CN105385314A - Water-based white polyester coil coating special for aluminum ceiling finish paint and preparation method of water-based white polyester coil coating - Google Patents
Water-based white polyester coil coating special for aluminum ceiling finish paint and preparation method of water-based white polyester coil coating Download PDFInfo
- Publication number
- CN105385314A CN105385314A CN201511007744.7A CN201511007744A CN105385314A CN 105385314 A CN105385314 A CN 105385314A CN 201511007744 A CN201511007744 A CN 201511007744A CN 105385314 A CN105385314 A CN 105385314A
- Authority
- CN
- China
- Prior art keywords
- finish paint
- white polyester
- water
- polyester
- coiled material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses water-based white polyester coil coating special for aluminum ceiling finish paint and a preparation method of the water-based white polyester coil coating. The coil coating is prepared from, by weight, 5%-20% of deionized water, 2%-4% of solvent, 1%-2% of dispersing agent, 0.5%-1% of catalyst, 5%-10% of amino resin, 1%-2% of adherence promoter, 0.3%-0.5% of antifoaming agent, 0.3%-0.6% of flatting agent, 20%-40% of titanium dioxide, 5%-10% of water-based polyester modified epoxy, 30%-50% of water-based organosilicone modified polyester resin and 1%-3% of modifier. The flexibility of the coil coating can meet the construction requirement of an aluminum ceiling, and the advantage of being environment friendly is achieved. The easy-to-implement preparation method of the water-based white polyester coil coating for the aluminum ceiling finish paint is further disclosed.
Description
Technical field
The present invention relates to fine chemistry industry technical field of coatings, in particular to a kind of coil coating and preparation method thereof of aluminium sheet roller coat.
Background technology
Aluminium material roll-coating plate is the starting material of the building decorative plates of current widespread use, wherein needs to use the building products of aluminium material roll-coating plate to comprise: aluminium-plastic panel, aluminium smallpox, heavy construction interior wall and cladding panel, industrial factory building roof tiling plate, advertisement decoration panel, civilian door trim panels, Household ornament wallboard, furniture panel, home appliance panel and digital product metal decking etc.The various colors of aluminium material roll-coating plate, almost nature all colours all can reproduce, and simultaneously by different coating and application techniques, can present 3D, three-dimensional pattern, the effects such as simulated stone texture, trees texture, leather texture and metal texture.Wherein, aluminium smallpox is the home decoration material risen in recent years, to substitute original gypsum, wood finishing material, widely applies on family's furred ceiling, body of wall and kitchen cabinet decoration, has the features such as environmental protection, recyclable, various colors.
Aluminium smallpox is formed after the aluminium volume continuously produced on Large Painting Workshop by coil coating is cut, wherein, application uses the coil coating of oiliness in a large number, but, because aluminium smallpox processing request is different from the other materials such as aluminium-plastic panel, require that when impact briquetting edge can not be broken, this has high requirement to the snappiness of aluminium sheet and coil coating, so the coil coating used must have excellent bending property, only have some polyesters coating can reach this performance at present.
Along with country improves constantly the requirement of environmental protection, national environmental protection regulation is to the restriction of VOC and the people enhancing to environment and health perception, research and development water-based aluminium smallpox coil coating substitutes current oiliness aluminium smallpox coil coating becomes trend, but, current aqueous coil coating major part is water soluble acrylic acid and common water borne polyester coating, and its snappiness cannot reach the construction requirement of aluminium smallpox.
Summary of the invention
The object of the invention is to the technical deficiency overcoming the environmental issue of above-mentioned prior art oiliness coil coating existence and the snappiness difference of aqueous coil coating existence, thus provide a kind of snappiness can reach aluminium smallpox construction requirement and be rich in the aqueous coil coating of environmental protection.
