CN106011822B - 一种钕铁硼磁性材料磷化液 - Google Patents
一种钕铁硼磁性材料磷化液 Download PDFInfo
- Publication number
- CN106011822B CN106011822B CN201610550050.6A CN201610550050A CN106011822B CN 106011822 B CN106011822 B CN 106011822B CN 201610550050 A CN201610550050 A CN 201610550050A CN 106011822 B CN106011822 B CN 106011822B
- Authority
- CN
- China
- Prior art keywords
- magnet
- neodymium
- iron
- phosphating
- phosphatization
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及钕铁硼磁性材料表面处理领域,主要应用于钕铁硼磁性材料表面防腐,其特征在于:磷酸二氢锌30‑100g/L,磷酸100‑200g/L,鞣酸10‑15g/L,硝酸钙5‑10g/L,钼酸铵10‑20g/L,植酸50‑70g/L,辅助成膜剂10‑30g/L,其余为水。使用本发明的磷化液处理钕铁硼材料,由于磷化液酸性弱,对磁体无腐蚀,磷化前后磁体的不可逆、磁通(Br)、矫顽力(Hcj)等磁性能保持不变,尤其针对于厚度小于5mm,单重小于5g的小片磁体。且磷化液中加入植酸,成膜速度快,磷化膜小于2µm,远远薄于传统磷化膜,但耐蚀性仍然比传统磷化液好,其耐高温湿热时间4小时,磁体表面无红锈,可作为最终的防护膜层。
Description
技术领域
本发明涉及磁体技术领域,具体涉及一种钕铁硼磁性材料磷化液,主要应用于钕铁硼磁性材料表面防腐。
背景技术
钕铁硼磁体作为第三代稀土永磁材料,具有极高的磁能积和矫顽力,同时高能量密度的优点使其不仅广泛应用于信息技术、汽车、核磁共振和电机等领域,在风力发电和混合动力车等环保新能源领域的应用也日趋增多。钕铁硼的高磁性能源于其特殊的化学成分和晶相结构:钕铁硼磁体由Nd2Fe14B主相和晶间富Nd相构成,这种多相结构的各相之间电化学位相差较大,易引起电化学腐蚀,而钕又是化学活性最高的元素之一,在潮湿的环境下,磁体表面易形成局部腐蚀的微电池,增大了腐蚀速度,锈蚀后磁体磁性能下降,限制了其应用,故使用前需要在其表面涂敷耐蚀层。鉴于钕铁硼磁性材料的市场前景及重要地位,国内外诸多研究人员、生产商研究了钕铁硼磁性材料的表面防腐技术,其中包括金属涂层、有机涂层、复合涂层等。但是这些防腐技术工艺操作复杂,对环境污染严重,成本较高,对磁体形状尺寸要求较高,且表面处理后影响磁体的磁性能,所以大大限制了其应用范围。
专利201210151991.4提出了钕铁硼磁性材料锌系磷化液及其使用方法,但是其主要作用是作为喷涂等底层处理。
专利201210481482.8提出了一种提高钕铁硼永磁体表面磷化膜耐蚀性的方法,但是其磷化时间长、磷化工艺复杂,能耗大且生产效率低。
专利201510412944.4提出了一种作为磁性材料终处理防护层磷化液,但是此磷化液配方复杂,且磷化液温度较高,没有分析对磁体磁性能的影响。
发明内容
