CN107459302A - Artificial stone slurry and its curing molding do not expect artificial stone undisguisedly - Google Patents

Artificial stone slurry and its curing molding do not expect artificial stone undisguisedly Download PDF

Info

Publication number
CN107459302A
CN107459302A CN201710560574.8A CN201710560574A CN107459302A CN 107459302 A CN107459302 A CN 107459302A CN 201710560574 A CN201710560574 A CN 201710560574A CN 107459302 A CN107459302 A CN 107459302A
Authority
CN
China
Prior art keywords
artificial stone
parts
raw
stone slurry
slurry
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201710560574.8A
Other languages
Chinese (zh)
Inventor
刘辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhuo Hun New Material Technology (shanghai) Co Ltd
Original Assignee
Zhuo Hun New Material Technology (shanghai) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhuo Hun New Material Technology (shanghai) Co Ltd filed Critical Zhuo Hun New Material Technology (shanghai) Co Ltd
Priority to CN201710560574.8A priority Critical patent/CN107459302A/en
Publication of CN107459302A publication Critical patent/CN107459302A/en
Withdrawn legal-status Critical Current

Abstract

Artificial stone is not expected undisguisedly the invention discloses a kind of artificial stone slurry and its curing molding, and the artificial stone slurry includes raw material and accounts for the water of the raw material weight 16~18%;The raw material includes 100 parts of cement, color sand includes 58~62 parts of the yellow fraction silica sand of 60 mesh and 58~62 parts of wherein described parts of yellow fraction silica sand of 70 mesh are parts by weight.Do not expect that artificial stone is mixed colours with pigment powder, has similar marmorean color and texture undisguisedly as described in artificial stone slurry curing shaping;Compact structure, there is higher intensity, construction timber can be used as, and preparation method is easy, the cheap environmental protection of the prices of raw materials.

