CN107129193A - A kind of OK a karaoke club card tower textured man-made stone diamond stone sheet material and its production technology - Google Patents
A kind of OK a karaoke club card tower textured man-made stone diamond stone sheet material and its production technology Download PDFInfo
- Publication number
- CN107129193A CN107129193A CN201710358235.1A CN201710358235A CN107129193A CN 107129193 A CN107129193 A CN 107129193A CN 201710358235 A CN201710358235 A CN 201710358235A CN 107129193 A CN107129193 A CN 107129193A
- Authority
- CN
- China
- Prior art keywords
- colors
- karaoke club
- club card
- card tower
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of OK a karaoke club card tower textured man-made stone diamond stone sheet material of the present invention and its production technology, including major ingredient A colors, decorative pattern material B colors, inserts C colors, spray pattern material D colors；The raw material of major ingredient A colors includes 0.075~1mm particulate materials, 0.005~0.045mm silica flours；Colored pigment；Silane coupler；Unsaturated polyester resin；Curing agent；The component and proportioning of decorative pattern material B colors be：Inorganic pigment；Or organic pigment, 0.045~0.212mm silica flours；The raw material of inserts C colors includes 0.005~0.045mm silica flours；Colored pigment；Silane coupler；Unsaturated polyester resin；Curing agent；The component and proportioning of spray pattern material D colors be：Inorganic pigment；Or organic pigment, silane coupler；Unsaturated polyester resin and curing agent；Its is handsome in appearance, and pattern is distinct, and color is unique, and decorative pattern forms uniqueness；The decorative pattern of arbitrariness can be made by mould of different shapes；By producing dislocation combination, production efficiency is high, effectively reduces the fraction defective of product, can mass production.
Description
Technical field
The invention belongs to quartz technical field, specifically, it is related to a kind of OK a karaoke club card tower textured man-made stone diamond stone sheet material
And its production technology.
Background technology
In building decoration field, stone material with its it is attractive in appearance, graceful, ornamental strong the features such as turned into primary decoration material it
One.All the time, natural marble figue it is abundant, naturally, because its natural decorative effect, texture and by extensive use, but
Due to there is resource-constrained, there is aberration in large area paving and different degrees of radioactivity is exceeded, and hardness is low, and easy scratching etc. is asked
Topic, limits its comprehensive development to a certain extent.
Artificial quartz in lump be by quartz sand powder be main stuffing, using unsaturated polyester resin as adhesive, in vacuum shape
The Novel stone that high pressure is compressing under condition, shape under middle temperature state, it is a kind of "dead" pollution, the repeatable ring utilized
Guarantor, green building material and ornament materials.
Although artificial quartz in lump rich color is gorgeous, radiationless, wear-resisting, pressure-resistant, anti scuffing, anticorrosive, anti-aging, antiseepage
Thoroughly, but be due to without marmorean native texture and color, artificial quartz in lump class is cannot get big raising.It is domestic at present
The outer diamond plate for having imitating natural marble, but color is relatively stiff, and texture is unnatural.Meanwhile, pattern type artificial quartz in lump
Due to complex process, low production efficiency, and sheet material, the color in pressing process is easily interpenetrated sheet material, and fraction defective is high, from
And causing the supply of material few, price is high.
Particularly use demand of the recent domestic to natural OK a karaoke club Ka Ta so that originally natural OK a karaoke club card tower resource
It is more nervous；Pass through the natural OK a karaoke club Ka Ta of analog simulation skin pattern, it is possible to achieve more more rich than natural OK a karaoke club card tower color,
Flower pattern is fuller, and can realize the personalized customization of flower pattern, can meet a variety of market demands such as commercial family expenses.
Therefore, it is necessary to carry out upgrading or technological transformation to existing production technology.
The content of the invention
Instant invention overcomes shortcoming of the prior art, there is provided a kind of OK a karaoke club Ka Ta with natural marble stone material texture
Textured man-made stone diamond stone sheet material and its production technology, good product performance, production efficiency are high, and qualification rate is high.
In order to solve the above-mentioned technical problem, the present invention is achieved by the following technical solutions：
A kind of OK a karaoke club card tower textured man-made stone diamond stone sheet material, including major ingredient A colors, decorative pattern material B colors, inserts C colors, spray pattern material
D colors；
The raw material of the major ingredient A colors includes 0.075~1mm particulate materials, 0.005~0.045mm silica flours, coloured face
Material, silane coupler, unsaturated polyester resin and curing agent；
The component of the decorative pattern material B colors is：Inorganic pigment；Or inorganic pigment, 0.045~0.212mm silica flours；
The raw material of the inserts C colors includes 0.005~0.045mm silica flours, colored pigment, silane coupler, insatiable hunger
With polyester resin and curing agent；
The component of the spray pattern material D colors is：Inorganic pigment；Or inorganic pigment, silane coupler, unsaturated polyester resin and
Curing agent.
