CN105754442B - 耐水透气水包水多彩涂料配方及其制作方法 - Google Patents
耐水透气水包水多彩涂料配方及其制作方法 Download PDFInfo
- Publication number
- CN105754442B CN105754442B CN201610209668.6A CN201610209668A CN105754442B CN 105754442 B CN105754442 B CN 105754442B CN 201610209668 A CN201610209668 A CN 201610209668A CN 105754442 B CN105754442 B CN 105754442B
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- agent
- preservative
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开一种耐水透气水包水多彩涂料配方及其制作方法，该耐水透气水包水多彩涂料配方由以下质量份数的组分组成：保护胶：20‑30份；基础漆：32‑35份；去离子水：9‑11份；弹性硅丙乳液：25‑30份；丙二醇：2‑2.5份；成膜助剂：1.5‑2份；防腐剂1：0.15‑0.25份；防腐剂2：0.3‑0.5份；消泡剂：0.2‑0.3份；增稠剂：0.2‑0.3份。本发明通过上述组分配方改变多彩基础漆的疏水性与透气性，降低多彩保护胶的用量，避免添加阴离子润湿剂、焦磷酸钠等亲水物质，能够避免发生彩点喷涂至墙面后，彩点表面表干，但内部水分还没挥发而形成鼓泡的情况，制作出一种既耐水又透气的水包水多彩涂料。
Description
技术领域：
本发明涉及涂料技术领域，特指一种耐水透气水包水多彩涂料配方及其制作方法。
背景技术：
水包水多彩涂料是水性彩色乳胶涂料小液滴作分散相，保护胶水溶液作连续相的多相悬浮体系。要实现“水包水”悬浮体，必须把水性胶胶小液滴分散于保护胶水溶液中。这样，保护胶水溶液在小液滴表面形成一层不溶于水的保护层。这保护层能阻止乳胶小液滴向保护胶水溶液扩散，还能阻止注液滴之间相互聚集，并且这种保护状态将持续到施工早期的湿膜中，随着水及成膜助剂的挥发，分散相的胶胶小液滴相互堆砌、融合，最终形成坚固的多彩涂膜。
水性多彩涂料概念最早是在20世纪60年代由美国John C.Zola提出并成功制备了由彩色球粒水分散体分散在含成膜物质水分散介质中的多彩涂料。但这种彩色球粒强度不高，不适用于滚、刷涂[2]，且离子含量低时体系稳定性较差。后Cervelllati Gianfranco在John C.Zola基础上利用改性成膜物质制备水性多彩涂料，改进后能适用于滚涂刷涂，但仍存在离子含量低时稳定性差问题[3]。20世纪90年代，Edoardo Rossetti利用彩色胶体与Al离子反应制备多彩涂料方法，通过控制Al离子浓度能获得大量胶体坚硬的非水合彩色沉淀物，适用于刷涂，但此方法制备的多彩涂料在光滑表面易流挂，因而不能直接在底材上使用[4]。随后Germano Bolloni在US5340389中详细介绍了多彩涂料用保护胶的制备过程和在多彩涂料中的应用，用其方法制备的保护胶，胶体更加稳定，花纹效果更明显[5]。进入21世纪，功能性多彩涂料成为研究热点。Yoshikatsu Saito利用金属氧化物包覆片状硅制备的多彩涂料，具有良好耐候性，烧烤色差<0.5.
