CN104441820B - The artificial hole stone slab of a kind of MULTILAYER COMPOSITE and combinations thereof thing and preparation method thereof - Google Patents
The artificial hole stone slab of a kind of MULTILAYER COMPOSITE and combinations thereof thing and preparation method thereof Download PDFInfo
- Publication number
- CN104441820B CN104441820B CN201410659466.2A CN201410659466A CN104441820B CN 104441820 B CN104441820 B CN 104441820B CN 201410659466 A CN201410659466 A CN 201410659466A CN 104441820 B CN104441820 B CN 104441820B
- Authority
- CN
- China
- Prior art keywords
- surface layer
- stone slab
- hole stone
- multilayer composite
- mill base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
One aspect of the invention provides the artificial hole stone slab composition of a kind of MULTILAYER COMPOSITE, including surface layer composition, middle enhancement Layer and base pastes: wherein, described middle enhancement Layer is alkaline-resisting grid cloth；Described surface layer composition includes surface layer mill base, amphoteric metal and surface layer slurry.Present invention also offers the artificial hole stone slab of a kind of MULTILAYER COMPOSITE prepared by above-mentioned composition, including surface layer, middle enhancement Layer and bottom: wherein, surface layer is prepared by described surface layer composition.Present invention also offers the preparation method of a kind of above-mentioned artificial hole stone slab, will be coated on mould by surface layer mill base, and spread last layer amphoteric metal, again surface layer slurry is poured in mould, spread alkaline-resisting grid cloth, then pour base pastes, process can obtain through the demoulding and surface.The present invention obtains the hole size of hole stone slab, hole layout and superficial makings and all can be adjusted according to the demand of client, and lightweight cracking resistance；Preparation method flexible operation, low cost.
Description
Technical field
The present invention relates to a kind of hole stone slab, artificial hole stone slab particularly relating to a kind of MULTILAYER COMPOSITE and combinations thereof
Thing and preparation method thereof.
Background technology
Hole stone is because the surface of stone material has many holes to gain the name, and the formal name used at school of its stone material is travertine or lime
China, commercial, it is classified as marble class.The mankind are for a long time remote to use age of this stone material, can represent sieve
The building wrestling ring of Marvin's is exactly the former masterpiece of hole stone.
Natural cavity stone rich texture is gentle, clear-cut texture, and the sheet material reasonable organization made, concavo-convex harmony have
Natural, simple and unsophisticated decorative effect, can promote owing to it is distinctive the building of decoration have strong culture and
The advantage of history charm, and enjoy people to favor, the building and ornament materials of a kind of top grade.But due to sky
So hole stone intensity fragmentation poor, easy, limited cost of drawing materials is high, its hole skewness, deep mixed and deposit
At aberration, thus limit a large amount of uses of people.It is therefore desirable to a kind of form and dress can be developed
Decorations effect, close to natural cavity stone and intensity is high, price is low artificial stone, substitutes natural cavity stone.
CN102442807A discloses a kind of Lightweight composite travertine and preparation method thereof, and the method is to utilize to send out
Infusion foams after formation foam in foaming agent, and the compound mixing gained with other components is poured in mould
Arrive.The foam shape formed due to foaming agent is mostly spherical, and comparison rule, so utilizing this method to obtain
The shape of hole can not be adjusted by hole stone according to demand, and relative to the irregular holes of natural cavity stone,
The hole stone that the present invention obtains is unnatural, lacks artistry.
CN101020336A discloses a kind of artificial hole stone with true hole and preparation method thereof, the party
Method is to utilize with natural high-quality hole masonry for mould kind, and the software mould prepared as overmolding material using flexible material comes
Realize the effect of hole making hole stone have true nature.But, the method excessively idealizes, and gets rid of making soft
The complexity of body mould, the software mould simply removed in the raw material after solidification is exactly highly difficult.
CN101407427A discloses the production method of a kind of burrow stone imitation ceramic tile, and the method is mainly by adding
Enter and combine rice bran and/or the wood pore forming particles that obtains of chaff mixing granulation with former wax for stick, realize in ceramic tile
Imitative hole stone structure.But, when removing pore forming particles, as described in expository writing, former wax is by after heat sublimation, surplus
Lower rice bran and/or wood chaff brush, it is true that still can remain former wax and rice in the hole of the finished product finally given
Chaff and/or wood chaff, not only can affect use, also can affect attractive in appearance.
