CN106223018A - A kind of production method of super soft fabric - Google Patents
A kind of production method of super soft fabric Download PDFInfo
- Publication number
- CN106223018A CN106223018A CN201610785283.4A CN201610785283A CN106223018A CN 106223018 A CN106223018 A CN 106223018A CN 201610785283 A CN201610785283 A CN 201610785283A CN 106223018 A CN106223018 A CN 106223018A
- Authority
- CN
- China
- Prior art keywords
- parts
- production method
- super soft
- fabric
- soft fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the production method of a kind of super soft fabric, described fabric is made up of 25~40 parts of long-staple cotton fibers, 5~10 parts of bamboo fibres, 10~30 parts of Modal fibres, 10~20 parts of WATER-SOLUBLE PVA FIBERs, 3~5 parts of viscose anion function fiber weavings;Carry out pre-treatment, ferment treatment, stamp, steaming and color fixing and Final finishing processing, obtain product.Hinge structure, the present invention has higher water absorption and good permeability, can promote flexibility, can strengthen soft touch sensation simultaneously, and mechanical property is strong, and endurable performance is high.
Description
Technical field
The present invention relates to field of fabric producing technology, particularly to the production method of a kind of super soft fabric.
Background technology
Comfortable and easy to wear with its whole year containing cotton fabrics, the ventilative advantage such as moisture absorption, natural environmental-protective becomes deep by consumers in general
The underwear fabric liked.But through scouringing and bleaching, dyeing, after stamp processing or functional treatment, the oily wax on cotton fiber surface, lipid etc. are equal
It is removed, causes feel coarse, stiff, without smooth feeling;Especially the phase mutual friction in dress, washing process, causes fiber
Between hydrogen bond interconnect, be particularly easy to cause the fibrillation of cotton fiber, make fabric feeling become thick and stiff, fluffy sense decline.
Such as the processing method of a kind of super-soft home textile fabric that Shen Qing Publication day is 2013.03.20, a kind of super-soft home textile fabric
Processing method, it comprises the steps: mixed to knit → grey cloth pre-treatment → elementary fibril → ferment treatment → dyeing → secondary is former
Fibrillation → softness and resin finishing.Described super-soft home textile fabric is formed by tencel and cotton mixed knitting mutually, described tencel and cotton
It is tencel that yarn mixes the weight percent knitted: cotton=30~40:70~60, then obtain polyester slice through pelletizing;There is moisture absorption
Property is poor, the problem such as feel is coarse, easy endophytic bacteria;
Summary of the invention
It is an object of the invention to provide the production method of a kind of super soft fabric, to be solved technical problem is that: routine is knitted
Thing hygroscopicity is poor, feel endophytic bacteria coarse, easy.
The technical scheme is that the production method of a kind of super soft fabric, by 25~40
Part long-staple cotton fiber, 5~10 parts of bamboo fibres, 10~30 parts of Modal fibres, 10~20 parts of WATER-SOLUBLE PVA FIBERs, 3~5 parts stick
Glue anion function fiber weaving forms;Carry out pre-treatment, ferment treatment, stamp, steaming and color fixing and Final finishing processing, obtain product.
The invention has the beneficial effects as follows: long-staple cotton fiber, bamboo carbon fiber and viscose anion function fiber coordinate weaving, tool
Standby super flexible energy, and there is antibacterial, mildew-resistant, the function of health care;Furthermore long-staple cotton fiber and bamboo carbon fiber itself have higher
Water absorption;The present invention has also used WATER-SOLUBLE PVA FIBER can improve pliability and the water absorption of fabric;Modal fibre enters
One step strengthens hygroscopicity, promotes flexibility, can strengthen soft touch sensation simultaneously, and mechanical property is strong, and endurable performance is high.
On the basis of technique scheme, the present invention can also do following improvement.
Further, described ferment treatment uses cellulose treatment.
Further, described method of enzymatically treating is: put into by fabric in water, with the pH value of glacial acetic acid regulation water to 4.5~
5.5, add cellulase Tenzym100W 2~3%, be warming up to 56~59 DEG C, process 40~80min, then regulate pH with soda
Value, to 9~10.5, is warming up to 81~87 DEG C and processes 10~15min, terminate the catalyzing hydrolysis effect of enzyme, make enzyme inactivate.
Above-mentioned further scheme is used to provide the benefit that: to use ferment treatment to go fibrillation to obtain short flannel effect, it is achieved to knit
Beyond the region of objective existence sees the cleanest, the soft elegance of color and luster, soft, sliding glutinous, fine and smooth and simple to operate, it is to avoid traditional napping operation, work
Process flow shortens, and decreases energy consumption.
