CN106638008A - 一种cpu/tpu复合合成革的清洁生产方法 - Google Patents

一种cpu/tpu复合合成革的清洁生产方法 Download PDF

Info

Publication number
CN106638008A
CN106638008A CN201710047762.0A CN201710047762A CN106638008A CN 106638008 A CN106638008 A CN 106638008A CN 201710047762 A CN201710047762 A CN 201710047762A CN 106638008 A CN106638008 A CN 106638008A
Authority
CN
China
Prior art keywords
cpu
tpu
surface layer
office
synthetic leather
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201710047762.0A
Other languages
English (en)
Other versions
CN106638008B (zh
Inventor
马兴元
赵昭
丁博
段月
张铭芮
刘帅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shaanxi University of Science and Technology
Original Assignee
Shaanxi University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shaanxi University of Science and Technology filed Critical Shaanxi University of Science and Technology
Priority to CN201710047762.0A priority Critical patent/CN106638008B/zh
Publication of CN106638008A publication Critical patent/CN106638008A/zh
Application granted granted Critical
Publication of CN106638008B publication Critical patent/CN106638008B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种CPU/TPU复合合成革的清洁生产方法，采用干法合成革生产线，在基布上刮涂无溶剂浇注型聚氨酯发泡浆料，加热熟化后得到CPU发泡贝斯；采用压延生产线，将面层物料加入捏合机，经捏合工序后进入密炼机，经密炼工序后进入塑炼机，经塑炼工序后进入压延机，压延成面层薄膜，再与CPU发泡贝斯贴合，进行压花或吸纹，冷却后卷取，得到CUP/TPU复合合成革。本发明的工艺中不使用任何有机溶剂，没有任何溶剂污染；所述的工艺操作简单，工艺稳定；所得的产品力学性能优异，质量良好；产品能够集合CPU合成革和TPU合成革的优点，避免了二者的缺点。

Description

一种CPU/TPU复合合成革的清洁生产方法
技术领域
本发明涉及合成革的生产方法，特别涉及一种CPU/TPU复合合成革的清洁生产方法。
背景技术
