CN105598357A - 一种阻燃性高的消失模的涂料及其制备方法 - Google Patents
一种阻燃性高的消失模的涂料及其制备方法 Download PDFInfo
- Publication number
- CN105598357A CN105598357A CN201610033906.2A CN201610033906A CN105598357A CN 105598357 A CN105598357 A CN 105598357A CN 201610033906 A CN201610033906 A CN 201610033906A CN 105598357 A CN105598357 A CN 105598357A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- powders
- adsorbent
- fire retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种阻燃性高的消失模的涂料及其制备方法,涉及消失模生产技术领域,由以下重量组分制成,镁砂粉30~40、珠光粉25~30、云母粉15~25、石油焦粉3~8、硅溶胶3~8、白乳胶1~5、三乙醇胺0.3~0.5、羧甲基纤维素钠0.1~0.6、吸附剂1~6、阻燃剂0.3~2;阻燃剂包括全氯环戊癸烷5~8,氯菌酸3~5,三聚氰胺氰尿酸盐1~2和氯化金钾3~4。包括步骤,将镁砂粉、珠光粉、云母粉、石油焦粉、羧甲基纤维素钠、吸附剂磨粉筛选;将吸附剂、阻燃剂、羧甲基纤维素钠和三乙醇胺加水混合;再将镁砂粉、珠光粉、云母粉、石油焦粉、硅溶胶、白乳胶充分混合。本发明消失模在工件铸造时,粘结性高,无残渣,阻燃性比较好,稳定性高,有利于提高产品质量。<!-- 2 -->
Description
技术领域:
本发明涉及消失模生产技术领域,具体是一种阻燃性高的消失模的涂料及其制备方法。
背景技术:
消失模铸造是泡沫塑料模采用无黏结剂干砂结合抽真空技术的实型铸造。国内主要的叫法有“干砂实型铸造”、“负压实型铸造”,简称EPC铸造。消失模铸造是目前国际上最先进的铸造方法之一,被誉为铸造史上的一次“革命”,国内外称之为21世纪绿色铸造。消失模的现有技术中很多不是整体一次性成型的,需要通过粘结造型才能完成,且外部上有涂料,现有技术中的用于消失模粘结的涂料比较简单,而且黏性不高,阻燃性较差,稳定性差,容易产生残渣,影响铸造部件的外表面光滑度。
发明内容:
本发明所要解决的技术问题在于提供一种阻燃性高的消失模的涂料及其制备方法。
解决的技术问题所采用以下的技术方案:
一种阻燃性高的消失模的涂料,其特征在于:由以下重量份组分制成,
镁砂粉30~40份、珠光粉25~30份、云母粉15~25份、石油焦粉3~8份、硅溶胶3~8份、白乳胶1~5份、三乙醇胺0.3~0.5份、羧甲基纤维素钠0.1~0.6份、吸附剂1~6份、阻燃剂0.3~2份;所述的阻燃剂为按重量份包括全氯环戊癸烷5~8份,氯菌酸3~5份,三聚氰胺氰尿酸盐1~2份和氯化金钾3~4份。
优选由以下重量份组分制成,
涂料成分为镁砂粉35份、珠光粉28份、云母粉20份、石油焦粉6份、硅溶胶6份、白乳胶3份、三乙醇胺0.4份、羧甲基纤维素钠0.3份、吸附剂4份、阻燃剂1份;所述的阻燃剂为按重量份包括全氯环戊癸烷6份,氯菌酸4份,三聚氰胺氰尿酸盐1.5份和氯化金钾3.5份。
所述的吸附剂按重量份包括沸石粉5~8份、海泡石粉5~8份和膨润土10~20份。
一种阻燃性高的消失模的涂料的制备方法,其特征在于:包括以下步骤,
1)分别将镁砂粉、珠光粉、云母粉、石油焦粉、羧甲基纤维素钠、吸附剂分别进行磨粉筛选,筛网的大小为100~200目;
2)将吸附剂、阻燃剂、羧甲基纤维素钠和三乙醇胺加水充分混合,加水的百分比为30~40%;
3)再将镁砂粉、珠光粉、云母粉、石油焦粉、硅溶胶、白乳胶与步骤2)的混合物进行充分混合。
本发明中的外部涂料有较高的粘性,可以较好的附着在干砂的模腔内表面,且透气性好,高温下均匀度高无碎渣,本发明中的三乙醇胺在未浇筑前具有增稠保湿的效果,且铸造砂中难免还有一些含有金属化合物,三乙醇胺能够与金属离子型号才能较为稳定的络合物,放置金属离子可能对涂料性质产生影响。三乙醇胺在浇筑后高温下也会随之蒸发。
本发明中还添加了吸附剂,使得涂料吸附性强,均匀度高,稳定性好,不容易掉落,本发明中添加了阻燃剂,本发明中使用的阻燃剂具有较高的阻燃性能,而且能在涂料中形成一层薄膜,放置氧气的进入,从而还能起到防止金属表面被氧化的作用。