本发明的目的是克服现有技术的不足,提供一种新的钕铁硼磁性材料磷化液,不仅能提高磁体表面耐蚀性,可作为钕铁硼磁性材料最终防护层,同时不影响磁体磁性能。
根据本发明的钕铁硼磁性材料磷化液,其特征在于磷酸二氢锌30-100g/L,磷酸100-200g/L,鞣酸10-15g/L,硝酸钙 5-10g/L,钼酸铵10-20g/L,植酸50-70g/L,辅助成膜剂10-30g/L,其余为水。
辅助成膜剂为硝酸镍、硫酸镍或钨酸钠其中的一种或两种;磷化工作液游离酸2-6点,总酸8-15点。
根据本发明的钕铁硼磁性材料的磷化液磷化工艺,其特征在于磷化工艺为:脱脂—除锈—磷化(工作液游离酸2-6点,总酸8-15点,磷化工作液温度40-70℃,磷化时间20S-600S)—清洗—烘干,烘干后得到均匀而致密的磷化膜。
使用本发明的有益技术效果为:
1、磷化液处理钕铁硼材料,磷化液酸性弱,对磁体表面腐蚀小,磷化前后磁体的不可逆、磁通(Br)、矫顽力(Hcj)等磁性能几乎保持不变,尤其针对于厚度小于5mm,单重小于5g的小片磁体;
2、磷化液中加入植酸,植酸与钕铁硼表面迅速反应,形成的络合物难溶于溶液,均匀沉积在磁体表面,从而增加了产品的耐蚀性;
3、磷化成膜速度快,磷化膜均匀而致密,虽磷化膜小于2µm,但其耐蚀性好,高温湿热试验4小时,磁体仍然无红锈,可作为磁体最终的防护膜层,克服了传统磷化液耐蚀性差的弊端;
4、此磷化液配方简单、经济环保,磷化后产品表面无有害物质,表面成分主要为Zn、P等元素,且磷化工艺简单方便操作。
附图说明
图1为磁体磷化膜照片。
图2为表面磷化膜能谱分析。
具体实施方式
实施例1
钕铁硼基体尺寸为13.4mm*3.8mm*14.5mm,形状为异形,单重为4.430g磁体,磁通计型号HT700,线圈XQ-2。
一种钕铁硼磁性材料磷化液,由以下浓度的组份组成:磷酸二氢锌100g/L,磷酸200g/L,鞣酸15g/L,硝酸钙 10g/L,钼酸铵20g/L,植酸50g/L,辅助成膜剂30g/L,其余为水。将所述磷化液与纯水以体积比为3:1的比例混合,稀释,磷化工作液温度为 70℃,用NaOH调整磷化液酸度,游离酸5.5点,总酸13.5点,磁体除油、除锈后浸泡在磷化工作液中600S,清洗烘干后得到磷化磁体。本磷化液溶液性质稳定,得到的磷化膜致密均匀,做高温湿热试验4h磁体表面未出现红锈。磁体磷化前磁通(Br)为4.620 mWb,新磷化液磷化后磁体的Br为4.612mWb,磷化前后Br保持率高达99.8%,而传统磷化液磷化后磁体Br为4.528mWb,Br保持率仅98.0%,新磷化液与传统磷化液磷化前后磁体磁性能保持率对比见附表1。
实施例2
钕铁硼基体尺寸为13.4mm*3.8mm*14.5mm,形状为异形,单重为4.429g磁体,磁通计型号HT700,线圈XQ-2。
一种钕铁硼磁性材料磷化液,由以下浓度的组份组成 :磷酸二氢锌100g/L,磷酸180g/L,鞣酸13g/L,硝酸钙 7g/L,钼酸铵14g/L,植酸65g/L,辅助成膜剂15g/L,其余为水。将所述磷化液与纯水以体积比为4:1 的比例混合,稀释,磷化工作液温度为 50℃,用NaOH调整磷化液酸度,游离酸4.8点,总酸12.5点,磁体经除油、除锈后浸泡在磷化工作液中300S,清洗烘干后得到磷化磁体。本磷化液溶液性质稳定,得到的磷化膜致密均匀,做高温湿热试验2.5小时磁体表面未出现红锈。磁体磷化前Br为4.605 mWb,磷化后磁体的Br为4.597 mWb,磷化前后Br保持率高达99.8%,而传统磷化液磷化后磁体Br为4.508mWb,Br保持率仅97.9%,新磷化液与传统磷化液磷化前后磁体磁性能保持率对比见附表1。