合成革工业的主要产品包括人造革、合成革和超细纤维合成革，这些产品都是模拟天然皮革的组织结构和使用性能，并可作为天然皮革代用品的复合材料。通常情况下，大多以聚氨酯(PU)和聚氯乙烯(PVC)微孔涂层，模拟天然皮革的粒面层，以无纺布或纺织布为基材的模拟天然皮革的网状层。在通常的分类中，以纺织布为基材的称为人造革，以无纺布为基材的称为合成革，以超细纤维基布为基材的称为超细纤维合成革，这些广泛用于制作鞋、靴、箱包和球类等。从产量来看，我国塑料人造合、合成革产量从2009年的184.82万吨增长到2015年的343.8万吨，复合增长率达10.9％。但是近年来国内环保要求更加严格，重污染合成革产业发展受到限制，行业竞争日益激烈。从产品的性能要求来看，聚氨酯(PU)和聚氯乙烯(PVC)微孔涂层通常由不发泡的面层和发泡的下层构成，不发泡的面层能够满足产品表面的耐磨、抗划伤等使用性能要求，而发泡的下层能够满足产品柔软丰满的手感要求。因此，从技术角度来看，合成革涂层的技术主要包括面层技术和发泡层技术两个方面。
目前，PU合成革生产过程中，均采用有机溶剂型的PU树脂作为生产革制品发泡层和面层的基本原料，这种类型的PU树脂均通过甲苯、丁酮(MEK)和二甲基甲酰胺(DMF)等作为主要溶剂以溶剂聚合法制得。这些占整个树脂成分60％以上的有机溶剂基本上都是有害物质，而且对人体造成的危害是多方面的。其中，丁酮、丙酮和二甲基甲酰胺等溶剂都有相当大的毒副作用。合成革生产中用量最大的二甲基甲酰胺，对皮肤、眼部粘膜有强刺激性，吸入高浓度气体时，会刺激咽部引起恶心，经常接触，经皮肤侵入，会导致肝功能障碍；而且过多的吸入以上溶剂对女性孕育下一代将产生严重的负面影响。
另一方面，PVC人造革的生产中，塑化剂的添加量超过30％以上，相较于PVC的巨大分子量而言，塑化剂属于高度自由的小分子，随着时间变化PVC分子必定排挤塑化剂，造成塑化剂在PVC人造革的表面迁移。PVC塑化剂以邻苯二甲酸酯(Phthalate)系列为主，其使用量在占塑化剂的80％以上，而DOP、DEHP使用量超多60％。美国环保署的警告显示，塑化剂影响生殖与发育，也就是所谓的“环境荷尔蒙”，对发育中的男性生殖系统有很大的影响，其中幼儿所受的威胁要较成人更高。而且，PVC本身光热安定性不佳，生产PVC人造革时需要混入大量的重金属盐类稳定剂(包含铅、镉、锌、钡、锡)防止PVC降解。研究报告指出35℃以上甚至常温中PVC人造革中的氯离子会微量游离(0.1～10ppm)，而氯离子也是一种自由基，过往在PVC材料依靠稳定剂进行氯离子的捕捉，也就是说，PVC人造革在降解的过程中，无时无刻都在释放酸性气体HCl。
综上所述，无论是PU合成革或PVC人造革，都存在着环境污染或产品安全问题，依据目前的发展趋势，研究清洁化的生产工艺，生产环境友好型的聚氨酯合成革是一个必然的趋势。目前，研究和开发的清洁技术主要包括三个方面，即：水性聚氨酯合成革技术、无溶剂浇注型聚氨酯合(CPU)成革技术和热塑性聚氨酯(TPU)合成革技术。其中，以TPU为主要原料，采用压延法生产TPU合成革，生产中不需要任何溶剂，也不需要加入任何塑化剂，是一种非常环保的生产技术，而且成品革力学性能非常优异。但是目前的TPU合成革和CPU合成革存在以下问题：其一，用于合成革生产的TPU可选的硬度范围通常95A～65A之间(邵尔A硬度计测定)，没有低于65A的工业化TPU树脂，也就是说，要生产手感很软的TPU合成革，没有可选的TPU树脂，难以生产出柔软丰满的发泡层；其二，对于CPU合成革而言，由于反应会发泡，难以作为合成革的面层材料，目前，单纯的CPU合成革仍然采用溶剂型的面层树脂，但是CPU发泡涂层具有柔软丰满的手感。
发明内容
基于以上的技术背景，本发明无溶剂浇注型聚氨酯(CPU)发泡贝斯为基材，贴合热塑性聚氨酯(TPU)面层得到的一种新型的合成革。这种合成革生产中不使用任何有机溶剂，没有任何溶剂污染；工艺操作简单稳定；所得的产品力学性能优异，质量良好；产品能够集合CPU发泡涂层柔软的手感和TPU面层优异的力学性能，避免了CPU合成革溶剂型面层的污染，以及TPU发泡涂层手感僵硬的缺陷，具有很好的创新性。
为达到上述目的，本发明采用的技术方案是：
一种CPU/TPU复合合成革的清洁生产方法，包括以下步骤：
