CN105400285A - Pvc墙纸用高耐候水性油墨及其制备方法 - Google Patents
Pvc墙纸用高耐候水性油墨及其制备方法 Download PDFInfo
- Publication number
- CN105400285A CN105400285A CN201511028168.4A CN201511028168A CN105400285A CN 105400285 A CN105400285 A CN 105400285A CN 201511028168 A CN201511028168 A CN 201511028168A CN 105400285 A CN105400285 A CN 105400285A
- Authority
- CN
- China
- Prior art keywords
- pvc wallpaper
- weather resistant
- ink
- high weather
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种PVC墙纸用高耐候水性油墨,包括以下质量百分比的组份:水性色浆20~50%,水性树脂乳液30~60%,耐磨抗刮剂1~5%,成膜助剂0.5~3%,流平剂0.2~2%,消泡剂0.1~0.5%,防腐剂0.1%,纯净水5~20%。本发明引入了改性镁铝水滑石,可以有效吸收太阳光中的紫外光、红外光,从而减缓油墨的老化速度,提高了PVC墙纸印刷图案的耐候性,其墙纸的使用寿命得以延长;同时,使用较高耐候级别颜料,可耐受200℃以上高温的水性树脂乳液,使该水性PVC墙纸油墨的耐温耐候性能大大提升,即使在高温、日晒等条件下,油墨仍能很好地保持其原有特性,非常符合水性PVC墙纸油墨的高标准要求。
Description
技术领域
本发明涉及一种PVC墙纸用高耐候水性油墨及其制备方法,属于水性油墨技术领域。
背景技术
目前我国生产的壁纸按材料可分为纸基纸面壁纸、PVC壁纸、织物面壁纸、天然材料面壁纸、砂面壁纸、硅藻土壁纸、无纺布壁纸。PVC壁纸以纸为基材,以PVC为面层,并对PVC表层进行罩光封闭,然后加工压花印制等对PVC墙纸进行装饰美化。水性油墨以水作为溶剂,其他有机溶剂添加量小甚至不添加,不仅减少了印刷过程中溶剂挥发对现场印刷操作人员造成的身体损害,更使其装饰于家中时基本无残留溶剂挥发,降低对家庭成员造成的损害,因而更适用于PVC壁纸的印刷装饰。
目前市面上的水性PVC墙纸水性油墨,其耐水、耐摩擦、耐高温等性能都能满足市场的要求,然而,由于地球臭氧层的逐步破坏严重,到达地球表面的太阳光中的紫外线辐射量逐渐增强,波长短能量高穿透力弱的紫外光更易被印刷品吸收,导致印刷品容易黄变、褪色、粉化、脱落,另外,太阳光中的红外光、可见光、热、水气等也会加速这种破坏速度,致使油墨的耐候性难以达到比较理想的结果。
发明内容
本发明为了克服现有技术存在的不足,提供一种PVC墙纸用高耐候水性油墨及其制备方法。
本发明可以通过采取以下技术方案予以实现:
一种PVC墙纸用高耐候水性油墨,包括以下质量百分比的组份:水性色浆20~50%,水性树脂乳液30~60%,耐磨抗刮剂1~5%,成膜助剂0.5~3%,流平剂0.2~2%,消泡剂0.1~0.5%,防腐剂0.1%,纯净水5~20%。
优选的是,所述水性色浆包括以下质量百分比的组份:镁铝水滑石1~20%,颜料20~50%,水性树脂乳液15~60%,润湿分散剂0~5%,消泡剂0.1~0.5%,纯净水10~40%。
优选的是,所述镁铝水滑石为经过表面改性、具有特殊性能的镁铝水滑石,具有良好的红外吸收、紫外阻隔功能。
优选的是,所述水性树脂乳液为水性丙烯酸树脂、水性聚氨酯树脂、水性硅丙树脂中的一种或多种的混合物,且至少一种能够耐受200℃以上高温。