Summary of the invention
In order to overcome the deficiency in currently available technology, it is achieved a kind of method producing hole stone of more convenient high-quality,
The artificial hole stone slab that the invention provides a kind of MULTILAYER COMPOSITE and combinations thereof thing and preparation method thereof.This multilayer
Compound artificial hole stone slab not only its hole size, hole layout and superficial makings all can be according to the need of client
Asking and be adjusted, and have the feature of lightweight cracking resistance, additionally its preparation method also has flexible operation, cost
The advantage such as cheap.
The theme of first aspect present invention is the artificial hole stone slab composition of a kind of MULTILAYER COMPOSITE, and its feature exists
Surface layer composition, middle enhancement Layer and base pastes is included in, described artificial hole stone slab composition:
Described middle enhancement Layer is alkaline-resisting grid cloth；
Described surface layer composition includes surface layer mill base, amphoteric metal and surface layer slurry；
Wherein, component and the weight proportion thereof of described surface layer mill base includes:
Binder Materials 90-95 part,
Pigment 4-10 part；
Wherein, component and the weight proportion thereof of described surface layer slurry includes:
Wherein, component and the weight proportion thereof of described base pastes includes:
According to a kind of preferred embodiment of first aspect of the present invention, wherein, described amphoteric metal include beryllium, aluminium,
Any one or a few in gallium, zinc, germanium, indium, tin, antimony, thallium, lead, bismuth, polonium, preferably aluminium, can
To be aluminium foil, aluminium bits, any one or a few in aluminium wire, more preferably 5-80 mesh aluminium, wherein, optimum
Elect 20-60 mesh aluminium foil as.
According to a kind of preferred embodiment of first aspect of the present invention, wherein, described Binder Materials includes organic gel
Gel material and inorganic coagulation material, wherein, preferably inorganic coagulation material, including hydraulic cementing materials and non-
Portland cement in hydraulic cementing materials, more preferably hydraulic cementing materials, aluminate cement, sulphur aluminium
Lime in acid salt cement and/or on-hydraulic Binder Materials, any one or a few in gypsum, most preferably
For portland cement.
According to a kind of preferred embodiment of first aspect of the present invention, wherein, described aggregate include natural colour sand,
Any one or a few in artificial color sand, river sand, preferably 20-120 mesh.
According to a kind of preferred embodiment of first aspect of the present invention, wherein, described pigment can select this technology
The various pigment that field is conventional, such as the carbon black sold on market, iron oxide, cobalt oxide, titanium dioxide, paratonere
122 (being mainly composed of 2,9-dimethylquinacridone), organic light yellow, phthalocyanine blue, peacock green, lemon yellow,
Copper sulphate, acrylic paints etc..
According to a kind of preferred embodiment of first aspect of the present invention, wherein, described mineral admixture includes fine coal
In ash, breeze, stone flour, volcanic ash, silica flour any one or several.
According to a kind of preferred embodiment of first aspect of the present invention, wherein, described plasticiser, thickener, disappear
Infusion, retarder belong to polymeric additive, wherein:
Described plasticiser is preferably polycarboxylic acids dehydragent, and the synthon of described polycarboxylic acids dehydragent includes gathering
Oxygen alkane alkenyl monomer, also includes methacrylic acid, acrylic acid, maleic acid (or maleic anhydride), (methyl) alkene
Propyl sulfonic acid, styrene sulfonic acid or the salt of above-mentioned acid or ester or other derivative, also include sulfonation melamine
Amine formaldehyde condensation product, sulphonated naphtalene formaldehyde condensation product, modified lignosulfonates etc..Wherein, described polyoxy alkane thiazolinyl
Monomer can contain polyoxyethylene groups, polyoxypropylene base.
Wherein, described thickener includes cellulose family, polyacrylate, bentonite, association type polyurethanes
In any one or a few, more preferably, methylcellulose, carboxyl alkyl cellulose, hydroxy alkyl cellulose,
(methyl) acrylic acid or its ester or the homopolymers of salt or copolymer.
Wherein, any one during described defoamer includes silicon ether Copolymer, organosiloxane, polyethers and phosphate
Plant or several.
Wherein, described retarder include lignosulfonates and derivative, hydroxycarboxylic acid and its esters, carbohydrate,
Any one or a few of the weak acid such as zinc oxide, boric acid, phosphoric acid and its esters.