本发明的有益效果是:本发明消失模在工件铸造时,粘结性高,无残渣,阻燃性比较好,稳定性高,有利于提高产品质量。
具体实施方式:
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实例,进一步阐述本发明。
实施例1
一种阻燃性高的消失模的涂料,由以下重量份组分制成,
镁砂粉30份、珠光粉25份、云母粉15份、石油焦粉3份、硅溶胶3份、白乳胶1份、三乙醇胺0.3份、羧甲基纤维素钠0.1份、吸附剂1份、阻燃剂0.3份;阻燃剂为按重量份包括全氯环戊癸烷5份,氯菌酸35份,三聚氰胺氰尿酸盐1份和氯化金钾3份。
吸附剂按重量份包括沸石粉5份、海泡石粉5份和膨润土10份。
一种阻燃性高的消失模的涂料的制备方法,包括以下步骤,
1)分别将镁砂粉、珠光粉、云母粉、石油焦粉、羧甲基纤维素钠、吸附剂分别进行磨粉筛选,筛网的大小为100目;
2)将吸附剂、阻燃剂、羧甲基纤维素钠和三乙醇胺加水充分混合,加水的百分比为30%;
3)再将镁砂粉、珠光粉、云母粉、石油焦粉、硅溶胶、白乳胶与步骤2)的混合物进行充分混合。
实施例2
一种阻燃性高的消失模的涂料,由以下重量份组分制成,
镁砂粉35份、珠光粉28份、云母粉20份、石油焦粉6份、硅溶胶6份、白乳胶3份、三乙醇胺0.4份、羧甲基纤维素钠0.3份、吸附剂4份、阻燃剂1份;阻燃剂为按重量份包括全氯环戊癸烷6份,氯菌酸4份,三聚氰胺氰尿酸盐1.5份和氯化金钾3.5份。
吸附剂按重量份包括沸石粉6份、海泡石粉6份和膨润土15份。
一种阻燃性高的消失模的涂料的制备方法,包括以下步骤,
1)分别将镁砂粉、珠光粉、云母粉、石油焦粉、羧甲基纤维素钠、吸附剂分别进行磨粉筛选,筛网的大小为150目;
2)将吸附剂、阻燃剂、羧甲基纤维素钠和三乙醇胺加水充分混合,加水的百分比为35%;
3)再将镁砂粉、珠光粉、云母粉、石油焦粉、硅溶胶、白乳胶与步骤2)的混合物进行充分混合。
实施例3
一种阻燃性高的消失模的涂料,由以下重量份组分制成,
镁砂粉40份、珠光粉30份、云母粉25份、石油焦粉8份、硅溶胶8份、白乳胶5份、三乙醇胺0.5份、羧甲基纤维素钠0.6份、吸附剂6份、阻燃剂2份;阻燃剂为按重量份包括全氯环戊癸烷8份,氯菌酸5份,三聚氰胺氰尿酸盐2份和氯化金钾4份。
吸附剂按重量份包括沸石粉8份、海泡石粉8份和膨润土20份。
一种阻燃性高的消失模的涂料的制备方法,包括以下步骤,
1)分别将镁砂粉、珠光粉、云母粉、石油焦粉、羧甲基纤维素钠、吸附剂分别进行磨粉筛选,筛网的大小为200目;
2)将吸附剂、阻燃剂、羧甲基纤维素钠和三乙醇胺加水充分混合,加水的百分比为40%;
3)再将镁砂粉、珠光粉、云母粉、石油焦粉、硅溶胶、白乳胶与步骤2)的混合物进行充分混合。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (4)
1.一种阻燃性高的消失模的涂料,其特征在于:由以下重量份组分制成,
镁砂粉30~40份、珠光粉25~30份、云母粉15~25份、石油焦粉3~8份、硅溶胶3~8份、白乳胶1~5份、三乙醇胺0.3~0.5份、羧甲基纤维素钠0.1~0.6份、吸附剂1~6份、阻燃剂0.3~2份;所述的阻燃剂为按重量份包括全氯环戊癸烷5~8份,氯菌酸3~5份,三聚氰胺氰尿酸盐1~2份和氯化金钾3~4份。
2.根据权利要求1所述的一种阻燃性高的消失模的涂料,其特征在于:以下重量份组分制成,
涂料成分为镁砂粉35份、珠光粉28份、云母粉20份、石油焦粉6份、硅溶胶6份、白乳胶3份、三乙醇胺0.4份、羧甲基纤维素钠0.3份、吸附剂4份、阻燃剂1份;所述的阻燃剂为按重量份包括全氯环戊癸烷6份,氯菌酸4份,三聚氰胺氰尿酸盐1.5份和氯化金钾3.5份。
3.根据权利要求1所述的一种阻燃性高的消失模的涂料,其特征在于:所述的吸附剂按重量份包括沸石粉5~8份、海泡石粉5~8份和膨润土10~20份。
4.根据权利要求1所述的一种阻燃性高的消失模的涂料的制备方法,其特征在于:包括以下步骤,
1)分别将镁砂粉、珠光粉、云母粉、石油焦粉、羧甲基纤维素钠、吸附剂分别进行磨粉筛选,筛网的大小为100~200目;
2)将吸附剂、阻燃剂、羧甲基纤维素钠和三乙醇胺加水充分混合,加水的百分比为30~40%;
3)再将镁砂粉、珠光粉、云母粉、石油焦粉、硅溶胶、白乳胶与步骤2)的混合物进行充分混合。