(1)采用干法合成革生产线，在基布上刮涂无溶剂浇注型聚氨酯发泡浆料，加热熟化后得到CPU发泡贝斯；
(2)采用压延生产线，将面层物料加入捏合机，经捏合工序后进入密炼机，经密炼工序后进入塑炼机，经塑炼工序后进入压延机，压延成面层薄膜，再与CPU发泡贝斯贴合，进行压花或吸纹，冷却后卷取，得到CUP/TPU复合合成革。
本发明进一步的改进在于，所述的无溶剂浇注型聚氨酯发泡浆料通过以下过程制得：以重量份数计，在反应釜中加入相对分子质量为2000的聚合物二醇60～70份、液化二苯基甲烷二异氰酸酯8～10份以及N-乙基吗啉0.2～0.4份，混合后连续搅拌10min～15min。
本发明进一步的改进在于，聚合物二醇为聚酯二元醇或聚醚二元醇。
本发明进一步的改进在于，所述聚酯二元醇为聚己二酸聚酯二元醇或聚己内酯二元醇；所述聚醚二元醇为聚四氢呋喃醚二醇。
本发明进一步的改进在于，所述的CPU发泡贝斯的具体制备工艺为：采用干法合成革生产线，将无溶剂浇注型聚氨酯发泡浆料刮涂在基布上，控制涂层厚度为0.5mm～1.0mm，然后进入烘箱干燥，控制烘箱温度为110℃～140℃，使CPU彻底熟化后得到CPU发泡贝斯。
本发明进一步的改进在于，所述的面层物料以质量份数计，包括TPU 100份，粉状碳酸钙填料20～100份，色粉1～5份，季戊四醇亚磷酸酯0.05～0.1份，聚碳化二亚胺0.1～0.5份以及聚四氟乙烯微粉0.2～1.5份。
本发明进一步的改进在于，步骤(2)中所述捏合工序的技术条件为：将面层物料投入到高速捏合机中搅拌5min～10min，当物料温度至90℃～100℃时，放料。
本发明进一步的改进在于，所述密炼工序的技术条件为：将捏合后的物料放入密炼机中，以15～20℃/min的升温速率升温至110℃～170℃下密炼3min～5min。
本发明进一步的改进在于，所述塑炼工序的技术条件为：将密炼后的物料放入塑炼机中，以15～20℃/min的升温速率升温至130℃～170℃下塑炼5min～10min。
本发明进一步的改进在于，所述压延工序的技术条件为：塑炼后的物料进入压延机，面层薄膜的厚度为0.1mm～1.5mm，压延温度为130℃～175℃；
所述的基布是无纺布、针织布或机织布。
与现有技术相比，本发明具有的有益效果：本发明以无溶剂浇注型聚氨酯(CPU)发泡贝斯为基材，贴合热塑性聚氨酯(TPU)面层得到的一种新型的合成革。生产中不使用任何有机溶剂，没有任何溶剂污染；工艺操作简单稳定；所得的产品力学性能优异，质量良好；产品能够集合CPU发泡涂层柔软的手感和TPU面层优异的力学性能，避免了CPU合成革面层的污染，以及TPU发泡涂层手感僵硬的缺陷。
本发明和目前的技术相比有以下的特点和优势。
(1)CUP/TPU复合合成革工艺中不使用任何有机溶剂，没有任何溶剂污染，是一种完全清洁的生产工艺。
(2)CUP/TPU复合合成革工艺操作简单，生产效率高，生产效率高达42米/每分钟，并且工艺稳定。
(3)CUP/TPU复合合成革产品不含任何塑化剂和重金属，完全符合欧盟的相关标准。
(4)CUP/TPU复合合成革产品VOC(可挥发性有机物)更低，能满足汽车内饰的要求。
(5)产品能够集合CPU发泡涂层柔软的手感和TPU面层优异的力学性能，避免了CPU合成革溶剂型面层的污染，以及TPU发泡涂层手感僵硬的缺陷。
具体实施方式
下面通过具体实施方式对本发明作进一步的详细说明，但本发明并不只限于这些例子。
本发明中的色粉为一类着色剂。
实施例1
一种CPU/TPU复合合成革的清洁生产方法，包括以下步骤：
(1)采用干法合成革生产线，将无溶剂浇注型聚氨酯发泡浆料刮涂在无纺布上，控制涂层厚度为0.5mm，然后进入烘箱干燥，控制烘箱温度为140℃，使CPU彻底熟化后得到CPU发泡贝斯。
其中，无溶剂浇注型聚氨酯发泡浆料通过以下过程制得：以重量份数计，在反应釜中加入相对分子质量为2000的聚合物二醇60份、液化二苯基甲烷二异氰酸酯8份以及N-乙基吗啉0.2份，混合后连续搅拌10min，即可使用。
