CN105272035A - Artificial stone slurry and artificial stone prepared from same through curing forming - Google Patents

Artificial stone slurry and artificial stone prepared from same through curing forming Download PDF

Info

Publication number
CN105272035A
CN105272035A CN201510698606.1A CN201510698606A CN105272035A CN 105272035 A CN105272035 A CN 105272035A CN 201510698606 A CN201510698606 A CN 201510698606A CN 105272035 A CN105272035 A CN 105272035A
Authority
CN
China
Prior art keywords
parts
rostone
slurry
artificial stone
raw material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510698606.1A
Other languages
Chinese (zh)
Inventor
刘辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI ZHUO'OU BUILDING DECORATION ENGINEERING Co Ltd
Original Assignee
SHANGHAI ZHUO'OU BUILDING DECORATION ENGINEERING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI ZHUO'OU BUILDING DECORATION ENGINEERING Co Ltd filed Critical SHANGHAI ZHUO'OU BUILDING DECORATION ENGINEERING Co Ltd
Priority to CN201510698606.1A priority Critical patent/CN105272035A/en
Publication of CN105272035A publication Critical patent/CN105272035A/en
Pending legal-status Critical Current

Abstract

The invention discloses artificial stone slurry and artificial stone prepared from the same through curing forming. The artificial stone slurry comprises raw materials and water accounting for 16%-18% of the raw materials, wherein the raw materials comprise components in parts by weight as follows: 100 parts of cement, 100 parts of colored sand, 15 parts of shells, 7 parts of glue and 1-1.6 parts of an acrylic emulsion. Uneven broken shells are distributed on the artificial stone prepared from the artificial stone slurry through curing forming and are subjected to color mixing through pigment powder, and the artificial stone has colors and texture similar to marble; the artificial stone prepared from the artificial stone slurry through curing forming is compact in structure, has higher strength and can be taken as a building material, a preparation method is simple and easy, the raw materials are cheap and environment-friendly.