实施例3
钕铁硼基体尺寸为13.4mm*3.8mm*14.5mm,形状为异形,单重为4.432g磁体,磁通计型号HT700,线圈XQ-2。
一种钕铁硼磁性材料磷化液,由以下浓度的组份组成 :磷酸二氢锌60g/L,磷酸150g/L,鞣酸10g/L,硝酸钙 5g/L,钼酸铵10g/L,植酸68g/L,辅助成膜剂17g/L,其余为水。将所述磷化液与纯水以体积比为6:1 的比例混合,稀释,磷化工作液温度为 50℃,用NaOH调整磷化液酸度,游离酸4.5点,总酸12.0点,磁体经除油、除锈后浸泡在磷化工作液中60S,清洗烘干后得到磷化磁体。本磷化液溶液性质稳定,得到的磷化膜致密均匀,做高温湿热试验2小时磁体表面未出现红锈。磷化前磁体Br为4.638 mWb,新磷化液磷化后磁体的Br为4.629 mWb,磷化前后Br保持率高达99.8%,而传统磷化液磷化后磁体Br为4.546mWb,Br保持率仅98.2%,新磷化液与传统磷化液磷化前后磁体磁性能保持率对比见附表1。
实施例4
钕铁硼基体尺寸为13.4mm*3.8mm*14.5mm,形状为异形,单重为4.428g磁体,磁通计型号HT700,线圈XQ-2。
一种钕铁硼磁性材料磷化液,由以下浓度的组份组成 :磷酸二氢锌30g/L,磷酸100g/L,鞣酸10g/L,硝酸钙 8g/L,钼酸铵10g/L,植酸70g/L,辅助成膜剂15g/L,其余为水。将所述磷化液与纯水以体积比为5:2的比例混合,稀释,磷化工作液温度为 50℃,用NaOH调整磷化液酸度,游离酸2.0点,总酸8.0点,对除锈后的磁性材料浸泡磷化工作液中20S,清洗烘干后,得到磷化磁体。本磷化液溶液性质稳定,得到的磷化膜致密均匀,做高温湿热试验2h磁体表面未出现红锈。磷化前磁体Br为4.602 mWb,磷化后磁体的Br为4.590 mWb,磷化前后Br保持率高达99.7%,而传统磷化液磷化后磁体Br为4.519mWb,Br保持率仅98.2%,新磷化液与传统磷化液磷化前后磁体磁性能保持率对比见附表1。
附表1
新磷化液与传统磷化液磷化前后磁体磁性能保持率对比表
Claims (5)
1.一种钕铁硼磁性材料磷化液,其特征在于:由以下组份组成,
磷酸二氢锌30-100g/L,磷酸100-200g/L,鞣酸10-15g/L,硝酸钙 5-10g/L,钼酸铵10-20g/L,植酸50-70g/L,辅助成膜剂10-30g/L,其余为水;所述辅助成膜剂为硝酸镍、硫酸镍或钨酸钠其中的一种或两种;磷化工作液游离酸2-6点,总酸8-15点。
2.根据权利要求1所述的一种钕铁硼磁性材料磷化液,其特征在于:由以下组份组成:磷酸二氢锌40-90g/L,磷酸100-180g/L,鞣酸12-15g/L,硝酸钙 7-10g/L,钼酸铵13-20g/L,植酸50-65g/L,辅助成膜剂15-25g/L,其余为水。
3.权利要求1-2任一一种钕铁硼磁性材料磷化液的使用方法,其特征在于:磷化工艺步骤包括脱脂—除锈—磷化—清洗—烘干。
4.根据权利要求3所述的一种钕铁硼磁性材料磷化液的使用方法,其特征在于:磷化步骤中的工作液温度40-70℃,磷化时间20S-600S,磷化液与水的体积比为3-6:1。
5.根据权利要求3所述的一种钕铁硼磁性材料磷化液的使用方法,其特征在于:对于厚度小于5mm,单重小于5g的磁体,磷化步骤后磁体Br保持率≥99.5%。