CN107556815A - 一种水性印刷油墨及其制备方法 - Google Patents
一种水性印刷油墨及其制备方法 Download PDFInfo
- Publication number
- CN107556815A CN107556815A CN201710979589.8A CN201710979589A CN107556815A CN 107556815 A CN107556815 A CN 107556815A CN 201710979589 A CN201710979589 A CN 201710979589A CN 107556815 A CN107556815 A CN 107556815A
- Authority
- CN
- China
- Prior art keywords
- water
- printing ink
- based printing
- ink
- printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及印刷油墨技术领域,尤其是涉及一种水性印刷油墨及其制备方法。本发明的水性印刷油墨的溶剂基本是水,能够满足净味安全的要求;印刷后印品附着力不会退化,且在印刷过程无需加氨水调pH值,生产环境和生产过程安全健康;着色力、附着力、光泽、贮存稳定性、耐候性性能方面与油性油墨接近甚至优于油性油墨,非常适合凹版塑料复合印刷和表印印刷使用;通用于经表面处理的PET、PVC收缩膜、BOPP、PE等极性基材,具有低能耗、快速固化、零VOC排放的特点,符合生态、经济、节能的原则。
Description
技术领域
本发明涉及印刷油墨技术领域,尤其是涉及一种水性印刷油墨及其制备方法。
背景技术
油墨是印刷过程中用于形成图文信息的物质,直接决定印刷品上图像的阶调、色彩、清晰度等,在印刷图文再现中起决定作用。目前市面上用于包装印刷行业的油墨以油性油墨为主。油墨以醇、酯、醚、酮、汽油等作为溶剂,对生态环境的污染性和对生产和使用工人健康的侵害性较大,同时油性油墨自身的缺点和不足,其应用的局限性日趋明显。此外,国家环保正策的施行,油性油墨的使用成本和维护成本也日趋提高,进一步限制了其应用。
为了解决油性油墨自身的缺点和不足,水性印刷油墨应运而生并得到快速的发展。与油性油墨相比,水性印刷油墨的环保性能更进一步。水性印刷油墨不仅不含芳香烃溶剂,而且VOC也大大减少。目前,市面上已出现可用于于BOPP、PET、PP、NY等包装基材的水性油墨,但是印品和油墨在贮存过程的干燥性、光泽度、附着力、耐抗性都有不同程度的退化,明显不能满足包装印刷业的要求。
发明内容
为了解决现有技术的不足,本发明的目的是提供一种性能优良的水性印刷油墨。本发明的水性印刷油墨在着色力、附着力、光泽、贮存稳定性、耐候性性能方面与油性油墨接近甚至优于油性油墨,非常适合凹版塑料复合印刷和表印印刷。
本发明是通过以下技术方案实现的:
一种水性印刷油墨,包括以下按重量百分比计的组分:
一种水性印刷油墨,包括以下按重量百分比计的组分:
优选地,所述丙烯酸乳液是苯丙烯酸乳液。
优选地,所述丙烯酸单体具有核壳结构。
优选地,所述水性聚氨酯是氨基化的水性聚氨酯。
优选地,所述交联剂为硅烷类交联剂。
优选地,所述消泡剂为水性聚醚或有机硅类消泡剂。
优选地,所述蜡乳液为非离子蜡乳液或阴离子蜡乳液中的一种或两种混合。
上述水性印刷油墨的制备方法,包括以下步骤:
(1)将丙烯酸乳液、颜料、分散剂、润湿剂、消泡剂、1/2用量的水混合搅拌分散均匀;
(2)在25℃研磨温度研磨至细度5微米以下;