Description

The rostone of rostone slurry and solidifying formation thereof
Technical field
The invention belongs to rostone technical field, be specifically related to the rostone of a kind of rostone slurry and solidifying formation thereof.
Background technology
Along with the development of modem architectural ornament industry, people are also thereupon more extensive for the requirement of environmental decoration.And the produce of many preciousnesses are by the exploitation of madness and predation without restraint on the earth, a large amount of non-renewable materials is faced with exhaustion and disappearance.And the birth of colored rostone as recyclable materials, be namely the product that this environment of times beautifies trend.Especially because this product color is abundant, various shapes, durable in use, process simple, cheap, possess again the characteristic of energy-saving and environment friendly simultaneously, therefore can meet the contemporary high standard for the various unlike material effects of building decoration, landscaping and high request completely.
Summary of the invention
The object of the present invention is to provide and a kind ofly may be used for making the rostone slurry of the rostone with class chrysodor color and texture and the rostone of solidifying formation thereof, i.e. Beirut.
Rostone slurry of the present invention comprises: raw material and the water accounting for raw material 16 ~ 18%, and wherein said raw material comprises: 100 parts of cement, 100 parts of color sand, 15 parts of shells, 7 parts of glue and 1 ~ 1.6 part of third breast, wherein said part is weight part.
Described raw material can also comprise admixture, and described admixture is selected from following material group: fluidizer, retardant (suitably add time as higher in summer temperature can delay solidification), hardening accelerator (suitably add time as lower in winter temperature and can accelerate solidification), frostproofer (suitably add time as lower in winter temperature can anti-freezing anti-cracking) and brightening agent.
Described raw material can also comprise water reducer and 0.06 part of Mierocrystalline cellulose, and wherein said water reducer is 4 ~ 5mL:1kg with the ratio of cement.Described water reducer can improve early strength, and described water reducer can select polycarboxylate high-efficiency water reducing agent, such as SiKaSNN water reducer.The consumption of water reducer and water adjusts according to weather, and high temperature drying weather suitably can reduce the consumption of described water reducer, otherwise suitably increases consumption.Described Mierocrystalline cellulose can select Vltra tears, to improve Total Product intensity.
Described raw material can also comprise 1.5 parts of anti-fissuring agents.
Described raw material can also comprise 2.13 ~ 2.15 parts of pigment powder, and described pigment powder comprises 1.79 ~ 1.81 parts of preferably 1.8 parts of titanium dioxides, 0.176 ~ 0.184 part of preferably 0.18 part of fiery bloom, 0.096 ~ 0.104 part of preferably 0.1 part of iron oxide yellow powder, 0.028 ~ 0.032 part of preferred 0.03 part of cologne earth powder and 0.028 ~ 0.032 part preferably 0.03 part of iron black powder.
Described color sand consists of 64 ~ 72 parts of preferably 70 part of 60 object water ash silica sand and 28 ~ 32 parts preferably 30 part of 70 object water ash silica sands, and described order is the screen size that material sieves.
Described glue is mass ratio is 801 building adhesives of 2:1 and the mixture of white glue with vinyl, and described white glue with vinyl is venamul.
Described cement is white portland cement, such as A Erbo Portland board white portland cement, is characterized in that whiteness is high and does not affect component strength, can prepare any color to reach the texture effect of various material simultaneously.The broken shell of described shell to be particle diameter be 3mm ~ 1cm; Described third breast is acrylate copolymer emulsion.
The prefabricated mold cured of described rostone slurry is shaped, then economy-combat polishingization can obtain different, the rostone with similar marbling effect of texture excellence.
The present invention actively progressive effect is: rostone of the present invention is using silicate cement and water ash silica sand as base-material, adopt 801 building adhesives of 2:1 and the mixing glue of venamul, add uneven broken shell and mix colours with pigment powder, again through solidifying formation, color and texture have similar marmorean effect, add fiber in addition and usually strengthen bulk strength, can be used as construction timber.
Rostone of the present invention is drawn materials and is required simple, does not require special natural resources, relative to other of building decoration with materials, has and does not consume the advantages such as the former material of nature, material construction are cheap, therefore the popularizing of advantageous product.Secondly, because the making processes of whole product all adopts energy saving and environment friendly material, making product have good environment friendly and design versatility, is therefore a kind of working method of energy-saving and environment friendly.
Embodiment
The making of embodiment 1 rostone
The raw material of rostone slurry:
The raw material of table 1 rostone slurry and consumption
Wherein, cement is A Erbo Portland board white portland cement, and mixing 801 building adhesives of the glue amount of attaching most importance to than 2:1 and the mixture of venamul, water reducer is SiKaSNN water reducer, and Mierocrystalline cellulose is Vltra tears.
The concrete operation step of rostone processing:
The preparation of step one, slurry
Other raw materials in table 1 except shell and water reducer add in stirrer by 1, stir 15 ~ 30 minutes;
Raw material after stirring proceeds in dnockout bucket by 2, and add water reducer and raw material gross weight 16% is water, stirs 5 ~ 10 minutes obtained slurries.
Step 2, solidification
Slurry obtained for step one to be put into inside ready mould by 1;
Mould is positioned in shock platforms by 2, starting shock platform, shakes 3 ~ 5 minutes, ensures that pulp surface is smooth and thickness is 3cm ~ 5cm;
3 shaken after, mould is lifted to place smooth between steam coach, guarantee that die layout is smooth, covered by slurry with black thin film comprehensively, open steam, steam 12 ~ 24 hours, slurry is solidified into the product of predetermined form in a mold;
Product in mould is carried out demoulding process by 4, and the product after completing the demoulding carries out first repairing treatment, and the slurry namely utilizing the step one removing shell to obtain in 24h is repaired, and takes out overlap and the burr of product; The product repaired covers with black thin film more comprehensively and continues steaming 5 ~ 7 days, the product after being solidified completely.
Step 3, polishing
Completely crued for the step 2 product sander being provided with smart steel abrasive disc is carried out first time corase grind by 1, and thickness about 3 ~ 5mm is till getting shell;
2 carry out second time corase grind with the sander being provided with flap, until the marks on surface of first pass corase grind is polished;
3 with being provided with the sander of 50 object water mill sheets to carrying out first time fine grinding through the product of second time corase grind;
4 carry out second time fine grinding and polishing process, until product surface has certain smooth finish with the sander being provided with 150 object water mill sheets;
5 carry out third time fine grinding and the photochemical process of first pass with the sander being provided with 300 order water mill sheets;
6 carry out second time optical processing with the sander being provided with 500 object water mill sheets;
7 carry out third time photochemical process with the sander being provided with 1000 object water mill sheets;
8 carry out the 4th photochemical process with the sander being provided with 2000 object water mill sheets.
Step 4, surperficial thinning processing
The 1 former stone glue of product of polishing through step 3 carries out second time and repairs, and guarantees product surface pore-free, waits to repair dry rear grinding machine repair part is tied, and dries;
2 use vinegar clean surface, prevent the anti-alkali of product;
Product surface to be waxed (protoparaffin wax) and to towel off evenly by 3, treats that protoparaffin wax slightly dry steel wool polishing product surface increases product surface smooth finish, both obtained product rostones.
Effect example
1, unlimited plasticity-
Rostone of the present invention is stirred according to a certain ratio by raw material, and build shaping in mould, moulding is rich and varied, can be in strip, the different shaping effect such as hollow out, embossment; Also can make kinds of surface effect, comprise polishing, sub-light, fine grinding, baked wheaten cake, the process of water cutter and sandblast; With the toning of pigment powder, rich palette is various.
2, there is marbling effect
Rostone slurry of the present invention adopts white cement, water sand-lime and shell as base-material, uniform stirring, and through overcuring polishing, any surface finish pore-free, uniform hue, aberration are less, decorative pattern is attractive in appearance, have similar marmorean effect.
3, low, the environmental protection of cost
Rostone of the present invention belongs to recyclable materials and cost is lower, is conducive to environmental protection; Starting material containing radioactive nuleus element, are not national radionuclide amount category-A environment-friendly materials.
4, structure properties is good
As shown in table 2 is rostone parameters of the present invention, meets the standard-required of building and ornament materials.
Table 2 rostone parameter of the present invention
To sum up, rostone of the present invention can reach similar marmorean effect in color texture texture etc., and structural strength is better, can be used as construction timber, and making method is easy, the cheap environmental protection of the prices of raw and semifnished materials.
The present invention is not limited to above-mentioned concrete embodiment, and those of ordinary skill in the art is from above-mentioned design, and without performing creative labour, all conversion made, all drop within protection scope of the present invention.