Description

Artificial stone slurry and its curing molding do not expect artificial stone undisguisedly
Technical field
The invention belongs to artificial stone technical field, and in particular to a kind of artificial stone slurry and its curing molding are not expected undisguisedly Artificial stone.
Background technology
With the development of modem architectural ornament industry, requirement of the people for environmental decoration is also more extensive therewith.And The predation of many precious produce by the exploitation of madness and without restraint, substantial amounts of non-renewable material are faced with exhaustion and disappeared on the earth Lose.And the birth of the colored artificial stone as recyclable materials, it is the product that the beautification of this environment of times tends to.Especially by In the product color is abundant, various shapes, durable in use, processing is simple, cheap, while but also with energy-saving and environment friendly Characteristic, therefore the present age can be met for building decoration, the high standard and height of the various unlike material effects of landscaping completely It is required that.
The content of the invention
Artificial stone is not expected undisguisedly it is an object of the invention to provide a kind of artificial stone slurry and its curing molding so that should Not expecting artificial stone undisguisedly has similar marble color and a texture, and its bending resistance, resistance to compression equal strength standard are higher.
Therefore, the invention provides a kind of artificial stone slurry, including:Raw material and account for the raw material weight 16~18% Water;The raw material includes 100 parts of cement, 58~62 parts of the yellow fraction silica sand of 60 mesh, 58~62 parts of yellow fraction silica sand, the epoxy glue of 70 mesh 4~8 parts of 7 parts of water and the third breast.
The positive effect of the artificial stone slurry of the present invention is:The artificial stone slurry using cement and yellow fraction silica sand as Raw material, using mixture glue with after the third breast condensation by mixing, may be formed at color and there is similar marmorean effect on texture Artificial stone, as construction timber, its bending resistance, resistance to compression equal strength standard are higher.
As the preferred embodiment of the present invention, the raw material can also include additive, and the additive is selected from following One or more combinations in material group:(such as summer temperature is properly added when higher can delay admittedly for plasticiser, retarder Change), early strength agent (such as winter temperature is properly added when relatively low can accelerate to solidify), antifreezing agent it is (appropriate when such as winter temperature is relatively low Addition can be with anti-freezing anti-cracking) and brightener.
As the preferred embodiment of the present invention, the raw material can also include 0.06 part of water reducer and cellulose, wherein The ratio between the water reducer and cement are 4~5mL:1kg.The water reducer can improve early strength, and the water reducer can be selected poly- Carboxylate high efficiency water reducing agent, such as SiKa SNN water reducers.The dosage of water reducer and water adjusts according to weather, high temperature drying weather The dosage of the water reducer can be suitably reduced, on the contrary but appropriate increase dosage.It is fine that hydroxypropyl methyl can be selected in the cellulose Dimension element, to improve product bulk strength.
As the preferred embodiment of the present invention, the raw material can also include 2 parts of antimitotic agent.
As the preferred embodiment of the present invention, the raw material can also include 2.91~2.93 parts of pigment powder, the face Feed powder includes 2.59~2.61 parts of titanium dioxide, 0.23~0.25 part of iron oxide yellow powder, 0.03~0.05 part of iron oxide red and iron black powder 0.03 ~0.05 part.Wherein, the titanium dioxide is preferably 2.60 parts, and the iron oxide yellow powder is preferably 0.24 part, and the iron oxide red is preferably 0.04 part, the black powder of patch is preferably 0.04 part.
As the preferred embodiment of the present invention, the yellow fraction silica sand 58-62 part and 70 purposes of the color sand composition for 60 mesh Yellow fraction silica sand 58-62 parts, described mesh are the screen size of material sieving.Wherein, the yellow fraction silica sand of 60 mesh is preferably 60 parts, institute The yellow fraction silica sand for stating 70 mesh is preferably 60 parts.
As the preferred embodiment of the present invention, the mixture glue is that mass ratio is 2:1 801 building adhesives and white glue with vinyl Mixture, the white glue with vinyl is venamul.
As the preferred embodiment of the present invention, the cement is white portland cement, such as A Erbo Portland boards White portland cement, whiteness height is characterized in without influenceing component strength, while can prepare any color to reach various The texture effect of material.Third breast goes through emulsion of rubbing for ROHM AND HAAS hundred.
Artificial stone is not expected undisguisedly using the shaping of above-mentioned artificial stone slurry curing present invention also offers a kind of.
It is described not expect undisguisedly artificial stone by the artificial stone slurry with prefabricated mould as the preferred embodiment of the present invention Have curing molding, then through photochemical obtain of polishing.Described not expect that artificial stone is different undisguisedly, texture is excellent to be had similar to Dali Stone effect.
The raw material materials of the artificial stone of the present invention require simple, special natural resources are not required, relative to building decoration Other use material, have the advantages that not consume that nature former material, material construction are cheap, therefore advantageous product is popularized.Its It is secondary, because the manufacturing process of whole product uses material using energy saving and environment friendly, make product that there is good environment friendly and set Versatility is counted, therefore is a kind of artificial stone of energy-saving and environment friendly.
Embodiment
Embodiment 1 does not expect the making of artificial stone undisguisedly
The raw material proportioning of the artificial stone slurry of the present invention:
Table 1 does not expect the raw material and dosage of artificial stone slurry undisguisedly
Wherein, cement is A Erbo Portland board white portland cements, and mixture glue is weight than 2:1 801 buildings The mixture of glue and venamul, water reducer are SiKa SNN water reducers, and cellulose is hydroxypropyl methyl cellulose.
The concrete operation step of artificial stone processing is not expected undisguisedly:
Step 1: the preparation of slurry
1 adds other raw materials in table 1 in addition to water reducer in mixer, stirs 15~30 minutes;
2 are transferred to the raw material after stirring in dnockout bucket, add water reducer and 16% water of raw material gross weight, stirring 5~10 minutes obtained slurries.
Step 2: solidification
1 is put into slurry made from step 1 inside the mould being already prepared to;
2 are positioned over mould in shock platforms, starting shock platform, shake 3~5 minutes, ensure pulp surface it is smooth and Thickness is 3cm~5cm;
After the completion of 3 vibrations, mould is lifted into the smooth place in steam workshop, it is ensured that die layout is smooth, uses black thin film Slurry is covered comprehensively, opens steam, is steamed 12~24 hours, slurry is solidified into the product of predetermined kenel in a mold;
Product in mould is carried out demoulding processing by 4, is carried out first repairing treatment to the product after the completion of the demoulding, that is, is existed Repaired in 24h using slurry made from step 1, and take out the overlap and burr of product;The product repaired uses black again Covering continues steaming 5~7 days to film comprehensively, the product after being fully cured.
Step 3: polishing
The product that step 2 is fully cured is carried out photochemical place for the first time by 1 with the sander for the water mill piece for being provided with 1000 mesh Reason;
3, treat that product dries completely after photochemical processing for the first time, uniformly spray protective agent A agent.
3, carry out photochemical place for the second time with the sander for the water mill piece for being provided with 2000 mesh after spending 12 hours in protective agent A agent Reason.
4, treat that product dries after second of photochemical processing and clean surface with vinegar, prevent the anti-alkali of product;
Step 4: surface micronization processes
1 carries out second through the product that step 3 has been polished with step 1 slurry repairs, it is ensured that product surface pore-free, etc. Repair part is tied with grinding machine after repairing is dry, upper protection;
3 uniformly spray product surface brightener B agent, and wool head polishing machine polishing is used after brightener B agent is dried, Increase product surface finish, that is, product artificial stone is made.
Effect example
1st, unlimited plasticity
The artificial stone of the present invention is to stir raw material according to a certain ratio, and the pouring molding in mould, moulding is rich and varied, can With into the different shaping effect such as stripe shape, hollow out, embossment;It may be alternatively configured a variety of surface effects, including polishing, matt, fine grinding, fire Burn, water knife handles and sandblasted;Mixed colours with pigment powder, rich palette is various.
2nd, there is marbling effect
The artificial stone slurry of the present invention is used as base-material using white cement and yellow fraction silica sand, uniform stirring, by solidification polishing, Any surface finish pore-free, uniform hue, aberration are smaller, have similar marmorean effect.Also, compared to the decorations undisguisedly expected Face, concrete or artificial stone, artificial stone of the invention are neat and artistic with the facing do not expected undisguisedly, its appearance.
3rd, cost is low, environmentally friendly
The artificial stone category recyclable materials and cost of the present invention are relatively low, are advantageous to environmental protection;Raw material do not contain radioactive nucleus Element, it is national radionuclide amount A class environment-friendly materials.
4th, structural behaviour is good
It is as shown in table 2 the artificial stone parameters of the present invention, meets the standard requirement of building and ornament materials.
The artificial stone parameter of the present invention of table 2
To sum up, artificial stone of the invention is attained by similar marmorean effect, structure in color texture texture etc. Intensity is preferable, can be used as construction timber, and preparation method is easy, the cheap environmental protection of the prices of raw materials, especially for traditional people Stone is made, its bending resistance, tension equal strength standard are higher.
The present invention is not limited to above-mentioned specific embodiment, one of ordinary skill in the art from above-mentioned design, Without performing creative labour, a variety of conversion made, it is within the scope of the present invention.