(3)加入丙烯酸单体、水性聚氨酯、抗刮剂、蜡乳液、和剩余的水的混合物,分散25-30分钟;
(4)最后加入交联剂并分散15-20分钟,静置3-5小时后用100目纱网过滤即得水性印刷油墨。
本发明的有益效果:
(1)本发明的水性印刷油墨的溶剂主要是水,能够满足净味安全的环保要求;
(2)本发明的水性印刷油墨印刷后印品附着力不会退化,且在印刷过程无需加氨水调pH值,,生产环境和生产过程安全健康;
(3)本发明的水性印刷油墨在着色力、附着力、光泽、贮存稳定性、耐候性性能方面与油性油墨接近甚至优于油性油墨,非常适合凹版塑料复合印刷和表印印刷使用;
(4)本发明是水性印刷油墨能够通用于经表面处理的PET、PVC收缩膜、BOPP、PE等极性基材,具有低能耗、快速固化、零VOC排放的特点,符合生态、经济、节能的原则。
具体实施方式
以下结合具体实施例,对本发明作进一步说明。
实施例1
一种水性印刷油墨,包括以下按重量百分比计的组分:
上述性印刷油墨的制备方法,包括以下步骤:
(1)将苯丙烯酸乳液、颜料、分散剂、润湿剂、水性聚醚、1/2用量的水混合搅拌分散均匀;
(2)在50℃下研磨至细度5微米以下;
(3)加入丙烯酸单体、氨基化水性聚氨酯、抗刮剂、蜡乳液、和剩余的水的混合物,分散25-30分钟;
(4)最后加入交联剂并分散15-20分钟,静置3-5小时后用100目纱网过滤即得水性印刷油墨。
实施例2
一种水性印刷油墨,包括以下按重量百分比计的组分:
所述水性印刷油墨的制备方法同实施例1。
实施例3
一种水性印刷油墨,包括以下按重量百分比计的组分:
性能测试
实施例1-3中的水性印刷油墨的性能结果列在表1中。
表1实施例1-3中的水性印刷油墨的性能
由上表可以看出,本发明的油墨综合性能良好,在附着力、干燥性、粘性、遮盖力、着色力、流动性、气味、稳定性方面都能满足需求。
将实施例1的水性印刷油墨与市场上的油性油墨进行对比,结果列在表2中。
表2实施例1的水性印刷油墨与市场上油性油墨对比
由表2可见,本发明的水性印刷油墨的附着力、干燥性、反粘性、遮盖力、着色力等性能与市场上的油性油墨性能相当,但在稳定性方面优于市面上的油性油墨,而最大的区别是本发明的水性油墨净味,而油性油墨则充满有毒气味,生产和环境安全难以保障。
Claims (9)
1.一种水性印刷油墨,其特征在于,包括以下按重量百分比计的组分:
2.根据权利要求1所述的水性印刷油墨,其特征在于,包括以下按重量百分比计的组分:
3.根据权利要求1或2所述的水性印刷油墨,其特征在于,所述丙烯酸乳液是苯丙烯酸乳液。
4.根据权利要求1或2所述的水性印刷油墨,其特征在于,所述丙烯酸单体具有核壳结构。
5.根据权利要求1或2所述的水性印刷油墨,其特征在于,所述水性聚氨酯是氨基化的水性聚氨酯。
6.根据权利要求1或2所述的水性印刷油墨,其特征在于,所述交联剂为硅烷类交联剂。
7.根据权利要求1或2所述的水性印刷油墨,其特征在于,所述消泡剂为水性聚醚或有机硅类消泡剂。
8.根据权利要求1或2所述的水性印刷油墨,其特征在于,所述蜡乳液为非离子蜡乳液或阴离子蜡乳液中的一种或两种混合。
9.权利要求1-8中任一项所述的水性印刷油墨的制备方法,其特征在于,包括以下步骤:
(1)将丙烯酸乳液、颜料、分散剂、润湿剂、消泡剂、1/2用量的水混合搅拌分散均匀;
(2)在25℃研磨温度研磨至细度5微米以下;
(3)加入丙烯酸单体、水性聚氨酯、抗刮剂、蜡乳液、和剩余的水的混合物,分散25-30分钟;
(4)最后加入交联剂并分散15-20分钟,静置3-5小时后用100目纱网过滤即得水性印刷油墨。