CN106191486A - 一种烤瓷牙用复合材料的制备方法 - Google Patents
一种烤瓷牙用复合材料的制备方法 Download PDFInfo
- Publication number
- CN106191486A CN106191486A CN201610822416.0A CN201610822416A CN106191486A CN 106191486 A CN106191486 A CN 106191486A CN 201610822416 A CN201610822416 A CN 201610822416A CN 106191486 A CN106191486 A CN 106191486A
- Authority
- CN
- China
- Prior art keywords
- mixture
- baking
- composite
- preparation
- ceramic tooth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种烤瓷牙用复合材料的制备方法,该复合材料由秸秆,镍,钼,纳米银,铁,锰和钛混合而成。制备方法:步骤1.按质量百分比计取秸秆,镍,钼,铁,锰和钛,加入球磨机中混合,边搅拌边研磨后得混合物Ⅰ;步骤2.将混合物Ⅰ用超声波破碎1‑3小时得混合物Ⅱ;步骤3.再将混合物Ⅱ置于坩埚中搅拌混合,再加入纳米银搅拌并加热到1400‑1700℃,保温3‑5小时,将熔液导入模具中,以5‑10℃/min降温1‑3min后再以10‑15℃/min降温形成铸快,表面整理后即可。本复合材料耐用,具有良好的前景。
Description
技术领域
本发明涉及陶瓷牙材料领域,具体涉及一种烤瓷牙用复合材料及其制备方法。
背景技术
牙齿患病率较高,在我国,牙齿患者达到8亿之多,而牙齿缺损、牙列缺裂和牙列缺失又是牙病中的常见疾病,通常采用义齿进行修复。复合材料材料强度、硬度、耐磨性、耐久性和韧性等力学性能优良,成了主要的修复材料。
金属烤瓷牙是经高温将烤瓷粉熔附在复合材料底材上形成的口腔修复体,所述的烤瓷牙就是在金属牙冠上涂覆一层釉料类材料,通过高温煅烧使釉料材料熔融形成近似于真牙的颜色和光泽的义齿修复体,既具有金属材料强度高、韧性好等优点,又具有陶瓷材料的耐腐蚀性及较好的生物相容性等特点。
目前,金属烤瓷牙多以普通镍铬复合材料烤瓷牙居多,使用后可能会与人体发生过敏反应,所以需要研发新的复合材料材料,或者煅烧参数,寻求高质量的烤瓷牙。
发明内容
针对现有技术的不足,本发明的目的在于提供一种烤瓷牙用复合材料及其制备方法,所得烤瓷牙经久耐用。
一种烤瓷牙用复合材料,包括以下按质量百分比计的原料:秸秆10-15%,镍16-22%,钼1-6%,纳米银6-8%,铁0.5-1.2%,锰2-6%,余量为钛。
作为优选的是,上述烤瓷牙用复合材料,包括以下按质量百分比计的原料:秸秆粉12-14%,镍18-20%,钼2-5%,纳米银6-8%,铁0.8-1.0%,锰4-6%,余量为钛。
上述烤瓷牙用贵复合材料的制备方法,包括以下步骤:
步骤1,按质量百分比计取秸秆,镍,钼,铁,锰和钛,加入球磨机中混合,边搅拌边研磨后得混合物Ⅰ;
步骤2,将混合物Ⅰ用超声波破碎1-3小时得混合物Ⅱ;
步骤3,再将混合物Ⅱ置于坩埚中搅拌混合,再加入纳米银搅拌并加热到1400-1700℃,保温3-5小时,将熔液导入模具中,以5-10℃/min降温1-3min后再以10-15℃/min降温形成铸快,表面整理后即可。
作为上述烤瓷牙用复合材料的制备方法,步骤1,球磨4-5h。
作为上述烤瓷牙用复合材料的制备方法,步骤2,超声波功率为30-45W。
作为上述烤瓷牙用复合材料的制备方法,步骤3,搅拌速度为120-240rpm。
有益效果
本发明复合材料利用秸秆为原料,结合贵金属制成复合材料,硬度高,耐高温,耐酸碱,并且具有抑菌的效果,改善了陶瓷材料易碎、硬度差的问题,另外,秸秆的价格低,降低了烤瓷牙的成本。
具体实施方式
实施例1