国内“水包水”多彩涂料起步于20世纪90年代，以段玉忠[7]为代表的专家对多彩涂料进行了一些探索性研究。随后丁铸为代表的团队将成型的“水包水”多彩涂料研制成功。21世纪初，以张道银[9]等为代表对“水包水”研发进行了细致的条件性试验研究，对多彩涂料的分散体系进行了细致的研究。杭州传化涂料的吴庆喜[10]等对硅丙树脂和纯丙树脂体系利用保护胶技术的“水包水”多彩涂料进行了条件研究和工艺性能研究。
近期，国内外关于“水包水”多彩涂料的研究已由装饰性向功能性转变，如环保低VOC,耐污优异多彩涂料等。
目前市场上的“水包水”产品大部分还存在以下问题：色点渗色，后增稠，彩点硬化易碎，批次间不稳定，耐水(白)性差，温度高时涂层鼓泡等。其中以耐水(白)性、高温时涂层鼓泡这两个问题最为常见。耐水(白)差是因为“水包水”多彩中一般添加了2％左右的保护胶，有的配方还添加了焦磷酸钠、阴离子润湿剂等耐水性差的助剂。高温鼓泡是因为彩点喷涂至墙面后，彩点表面表干，但内部水分还没挥发而形成鼓泡。
发明人进行了大量实验，开发出一款既耐水又透气的“水包水”多彩涂料。
发明内容：
本发明的目的在于克服现有技术的不足，提供一种耐水透气水包水多彩涂料配方及其制作方法。
为了解决上述技术问题，本发明采用了下述技术方案：1、耐水透气水包水多彩涂料配方，由以下质量份数的组分组成：保护胶：20-30份；基础漆：32-35份；去离子水：9-11份；弹性硅丙乳液：25-30份；丙二醇：2-2.5份；成膜助剂：1.5-2份；防腐剂1：0.15-0.25份；防腐剂2：0.3-0.5份；消泡剂：0.2-0.3份；增稠剂：0.2-0.3份。
进一步而言，上述技术方案中，所述的耐水透气水包水多彩涂料由以下质量份数的组分组成：保护胶：20份；基础漆：33.2份；去离子水：11份；弹性硅丙乳液：30份；丙二醇：2.5份；成膜助剂：2份；防腐剂1：0.2份；防腐剂2：0.5份；消泡剂：0.3份；增稠剂：0.3份。
进一步而言，上述技术方案中，所述的耐水透气水包水多彩涂料由以下质量份数的组分组成：保护胶：25份；基础漆：35份；去离子水：9份；弹性硅丙乳液：26.6份；丙二醇：2份；成膜助剂：1.5份；防腐剂1：0.2份；防腐剂2：0.3份；消泡剂：0.2份；增稠剂：0.2份。
进一步而言，上述技术方案中，所述的耐水透气水包水多彩涂料所述的基础漆由以下质量份数的组分组成：纯净水：50-55份；防腐剂：0.15-0.25份；分散剂：0.2-0.3份；润湿剂：0.1-0.2份；消泡剂：0.2-0.3份；纤维素：0.7-0.9份；钛白粉：1-2份；合成硅酸铝：2-3份；高遮盖力粉：3-5份；PH调节剂：0.1-0.2份；疏水改性树脂：0.5-1份；弹性硅丙乳液：25-30份；成膜助剂：1-1.5份；保护胶：2.5-3份；消泡剂：0.2-0.3份；增稠剂1：0.2-0.3份；增稠剂2:0.2-0.3份。
进一步而言，上述技术方案中，所述的耐水透气水包水多彩涂料所述的保护胶由以下质量份数的组分组成：纯净水：93份；S482保护胶粉：7份。
一种耐水透气水包水多彩涂料的制作方法，包括以下步骤：
(1)配备基础漆：
将以下组分：纯净水、防腐剂、分散剂、润湿剂、消泡剂、纤维素、钛白粉、合成硅酸铝、高遮盖力粉、PH调节剂、疏水改性树脂、弹性硅丙乳液、成膜助剂、保护胶、消泡剂、增稠剂1、增稠剂2混合搅拌直到得到基础漆溶液，并且控制粘度在115-125KU范围内；