Claims (9)

1. a rostone slurry, it water comprising raw material and account for raw material 16 ~ 18%, wherein said raw material comprises: 100 parts of cement, 100 parts of color sand, 15 parts of shells, 7 parts of glue and 1 ~ 1.6 part of third breast, wherein said part is weight part.
2. rostone slurry as claimed in claim 1, it is characterized in that described raw material also comprises admixture, described admixture is selected from following material group: fluidizer, retardant, hardening accelerator, frostproofer and brightening agent.
3. rostone slurry as claimed in claim 1, it is characterized in that described raw material also comprises water reducer and 0.06 part of Mierocrystalline cellulose, wherein said water reducer is 4 ~ 5mL:1kg with the ratio of cement.
4. rostone slurry as claimed in claim 1, characterized by further comprising 1.5 parts of anti-fissuring agents.
5. rostone slurry as claimed in claim 1, it is characterized in that described color sand consists of 64 ~ 72 parts of preferably 70 part of 60 object water ash silica sand and 28 ~ 32 parts preferably 30 part of 70 object water ash silica sands, described order is the screen size that material sieves.
6. rostone slurry as claimed in claim 1, it is characterized in that described raw material also comprises 2.13 ~ 2.15 parts of pigment powder, described pigment powder comprises 1.79 ~ 1.81 parts of preferably 1.8 parts of titanium dioxides, 0.176 ~ 0.184 part of preferably 0.18 part of fiery bloom, 0.096 ~ 0.104 part of preferably 0.1 part of iron oxide yellow powder, 0.028 ~ 0.032 part of preferred 0.03 part of cologne earth powder and 0.028 ~ 0.032 part preferably 0.03 part of iron black powder.
7. rostone slurry as claimed in claim 1, it is characterized in that described glue be mass ratio is 801 building adhesives of 2:1 and the mixture of white glue with vinyl, described white glue with vinyl is venamul.
8. rostone slurry as claimed in claim 1, is characterized in that described cement is white portland cement; The broken shell of described shell to be particle diameter be 3mm ~ 1cm; Described third breast is acrylate copolymer emulsion.
9. the rostone be shaped by the rostone slurry curing described in any one of claim 1 ~ 8.
CN201510698606.1A 2015-10-23 2015-10-23 Artificial stone slurry and artificial stone prepared from same through curing forming Pending CN105272035A (en)