Another object of the present invention is also that providing a kind of implements the special aqueous white polyester coiled material preparation method for coating of easy aluminium smallpox finish paint
The object of the present invention is achieved like this:
The aqueous white polyester coiled material coating that aluminium smallpox finish paint is special, is characterized in that, comprise following component and weight percent thereof:
Deionized water: 5-20%;
Solvent: 2-4%;
Dispersion agent: 1-2%;
Catalyzer: 0.5-1%;
Aminoresin: 5-10%;
Adhesive agent: 1%-2%;
Defoamer: 0.3-0.5%;
Flow agent: 0.3-0.6%;
Titanium dioxide: 20-40%;
Waterborne polyester modified epoxy: 5%-10%;
Waterborne organic silicon modified polyester resin 30-50%;
Conditioning agent: 1-3%.
Object of the present invention can also adopt following technical measures to solve:
As scheme more specifically, described solvent comprises propandiol butyl ether and/or propylene glycol monomethyl ether, that is: solvent can be grouped into by one or both one-tenth following: propandiol butyl ether, propylene glycol monomethyl ether.
Further, described dispersion agent comprises polyurethane copolymer and/or amide polymer, that is: dispersion can be made up of following one or two kinds of compositions: polyurethane copolymer and amide polymer.
Further, described catalyzer comprises Witco 1298 Soft Acid and/or different eo-acid, that is: catalyzer is made up of a kind of or two kinds of compositions: Witco 1298 Soft Acid and different eo-acid.
Further, described defoamer is fluorine-containing broken bubble polymers soln, and described adhesive agent are high phosphoric acid ester polyester polymers.
Further, described amino tree refers to be made up of two kinds or three kinds of compositions: full methyl-etherified melamine resin, part methyl-etherified melamine resin and closure isocyanic ester; Wherein, using part methyl-etherified melamine resin and closure isocyanic ester to arrange in pairs or groups result of use can be better.
Described adhesive agent are phosphoric acid open loop epoxide group polymkeric substance further, and titanium dioxide is water-based Rutile type Titanium Dioxide.
Further, described conditioning agent is ammoniacal liquor and/or dimethylethanolamine, that is: conditioning agent is one or both in ammoniacal liquor and dimethylethanolamine.
Further, described flow agent is polyester modification organopolysiloxane solution.
Further, described deionized water is the deionized water using RO reverse osmosis to produce.
The aqueous white polyester coiled material coating that aluminium smallpox finish paint of the present invention is special, by adopting the resin of two kinds of different characteristics, the present invention is made not only to have adhesion property water-soluble and excellent fully, possess the bending property of the 0T needed for aluminium smallpox simultaneously, thus reach the construction requirement of aluminium smallpox in impact briquetting process.
As the technical essential of key, in order to ensure the adhesion property water-soluble and excellent fully that the present invention possesses, formula employs following scheme: use and by solid part be: 70-90%, viscosity is the epoxy resin of the high-solid lower-viscosity middle-molecular-weihydroxyethyl of the polyester modification of 200-300pa.s/25 DEG C, because it has excellent sticking power and snappiness to polar metal ground, possess again good water-soluble simultaneously.
As the technical essential of key, in order to ensure the water-soluble fully and OT bending property (as shown in Figure 2) that the present invention possesses, following scheme is employed: use solid part is: 45-55% above formula, viscosity is 300-400pa.s/25 DEG C, and having the cyclic organic intermediate modified polyester resin of the macromolecule of excellent flexibility, the feature of this resin is exactly snappiness water-soluble and good fully.