(2)配备基础漆颜色：
将步骤(1)得到的基础漆和颜色填料很合，得出所需色漆；
(3)配备保护胶：
将93份纯净水和7份S482保护胶粉混合，得出保护胶；
(4)造粒：
将(3)制备好的保护胶加入分散缸，并逐步加入(2)中的色漆，控制搅拌速度与时间以生产所需尺寸的彩点；
(5)在步骤4所得物中逐步加入以下成分：去离子水、弹性硅丙乳液、丙二醇、成膜助剂、防腐剂1、防腐剂2、消泡剂、增稠剂，搅拌均匀并控制粘度在75-85KU。
采用上述技术方案后，本发明与现有技术相比较具有如下有益效果：本发明通过上述组分配方改变多彩基础漆的疏水性与透气性，降低多彩保护胶的用量，避免添加阴离子润湿剂、焦磷酸钠等亲水物质，能够避免发生彩点喷涂至墙面后，彩点表面表干，但内部水分还没挥发而形成鼓泡的情况，制作出一种既耐水又透气的水包水多彩涂料。
具体实施方式：
下面结合具体实施例对本发明进一步说明。
耐水透气水包水多彩涂料配方，由以下质量份数的组分组成：保护胶：20-30份；基础漆：32-35份；去离子水：9-11份；弹性硅丙乳液：25-30份；丙二醇：2-2.5份；成膜助剂：1.5-2份；防腐剂1：0.15-0.25份；防腐剂2：0.3-0.5份；消泡剂：0.2-0.3份；增稠剂：0.2-0.3份。
优选地，耐水透气水包水多彩涂料配方，由以下质量份数的组分组成：保护胶：20份；基础漆：33.2份；去离子水：11份；弹性硅丙乳液：30份；丙二醇：2.5份；成膜助剂：2份；防腐剂1：0.2份；防腐剂2：0.5份；消泡剂：0.3份；增稠剂：0.3份。
优选地，耐水透气水包水多彩涂料配方，由以下质量份数的组分组成：保护胶：25份；基础漆：35份；去离子水：9份；弹性硅丙乳液：26.6份；丙二醇：2份；成膜助剂：1.5份；防腐剂1：0.2份；防腐剂2：0.3份；消泡剂：0.2份；增稠剂：0.2份。
上述的成膜助剂为：醇酯12，防腐剂1为:异噻唑啉酮，防腐剂2为：BI T
消泡剂为：矿物油，增稠剂为：改性丙烯酸
防腐剂2所指的BIT英文名称是2-n-Octyl-4-isothiazolin-3-one，中文名称是2-正辛基-4-异噻唑啉-3-酮，用作有机合成中间体.为液态，溶于有机溶剂，微溶于水，是一种低毒、高效、广谱型防霉剂，对霉菌具有很强的杀灭作用，能达到理想的防霉效果。可广泛应用于涂料、油漆、润滑油、鞋油、皮革化学、木材制品和文物保护等诸多产品中。
耐水透气水包水多彩涂料配方中基础漆由以下质量份数的组分组成：纯净水：50-55份；防腐剂：0.15-0.25份；分散剂：0.2-0.3份；润湿剂：0.1-0.2份；消泡剂：0.2-0.3份；纤维素：0.7-0.9份；钛白粉：1-2份；合成硅酸铝：2-3份；高遮盖力粉：3-5份；PH调节剂：0.1-0.2份；疏水改性树脂：0.5-1份；弹性硅丙乳液：25-30份；成膜助剂：1-1.5份；保护胶：2.5-3份；消泡剂：0.2-0.3份；增稠剂1：0.2-0.3份；增稠剂2:0.2-0.3份。
