CN105774157A - 一种大型油囊水囊用tpu复合面料 - Google Patents

一种大型油囊水囊用tpu复合面料 Download PDF

Info

Publication number
CN105774157A
CN105774157A CN201610192952.7A CN201610192952A CN105774157A CN 105774157 A CN105774157 A CN 105774157A CN 201610192952 A CN201610192952 A CN 201610192952A CN 105774157 A CN105774157 A CN 105774157A
Authority
CN
China
Prior art keywords
tpu
type
polyether
polyester
corona
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201610192952.7A
Other languages
English (en)
Other versions
CN105774157B (zh
Inventor
徐咏春
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong yuqilu Plastic Technology Co.,Ltd.
Original Assignee
Guangzhou Yu Qilu Plastic Cement Science And Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangzhou Yu Qilu Plastic Cement Science And Technology Ltd filed Critical Guangzhou Yu Qilu Plastic Cement Science And Technology Ltd
Priority to CN201610192952.7A priority Critical patent/CN105774157B/zh
Publication of CN105774157A publication Critical patent/CN105774157A/zh
Application granted granted Critical
Publication of CN105774157B publication Critical patent/CN105774157B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种大型油囊水囊用TPU复合面料，其由上至下依次包括聚酯型TPU面膜层、第一胶水粘合层、纤维布层及第二胶水粘合层、聚醚型TPU底膜层，所述纤维布层经过电晕处理。本发明对聚酯型TPU材料进行了改性，采用三元乙丙烯橡胶和聚碳化二亚胺两种材料混合聚酯型TPU制成的薄膜，同时具有较强的耐油性和耐水解性能，结合聚醚型TPU薄膜，使得复合而成的面料耐油性和耐水解性能进一步增强，同时对纤维布进行电辊处理后再与PUR热熔胶结合，增强了复合面料的剥离强度，使得复合面料综合性能好，可以用于制作油囊或者水囊。