The theme of second aspect present invention is a kind of MULTILAYER COMPOSITE prepared by composition described in claim 1
Artificial hole stone slab, it is characterised in that described artificial hole stone slab includes surface layer, middle enhancement Layer and bottom:
Described middle enhancement Layer is alkaline-resisting grid cloth, between described surface layer and bottom；
Described surface layer is prepared by described surface layer composition, the color top layer prepared including described surface layer mill base and described
Surface layer basic unit prepared by surface layer slurry, described surface layer basic unit at least partly contains described with color top layer contact portion
The hole that amphoteric metal and described surface layer mill base, surface layer slurry reaction are formed.
The theme of third aspect present invention is the artificial hole stone slab of MULTILAYER COMPOSITE described in a kind of second aspect theme
Preparation method, described preparation method includes:
Step 1: prepare mould, and injector surface is standby；
Step 2: according to component and the weight thereof of surface layer mill base, surface layer slurry and base pastes described in first aspect
Proportioning preparation surface layer mill base, surface layer slurry and base pastes；
Step 3: described surface layer mill base is coated on described die surface；
Step 4: amphoteric metal is spread on described surface layer mill base；
Step 5: described surface layer slurry is poured to described mould；
Step 6: alkaline-resisting grid cloth is laid on described surface layer slurry；
Step 7: described base pastes is cast on described alkaline-resisting grid cloth；
Step 8: under 10-100 DEG C of temperature conditions after maintenance at least 10 hours, processes through the demoulding and surface,
I.e. obtain the artificial hole stone slab of MULTILAYER COMPOSITE.
According to a kind of preferred embodiment of third aspect of the present invention, wherein, described step 2 is according to first aspect
The component described in subject content and weight proportion prepare surface layer mill base, surface layer slurry and base pastes, its
In, it is preferable that the preparation of described surface layer slurry and base pastes is component to be put in mixer, and mixes suitable
Amount water, wherein:
Component and the weight proportion thereof of described surface layer mill base include:
Binder Materials 90-95 part,
Pigment 4-10 part；
Component and the weight proportion thereof of described surface layer slurry include:
Component and the weight proportion thereof of described base pastes include:
According to a kind of preferred embodiment of third aspect of the present invention, wherein, in described step 8, described temperature
Being preferably 20-50 DEG C, described curing time is preferably 12-24 hour.
According to a kind of preferred embodiment of third aspect of the present invention, wherein, in described step 8, described surface
Process includes any one or a few in polishing, polishing, ball blast.
The present invention utilizes the hydroxide ion in amphoteric metal and cement to react generation gas, and gas is expanding
During be trapped in slurry, slip surface formed hole.The MULTILAYER COMPOSITE artificial hole slabstone that the present invention produces
Material not only good decorating effect, has extremely strong expressive force, hole size, hole layout and superficial makings
Demand according to client is adjusted, and has the feature of lightweight, cracking resistance.It addition, compared with prior art,
It is convenient that the preparation method of the present invention produces, and can effectively save production cost, have the strongest operability.
Detailed description of the invention
First aspect present invention provides the artificial hole stone slab composition of a kind of MULTILAYER COMPOSITE, it is characterised in that
Described artificial hole stone slab composition includes surface layer composition, middle enhancement Layer and base pastes:
Described middle enhancement Layer is alkaline-resisting grid cloth；
Described surface layer composition includes surface layer mill base, amphoteric metal and surface layer slurry；
Wherein, component and the weight proportion thereof of described surface layer mill base includes:
Binder Materials 90-95 part,
Pigment 4-10 part；
Wherein, component and the weight proportion thereof of described surface layer slurry includes:
Wherein, component and the weight proportion thereof of described base pastes includes:
Second aspect present invention provides the people of a kind of MULTILAYER COMPOSITE prepared by composition described in claim 1
Make hole stone slab, it is characterised in that described artificial hole stone slab includes surface layer, middle enhancement Layer and bottom:
Described middle enhancement Layer is alkaline-resisting grid cloth, between described surface layer and bottom；
Described surface layer is prepared by described surface layer composition, the color top layer prepared including described surface layer mill base and described
Surface layer basic unit prepared by surface layer slurry, described surface layer basic unit at least partly contains described with color top layer contact portion
The hole that amphoteric metal and described surface layer mill base, surface layer slurry reaction are formed.
Third aspect present invention provides the artificial hole stone slab of MULTILAYER COMPOSITE described in a kind of second aspect theme
Preparation method, described preparation method includes:
Step 1: prepare mould, and injector surface is standby；
Step 2: according to component and the weight thereof of surface layer mill base, surface layer slurry and base pastes described in first aspect
Proportioning preparation surface layer mill base, surface layer slurry and base pastes；
Step 3: described surface layer mill base is coated on described die surface；
Step 4: amphoteric metal is spread on described surface layer mill base；
Step 5: described surface layer slurry is poured to described mould；
Step 6: alkaline-resisting grid cloth is laid on described surface layer slurry；
Step 7: described base pastes is cast on described alkaline-resisting grid cloth；
Step 8: under 10-100 DEG C of temperature conditions after maintenance at least 10 hours, processes through the demoulding and surface,
I.e. obtain the artificial hole stone slab of MULTILAYER COMPOSITE.