优选地：耐水透气水包水多彩涂料配方中基础漆由以下质量份数的组分组成：纯净水：55份；防腐剂：0.15份；分散剂：0.2份；润湿剂：0.1份；消泡剂：0.2份；纤维素：0.7份；钛白粉：1份；合成硅酸铝：3份；高遮盖力粉：5份；PH调节剂：0.1份；疏水改性树脂：0.5份；弹性硅丙乳液：29.45份；成膜助剂：1份；保护胶：3份；消泡剂：0.2份；增稠剂1：0.2份；增稠剂2:0.2份。
优选地：耐水透气水包水多彩涂料配方中基础漆由以下质量份数的组分组成：纯净水：55份；防腐剂：0.2份；分散剂：0.3份；润湿剂：0.2份；消泡剂：0.3份；纤维素：0.9份；钛白粉：1份；合成硅酸铝：2份；高遮盖力粉：4份；PH调节剂：0.2份；疏水改性树脂：1份；弹性硅丙乳液：30份；成膜助剂：1份；保护胶：3份；消泡剂：0.3份；增稠剂1：0.3份；增稠剂2:0.3份。
上述的基础漆组分中，防腐剂为：异噻唑啉酮，分散剂为：聚丙烯酸铵盐润湿剂为：非离子型润湿剂，消泡剂为：矿物油，纤维素为：改性羟乙基纤维素，高遮盖力粉为：片状锻烧高岭土，PH调节剂为：有机胺，成膜助剂为：醇酯十二，消泡剂为：矿物油，增稠剂1为：改性丙烯酸，增稠剂2为:丙烯酸。
耐水透气水包水多彩涂料配方中保护胶由以下质量份数的组分组成：纯净水：93份；S482保护胶粉：7份。
下面列举两个具体组分方案：
方案一：
耐水透气水包水多彩涂料配方，由以下质量份数的组分组成：保护胶：20份；基础漆：33.2份；去离子水：11份；弹性硅丙乳液：30份；丙二醇：2.5份；成膜助剂：2份；防腐剂1：0.2份；防腐剂2：0.5份；消泡剂：0.3份；增稠剂：0.3份。
其中，基础漆由以下质量份数的组分组成：纯净水：55份；防腐剂：0.15份；分散剂：0.2份；润湿剂：0.1份；消泡剂：0.2份；纤维素：0.7份；钛白粉：1份；合成硅酸铝：3份；高遮盖力粉：5份；PH调节剂：0.1份；疏水改性树脂：0.5份；弹性硅丙乳液：29.45份；成膜助剂：1份；保护胶：3份；消泡剂：0.2份；增稠剂1：0.2份；增稠剂2:0.2份。
保护胶由以下质量分数的组分组成：纯净水：93份；S482保护胶粉：7份。方案二：
耐水透气水包水多彩涂料配方，由以下质量份数的组分组成：保护胶：25份；基础漆：35份；去离子水：9份；弹性硅丙乳液：26.6份；丙二醇：2份；成膜助剂：1.5份；防腐剂1：0.2份；防腐剂2：0.3份；消泡剂：0.2份；增稠剂：0.2份。
其中，
基础漆由以下质量份数的组分组成：纯净水：55份；防腐剂：0.2份；分散剂：0.3份；润湿剂：0.2份；消泡剂：0.3份；纤维素：0.9份；钛白粉：1份；合成硅酸铝：2份；高遮盖力粉：4份；PH调节剂：0.2份；疏水改性树脂：1份；弹性硅丙乳液：30份；成膜助剂：1份；保护胶：3份；消泡剂：0.3份；增稠剂1：0.3份；增稠剂2:0.3份。
保护胶由以下质量分数的组分组成：纯净水：93份；S482保护胶粉：7份。
按照上述的两种成分配方组合，均可得出耐水又透气的水包水多彩涂料。
上述耐水透气水包水多彩涂料的制作方法，以方案一为例，包括以下步骤：
(1)配备基础漆：
将以下组分：纯净水、防腐剂、分散剂、润湿剂、消泡剂、纤维素、钛白粉、合成硅酸铝、高遮盖力粉、PH调节剂、疏水改性树脂、弹性硅丙乳液、成膜助剂、保护胶、消泡剂、增稠剂1、增稠剂2按照方案1中的组份混合搅拌直到得到基础漆溶液，搅拌速度为1200rpm，搅拌时间为10-15分钟，并且控制粘度在115-125KU范围内；