Further, the major ingredient A colors are 85~95 parts of total material, and decorative pattern material B colors are 1~2 part of total material；Inserts C colors
3-11 parts；1-2 parts of spray pattern material D colors.
Further, the major ingredient A colors include according to percentage by weight：0.075~1mm particulate materials 55%~65%；
0.005~0.045mm silica flours 20%~30%；Colored pigment 0.01%~3%；Silane coupler 0.1%~1%；Insatiable hunger
With polyester resin 8%~14%；Curing agent 0.8%~1.4%.
Further, according to percentage by weight, the component and proportioning of the decorative pattern material B colors are：Inorganic pigment 100%；Or nothing
Machine pigment 1%~30%, 0.045~0.212mm silica flours 70%~99%.
Further, according to percentage by weight, the component and proportioning of the decorative pattern material C colors are：0.005~0.045mm quartz
Powder 75%~90%, colored pigment 0.01%~3%, silane coupler 0.1%~1%, unsaturated polyester resin 8%~14%
With curing agent 0.8%~1.4%.
Further, according to percentage by weight, the component and proportioning of the decorative pattern material D colors are：Inorganic pigment 100%；Or nothing
Machine pigment 1%~30%, 0.045~0.212mm silica flours 70%~99%；Or colored pigment 0.01%~3%, silane are even
Join agent 0.1%~1%, unsaturated polyester resin 94.6%~99.09% and curing agent 0.8%~1.4%.
Further, during the unsaturated polyester resin is epoxy resin, phenolic resin, acrylic resin and polyurethane resin
One or more；The colored pigment is the one or more of inorganic pigment or organic pigment or mill base；The curing agent is
Peroxidating (2 ethyl hexanoic acid) tert-butyl ester, methyl ethyl ketone peroxide, peroxidized t-butyl perbenzoate, dibenzoyl peroxide and fat
One or more in polyamine.
Further, the inorganic pigment be titanium white, medium chrome yellow, iron oxide yellow, iron oxide red, barba hispanica, cadmium red, cadmium yellow, carbon black or iron oxide black,
The organic pigment is pigment scarlet powder, azophosphine, dark green or phthalocyanine blue, and the mill base is white slurry, black wash, bright red slurry, dark green
Slurry or phthalocyanine blue slurry.
Further, the silane coupler is γ-methacryloxypropyl trimethoxy silane, γ-(2,3- epoxies
Third oxygen) propyl trimethoxy silicane, N- β (aminoethyl)-γ-aminopropyltriethoxy dimethoxysilane, N- (β-aminoethyl)-γ-
Aminopropyl triethoxysilane, N- β (aminoethyl)-γ-aminopropyltrimethoxysilane, anilinomethyl triethoxysilane, γ-
Aminopropyl triethoxysilane, VTES, vinyltrimethoxy silane and γ-chloropropyl triethoxy silicon
One or more in alkane.
A kind of production technology of OK a karaoke club card tower textured man-made stone diamond stone sheet material, comprises the following steps：
(1) each material is weighed according to formula；
(2) stir：1. particulate material, the silane coupler of major ingredient A colors step (1) weighed are stirred in double planetary
It is pre-mixed in bucket；The curing agent mixed, colored pigment and unsaturated polyester resin are poured into double planetary agitator to enter
Row mixing, then adds 0.005~0.045mm silica flours and is mixed, 15~55Hz of stirring frequency, and mixing time 180~
600s；
2. decorative pattern material B colorants rub material by manually sieving uniformly；
3. inserts C colorants are stirred：Silane coupler, curing agent, colored pigment and the unsaturation that step (1) is weighed
Polyester resin is poured into be mixed in double planetary agitator, is then added 0.005~0.045mm silica flours and is mixed, is stirred
Mix 15~55Hz of frequency, 180~600s of mixing time；
4. spray pattern material D colorants are stirred：1. the material that step (1) is weighed is pre-mixed standby in powder beater agitator；
2. the material resin weighed, silane coupler, color, curing agent are scattered in homogenizer agitator high speed；Stirring frequency
15~55Hz of rate, 60~240s of mixing time；
(3) distributing mode and texture operation technique：
1. first ready OK a karaoke club card tower mould in advance is put into charge car；
2. major ingredient A colors are filled full whole charge car by artificial cloth again, OK a karaoke club card tower mould is flooded；
3. starting the preformer material good to cloth carries out precompressed；
Separated 4. an OK a karaoke club card tower mould lifts with major ingredient A colors；
5. ready spray pattern D colors, the requirement of OK a karaoke club card tower drawings marked is compareed to OK a karaoke club card by dry powder spray gun in advance