Description

一种大型油囊水囊用TPU复合面料
技术领域
本发明TPU复合面料技术领域，具体涉及一种可用于制作大型油囊或水囊的TPU复合面料。
背景技术
油囊水囊是用于储存和输送油、水待液体货物的工具。该类工具要求其材料本身应当具有高强度、高弹性以及优良的耐油性和耐水性，适应环境的性能强。公开号为CN104527190A的中国发明专利申请公开了一种储油囊用TPU复合材料，该申请中指出：传统的储油囊用TPU复合材料多是采用聚酯型TPU材料，虽具有优异的耐油性，但是耐水解性差，耐寒性能－25至－30℃，同时，材料的撕裂强度受到胶水的影响耐降低，影响到材料的使用性能，产生安全隐患。于是，该申请提出的技术方案是：采用水性聚氨酯涂层剂对纤维网进行改性处理，以提高PU胶水在纤维表面的附着力，从而提高复合材料的剥离强度；同时，选用聚醚型TPU树脂为原料提高复合材料的耐水解性。该技术方案虽然相比传统的复合材料在耐水性能上有所改进，但其耐水性能仍然不能达到大型水囊的使用要求。
发明内容
本发明的目的在于克服上述现有技术的缺陷，提供一种大型油囊水囊用TPU复合面料，其同时兼职了耐油性和耐水解性，同时也具有较高的剥离强度，既适用于大型油囊也适用于大型水囊。
为实现上述目的，本发明采用如下技术方案：
一种大型油囊水囊用TPU复合面料，其由上至下依次包括聚酯型TPU面膜层、第一胶水粘合层、纤维布层及第二胶水粘合层、聚醚型TPU底膜层，所述纤维布层经过电晕处理。
进一步的，所述聚酯型TPU面膜层按质量百分数计包括，聚酯型TPU83～87％、三元乙丙烯橡胶2～8％、聚碳化二亚胺3～10％、色母0.5～2％及碳酸钙0.1～1％。
进一步的，所述第一胶水粘合层和第二胶水粘合层均为PUR热熔胶层。
进一步的，所述聚醚型TPU底膜层按质量百分数计包括，聚醚型TPU80～90％、丙烯酸酯类单体5～15％、碳酸钙3～10％。
进一步的，本发明的大型油囊水囊用TPU复合面料，采用以下方法制备而成：
1)取纤维布布置在电晕辊上进行第一次电晕；
2)第一次电晕完成后，将纤维布未电晕的表面布置在电晕辊上与电晕辊接触，进行第二次电晕；
3)在纤维布的上下表面上均涂覆上PUR热熔胶；
4)制备聚酯型TPU面膜，按重量百分数计，取聚酯型TPU83～87％、三元乙丙烯橡胶2～8％、聚碳化二亚胺3～10％、色母0.5～2％及碳酸钙0.1～1％混匀后干燥，然后流延加工成聚酯型TPU面膜；
5)制备聚醚型TPU底膜，按质量百分数计，取聚醚型TPU80～90％、丙烯酸酯类单体5～15％、碳酸钙3～10％混匀后干燥，然后流延加工成聚醚型TPU底膜；
6)将涂覆了PUR热熔胶的纤维布用热风预热后，再在表面和底别分别贴合聚酯型TPU面膜和聚醚型TPU底膜。
与现有技术相比，本发明的有益效果是：
本发明对聚酯型TPU材料进行了改性，采用三元乙丙烯橡胶和聚碳化二亚胺两种材料混合聚酯型TPU制成的薄膜，同时具有较强的耐油性和耐水解性能，结合聚醚型TPU薄膜，使得复合而成的面料耐油性和耐水解性能进一步增强，同时对纤维布进行电辊处理后再与PUR热熔胶结合，增强了复合面料的剥离强度，使得复合面料综合性能好，可以用于制作油囊或者水囊。
附图说明
图1为本发明的TPU复合面料的结构示意图。
具体实施方式
下面结合附图和具体实施例子对本发明做进一步详细介绍。
实施例1
一种大型油囊水囊用TPU复合面料，其由上至下依次包括聚酯型TPU面膜层1、第一胶水粘合层2、纤维布层3及第二胶水粘合层4、聚醚型TPU底膜层5，所述纤维布层3经过电晕处理。
所述大型油囊水囊用TPU复合面料采用以下方法制备而成：
1)取纤维布布置在电晕辊上进行第一次电晕。
2)第一次电晕完成后，将纤维布未电晕的表面布置在电晕辊上与电晕辊接触，进行第二次电晕。
3)在双面经过电晕处理后的纤维布的上下表面上均涂覆上PUR热熔胶；
4)制备聚酯型TPU面膜，按重量百分数计，取聚酯型TPU83％、三元乙丙烯橡胶5％、聚碳化二亚胺10％、色母1％及碳酸钙1％混匀后干燥，然后流延加工成聚酯型TPU面膜，挤出模头的温度为170～180℃。
5)制备聚醚型TPU底膜，按质量百分数计，取聚醚型TPU90％、丙烯酸酯类单体7％、碳酸钙3％混匀后干燥，然后流延加工成聚醚型TPU底膜。
6)将涂覆了PUR热熔胶的纤维布用110～120℃热风预热后，再在表面和底别分别贴合聚酯型TPU面膜和聚醚型TPU底膜。
实施例2
一种大型油囊水囊用TPU复合面料，其由上至下依次包括聚酯型TPU面膜层1、第一胶水粘合层2、纤维布层3及第二胶水粘合层4、聚醚型TPU底膜层5，所述纤维布层3经过电晕处理。
所述大型油囊水囊用TPU复合面料采用以下方法制备而成：
1)取纤维布布置在电晕辊上进行第一次电晕。
2)第一次电晕完成后，将纤维布未电晕的表面布置在电晕辊上与电晕辊接触，进行第二次电晕。
3)在双面经过电晕处理后的纤维布的上下表面上均涂覆上PUR热熔胶；
4)制备聚酯型TPU面膜，按重量百分数计，取聚酯型TPU87％、三元乙丙烯橡胶8％、聚碳化二亚胺3％、色母1.5％及碳酸钙0.5％混匀后干燥，然后流延加工成聚酯型TPU面膜，挤出模头的温度为170～180℃。
5)制备聚醚型TPU底膜，按质量百分数计，取聚醚型TPU80％、丙烯酸酯类单体15％、碳酸钙5％混匀后干燥，然后流延加工成聚醚型TPU底膜。
6)将涂覆了PUR热熔胶的纤维布用110～120℃热风预热后，再在表面和底别分别贴合聚酯型TPU面膜和聚醚型TPU底膜。
实施例3
一种大型油囊水囊用TPU复合面料，其由上至下依次包括聚酯型TPU面膜层1、第一胶水粘合层2、纤维布层3及第二胶水粘合层4、聚醚型TPU底膜层5，所述纤维布层3经过电晕处理。
所述大型油囊水囊用TPU复合面料采用以下方法制备而成：
1)取纤维布布置在电晕辊上进行第一次电晕。
2)第一次电晕完成后，将纤维布未电晕的表面布置在电晕辊上与电晕辊接触，进行第二次电晕。
3)在双面经过电晕处理后的纤维布的上下表面上均涂覆上PUR热熔胶；
4)制备聚酯型TPU面膜，按重量百分数计，取聚酯型TPU85％、三元乙丙烯橡胶2％、聚碳化二亚胺10％、色母2％及碳酸钙1％混匀后干燥，然后流延加工成聚酯型TPU面膜，挤出模头的温度为170～180℃。
5)制备聚醚型TPU底膜，按质量百分数计，取聚醚型TPU85％、丙烯酸酯类单体5％、碳酸钙10％混匀后干燥，然后流延加工成聚醚型TPU底膜。
6)将涂覆了PUR热熔胶的纤维布用110～120℃热风预热后，再在表面和底别分别贴合聚酯型TPU面膜和聚醚型TPU底膜。
对实施例1至3所制得的TPU复合面料进行测试，检测其耐油性、耐水解性和剥离强度及耐寒性，检测结果如下表所示：
实施例1 实施例2 实施例3
剥离强度(N/5cm) 140 141 141
耐油性 优 优 优
耐水解性 优 优 优
耐寒性(℃) -42～-49 －42～－52 －42～－50
对于本领域的技术人员来说，可根据以上描述的技术方案以及构思，做出其它各种相应的改变以及变形，而所有的这些改变以及变形都应该属于本发明权利要求的保护范围之内。