优选的是,所述颜料为较高耐候级别的无机颜料或有机彩色颜料或其两者的混合物,用于调制PVC墙纸用高耐候水性油墨所需要的颜色。
优选的是,所述耐磨抗刮剂为聚乙烯蜡浆、聚四氟乙烯蜡浆、有机硅表面活性剂中的一种或多种的混合物。
优选的是,所述成膜助剂为丙二醇甲醚、二丙二醇甲醚、丙二醇丁醚、二丙二醇丁醚中的任意一种或多种的混合物。
优选的是,所述的流平剂为氟改性丙烯酸酯共聚物、聚醚改性硅氧烷、磷酸酯改性丙烯酸共聚物中的一种或多种的混合物。
优选的是,所述的消泡剂为聚硅氧烷、矿物油、聚醚高碳醇、植物油及其改性化合物中的一种或多种的混合物
优选的是,所述的润湿分散剂为聚乙二醇型多元醇、聚乙烯亚胺衍生物、脂肪酸环氧乙烷的加成物等高分子嵌段共聚物溶液中的一种或其多种的混合物,用于稳定颜料,使其在油墨中均匀分散,不浮色发花或沉降分层。
一种PVC墙纸用高耐候水性油墨的制备方法,包括以下步骤:
(1)、制备水性色浆:按所述的质量百分比,将镁铝水滑石、颜料、水性树脂乳液、润湿分散剂、消泡剂、纯净水加入分散机中分散均匀,之后加入研磨机中循环研磨,控制色浆细度在15μm以下、粘度20~40秒、PH值7.5~8.5,即得到所需水性色浆;
(2)、制备高耐候油墨:按所述的质量百分比,将水性色浆、水性树脂乳液、耐磨抗刮剂、流平剂、消泡剂、部分纯净水加入搅拌器,以300~500rpm的转速搅拌,充分分散均匀,加入防腐剂、余量纯净水,即得所述PVC墙纸用高耐候水性油墨。
与现有技术相比较,本发明的有益效果是:。
(1)本发明引入了改性镁铝水滑石,可以有效吸收太阳光中的紫外光、红外光,从而减缓油墨的老化速度,提高了PVC墙纸印刷图案的耐候性,其墙纸的使用寿命得以延长。
(2)本发明使用较高耐候级别颜料,至少一种可耐受200℃以上高温的水性树脂乳液,使该水性PVC墙纸油墨的耐温耐候性能大大提升,即使在高温、日晒等条件下,油墨仍能很好地保持其原有特性,非常符合水性PVC墙纸油墨的高标准要求。
(3)本发明所用材料均为经济环保型原料,特别是镁铝水滑石,其价格便宜,添加量低却性能优越,可以减少高耐候级别颜料、高耐温树脂的使用量,从而使油墨的成本得以降低,性能却更佳,更能满足高耐候PVC墙纸油墨的市场需求。
具体实施方式
以下对本发明的最佳实施例作详细描述。
实施例1~5
实施例1~5的PVC纸用高耐候水性油墨的质量百分比如表1所示。
表1
乙醇为非必须添加的溶剂,仅提供快干性及少许流平效果,为国家法规允许添加的非有毒溶剂。
在上述实施例中,水性色浆由质量百分比为20~50%的颜料、15~60%的水性树脂乳液、1~20%的镁铝水滑石、0~5%的润湿分散剂、0.1~0.5%的消泡剂、10~40%的纯净水在砂磨机中研磨而成,其中,颜料为金红石钛白粉、PR57:1、PY14、PB15:3或DL-3炭黑中的一种,具体取值如表2所示。
表2
所述镁铝水滑石为经过表面改性、具有特殊性能的镁铝水滑石,具有良好的红外吸收、紫外阻隔功能,可以作为光稳定剂、紫外吸收剂应用于水性油墨领域;所述水性树脂乳液为水性丙烯酸树脂、水性聚氨酯树脂、水性硅丙树脂中的一种或多种的混合物,且至少一种能够耐受200℃以上高温,优选采用水性丙烯酸树脂;所述耐磨抗刮剂为聚乙烯蜡浆、聚四氟乙烯蜡浆、有机硅表面活性剂中的一种或多种的混合物,优选采用聚四氟乙烯蜡浆作为耐磨抗刮剂;所述成膜助剂为丙二醇甲醚、二丙二醇甲醚、丙二醇丁醚、二丙二醇丁醚中的任意一种或多种的混合物;所述的流平剂为氟改性丙烯酸酯共聚物、聚醚改性硅氧烷、磷酸酯改性丙烯酸共聚物中的一种或多种的混合物;所述的消泡剂为聚硅氧烷、矿物油、聚醚高碳醇、植物油及其改性化合物中的一种或多种的混合物;所述的润湿分散剂为聚乙二醇型多元醇、聚乙烯亚胺衍生物、脂肪酸环氧乙烷的加成物等高分子嵌段共聚物溶液中的一种或其多种的混合物,用于稳定颜料,使其在油墨中均匀分散,不浮色发花或沉降分层。上述各原料都是已知的物质,均可以购买到。