Tower mould carries out dry powder spray pattern；Or ready spray pattern D colors in advance, OK a karaoke club card tower drawings marked is compareed by liquid spray gun
It is required that carrying out slurry spray pattern to OK a karaoke club card tower mould；
6. an inserts C color being stirred in advance is placed on above ground quartz plate；
7. first layer completes filling C material, decorative pattern material B colors are sieved above inserts C colors completing；It is being sieved decorative pattern material again
Inserts C colors are spread above the material of B colors；Sieve upper decorative pattern material B colors again again；Inserts C colors are finally then covered with, pass through multiple-layer stacked
Form folder line texture；
8. the shape that ready folder line texture is pressed into cuboid by preformer is stand-by；
9. it is long according to the folder line texture that the sheet material of different-thickness is cut into the folder line texture pressed in advance by thickness guiding ruler
Cube is standby；
10. the OK a karaoke club Ka Ta to pressing and foring OK a karaoke club card tower pattern in advance is required according to OK a karaoke club card tower drawing standard
Mould white space is filled with folder line texture cuboid；
11. according to the difference of pattern, filling thickness, length, shape can be adjusted, all clear areas are filled up successively
The good material of cloth is simultaneously paved in domain；
(4) suppress：After cloth is completed, repressed vibration equipment is compressing under -0.1Mpa vacuum condition, pressure
50~200t, 30~55Hz of vibration frequency, 60~600s of time；
(5) heat cure：After vibration compacting, into curing apparatus, solidify at a temperature of 80~130 DEG C, hardening time
For 30~180 minutes；
(6) after the completion of solidifying, room temperature it is to be cooled completely after enter the fixed thickness of sheet material thicknessing machine, then set by water mill polishing
It is standby to be polished.
Compared with prior art, the beneficial effects of the invention are as follows：
A kind of OK a karaoke club card tower textured man-made stone diamond stone sheet material of the present invention and its production technology, the artificial stone made
Diamond stone is handsome in appearance, and pattern is distinct, and color is unique, and the species and flower of artificial quartz in lump are enriched similar to a kind of fish maw shape decorative pattern
Sample, enriches the species and style of artificial quartz in lump.The decorative pattern of arbitrariness can be made by mould of different shapes；Pass through
Production dislocation combination, production efficiency is high, effectively reduces the fraction defective of product, can mass production.
Embodiment
The preferred embodiments of the present invention are illustrated below, it will be appreciated that preferred embodiment described herein is only used
In the description and interpretation present invention, it is not intended to limit the present invention.
A kind of OK a karaoke club card tower textured man-made stone diamond stone sheet material, including major ingredient A colors, decorative pattern material B colors, inserts C colors, spray pattern material
D colors；
Major ingredient A colors include according to percentage by weight：0.075~1mm particulate materials 62%；0.005~0.045mm silica flours
24%；Colored pigment 2.4%；Silane coupler 0.6%；Unsaturated polyester resin 10%；Curing agent 1%.
According to percentage by weight, the component and proportioning of decorative pattern material B colors are：Inorganic pigment 20%, 0.045~0.212mm stones
English powder 80%.
According to percentage by weight, the component and proportioning of decorative pattern material C colors are：0.005~0.045mm silica flours 85%；It is coloured
Pigment 2.5%；Silane coupler 0.5%；Unsaturated polyester resin 11%；Curing agent 1%.
According to percentage by weight, the component and proportioning of decorative pattern material D colors are：Inorganic pigment 15%, 0.045~0.212mm stones
English powder 85%；Or colored pigment 2%, silane coupler 0.5%, unsaturated polyester resin 96.5% and curing agent 1%；
Unsaturated polyester resin can also be one in epoxy resin, phenolic resin, acrylic resin and polyurethane resin
Plant or a variety of.
Colored pigment is inorganic pigment, and inorganic pigment is titanium white, and curing agent is peroxidating (2 ethyl hexanoic acid) tert-butyl ester.
Silane coupler is γ-methacryloxypropyl trimethoxy silane and γ-(2,3- the third oxygen of epoxy) propyl group
The mixture of trimethoxy silane.