Claims (8)

  1. A kind of 1. artificial stone slurry, it is characterised in that including:Raw material and the water for accounting for the raw material weight 16~18%;The original Material includes 100 parts of cement, 58~62 parts of the yellow fraction silica sand of 60 mesh, 58~62 parts of the yellow fraction silica sand of 70 mesh, 7 parts of mixture glue and third 4~8 parts of breast.
  2. 2. artificial stone slurry as claimed in claim 1, it is characterised in that the raw material also includes additive, the additive One or more combinations in following material group:Plasticiser, retarder, early strength agent, antifreezing agent and brightener.
  3. 3. artificial stone slurry as claimed in claim 1, it is characterised in that the raw material also includes water reducer and cellulose 0.06 Part, the ratio between the water reducer and the cement are 4~5mL:1kg.
  4. 4. artificial stone slurry as claimed in claim 1, it is characterised in that also including 2 parts of antimitotic agent.
  5. 5. artificial stone slurry as claimed in claim 1, it is characterised in that the raw material also includes pigment powder 2.88~2.96 Part, the pigment powder includes 2.59~2.61 parts of titanium dioxide, 0.23~0.25 part of iron oxide yellow powder, 0.03~0.05 part of iron oxide red and iron Black 0.03~0.05 part of powder.
  6. 6. artificial stone slurry as claimed in claim 1, it is characterised in that the mixture glue is that mass ratio is 2:The 801 of 1 are built Glue and the mixture of white glue with vinyl are built, the white glue with vinyl is venamul.
  7. 7. artificial stone slurry as claimed in claim 1, it is characterised in that the cement is white portland cement;Described third Breast goes through emulsion of rubbing for ROHM AND HAAS hundred.
  8. What 8. a kind of artificial stone slurry curing as described in any one of claim 1~7 was molded does not expect artificial stone undisguisedly.
CN201710560574.8A 2017-07-11 2017-07-11 Artificial stone slurry and its curing molding do not expect artificial stone undisguisedly Withdrawn CN107459302A (en)