CN106076343A - 一种高选择性石油树脂加氢催化剂 - Google Patents
一种高选择性石油树脂加氢催化剂 Download PDFInfo
- Publication number
- CN106076343A CN106076343A CN201610555282.0A CN201610555282A CN106076343A CN 106076343 A CN106076343 A CN 106076343A CN 201610555282 A CN201610555282 A CN 201610555282A CN 106076343 A CN106076343 A CN 106076343A
- Authority
- CN
- China
- Prior art keywords
- catalyst
- oxide
- tio
- cuo
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高选择性石油树脂加氢催化剂,涉及催化剂制备技术领域,以氧化铜、镍和纳米二氧化钛为活性组分,纳米氧化铝为载体,所述活性组分与载体的质量比为2:8,氧化铜、镍与纳米二氧化钛的质量比为2:0.5:8。本发明先将氧化铜与镍负载于纳米二氧化钛上制得CuO‑Ni/TiO2,再均匀负载于纳米氧化铝上制得催化剂,该催化剂具有活性强、转化率和选择性高且稳定性好的特点,能有效改善石油树脂存在的颜色深、气味臭、热氧稳定性低、黏结力和相容性差等缺点,从而扩大石油树脂的应用范围。
Description
技术领域:
本发明涉及催化剂制备技术领域,具体涉及一种高选择性石油树脂加氢催化剂。
背景技术:
石油树脂是以乙烯装置的C5、C9馏分为主要原料,经聚合后制得的固态或粘稠状的低相对分子质量聚合物。由于石油树脂具有酸值小、混溶性好、熔点低、粘合性好、耐水和耐化学品等特点,因此被广泛应用于粘胶带、热熔胶、道路用涂料、油墨以及橡胶等方面。普通石油树脂存在颜色深、气味臭、热氧稳定性低、黏结力和相容性差等缺点,这些缺点主要是由于分子中的不饱和键含量高所致,而对石油树脂进行加氢改性能很好地解决此问题。
石油树脂的加氢难度较大,加氢工艺的操作条件严苛。目前我国对色度浅、热稳定性强的加氢石油树脂需求量增大,这将需要配合使用大量的加氢催化剂。而国内加氢工艺大多使用进口钯系催化剂,存在成本高的缺点,不利于在国内大量生产。
发明内容:
本发明所要解决的技术问题在于提供一种活性强、转化率和选择性高且稳定性好的高选择性石油树脂加氢催化剂。
本发明所要解决的技术问题采用以下的技术方案来实现:
一种高选择性石油树脂加氢催化剂,以氧化铜、镍和纳米二氧化钛为活性组分,纳米氧化铝为载体,所述活性组分与载体的质量比为2:8,氧化铜、镍与纳米二氧化钛的质量比为2:0.5:8;其制备方法为:先将氧化铜与镍负载于纳米二氧化钛上制得CuO-Ni/TiO2,再均匀负载于纳米氧化铝上制得催化剂。
其具体制备步骤如下:
(1)CuO-Ni/TiO2制备:将氧化铜和镍加入8-10倍重量的水中,充分分散后静置1h,再于超声频率40kHz、功率100W下超声处理30min,然后向处理液中加入纳米二氧化钛,混合均匀后于微波频率2450MHz、功率700W下微波处理10min,将所得混合物于100-110℃下干燥12h,再于500-600℃下焙烧3h,即得CuO-Ni/TiO2;
(2)催化剂制备:将制得的CuO--Ni/TiO2研磨成粉末,并加等量水搅拌制成膏状物,再加入载体纳米氧化铝,充分混合后于超声频率40kHz、功率50W下超声处理30min,处理结束后于0-5℃下静置3h,然后转入室温下使混合物自然恢复到室温,再于100-110℃下干燥8h,最后于550-650℃下焙烧5h,即得催化剂。
本发明的有益效果是:本发明先将氧化铜与镍负载于纳米二氧化钛上制得CuO-Ni/TiO2,再均匀负载于纳米氧化铝上制得催化剂,该催化剂适用于石油树脂的加氢反应,具有活性强、转化率和选择性高且稳定性好的特点,能有效改善石油树脂存在的颜色深、气味臭、热氧稳定性低、黏结力和相容性差等缺点,从而扩大石油树脂的应用范围。
具体实施方式:
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
实施例1
(1)CuO-Ni/TiO2制备:将氧化铜和镍加入8倍重量的水中,充分分散后静置1h,再于超声频率40kHz、功率100W下超声处理30min,然后向处理液中加入纳米二氧化钛,混合均匀后于微波频率2450MHz、功率700W下微波处理10min,将所得混合物于100-110℃下干燥12h,再于500-600℃下焙烧3h,即得CuO-Ni/TiO2;
(2)催化剂制备:将制得的CuO--Ni/TiO2研磨成粉末,并加等量水搅拌制成膏状物,再加入载体纳米氧化铝,充分混合后于超声频率40kHz、功率50W下超声处理30min,处理结束后于0-5℃下静置3h,然后转入室温下使混合物自然恢复到室温,再于100-110℃下干燥8h,最后于550-650℃下焙烧5h,即得催化剂。
其中,活性组分与载体的质量比为2:8,氧化铜、镍与纳米二氧化钛的质量比为2:0.5:8。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (2)
1.一种高选择性石油树脂加氢催化剂,其特征在于:以氧化铜、镍和纳米二氧化钛为活性组分,纳米氧化铝为载体,所述活性组分与载体的质量比为2:8,氧化铜、镍与纳米二氧化钛的质量比为2:0.5:8;其制备方法为:先将氧化铜与镍负载于纳米二氧化钛上制得CuO-Ni/TiO2,再均匀负载于纳米氧化铝上制得催化剂。
2.根据权利要求1所述的高选择性石油树脂加氢催化剂,其特征在于,其具体制备步骤如下:
(1)CuO-Ni/TiO2制备:将氧化铜和镍加入8-10倍重量的水中,充分分散后静置1h,再于超声频率40kHz、功率100W下超声处理30min,然后向处理液中加入纳米二氧化钛,混合均匀后于微波频率2450MHz、功率700W下微波处理10min,将所得混合物于100-110℃下干燥12h,再于500-600℃下焙烧3h,即得CuO-Ni/TiO2;
(2)催化剂制备:将制得的CuO--Ni/TiO2研磨成粉末,并加等量水搅拌制成膏状物,再加入载体纳米氧化铝,充分混合后于超声频率40kHz、功率50W下超声处理30min,处理结束后于0-5℃下静置3h,然后转入室温下使混合物自然恢复到室温,再于100-110℃下干燥8h,最后于550-650℃下焙烧5h,即得催化剂。