聚合物二醇为聚己二酸聚酯二元醇。
(2)采用压延生产线，将面层物料投入到高速捏合机中搅拌5min，当物料温度至90℃时，放料后进入密炼机，以15℃/min的升温速率升温至110℃下密炼5min后进入塑炼机，以15℃/min的升温速率升温至130℃下塑炼10min后进入压延机，压延成面层薄膜，面层薄膜的厚度为0.1mm，压延温度为130℃；再将面层薄膜与CPU发泡贝斯贴合，进行压花或吸纹，冷却后卷取，得到CUP/TPU复合合成革。
其中，面层物料以质量份数计，包括TPU 100份，粉状碳酸钙填料20份，色粉2份，季戊四醇亚磷酸酯0.05份，聚碳化二亚胺0.1份以及聚四氟乙烯微粉0.2份。
实施例2
一种CPU/TPU复合合成革的清洁生产方法，包括以下步骤：
(1)采用干法合成革生产线，将无溶剂浇注型聚氨酯发泡浆料刮涂在针织布上，控制涂层厚度为0.6mm，然后进入烘箱干燥，控制烘箱温度为110℃，使CPU彻底熟化后得到CPU发泡贝斯。
其中，无溶剂浇注型聚氨酯发泡浆料通过以下过程制得：以重量份数计，在反应釜中加入相对分子质量为2000的聚合物二醇70份、液化二苯基甲烷二异氰酸酯10份以及N-乙基吗啉0.3份，混合后连续搅拌15min，即可使用。
聚合物二醇为聚己内酯二元醇；
(2)采用压延生产线，将面层物料投入到高速捏合机中搅拌8min，当物料温度至100℃时，放料后进入密炼机，以20℃/min的升温速率升温至170℃下密炼3min后进入塑炼机，以20℃/min的升温速率升温至140℃下塑炼8min后进入压延机，压延成面层薄膜，面层薄膜的厚度为0.8mm，压延温度为175℃；再将面层薄膜与CPU发泡贝斯贴合，进行压花或吸纹，冷却后卷取，得到CUP/TPU复合合成革。
其中，面层物料以质量份数计，包括TPU 100份，粉状碳酸钙填料100份，色粉3份，季戊四醇亚磷酸酯0.05份，聚碳化二亚胺0.2份以及聚四氟乙烯微粉0.8份。
实施例3
一种CPU/TPU复合合成革的清洁生产方法，包括以下步骤：
(1)采用干法合成革生产线，将无溶剂浇注型聚氨酯发泡浆料刮涂在机织布上，控制涂层厚度为0.8mm，然后进入烘箱干燥，控制烘箱温度为120℃，使CPU彻底熟化后得到CPU发泡贝斯。
其中，无溶剂浇注型聚氨酯发泡浆料通过以下过程制得：以重量份数计，在反应釜中加入相对分子质量为2000的聚合物二醇65份、液化二苯基甲烷二异氰酸酯9份以及N-乙基吗啉0.4份，混合后连续搅拌12min，即可使用。
聚合物二醇为聚四氢呋喃醚二醇；
(2)采用压延生产线，将面层物料投入到高速捏合机中搅拌10min，当物料温度至95℃时，放料后进入密炼机，以18℃/min的升温速率升温至150℃下密炼4min后进入塑炼机，以17℃/min的升温速率升温至160℃下塑炼6min后进入压延机，压延成面层薄膜，面层薄膜的厚度为1.1mm，压延温度为140℃；再将面层薄膜与CPU发泡贝斯贴合，进行压花或吸纹，冷却后卷取，得到CUP/TPU复合合成革。
其中，面层物料以质量份数计，包括TPU 100份，粉状碳酸钙填料50份，色粉1份，季戊四醇亚磷酸酯0.08份，聚碳化二亚胺0.4份以及聚四氟乙烯微粉1.5份。
实施例4
一种CPU/TPU复合合成革的清洁生产方法，包括以下步骤：
(1)采用干法合成革生产线，将无溶剂浇注型聚氨酯发泡浆料刮涂在针织布上，控制涂层厚度为1mm，然后进入烘箱干燥，控制烘箱温度为130℃，使CPU彻底熟化后得到CPU发泡贝斯。
其中，无溶剂浇注型聚氨酯发泡浆料通过以下过程制得：以重量份数计，在反应釜中加入相对分子质量为2000的聚合物二醇68份、液化二苯基甲烷二异氰酸酯10份以及N-乙基吗啉0.2份，混合后连续搅拌10min，即可使用。
聚合物二醇为聚己二酸聚酯二元醇；