The artificial hole stone slab of MULTILAYER COMPOSITE provided with the present invention below and combinations thereof thing and preparation method thereof is
Example, is described in detail the technical scheme of described artificial hole stone slab and combinations thereof thing and preparation method thereof,
Preferably to explain the present invention.
Embodiment 1
One, the component of surface layer mill base, surface layer slurry and base pastes and weight proportion thereof
(1) component and the weight proportion thereof of surface layer mill base includes:
Portland cement 95 parts；
Pigment lemon yellow 5 parts.
(2) component and the weight proportion thereof of surface layer slurry includes:
(3) component and the weight proportion thereof of base pastes includes:
Two, the preparation method of the artificial hole stone slab of MULTILAYER COMPOSITE
Step 1: prepare mould, and injector surface is standby；
Step 2: Binder Materials, pigment, aggregate, mineral admixture, each component of polymeric additive are pressed
Above-mentioned weight proportion is put in mixer after weighing, and mixes appropriate water, prepares surface layer mill base, surface layer slurry
Standby with base pastes；
Step 3: the surface layer mill base prepared is coated on described die surface；
Step 4: 20-40 mesh aluminium foil is spread on described surface layer mill base according to customer demand pattern；
Step 5: the surface layer slurry prepared is poured to described mould；
Step 6: the alkaline-resisting grid cloth cut in advance is laid on described surface layer slurry；
Step 7: the base pastes prepared is cast on described alkaline-resisting grid cloth；
Step 8: under 20-50 DEG C of temperature conditions after maintenance 12-24 hour, processes through the demoulding and surface,
I.e. obtain the artificial hole stone slab of MULTILAYER COMPOSITE.
Embodiment 2
One, the component of surface layer mill base, surface layer slurry and base pastes and weight proportion thereof
(1) component and the weight proportion thereof of surface layer mill base includes:
Portland cement 95 parts；
Pigment iron oxide red 4 parts；
Pigment iron oxide black 1 part.
(2) component and the weight proportion thereof of surface layer slurry includes:
(3) component and the weight proportion thereof of base pastes includes:
Two, the preparation method of the artificial hole stone slab of MULTILAYER COMPOSITE
Step 1: prepare mould, and injector surface is standby；
Step 2: Binder Materials, pigment, aggregate, mineral admixture, each component of polymeric additive are pressed
Above-mentioned weight proportion is put in mixer after weighing, and mixes appropriate water, prepares surface layer mill base, surface layer slurry
Standby with base pastes；
Step 3: the surface layer mill base prepared is coated on described die surface；
Step 4: 20-40 mesh aluminium foil is spread on described surface layer mill base according to customer demand pattern；
Step 5: the surface layer slurry prepared is poured to described mould；
Step 6: the alkaline-resisting grid cloth cut in advance is laid on described surface layer slurry；
Step 7: the base pastes prepared is cast on described alkaline-resisting grid cloth；
Step 8: under 20-50 DEG C of temperature conditions after maintenance 12-24 hour, processes through the demoulding and surface,
I.e. obtain the artificial hole stone slab of MULTILAYER COMPOSITE.
Embodiment 3
One, the component of surface layer mill base, surface layer slurry and base pastes and weight proportion thereof
(1) component and the weight proportion thereof of surface layer mill base 1 includes:
Portland cement 95 parts,
Pigment lemon yellow 5 parts；
Component and the weight proportion thereof of surface layer mill base 2 include:
Portland cement 95 parts,
Orange 5 parts of pigment.