(2)配备基础漆颜色：
将步骤(1)得到的基础漆和颜色填料混合，得出所需色漆,所使用的颜色填料为氧化铁系列颜料；
(3)配备保护胶：
将93份纯净水和7份S482保护胶粉混合，得出保护胶；
(4)造粒：
将(3)制备好的保护胶加入分散缸，并逐步加入(2)中的色漆，控制搅拌速度与时间以生产所需尺寸的彩点，搅拌速度为200-400rpm，搅拌时间为3-5min。
(5)在步骤4所得物中逐步加入以下成分：去离子水、弹性硅丙乳液、丙二醇、成膜助剂、防腐剂1、防腐剂2、消泡剂、增稠剂，搅拌均匀并控制粘度在75-85KU。
通过上述步骤便可得出耐水透气水包水多彩涂料成品。
方案二的耐水透气水包水多彩涂料与方案一的制备步骤一样，仅仅是组分的配比不同，在此不再一一赘述。
当然，以上所述仅为本发明的具体实施例而已，并非来限制本发明实施范围，凡依本发明申请专利范围所述构造、特征及原理所做的等效变化或修饰，均应包括于本发明申请专利范围内。
Claims (1)
1.一种耐水透气水包水多彩涂料的制作方法，其特征在于：包括以下步骤：
(1)配备基础漆：
将以下组分：纯净水、防腐剂、分散剂、润湿剂、消泡剂、纤维素、钛白粉、合成硅酸铝、高遮盖力粉、PH调节剂、疏水改性树脂、弹性硅丙乳液、成膜助剂、保护胶、增稠剂1、增稠剂2混合搅拌直到得到基础漆溶液，搅拌速度为1200rpm，搅拌时间为10-15分钟，并且控制粘度在115-125KU范围内；
(2)配备基础漆颜色：
将步骤(1)得到的基础漆和颜色填料混合，得出所需色漆；
(3)配备保护胶：
将93份纯净水和7份S482保护胶粉混合，得出保护胶；
(4)造粒：
将(3)制备好的保护胶加入分散缸，并逐步加入(2)中的色漆，控制搅拌速度与时间以生产所需尺寸的彩点，搅拌速度为200-400rpm，搅拌时间为3-5分钟；
(5)在步骤(4)所得物中逐步加入以下成分：去离子水、弹性硅丙乳液、丙二醇、成膜助剂、防腐剂1、防腐剂2、消泡剂、增稠剂，搅拌均匀并控制粘度在75-85KU；
所述的耐水透气水包水多彩涂料由以下质量份数的组分组成：保护胶：25份；基础漆：35份；去离子水：9份；弹性硅丙乳液：26.6份；丙二醇：2份；成膜助剂：1.5份；防腐剂1：0.2份；防腐剂2：0.3份；消泡剂：0.2份；增稠剂：0.2份；
上述的成膜助剂为：醇酯十二，防腐剂1为:异噻唑啉酮，防腐剂2为：BIT，消泡剂为：矿物油，增稠剂为：改性丙烯酸；
所述的步骤(1)中基础漆由以下质量份数的组分组成：纯净水：50-55份；防腐剂：0.15-0.25份；分散剂：0.2-0.3份；润湿剂：0.1-0.2份；消泡剂：0.2-0.3份；纤维素：0.7-0.9份；钛白粉：1-2份；合成硅酸铝：2-3份；高遮盖力粉：3-5份；PH调节剂：0.1-0.2份；疏水改性树脂：0.5-1份；弹性硅丙乳液：25-30份；成膜助剂：1-1.5份；保护胶：2.5-3份；增稠剂1：0.2-0.3份；增稠剂2:0.2-0.3份；
上述的基础漆组分中，防腐剂为：异噻唑啉酮，分散剂为：聚丙烯酸铵盐，润湿剂为：
非离子型润湿剂，消泡剂为：矿物油，纤维素为：改性羟乙基纤维素，高遮盖力粉为：片状锻烧高岭土，PH调节剂为：有机胺，成膜助剂为：醇酯十二，增稠剂1为：改性丙烯酸，增稠剂2为:丙烯酸。