到协同兼容吸附的效果。
2)、纳米化设计
采用“乳液聚合发”制备的聚苯胺修饰膨润土纳米微球吸附材料，微球中位直径≤80nm；球内包覆直径≤10nm的多颗膨润土纳米颗粒。
3)、吸附剂快速分离
由于膨润土的吸水膨胀性，使其在污水处理后将其从母液中分离出来非常困难，该固-液分离科技难题是一直以来阻碍膨润土及其改性材料推广使用的主要因素。本发明采用苯胺包覆膨润土制备核壳结构设计的材料制备手段，使膨润土在吸附过程中，受到外壳聚苯胺的限制，不发生漂移，不会封堵无数颗聚苯胺修饰膨润土纳米微球之间的液体流经通道，从而提高了过滤效率。
4)、较大的吸附比表面积
通过工艺设计，使得聚苯胺修饰膨润土纳米微球吸附材料具有巨大的比表面积，比表面积来源于两方面，一是聚苯胺包覆层微多孔结构，其平均孔径≤2nm；二是聚苯胺包覆层内部存在大量的平均粒径≤10nm的膨润土纳米颗粒；这使得聚苯胺修饰膨润土纳米微球吸附材料具有巨大的比表面积。
附图说明
图1是本发明膨润土有机化及苯胺单体插层工艺流程图；
图2是本发明聚苯胺修饰膨润土纳米微球的制备流程图；
图3是本发明聚苯胺修饰膨润土纳米微球的扫描投射显微镜(TEM)图。
具体实施方式
下面结合附图及实施例对本发明的聚苯胺修饰膨润土纳米微球吸附材料及其制备方法做出详细说明。
第一步、本发明膨润土有机化及苯胺单体插层制备。
1)原料选取
膨润土(工业品)，表面活性剂十六烷基三甲基溴化铵(分析纯)，氢氧化钠(分析纯)，苯胺(分析纯)，蒸馏水(分析纯)。
2)制备工艺
选取一定量的膨润土，加入蒸馏水，搅拌的悬浮液，在悬浮液中添加表面活性剂十六烷基三甲基溴化铵，于容器中混合；在一定温度的水浴中热搅拌一段时间，使膨润土进行充分的有机化。然后，继续滴加一定浓度的苯胺溶液，于容器中混合，继续在水浴中加热搅拌，制备得苯胺单体插层有机化膨润土。苯胺单体插层有机化膨润土制备工艺如附图1所示。
3)制备原理
制备苯胺单体插层有机化膨润土主要涉及阳离子离子交换机理和相似相容原理等等。
十六烷基三甲基溴化铵在水溶液中将会能电离出NH4 +，根据膨润土的阳离子交换性，由于NH4 +离子半径小于Na+、Mg2+、K+、Ca2+等离子的半径，因此体积小的NH4 +离子置换出膨润土层间的Na+、Mg2+、K+、Ca2+等离子后，孔径增大，并削弱了原来层间的键力，层状晶格断开，蒙脱石内部随着八面体中阳离子的去除形成了暴露表面，它们之间以氢键连接，使得被阳离子交换之后的有机膨润土具有较强的化学活性、吸附性和催化性。
通过离子交换机理，有机膨润土的层间被十六烷基三甲基溴化铵填充，由于十六烷基三甲基溴化铵的有机特性，其具有亲油疏水的功能，根据相似相容原理，十六烷基三甲基溴化铵对有机小分子有相容性，使得溶液中的苯胺单体能被插层到膨润土层间，实现了苯胺对膨润土的层间插层。
膨润土的有机化及苯胺单体插层可以通过XRD、TG、DSC、TEM和SEM等测试仪器设备进行表征与效果评价。
第二步、本发明聚苯胺修饰膨润土纳米微球的制备
1)原料选取
苯胺单体插层有机化膨润土(本发明所述第一步制备的材料)；引发剂三氯化铁(分析纯)，乳化剂Span60(分析纯)，蒸馏水(分析纯)，氢氧化钠(分析纯)。