Claims (5)

1.一种大型油囊水囊用TPU复合面料，其特征在于：其由上至下依次包括聚酯型TPU面膜层、第一胶水粘合层、纤维布层及第二胶水粘合层、聚醚型TPU底膜层，所述纤维布层经过电晕处理。
2.如权利要求1所述的大型油囊水囊用TPU复合面料，其特征在于：所述聚酯型TPU面膜层按质量百分数计包括，聚酯型TPU83～87％、三元乙丙烯橡胶2～8％、聚碳化二亚胺3～10％、色母0.5～2％及碳酸钙0.1～1％。
3.如权利要求1所述的大型油囊水囊用TPU复合面料，其特征在于：所述第一胶水粘合层和第二胶水粘合层均为PUR热熔胶层。
4.如权利要求1所述的大型油囊水囊TPU复合面料，其特征在于：所述聚醚型TPU底膜层按质量百分数计包括，聚醚型TPU80～90％、丙烯酸酯类单体5～15％、碳酸钙3～10％。
5.如权利要求1所述的大型油囊水囊用TPU复合面料，其特征在于采用以下方法制备而成：
1)取纤维布布置在电晕辊上进行第一次电晕；
2)第一次电晕完成后，将纤维布未电晕的表面布置在电晕辊上与电晕辊接触，进行第二次电晕；
3)在纤维布的上下表面上均涂覆上PUR热熔胶；
4)制备聚酯型TPU面膜，按重量百分数计，取聚酯型TPU83～87％、三元乙丙烯橡胶2～8％、聚碳化二亚胺3～10％、色母0.5～2％及碳酸钙0.1～1％混匀后干燥，然后流延加工成聚酯型TPU面膜；
5)制备聚醚型TPU底膜，按质量百分数计，取聚醚型TPU80～90％、丙烯酸酯类单体5～15％、碳酸钙3～10％混匀后干燥，然后流延加工成聚醚型TPU底膜；
6)将涂覆了PUR热熔胶的纤维布用热风预热后，再在表面和底别分别贴合聚酯型TPU面膜和聚醚型TPU底膜。
CN201610192952.7A 2016-03-30 2016-03-30 一种大型油囊水囊用tpu复合面料 Active CN105774157B (zh)