Another object of the present invention is achieved in that
A preparation method for the aqueous white polyester coiled material coating that aluminium smallpox finish paint is special, is characterized in that: comprise the following steps,
Step one, resin pre-dispersed: first add waterborne organic silicon modified polyester resin and dispersion agent according to part by weight in dispersion cylinder, then add solvent;
Step 2, the pre-mixing of titanium dioxide: according to part by weight in dispersion cylinder, slowly adds titanium dioxide in slowly stirring, and then uses stirrer to stir 25-35 minute according to 1000-1500RPM rotating speed, the white slurry that obtained premix gets togather;
Step 3, the grinding of titanium dioxide: the white slurry that premix gets togather is ground by sand mill, makes mesh-of-grind reach 10 microns or below;
Step 4, adds other resin additive: use stirrer to stir according to 150-300RPM rotating speed, in stirring, slowly add waterborne polyester modified epoxy resin, aminoresin, adhesive agent, flow agent, defoamer and catalyzer respectively;
Step 5, adjusts viscosity and pH value: stirrer stirs according to 150-300RPM rotating speed, adds deionized water, and adjustment viscosity is to 125 ", and adjustment in use agent is transferred to pH value between 8.2-8.8;
Step 6, packaging: use 250-350 mesh filter screen to filter, be packaged in pail pack.
Further concrete scheme as above-mentioned preparation method:
As further scheme, in described step one, in dispersion cylinder, first add silicone modified polyester resin and dispersion agent according to the part by weight of 16:1:1, then add propandiol butyl ether.
As further scheme, in described step 2, refer to the weight of pre-dispersed mixture according to the tree that step one is obtained, slowly add titanium dioxide in slowly stirring in dispersion lacks in the ratio of 1:1, then use stirrer to stir 30 minutes according to 1000-1500RPM rotating speed.
As further scheme, in described step 5, adjustment viscosity " (is coated with 4-cup to 125.25 ± 1 DEG C), and adjustment in use agent is transferred to 8.5 pH value;
As further scheme, in described step 6, use 300 mesh filter screens to filter, be packaged in pail pack.
Beneficial effect of the present invention is as follows:
(1) the aqueous white polyester coiled material coating that aluminium smallpox finish paint of the present invention is special, by resin and the effective formulating of recipe of special preparation, thus obtain having adhesion property water-soluble and excellent fully, the bending property simultaneously possessing the 0T needed for aluminium smallpox also can reach the product of the construction requirement of aluminium smallpox in impact briquetting process, thus substitute oiliness aluminium smallpox coil coating, the pollution of reduction industry, reduce VOC discharge, make aluminium smallpox can more environmental protection must in applying widely, for building materials and ornaments industry provides more environmentfriendly products.
(2) preparation method of the aqueous white polyester coiled material coating that aluminium smallpox finish paint of the present invention is special, have and implement easily, obtained coil coating, the snappiness possessed can reach aluminium smallpox construction requirement and be rich in the advantage of environmental protection.
Accompanying drawing explanation
Fig. 1 is preparation method's flow diagram of the special aqueous white polyester coiled material coating of aluminium smallpox finish paint of the present invention;
Fig. 2 is the present invention about the curved explanatory view of T.
Specific embodiments
Below in conjunction with specific embodiment, the invention will be further described:
The aqueous white polyester coiled material coating that aluminium smallpox finish paint is special, is characterized in that: comprise following component and weight percent thereof:
Deionized water: 5-20%;
Solvent: 2-4%;
Dispersion agent: 1-2%;
Catalyzer: 0.5-1%;
Aminoresin: 5-10%;
Adhesive agent: 1%-2%;
Defoamer: 0.3-0.5%;
Flow agent: 0.3-0.6%;
Titanium dioxide: 20-40%;
Waterborne polyester modified epoxy: 5%-10%;
Waterborne organic silicon modified polyester resin 30-50%;
Conditioning agent: 1-3%.
As more particular embodiment of the present invention: above-mentioned solvent can comprise two kinds of compositions and weight ratio thereof: propandiol butyl ether 70% and propylene glycol monomethyl ether 30%.
Described catalyzer can comprise two kinds of compositions and weight ratio thereof: Witco 1298 Soft Acid and different eo-acid each 50%.
Described aminoresin can comprise three kinds of compositions and weight ratio thereof: full methyl-etherified melamine resin 45%, part methyl-etherified melamine resin 15% and closure isocyanic ester 45%.