Described stamp uses the mode of spray printing to carry out printing technology process;Wherein thickening agent is joined by following weight parts raw material
System: oxidation dye 15~50 parts, sodium alginate 10~25 parts, synthetic thickening agent 0.5~2 parts, sodium chloride 1~5 parts, surplus
Water;Add remaining raw material after heating water to 35~45 DEG C, after mix and blend 15min, be warming up to 55~65 DEG C, regulation pH to 6~
7。
Using above-mentioned further scheme to provide the benefit that: having colouring fast, printing quality is good, color fastness is high, friction jail
Degree height, technique simply easily industrial operation, improves work production efficiency and the advantage of product quality.
Further, carrying out steaming and color fixing by rapid ageing machine, steaming and color fixing temperature is 120~128 DEG C, during steaming and color fixing
Between be 8~10min.
Use above-mentioned further scheme to provide the benefit that: technique simply easily industrial operation, improve work production efficiency
Advantage with product quality.
Further, described Final finishing step is to impregnate in antibiotic finishing solution, wherein antibacterial finishing agent in antibiotic finishing solution
Weight percent content is 0.05~0.25%.
Further, described antibacterial finishing agent is made up of the component of following weight portion: lauryl glucosyl 30~50 parts,
Ethoxy quinoline 10~30 parts, hexamethylene 10~30 parts.
Above-mentioned further scheme is used to provide the benefit that: lauryl glucosyl, ethoxy quinoline and poly-six methylenes
Base biguanide hydrochloride is with the use of, antibacterial effect Synergistic.
Detailed description of the invention
Principle and feature to the present invention are described below, and example is served only for explaining the present invention, is not intended to limit
Determine the scope of the present invention.
Embodiment 1:
A kind of production method of super soft fabric, by 25 parts of long-staple cotton fibers, 5 parts of bamboo fibres, 10 parts of Modal fibres, 10 parts
WATER-SOLUBLE PVA FIBER, 3 parts of viscose anion function fiber weaving compositions;
First fabric is carried out pre-treatment;
Then fabric is put in water, with the pH value of glacial acetic acid regulation water to 4.5, add cellulase Tenzym100W
2%, it is warming up to 56 DEG C, processes 80min, then with soda regulation pH value to 9, be warming up to 81 DEG C and process 15min, terminate the catalysis of enzyme
Hydrolysis, makes enzyme inactivate.
Printing technology process is carried out again by the way of spray printing;Wherein thickening agent is by following weight parts preparation of raw material: oxygen
Change dyestuff 15 parts, sodium alginate 10 parts, synthetic thickening agent 0.5 part, 1 part of sodium chloride, the water of surplus;Add after heating water to 35 DEG C
Enter remaining raw material, after mix and blend 15min, be warming up to 55 DEG C, regulate pH to 6.
Carrying out steaming and color fixing by rapid ageing machine, steaming and color fixing temperature is 128 DEG C, and the steaming and color fixing time is 10min.
Last dipping in antibiotic finishing solution, obtains product after dipping.Wherein antibacterial finishing agent weight hundred in antibiotic finishing solution
Proportion by subtraction content is 0.05%, and described antibacterial finishing agent is made up of the component of following weight portion: lauryl glucosyl 30 parts, second
Phenoxyl quinoline 10 parts, hexamethylene 10 parts.
Embodiment 2:
A kind of production method of super soft fabric, by 32 parts of long-staple cotton fibers, 12 parts of bamboo fibres, 20 parts of Modal fibres, 15
Part WATER-SOLUBLE PVA FIBER, 4 parts of viscose anion function fiber weavings compositions;
First fabric is carried out pre-treatment;
Then fabric is put in water, with the pH value of glacial acetic acid regulation water to 5, add cellulase Tenzym100W
2.5%, it is warming up to 57 DEG C, processes 60min, then with soda regulation pH value to 9.5, be warming up to 84 DEG C and process 12min, terminate enzyme
Catalyzing hydrolysis effect, makes enzyme inactivate.
Printing technology process is carried out again by the way of spray printing;Wherein thickening agent is by following weight parts preparation of raw material: oxygen
Change dyestuff 32 parts, sodium alginate 17 parts, synthetic thickening agent 1.2 parts, 3 parts of sodium chloride, the water of surplus;Add after heating water to 40 DEG C
Enter remaining raw material, after mix and blend 15min, be warming up to 60 DEG C, regulate pH to 6.5.
