CN102978445A - 一种用于烤瓷牙镍铬基合金及其制备方法 - Google Patents
一种用于烤瓷牙镍铬基合金及其制备方法 Download PDFInfo
- Publication number
- CN102978445A CN102978445A CN2012104400964A CN201210440096A CN102978445A CN 102978445 A CN102978445 A CN 102978445A CN 2012104400964 A CN2012104400964 A CN 2012104400964A CN 201210440096 A CN201210440096 A CN 201210440096A CN 102978445 A CN102978445 A CN 102978445A
- Authority
- CN
- China
- Prior art keywords
- based alloy
- nickel
- chromium
- baking
- ingot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明介绍了一种用于烤瓷牙镍铬基合金及其制备方法，重量化学成分为：铬22~25%，钼4~8%，钨2~6%，铝1~2%，铌0.5~1%，钛1~2%，硅1~2%，铈0.2~0.5%，硼0.1~0.4%，其余为镍。将符合权利要求1化学成分的配料装入高温陶瓷坩埚中，并在真空中频或高频炉加热熔化；将高温熔化液搅拌5~10秒钟；将搅拌均匀的熔化液浇铸到方形模具或圆柱形模具中，自然冷却后形成铸块；将铸块经喷砂除去其表面附着物；最后将铸块抛光就成为烤瓷牙用镍铬基合金。本发明的合金强度、硬度和韧性适中，各种性能与进口产品接近，经烤瓷后，釉料层与金属基体的结合牢固，外观色泽一致、逼真、完美。
Description
技术领域
本发明涉及一种合金材料的技术，特别是一种用于烤瓷牙镍铬基合金及其制备方法。
背景技术
镍铬基合金是制作烤瓷牙的主要合金，它可以铸造牙冠、支架及其它金属部件。而大多数镍铬基合金存在的主要问题是：1）强度和硬度都较高，但韧性差，易断裂；2）二次熔化后各种性能有所降低，因此不能重复使用。
发明内容
本发明所要解决的技术问题是提供一种用于烤瓷牙镍铬基合金及其制备方法, 提供工序简单、操作方便的用于制作烤瓷牙牙冠和支架的镍铬基合金。
为了实现解决上述技术问题的目的，本发明采用了如下技术方案：
本发明的一种用于烤瓷牙镍铬基合金，其特征在于：镍铬基合金的重量化学成分为：铬22~25%，钼4~8%，钨2~6%，铝1~2%，铌0.5~1%，钛1~2%，硅1~2%，铈0.2~0.5%，硼0.1~0.4%，其余为镍。
本发明的一种用于烤瓷牙镍铬基合金的制备方法为：将符合上述化学成分的配料装入高温陶瓷坩埚中，并在真空中频或高频炉加热熔化；将高温熔化液搅拌5~10秒钟；将搅拌均匀的熔化液浇铸到方形模具或圆柱形模具中，自然冷却后形成铸块；将铸块经喷砂除去其表面附着物；最后将铸块抛光就成为烤瓷牙用镍铬基合金。
进一步优选的，所述的方形模具的规格为10×10×10mm，圆柱形模具的规格为Ф10×10mm。
通过采用上述技术方案，本发明具有以下的有益效果：
本发明的一种用于烤瓷牙镍铬基合金，其强度、硬度和韧性适中，各义齿加工厂试用表明，其各种性能与进口产品接近，经烤瓷后，釉料层与金属基体的结合牢固，外观色泽一致、逼真、完美。
具体实施方式
下面结合实施例对本专利进一步解释说明。但本专利的保护范围不限于具体的实施方式。
按以下化学组分配料（质量%）：
序号 镍 铬 钼 钨 铝 铌 钛 硅 铈 硼
A 61.2 23 5 6 1 0.5 1 2 0.2 0.1
B 62.1 25 4 2 2 1 2 1 0.5 0.4
C 59.5 22 8 4 2 0.8 1.5 1.5 0.4 0.3
D 59.3 24 6 5 1.5 0.7 1.8 1.2 0.3 0.2
E 60.6 23.5 7 3 1.8 0.6 1.3 1.8 0.2 0.2
将上述化学成分的配料装入高温坩埚中，并在真空中频或高频炉加热熔化；将高温熔化液搅拌5~10秒钟；将搅拌均匀的熔化液浇铸到10×10×10mm的方形模具或Ф10×10mm的圆柱形模具中，自然冷却后形成铸块；将铸块经喷砂除去其表面附着物；最后将铸块抛光就成为烤瓷牙用镍铬基合金。
Claims (3)
1.一种用于烤瓷牙镍铬基合金，其特征是：镍铬基合金的重量化学成分为：铬22~25%，钼4~8%，钨2~6%，铝1~2%，铌0.5~1%，钛1~2%，硅1~2%，铈0.2~0.5%，硼0.1~0.4%，其余为镍。
2.根据权利要求1所述用于烤瓷牙镍铬基合金的制备方法，其特征是：将符合权利要求1化学成分的配料装入高温陶瓷坩埚中，并在真空中频或高频炉加热熔化；将高温熔化液搅拌5~10秒钟；将搅拌均匀的熔化液浇铸到方形模具或圆柱形模具中，自然冷却后形成铸块；将铸块经喷砂除去其表面附着物；最后将铸块抛光就成为烤瓷牙用镍铬基合金。
3.根据权利要求1所述用于烤瓷牙镍铬基合金的制备方法，其特征是：所述的方形模具的规格为10×10×10mm，圆柱形模具的规格为：Ф10×10mm。