根据表格2的各种质量百分比组合制得的水性色浆的主要性能指标如表3所示。
表3
实施例1~5提供的PVC墙纸用高耐候水性油墨的制备过程是:
(1)制备水性色浆:按表2的配方,将颜料、水性树脂乳液、镁铝水滑石、润湿分散剂、消泡剂、纯净水加入分散机中分散均匀,之后加入研磨机中循环研磨,控制色浆细度在15μm以下、粘度20~40秒(察恩4#杯,25℃)、PH值7.5~8.5,即得到所需水性色浆。
(2)制备高耐候油墨:按表1的配方,将水性色浆、水性树脂乳液、耐磨抗刮剂、流平剂、消泡剂、防腐剂、纯净水加入搅拌器,以300~500rpm的转速搅拌,充分分散均匀,检测指标合格后,即得所述PVC墙纸用高耐候水性油墨。
比较试验:
(1)将实施例1~5制备得到的实验组油墨与对比组油墨根据相应颜色分别涂布在PVC墙纸上,分别烘干、自然冷却即可。
(2)检测实验组油墨与对比组油墨在PVC墙纸上涂布后的各项性能指标。这里以实施例3为基础,测得的性能指标具体如表4所示。
表4
从表4可以看出,本发明得到的PVC墙纸用高耐候水性油墨,成膜性好、透明度高、附着牢度好,耐磨性好,特别是耐热、耐黄变、耐候性突出。
Claims (10)
1.一种PVC墙纸用高耐候水性油墨,其特征在于包括以下质量百分比的组份:水性色浆20~50%,水性树脂乳液30~60%,耐磨抗刮剂1~5%,成膜助剂0.5~3%,流平剂0.2~2%,消泡剂0.1~0.5%,防腐剂0.1%,纯净水5~20%。
2.根据权利要求1所述的PVC墙纸用高耐候水性油墨,其特征在于所述水性色浆包括以下质量百分比的组份:镁铝水滑石1~20%,颜料20~50%,水性树脂乳液15~60%,润湿分散剂0~5%,消泡剂0.1~0.5%,纯净水10~40%。
3.根据权利要求2所述的PVC墙纸用高耐候水性油墨,其特征在于所述水性树脂乳液为水性丙烯酸树脂、水性聚氨酯树脂、水性硅丙树脂中的一种或多种的混合物。
4.根据权利要求2所述的PVC墙纸用高耐候水性油墨,其特征在于所述颜料为无机颜料或有机彩色颜料或其两者的混合物。
5.根据权利要求1所述的PVC墙纸用高耐候水性油墨,其特征在于所述耐磨抗刮剂为聚乙烯蜡浆、聚四氟乙烯蜡浆、有机硅表面活性剂中的一种或多种的混合物。
6.根据权利要求1所述的PVC墙纸用高耐候水性油墨,其特征在于所述成膜助剂为丙二醇甲醚、二丙二醇甲醚、丙二醇丁醚、二丙二醇丁醚中的任意一种或多种的混合物。
7.根据权利要求1所述的PVC墙纸用高耐候水性油墨,其特征在于所述的流平剂为氟改性丙烯酸酯共聚物、聚醚改性硅氧烷、磷酸酯改性丙烯酸共聚物中的一种或多种的混合物。
8.根据权利要求1所述的PVC墙纸用高耐候水性油墨,其特征在于所述的消泡剂为聚硅氧烷、矿物油、聚醚高碳醇、植物油及其改性化合物中的一种或多种的混合物。
9.根据权利要求1所述的PVC墙纸用高耐候水性油墨,其特征在于所述的润湿分散剂为聚乙二醇型多元醇、聚乙烯亚胺衍生物、脂肪酸环氧乙烷的加成物等高分子嵌段共聚物溶液中的一种或其多种的混合物。
10.一种PVC墙纸用高耐候水性油墨的制备方法,其特征在于包括以下步骤:
(1)、制备水性色浆:按所述的质量百分比,将镁铝水滑石、颜料、水性树脂乳液、润湿分散剂、消泡剂、纯净水加入分散机中分散均匀,之后加入研磨机中循环研磨,控制色浆细度在15μm以下、粘度20~40秒、PH值7.5~8.5,即得到所需水性色浆;
(2)、制备高耐候油墨:按所述的质量百分比,将水性色浆、水性树脂乳液、耐磨抗刮剂、流平剂、消泡剂、部分纯净水加入搅拌器,以300~500rpm的转速搅拌,充分分散均匀,加入防腐剂、余量纯净水,即得所述PVC墙纸用高耐候水性油墨。