Carrying out steaming and color fixing by rapid ageing machine, steaming and color fixing temperature is 124 DEG C, and the steaming and color fixing time is 9min.
Last dipping in antibiotic finishing solution, obtains product after dipping.Wherein antibacterial finishing agent weight hundred in antibiotic finishing solution
Proportion by subtraction content is 0.15%, and described antibacterial finishing agent is made up of the component of following weight portion: lauryl glucosyl 40 parts, second
Phenoxyl quinoline 20 parts, hexamethylene 20 parts.
Embodiment 3:
A kind of production method of super soft fabric, by 40 parts of long-staple cotton fibers, 10 parts of bamboo fibres, 30 parts of Modal fibres, 20
Part WATER-SOLUBLE PVA FIBER, 5 parts of viscose anion function fiber weavings compositions;
First fabric is carried out pre-treatment;
Then fabric is put in water, with the pH value of glacial acetic acid regulation water to 5.5, add cellulase Tenzym100W
3%, it is warming up to 59 DEG C, processes 40min, then with soda regulation pH value to 10.5, be warming up to 87 DEG C and process 10min, terminate enzyme
Catalyzing hydrolysis effect, makes enzyme inactivate.
Printing technology process is carried out again by the way of spray printing;Wherein thickening agent is by following weight parts preparation of raw material: oxygen
Change dyestuff 50 parts, sodium alginate 25 parts, synthetic thickening agent 2 parts, 5 parts of sodium chloride, the water of surplus;Add after heating water to 45 DEG C
Remaining raw material, is warming up to 65 DEG C after mix and blend 15min, regulate pH to 7.
Carrying out steaming and color fixing by rapid ageing machine, steaming and color fixing temperature is 128 DEG C, and the steaming and color fixing time is 8min.
Last dipping in antibiotic finishing solution, obtains product after dipping.Wherein antibacterial finishing agent weight hundred in antibiotic finishing solution
Proportion by subtraction content is 0.25%, and described antibacterial finishing agent is made up of the component of following weight portion: lauryl glucosyl 50 parts, second
Phenoxyl quinoline 30 parts, hexamethylene 30 parts.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all spirit in the present invention and
Within principle, any modification, equivalent substitution and improvement etc. made, should be included within the scope of the present invention.
Claims (7)
1. the production method of a super soft fabric, it is characterised in that:
Described fabric is by 25~40 parts of long-staple cotton fibers, 5~10 parts of bamboo fibres, 10~30 parts of Modal fibres, 10~20 parts of water
Soluble PVA fiber, 3~5 parts of viscose anion function fiber weaving compositions;
Carry out pre-treatment, ferment treatment, stamp, steaming and color fixing and Final finishing processing, obtain product.
A kind of production method of super soft fabric, it is characterised in that: described ferment treatment uses cellulose
Ferment treatment.
A kind of production method of super soft fabric, it is characterised in that: described method of enzymatically treating is: will
Fabric is put in water, with the pH value of glacial acetic acid regulation water to 4.5~5.5, adds cellulase Tenzym100W 2~3%, rises
Temperature to 56~59 DEG C, process 40~80min, then with soda regulation pH value to 9~10.5, be warming up to 81~87 DEG C process 10~
15min, terminates the catalyzing hydrolysis effect of enzyme, makes enzyme inactivate.
A kind of production method of super soft fabric, it is characterised in that: described stamp uses the side of spray printing
Formula carries out printing technology process;Wherein thickening agent is by following weight parts preparation of raw material: oxidation dye 15~50 parts, sodium alginate
10~25 parts, synthetic thickening agent 0.5~2 parts, sodium chloride 1~5 parts, the water of surplus;It is added after heating water to 35~45 DEG C
Remaining raw material, is warming up to 55~65 DEG C after mix and blend 15min, regulate pH to 6~7.
A kind of production method of super soft fabric, it is characterised in that: steamed by rapid ageing machine
Changing fixation, steaming and color fixing temperature is 120~128 DEG C, and the steaming and color fixing time is 8~10min.
6. according to the production method of super soft fabric a kind of described in any one of claim 1 to 5, it is characterised in that: described Final finishing
Step be in antibiotic finishing solution impregnate, wherein in antibiotic finishing solution antibacterial finishing agent weight percent content be 0.05~
0.25%.
A kind of production method of super soft fabric, it is characterised in that: described antibacterial finishing agent is by as follows
The component composition of weight portion: lauryl glucosyl 30~50 parts, ethoxy quinoline 10~30 parts, cosmocil stearate
Hydrochlorate 10~30 parts.