CN105562596A - 一种铸铁件用消失模的涂料及其制备方法 - Google Patents

一种铸铁件用消失模的涂料及其制备方法 Download PDF

Info

Publication number
CN105562596A
CN105562596A CN201610035946.0A CN201610035946A CN105562596A CN 105562596 A CN105562596 A CN 105562596A CN 201610035946 A CN201610035946 A CN 201610035946A CN 105562596 A CN105562596 A CN 105562596A
Authority
CN
China
Prior art keywords
parts
coating
preparation
hours
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610035946.0A
Other languages
English (en)
Inventor
李新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Yong Chang Foundry Goods Co Ltd
Original Assignee
Anhui Yong Chang Foundry Goods Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Yong Chang Foundry Goods Co Ltd filed Critical Anhui Yong Chang Foundry Goods Co Ltd
Priority to CN201610035946.0A priority Critical patent/CN105562596A/zh
Publication of CN105562596A publication Critical patent/CN105562596A/zh
Pending legal-status Critical Current

Abstract

一种铸铁件用消失模的涂料及其制备方法，涉及消失模生产技术领域，由以下重量份组分制成，100～200目的石英砂颗粒60～70份，150～200目的铝矾土35～50份，聚乙烯醇0.8～1.6份，活化膨润土2～5份，阻燃剂2～4份，羧甲基纤维素0.3～0.6份，有机短纤维0.3～0.5份。包括以下步骤1)将活化润土用1：6的水调成浆，放置24小时备用；2)CMC以1：30的水浸泡8小时备用；3)PVA用1：10的开水溶解搅拌均匀；4)将耐火骨料、有机短纤维放和阻燃剂在搅拌机内干混均匀，5)将步骤4)的混合物再加入到步骤1)、2)和3)的三种液体的混合物中并搅拌混合均匀。本发明适用于铸铁件，自干性好，不开裂，透气性好，阻燃性比较好，稳定性高。

Description

一种铸铁件用消失模的涂料及其制备方法
技术领域：
本发明涉及消失模生产技术领域，具体是一种铸铁件用消失模的涂料及其制备方法。
背景技术：
消失模铸造是泡沫塑料模采用无黏结剂干砂结合抽真空技术的实型铸造。国内主要的叫法有“干砂实型铸造”、“负压实型铸造”，简称EPC铸造。消失模铸造是目前国际上最先进的铸造方法之一，被誉为铸造史上的一次“革命”，国内外称之为21世纪绿色铸造。消失模的现有技术中很多不是整体一次性成型的，需要通过粘结造型才能完成，且外部上有涂料，现有技术中的用于消失模粘结的涂料比较简单，组分单一，而且黏性不高，阻燃性较差，稳定性差，对于不同的铸造材料，由于材料的不同，温度以及其他因素的存在，组分单一的涂料用于铸铁件时，可能会对铸铁件的性能产生影响。
发明内容：
本发明所要解决的技术问题在于提供一种，阻燃性高，稳定性好，不会影响铸铁性能的铸铁件用消失模涂料及其制备方法。
解决的技术问题所采用以下的技术方案：
一种铸铁件用消失模的涂料，其特征在于：由以下重量份组分制成
所述的阻燃剂为按重量份包括全氯环戊癸烷5份，三聚氰胺氰尿酸盐1.5份和氯化金钾3份。
一种铸铁件用消失模的涂料的制备方法，其特征在于：包括以下步骤
1)将活化润土用1：6的水调成浆，放置24～30小时备用；
2)CMC以1：30的水浸泡8～16小时备用；
3)PVA用1：10的开水溶解搅拌均匀；
4)将耐火骨料、有机短纤维放和阻燃剂在搅拌机内干混均匀，
5)将步骤4)的混合物再加入到步骤1)、2)和3)的三种液体的混合物中并搅拌混合均匀。
本发明中添加了阻燃剂，本发明中使用的阻燃剂具有较高的阻燃性能，而且能在涂料中形成一层薄膜，放置氧气的进入，从而还能起到防止金属表面被氧化的作用。
本发明所得涂料pH值在6～9之间，100ml涂料在12小时内的悬浮性100％，粘度20～40，涂层厚1～2.5mm，密度(波美度)60～75，纤维素气化后，透气性45～80ml/mm2·s，为未加有机短纤维的2倍以上，自干性好，自干后涂层不开裂，涂挂时具有良好的流平性和不流淌性。
本发明的有益效果是：本发明适用于铸铁件，自干性好，不开裂，透气性好，阻燃性比较好，稳定性高，有利于提高产品质量。
具体实施方式：
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实例，进一步阐述本发明。
实施例1
一种铸铁件用消失模的涂料，由以下重量份组分制成
阻燃剂为按重量份包括全氯环戊癸烷5份，三聚氰胺氰尿酸盐1.5份和氯化金钾3份。
一种铸铁件用消失模的涂料的制备方法，其特征在于：包括以下步骤
1)将活化润土用1：6的水调成浆，放置24小时备用；
2)CMC以1：30的水浸泡8小时备用；
3)PVA用1：10的开水溶解搅拌均匀；
4)将耐火骨料、有机短纤维放和阻燃剂在搅拌机内干混均匀，
5)将步骤4)的混合物再加入到步骤1)、2)和3)的三种液体的混合物中并搅拌混合均匀。
实施例2
一种铸铁件用消失模的涂料，：由以下重量份组分制成
阻燃剂为按重量份包括全氯环戊癸烷5份，三聚氰胺氰尿酸盐1.5份和氯化金钾3份。
一种铸铁件用消失模的涂料的制备方法，包括以下步骤
1)将活化润土用1：6的水调成浆，放置30小时备用；
2)CMC以1：30的水浸泡16小时备用；
3)PVA用1：10的开水溶解搅拌均匀；
4)将耐火骨料、有机短纤维放和阻燃剂在搅拌机内干混均匀，
5)将步骤4)的混合物再加入到步骤1)、2)和3)的三种液体的混合物中并搅拌混合均匀。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (3)

1.一种铸铁件用消失模涂料，其特征在于：由以下重量份组分制成
2.根据权利要求1所述的一种铸铁件用消失模涂料的制备方法,其特征在于：所述的阻燃剂为按重量份包括全氯环戊癸烷5份，三聚氰胺氰尿酸盐1.5份和氯化金钾3份。
3.根据权利要求1所述的一种铸铁件用消失模涂料的制备工艺，其特征在于：包括以下步骤
1)将活化润土用1：6的水调成浆，放置24～30小时备用；
2)CMC以1：30的水浸泡8～16小时备用；
3)PVA用1：10的开水溶解搅拌均匀；
4)将耐火骨料、有机短纤维放和阻燃剂在搅拌机内干混均匀，
5)将步骤4)的混合物再加入到步骤1)、2)和3)的三种液体的混合物中并搅拌混合均匀。
CN201610035946.0A 2016-01-19 2016-01-19 一种铸铁件用消失模的涂料及其制备方法 Pending CN105562596A (zh)