(2)采用压延生产线，将面层物料投入到高速捏合机中搅拌5min，当物料温度至92℃时，放料后进入密炼机，以20℃/min的升温速率升温至130℃下密炼4min后进入塑炼机，以19℃/min的升温速率升温至170℃下塑炼5min后进入压延机，压延成面层薄膜，面层薄膜的厚度为1.5mm，压延温度为160℃；再将面层薄膜与CPU发泡贝斯贴合，进行压花或吸纹，冷却后卷取，得到CUP/TPU复合合成革。
其中，面层物料以质量份数计，包括TPU 100份，粉状碳酸钙填料70份，色粉5份，季戊四醇亚磷酸酯0.1份，聚碳化二亚胺0.5份以及聚四氟乙烯微粉份。
本发明的工艺中不使用任何有机溶剂，没有任何溶剂污染；所述的工艺操作简单，工艺稳定；所得的产品力学性能优异，质量良好；产品能够集合CPU合成革和TPU合成革的优点，避免了二者的缺点。

Claims (10)

1.一种CPU/TPU复合合成革的清洁生产方法，其特征在于，包括以下步骤：
(1)采用干法合成革生产线，在基布上刮涂无溶剂浇注型聚氨酯发泡浆料，加热熟化后得到CPU发泡贝斯；
(2)采用压延生产线，将面层物料加入捏合机，经捏合工序后进入密炼机，经密炼工序后进入塑炼机，经塑炼工序后进入压延机，压延成面层薄膜，再与CPU发泡贝斯贴合，进行压花或吸纹，冷却后卷取，得到CUP/TPU复合合成革。
2.根据权利要求1所述的一种CPU/TPU复合合成革的清洁生产方法，其特征在于，所述的无溶剂浇注型聚氨酯发泡浆料通过以下过程制得：以重量份数计，在反应釜中加入相对分子质量为2000的聚合物二醇60～70份、液化二苯基甲烷二异氰酸酯8～10份以及N-乙基吗啉0.2～0.4份，混合后连续搅拌10min～15min。
3.根据权利要求1所述的一种CPU/TPU复合合成革的清洁生产方法，其特征在于，聚合物二醇为聚酯二元醇或聚醚二元醇。
4.根据权利要求1所述的一种CPU/TPU复合合成革的清洁生产方法，其特征在于，所述聚酯二元醇为聚己二酸聚酯二元醇或聚己内酯二元醇；所述聚醚二元醇为聚四氢呋喃醚二醇。
5.根据权利要求1所述的一种CPU/TPU复合合成革的清洁生产方法，其特征在于，所述的CPU发泡贝斯的具体制备工艺为：采用干法合成革生产线，将无溶剂浇注型聚氨酯发泡浆料刮涂在基布上，控制涂层厚度为0.5mm～1.0mm，然后进入烘箱干燥，控制烘箱温度为110℃～140℃，使CPU彻底熟化后得到CPU发泡贝斯。
6.根据权利要求1所述的一种CPU/TPU复合合成革的清洁生产方法，其特征在于，所述的面层物料以质量份数计，包括TPU 100份，粉状碳酸钙填料20～100份，色粉1～5份，季戊四醇亚磷酸酯0.05～0.1份，聚碳化二亚胺0.1～0.5份以及聚四氟乙烯微粉0.2～1.5份。
7.根据权利要求1所述的一种CPU/TPU复合合成革的清洁生产方法，其特征在于，步骤(2)中所述捏合工序的技术条件为：将面层物料投入到高速捏合机中搅拌5min～10min，当物料温度至90℃～100℃时，放料。
8.根据权利要求1所述的一种CPU/TPU复合合成革的清洁生产方法，其特征在于，所述密炼工序的技术条件为：将捏合后的物料放入密炼机中，以15～20℃/min的升温速率升温至110℃～170℃下密炼3min～5min。
9.根据权利要求1所述的一种CPU/TPU复合合成革的清洁生产方法，其特征在于，所述塑炼工序的技术条件为：将密炼后的物料放入塑炼机中，以15～20℃/min的升温速率升温至130℃～170℃下塑炼5min～10min。
10.根据权利要求1所述的一种CPU/TPU复合合成革的清洁生产方法，其特征在于，所述压延工序的技术条件为：塑炼后的物料进入压延机，面层薄膜的厚度为0.1mm～1.5mm，压延温度为130℃～175℃；
所述的基布是无纺布、针织布或机织布。
CN201710047762.0A 2017-01-22 2017-01-22 一种cpu/tpu复合合成革的清洁生产方法 Active CN106638008B (zh)