一种烤瓷牙用复合材料,包括以下按质量百分比计的原料:秸秆10%,镍16%,钼1%,纳米银6%,铁0.5%,锰2%,余量为钛。
上述烤瓷牙用复合材料的制备方法,包括以下步骤:
步骤1,按质量百分比计取秸秆,镍,钼,铁,锰和钛,加入球磨机中混合,边搅拌边研磨4h后得混合物Ⅰ;
步骤2,将混合物Ⅰ用30W超声波破碎1小时得混合物Ⅱ;
步骤3,再将混合物Ⅱ置于坩埚中搅拌混合,加入纳米银以120rpm搅拌并加热到1400℃,保温3小时,将熔液导入模具中,以5℃/min降温1-3min后再以10℃/min降温后形成铸快,表面整理后即可。
实施例2
一种烤瓷牙用复合材料,包括以下按质量百分比计的原料:秸秆12%,镍18%,钼2%,纳米银6%,铁0.8%,锰4%,余量为钛。
上述烤瓷牙用复合材料的制备方法,包括以下步骤:
步骤1,按质量百分比计取秸秆,镍,钼,铁,锰和钛,加入球磨机中混合,边搅拌边研磨4.5h后得混合物Ⅰ;
步骤2,将混合物Ⅰ用38W超声波破碎1.8小时得混合物Ⅱ;
步骤3,再将混合物Ⅱ置于坩埚中搅拌混合,再加入纳米银以160rpm搅拌并加热到1500℃,保温4小时,将熔液导入模具中,以7℃/min降温2min后再以12℃/min降温后形成铸快,表面整理后即可。
实施例3
一种烤瓷牙用复合材料,包括以下按质量百分比计的原料:秸秆14%,镍20%, 5%,纳米银8%,铁1.0%,锰6%,余量为钛。
上述烤瓷牙用复合材料的制备方法,包括以下步骤:
步骤1,按质量百分比计取秸秆,镍,钼,铁,锰和钛,加入球磨机中混合,边搅拌边研磨5h后得混合物Ⅰ;
步骤2,将混合物Ⅰ用40W超声波破碎2.4小时得混合物Ⅱ;
步骤3,再将混合物Ⅱ置于坩埚中搅拌混合,以200rpm搅拌并加热到1600℃,保温4.8小时,将熔液导入模具中,以8℃/min降温3min后再以14℃/min降温后形成铸快,表面整理后即可。
实施例4
一种烤瓷牙用复合材料,包括以下按质量百分比计的原料:秸秆15%,镍22%,钼6%,纳米银8%,铁1.2%,锰6%,余量为钛。
上述烤瓷牙用复合材料的制备方法,包括以下步骤:
步骤1,按质量百分比计取秸秆,镍,钼,铁,锰和钛,加入球磨机中混合,边搅拌边研磨5h后得混合物Ⅰ;
步骤2,将混合物Ⅰ用45W超声波破碎3小时得混合物Ⅱ;
步骤3,再将混合物Ⅱ置于坩埚中搅拌混合,以240rpm搅拌并加热到1700℃,保温5小时,将熔液导入模具中,以10℃/min降温3min后再以15℃/min降温降温后形成铸快,表面整理后即可。
对比例
一种烤瓷牙用复合材料,包括以下按质量百分比计的原料:秸秆10%,镍16%,钼1%,铁0.5%,锰2%,余量为钛。
上述烤瓷牙用复合材料的制备方法,包括以下步骤:
步骤1,按质量百分比计取秸秆,镍,钼,铁,锰和钛,加入球磨机中混合,边搅拌边研磨4h后得混合物Ⅰ;
步骤2,将混合物Ⅰ用30W超声波破碎1小时得混合物Ⅱ;
步骤3,再将混合物Ⅱ置于坩埚中搅拌混合,加入纳米银以120rpm搅拌并加热到1400℃,保温3小时,将熔液导入模具中,以5℃/min降温1-3min后再以10℃/min降温后形成铸快,表面整理后即可。
性能试验
将本发明制备的复合材料和对比例相比,所得数据如下表所示。
通过比较实施例1-4和对比例可知,本发明的复合材料改善了陶瓷材料的性能,硬度高、耐高温、耐酸碱性好,另外具有抗菌能力,作为陶瓷牙的材料可以更好地保护牙齿的质量,延长使用时间。
Claims (1)
1.一种烤瓷牙用复合材料的制备方法,其特征在于,烤瓷牙用复合材料包括以下按质量百分比计的原料:秸秆10-15%,镍16-22%,钼1-6%,纳米银6-8%,铁0.5-1.2%,锰2-6%,余量为钛;
所述的烤瓷牙用复合材料的制备方法,包括以下步骤:
步骤1,按质量百分比计取秸秆,镍,钼,铁,锰和钛,加入球磨机中混合,边搅拌边研磨后得混合物Ⅰ;
步骤2,将混合物Ⅰ用超声波破碎1-3小时得混合物Ⅱ;
步骤3,再将混合物Ⅱ置于坩埚中搅拌混合,再加入纳米银搅拌并加热到1400-1700℃,保温3-5小时,将熔液导入模具中,以5-10℃/min降温1-3min后再以10-15℃/min降温形成铸快,表面整理后即可。