Described dispersion agent is amide polymer, and defoamer is fluorine-containing broken bubble polymers soln; And described adhesive agent are high phosphoric acid ester polyester polymers, flow agent is polyester modification organopolysiloxane solution, and described conditioning agent is dimethylethanolamine.
Just the present invention makes following specific embodiment below:
Embodiment 1: its each component of aqueous white polyester coiled material coating that a kind of aluminium smallpox finish paint is special and mass percent as follows:
Deionized water: 11.02%
Solvent: 1.69%
Dispersion agent: 1.69%
Catalyzer: 0.42%
Amino tree refers to: 5.5%
Adhesive agent: 1.69%
Defoamer: 0.42%
Flow agent: 0.42%
Titanium dioxide: 28%
Waterborne polyester modified epoxy: 6.78%
Waterborne organic silicon modified polyester resin 40.68%.
Conditioning agent: 1.69%
Below with regard to its concrete preparation method, be described in detail as follows:
As shown in Figure 1: a kind of preparation method of aqueous white polyester coiled material coating as special in above-mentioned aluminium smallpox finish paint, is characterized in that: comprise the following steps,
Step one, resin pre-dispersed: first add silicone modified polyester resin and dispersion agent according to the ratio of 16:1:1 in dispersion cylinder, then add propandiol butyl ether;
Step 2, the pre-mixing of titanium dioxide: according to the ratio to step one weight 1:1 in dispersion cylinder, slowly adds titanium dioxide in slowly stirring, and then uses stirrer to stir 30 minutes according to 1000-1500RPM rotating speed;
Step 3, the grinding of titanium dioxide: the white slurry that premix gets togather is ground by sand mill, makes mesh-of-grind reach less than 10 microns;
Step 4, adds other resin additive: use stirrer to stir according to 150-300RPM rotating speed, in stirring, slowly add polyester modified epoxy resin, aminoresin, adhesive agent, flow agent, defoamer, catalyzer respectively;
Step 5, adjusts viscosity and pH value: stirrer stirs according to 150-300RPM rotating speed, adds deionized water, and adjustment viscosity " (is coated with 4-cup to 125.25 ± 1 DEG C), and adjustment in use agent is transferred to 8.5 pH value;
Step 6, packaging: use 300 mesh filter screens to filter, be packaged in pail pack.
As shown in Figure 2, about the explanation that T is curved, in order to ensure the water-soluble fully and OT bending property that the present invention possesses, following scheme is employed: use solid part is: 45-55% above formula, viscosity is 300-400pa.s/25 DEG C, and having the cyclic organic intermediate modified polyester resin of the macromolecule of excellent flexibility, the feature of this resin is exactly snappiness water-soluble and good fully.
Coating performance is tested: test according to GB/T17748-2008 " building curtain wall composited aluminum and plastic decking " standard: test condition: PMT/ DEG C: 216-224 DEG C; Base material: 0.40mm aluminium sheet; Dried film thickness: 19 ± 1 μm; See the following form:
| project | testing standard | technical indicator | detected result |
| outward appearance | gB/T1729 | flat smooth | detected result |
| solid part % | gB/T1725 | >=50 | qualified |
| viscosity (is coated with 4-cup.S/25 ± 1 DEG C) | gB/T1723 | 125 ± 5 "/25 ± 1 DEG C | 120 "/30 DEG C |
| fineness μm | gB/T1724 | ≤ 15 μm | qualified |
| proportion/25 DEG C | gB/T1756 | protocol value | qualified |
| echo power (drawing lattice) | gB/T9286 | ≤ 1 grade | 0 grade |
| hardness (pencil) | gB/T6739 | >=2H | 2H |
| impact | gB/T1732 | >=5J | qualified |
| flexing | gB/T17748-1999 (6.7) | horizontal 2T indulges 1T | qualified |
| resistance to boiling water | 99 DEG C ± 1 DEG C × (1HR or 2HR) | the 2h of resistance to boiling water | qualified |
| solvent resistant (MEK) | nCCA II-18 | >=100 | > 100 |
Claims (10)
1. the aqueous white polyester coiled material coating that aluminium smallpox finish paint is special, is characterized in that, comprise following component and weight percent thereof:
Deionized water: 5-20%;
Solvent: 2-4%;
Dispersion agent: 1-2%;
Catalyzer: 0.5-1%;
Aminoresin: 5-10%;
Adhesive agent: 1%-2%;
Defoamer: 0.3-0.5%;
Flow agent: 0.3-0.6%;
Titanium dioxide: 20-40%;
Waterborne polyester modified epoxy: 5%-10%;
Waterborne organic silicon modified polyester resin 30-50%;
Conditioning agent: 1-3%.