2)制备工艺
选取一定量按本发明第一步所述的苯胺单体插层有机化膨润土，加入蒸馏水，加入乳化剂Span60，加入氢氧化钠，制备成悬浮状水溶液，搅拌加热一段时间后，滴加引发剂三氯化铁，于容器中充分混合；升温搅拌，使苯胺膨润土表面发生聚合反应并成微球态分布；然后离心洗涤、真空抽提后，制备得聚苯胺修饰膨润土纳米微球吸附材料。聚苯胺修饰膨润土纳米微球吸附材料工艺流程如附图2所示。
3)制备原理
采用无水三氯化铁构成引发体系，制备聚苯胺修饰膨润土纳米微球吸附材料时，首先是氯化铁引发生成正氮离子活性中心：
该活性中心将进攻下一个苯胺分子的对位氢，端头的伯胺被氧化成正氮结构，通过亲电取代实现了聚苯胺的链增长：
最后合成聚苯胺产物分子的结构是：
其中n代表链节数，而y和1-y分别代表一个平均链节中苯式和醌式两种结构所占百分比。当y＝0时，为完全氧化态全醒式结构，由醌二亚胺构成了聚苯胺的分子整链；当y＝1时，为完全还原态全苯式结构，由苯二胺构成了聚苯胺的分子整链；而当y＝0.5时，为中间氧化苯醌交替结构。
下面通过具体实施例来进一步说明本发明。
实施例1
第一步、膨润土的有机化及苯胺单体插层制备：
选取10％膨润土，加入75％蒸馏水，0.02％的表面活性剂十六烷基三甲基溴化铵，11.7％的氢氧化钠，于容器中混合；40℃水浴加热2h，进行浸渍；然后加入3.28％的苯胺，继续水浴加热至60℃，搅拌4h，使苯胺插层入膨润土层间；制得苯胺单体插层有机化膨润土。
第二步、聚苯胺修饰膨润土纳米微球吸附材料的制备：
选取本发明第一步制取的苯胺单体插层有机化膨润土10％，加入80％的蒸馏水，0.3％的乳化剂Span60，9.68％的氢氧化钠，于容器中混合制备成悬浮状水溶液，搅拌加热一段时间后，滴加引发剂三氯化铁0.02％，升温水浴加热至70℃，搅拌4h，使苯胺膨润土表面发生聚合反应并成微球态分布；然后离心洗涤、真空抽提后，制得聚苯胺修饰膨润土纳米微球吸附材料。
实施例2
第一步、膨润土的有机化及苯胺单体插层制备：
选取14.5％膨润土，加入65％蒸馏水，0.04％的表面活性剂十六烷基三甲基溴化铵，14.5％的氢氧化钠，于容器中混合；42℃水浴加热1.5h，进行浸渍；然后加入5.96％的苯胺，继续水浴加热至62℃，搅拌3.2h，使苯胺插层入膨润土层间；制得苯胺单体插层有机化膨润土。
第二步、聚苯胺修饰膨润土纳米微球吸附材料的制备：
选取本发明第一步制取的苯胺单体插层有机化膨润土16％，加入72％的蒸馏水，0.4％的乳化剂Span60，11.56％的氢氧化钠，于容器中混合制备成悬浮状水溶液，搅拌加热一段时间后，滴加引发剂三氯化铁0.06％，升温水浴加热至76℃，搅拌3h，使苯胺膨润土表面发生聚合反应并成微球态分布；然后离心洗涤、真空抽提后，制得聚苯胺修饰膨润土纳米微球吸附材料。
实施例3
第一步、膨润土的有机化及苯胺单体插层制备：
选取20％膨润土，加入60％蒸馏水，0.06％的表面活性剂十六烷基三甲基溴化铵，12.4％的氢氧化钠，于容器中混合；50℃水浴加热1h，进行浸渍；然后加入7.54％的苯胺，继续水浴加热至70℃，搅拌2h，使苯胺插层入膨润土层间；制得苯胺单体插层有机化膨润土。