(2) component and the weight proportion thereof of surface layer slurry includes:
(3) component and the weight proportion thereof of base pastes includes:
Two, the preparation method of the artificial hole stone slab of MULTILAYER COMPOSITE
Step 1: prepare mould, and injector surface is standby；
Step 2: Binder Materials, pigment, aggregate, mineral admixture, each component of polymeric additive are pressed
Above-mentioned weight proportion is put in mixer after weighing, and mixes appropriate water, preparation surface layer mill base 1 and surface layer look
Slurry 2, surface layer slurry and base pastes are standby；
Step 3: the surface layer mill base 1 prepared and surface layer mill base 2 are coated on described mould according to particular texture
Surface；
Step 4: 30～60 mesh aluminium foils are spread on described surface layer mill base according to customer demand pattern；
Step 5: the surface layer slurry prepared is poured to described mould；
Step 6: the alkaline-resisting grid cloth cut in advance is laid on described surface layer slurry；
Step 7: the base pastes prepared is cast on described alkaline-resisting grid cloth；
Step 8: under 20-50 DEG C of temperature conditions after maintenance 12-24 hour, processes through the demoulding and surface,
I.e. obtain the artificial hole stone slab of MULTILAYER COMPOSITE.
Artificial hole stone prepared by above-mentioned 3 embodiments, compared with the conventional method, has method uniqueness, produces spirit
Alive, with low cost, simple to operate, the feature of good decorating effect, is the external wall decorative material of a kind of higher gears.
Being described in detail the specific embodiment of the present invention above, but it is intended only as example, the present invention is also
It is not restricted to particular embodiments described above.To those skilled in the art, any the present invention is carried out
Equivalent modifications and substitute the most all among scope of the invention.Therefore, without departing from the spirit of the present invention and model
Enclose lower made impartial conversion and amendment, all should contain within the scope of the invention.
Claims (7)
1. the artificial hole stone slab composition of a MULTILAYER COMPOSITE, it is characterised in that described artificial hole stone slab
Composition includes surface layer composition, middle enhancement Layer and base pastes:
Described middle enhancement Layer is alkaline-resisting grid cloth；
Described surface layer composition includes surface layer mill base, amphoteric metal and surface layer slurry；
Wherein, component and the weight proportion thereof of described surface layer mill base includes:
Binder Materials 90-95 part,
Pigment 4-10 part；
Wherein, component and the weight proportion thereof of described surface layer slurry includes:
Wherein, component and the weight proportion thereof of described base pastes includes:
Described amphoteric metal includes any one or a few in aluminium foil, aluminium bits, aluminium wire；
Described Binder Materials includes in portland cement, aluminate cement, sulphate aluminium cement, lime, gypsum
Any one or a few；
Described mineral admixture include in flyash, breeze, stone flour, volcanic ash, silica flour any one or
Several.
The most artificial hole stone slab composition of MULTILAYER COMPOSITE, it is characterised in that described bone
Material includes any one or a few in natural colour sand, artificial color sand, river sand.
The most artificial hole stone slab composition of MULTILAYER COMPOSITE, it is characterised in that described bone
Material is 20-120 mesh.
4. the artificial hole stone slab of the MULTILAYER COMPOSITE prepared by composition described in claim 1, it is characterised in that
Described artificial hole stone slab includes surface layer, middle enhancement Layer and bottom:
Described middle enhancement Layer is alkaline-resisting grid cloth, between described surface layer and bottom；
Described surface layer is prepared by described surface layer composition, the color top layer prepared including described surface layer mill base and described
Surface layer basic unit prepared by surface layer slurry, described surface layer basic unit at least partly contains described with color top layer contact portion
The hole that amphoteric metal and described surface layer mill base, surface layer slurry reaction are formed.
5. the preparation method of the artificial hole stone slab of MULTILAYER COMPOSITE described in a claim 4, it is characterised in that institute
State preparation method to include:
Step 1: prepare mould, and injector surface is standby；
Step 2: according to claim 1 surface layer mill base, surface layer slurry and base pastes component and weight
Amount proportioning preparation surface layer mill base, surface layer slurry and base pastes；
Step 3: described surface layer mill base is coated on described die surface；
Step 4: amphoteric metal is spread on described surface layer mill base；
Step 5: described surface layer slurry is poured to described mould；
Step 6: alkaline-resisting grid cloth is laid on described surface layer slurry；
Step 7: described base pastes is cast on described alkaline-resisting grid cloth；
Step 8: under 10-100 DEG C of temperature conditions after maintenance at least 10 hours, processes through the demoulding and surface,
I.e. obtain the artificial hole stone slab of MULTILAYER COMPOSITE.
The preparation method of the artificial hole stone slab of MULTILAYER COMPOSITE the most according to claim 5, it is characterised in that institute
Stating in step 8, described temperature is 20-50 DEG C, and described curing time is 12-24 hour.
The preparation method of the artificial hole stone slab of MULTILAYER COMPOSITE the most according to claim 5, it is characterised in that institute
Stating in step 8, the process of described surface includes any one or a few in polishing, polishing, ball blast.