2. the aqueous white polyester coiled material coating that aluminium smallpox finish paint is special according to claim 1, it is characterized in that, described solvent comprises propandiol butyl ether and/or propylene glycol monomethyl ether.
3. the aqueous white polyester coiled material coating that aluminium smallpox finish paint is special according to claim 1, it is characterized in that, described dispersion agent comprises polyurethane copolymer and/or amide polymer.
4. the aqueous white polyester coiled material coating that aluminium smallpox finish paint is special according to claim 1, is characterized in that, described catalyzer comprises Witco 1298 Soft Acid and/or different eo-acid.
5. the aqueous white polyester coiled material coating that aluminium smallpox finish paint is special according to claim 1, is characterized in that, described defoamer is fluorine-containing broken bubble polymers soln.
6. the aqueous white polyester coiled material coating that aluminium smallpox finish paint is special according to claim 1, is characterized in that, described adhesive agent are phosphoric acid open loop epoxide group polymkeric substance, and titanium dioxide is water-based Rutile type Titanium Dioxide.
7. the aqueous white polyester coiled material coating that aluminium smallpox finish paint is special according to claim 1, is characterized in that, described conditioning agent is ammoniacal liquor and/or dimethylethanolamine.
8. the aqueous white polyester coiled material coating that aluminium smallpox finish paint is special according to claim 1, it is characterized in that, described waterborne polyester modified epoxy resin is the epoxy resin of the high-solid lower-viscosity middle-molecular-weihydroxyethyl by polyester modification, it is rich in sticking power and snappiness to polar metal ground, its solid part is 70-90%, and viscosity is 200-300pa.s/25 DEG C.
9. the aqueous white polyester coiled material coating that aluminium smallpox finish paint is special according to claim 1, it is characterized in that, described waterborne organic silicon modified polyester resin is the cyclic organic intermediate modified polyester resin being rich in flexible macromolecule, its solid part is 45-55%, and viscosity is 300-400pa.s/25 DEG C.
10. a preparation method for the aqueous white polyester coiled material coating that aluminium smallpox finish paint is special as claimed in claim 1, is characterized in that: comprise the following steps,
Step one, resin pre-dispersed: first add waterborne organic silicon modified polyester resin and dispersion agent according to part by weight in dispersion cylinder, then add solvent;
Step 2, the pre-mixing of titanium dioxide: according to part by weight in dispersion cylinder, slowly adds titanium dioxide in slowly stirring, and then uses stirrer to stir 25-35 minute according to 1000-1500RPM rotating speed, the white slurry that obtained premix gets togather;
Step 3, the grinding of titanium dioxide: the white slurry that premix gets togather is ground by sand mill, makes mesh-of-grind reach 10 microns or below;
Step 4, adds other resin additive: use stirrer to stir according to 150-300RPM rotating speed, in stirring, slowly add waterborne polyester modified epoxy resin, aminoresin, adhesive agent, flow agent, defoamer and catalyzer respectively;
Step 5, adjusts viscosity and pH value: stirrer stirs according to 150-300RPM rotating speed, adds deionized water, and adjustment viscosity is to 125 ", and adjustment in use agent is transferred to pH value between 8.2-8.8;
Step 6, packaging: use 250-350 mesh filter screen to filter, be packaged in pail pack.