第二步、聚苯胺修饰膨润土纳米微球吸附材料的制备：
选取本发明第一步制取的苯胺单体插层有机化膨润土10％，加入80％的蒸馏水，0.3％的乳化剂Span60，9.68％的氢氧化钠，于容器中混合制备成悬浮状水溶液，搅拌加热一段时间后，滴加引发剂三氯化铁0.02％，升温水浴加热至70℃，搅拌4h，使苯胺膨润土表面发生聚合反应并成微球态分布；然后离心洗涤、真空抽提后，制得聚苯胺修饰膨润土纳米微球吸附材料。
请参阅图3，是本发明聚苯胺修饰膨润土纳米微球的扫描投射显微镜(TEM)图，通过工艺设计，使得聚苯胺修饰膨润土纳米微球吸附材料具有巨大的比表面积，比表面积来源于两方面，一是聚苯胺包覆层微多孔结构，其平均孔径≤2nm；二是聚苯胺包覆层内部存在大量的平均粒径≤10nm的膨润土纳米颗粒；这使得聚苯胺修饰膨润土纳米微球吸附材料具有巨大的比表面积。
Claims (10)
1.一种聚苯胺修饰膨润土纳米微球吸附材料，其特征在于，该材料由下述重量百分比的原料制备而成：
2.根据权利要求1所述的聚苯胺修饰膨润土纳米微球吸附材料，其特征在于，所述引发剂为三氯化铁。
3.根据权利要求1所述的聚苯胺修饰膨润土纳米微球吸附材料，其特征在于，所述乳化剂为Span60。
4.根据权利要求1所述的聚苯胺修饰膨润土纳米微球吸附材料，其特征在于，所述苯胺单体插层有机化膨润土由下述重量百分比的原料制备而成：
5.根据权利要求4所述的聚苯胺修饰膨润土纳米微球吸附材料，其特征在于，所述膨润土的主要成分为蒙脱石。
6.根据权利要求4所述的聚苯胺修饰膨润土纳米微球吸附材料，其特征在于，所述表面活性剂为十六烷基三甲基溴化铵。
7.一种基于权利要求1所述的聚苯胺修饰膨润土纳米微球吸附材料的制备方法，其特征在于，该方法包括下述两个步骤：
第一步、膨润土的有机化及苯胺单体插层制备：
选取重量百分比为10—20％的膨润土，60—75％的蒸馏水，9—15％的氢氧化钠，0.01％—％0.06的表面活性剂，于容器中混合；在40—50℃水浴中热搅拌1—2h，使膨润土有机化制得有机化膨润土，然后继续滴加3—8％的苯胺，于容器中混合；在60—70℃水浴中热搅拌2—4h，制备得苯胺单体插层有机化膨润土；
第二步、聚苯胺修饰膨润土纳米微球吸附材料的制备；
选取重量百分比为10—20％的步骤一制取的苯胺单体插层有机化膨润土，60—80％的蒸馏水，0.02％—0.06％的引发剂，0.3％—0.5％的乳化剂，9—12％的氢氧化钠，于容器中混合；在70—80℃水浴中热搅拌2—4h，然后离心洗涤、真空抽提后，制备得聚苯胺修饰膨润土纳米微球吸附材料。
8.根据权利要求7所述的聚苯胺修饰膨润土纳米微球吸附材料的制备方法，其特征在于，所述引发剂为三氯化铁。
9.根据权利要求7所述的聚苯胺修饰膨润土纳米微球吸附材料的制备方法，其特征在于，所述乳化剂为Span60。
10.根据权利要求7所述的聚苯胺修饰膨润土纳米微球吸附材料的制备方法，其特征在于，所述表面活性剂为十六烷基三甲基溴化铵。