A kind of production technology of OK a karaoke club card tower textured man-made stone diamond stone sheet material, comprises the following steps：
(1) each material is weighed according to formula；
(2) stir：1. particulate material, the silane coupler of major ingredient A colors step (1) weighed are stirred in double planetary
It is pre-mixed in bucket；The curing agent mixed, colored pigment and unsaturated polyester resin are poured into double planetary agitator to enter
Row mixing, then adds 0.005~0.045mm silica flours and is mixed, 15~55Hz of stirring frequency, and mixing time 180~
600s；
2. decorative pattern material B colorants rub material by manually sieving uniformly；
3. inserts C colorants are stirred：Silane coupler, curing agent, colored pigment and the unsaturation that step (1) is weighed
Polyester resin is poured into be mixed in double planetary agitator, is then added 0.005~0.045mm silica flours and is mixed, is stirred
Mix 15~55Hz of frequency, 180~600s of mixing time；
4. spray pattern material D colorants are stirred：1. the material that step (1) is weighed is pre-mixed standby in powder beater agitator；
2. the material resin weighed, silane coupler, color, curing agent are scattered in homogenizer agitator high speed；Stirring frequency
15~55Hz of rate, 60~240s of mixing time；
(3) distributing mode and texture operation technique 1：First ready OK a karaoke club card tower mould in advance is put into charge car；
2. major ingredient A colors are filled full whole charge car by artificial cloth again, 3. flood OK a karaoke club card tower mould, and 4. start preformer to cloth
Good material carries out precompressed, and 5. again by lifting charge car, and 6. lift OK a karaoke club card tower mould and separated with major ingredient A colors；7. in advance
Ready spray pattern D colors, compare the requirement of OK a karaoke club card tower drawings marked by dry powder spray gun and carry out dry powder spray to OK a karaoke club card tower mould
Line；8. an inserts C color being stirred in advance is placed on above ground quartz plate, each layer of preparation 5-10kg inserts C colors；9.
First layer completes filling C material, and decorative pattern material B colors are sieved above inserts C colors completing；It is being sieved again on the material of decorative pattern material B colors
Spread inserts C colors in face；Sieve upper decorative pattern material B colors again again；Inserts C colors are finally then covered with, pass through multiple-layer stacked formation folder line
Texture；10. the shape that ready folder line texture is pressed into 1000*500*5-20mm by preformer is stand-by；11. according to difference
The cuboid that the folder line texture pressed in advance is cut into 200*30*5-20mm by the sheet material of thickness by thickness guiding ruler is standby；12. piece
It is long with folder line texture to the white space for pressing and foring OK a karaoke club card tower pattern in advance according to the requirement of OK a karaoke club card tower drawing standard
Cube material is filled；13. according to the difference of pattern, filling thickness, length, shape can be adjusted, fill up successively all
White space and the good material of cloth is paved；
(4) suppress：After cloth is completed, repressed vibration equipment is compressing under -0.1Mpa vacuum condition, pressure
50~200t, 30~55Hz of vibration frequency, 60~600s of time；
(5) heat cure：After vibration compacting, into curing apparatus, solidify at a temperature of 80~130 DEG C, hardening time
For 30~180 minutes；
(6) after the completion of solidifying, room temperature it is to be cooled completely after enter the fixed thickness of sheet material thicknessing machine, then set by water mill polishing
It is standby to be polished.
Finally it should be noted that：The preferred embodiments of the present invention are these are only, are not intended to limit the invention, although
The present invention is described in detail with reference to embodiment, for those skilled in the art, it still can be to foregoing
Technical scheme described in each embodiment is modified, or to which part technical characteristic carry out equivalent substitution, but it is all
Within the spirit and principles in the present invention, any modification, equivalent substitution and improvements made etc. should be included in the protection of the present invention
Within the scope of.
Claims (10)
1. a kind of OK a karaoke club card tower textured man-made stone diamond stone sheet material, it is characterised in that：Including major ingredient A colors, decorative pattern material B colors, inserts C
Color, spray pattern material D colors；
The raw material of the major ingredient A colors includes 0.075~1mm particulate materials, 0.005~0.045mm silica flours, colored pigment, silicon
Alkane coupling agent, unsaturated polyester resin and curing agent；
The component of the decorative pattern material B colors is：Inorganic pigment；Or inorganic pigment, 0.045~0.212mm silica flours；
It is poly- that the raw material of the inserts C colors includes 0.005~0.045mm silica flours, colored pigment, silane coupler, unsaturation
Ester resin and curing agent；
The component of the spray pattern material D colors is：Inorganic pigment；Or inorganic pigment, silane coupler, unsaturated polyester resin and solidification
Agent.
2. a kind of OK a karaoke club card tower textured man-made stone diamond stone sheet material according to claim 1, it is characterised in that：The major ingredient A colors
For 85~95 parts of total material, decorative pattern material B colors are 1~2 part of total material；3-11 parts of inserts C colors；1-2 parts of spray pattern material D colors.
3. a kind of OK a karaoke club card tower textured man-made stone diamond stone sheet material according to claim 1, it is characterised in that：The major ingredient A colors
Include according to percentage by weight：0.075~1mm particulate materials 55%~65%；0.005~0.045mm silica flours 20%~
30%；Colored pigment 0.01%~3%；Silane coupler 0.1%~1%；Unsaturated polyester resin 8%~14%；Curing agent
0.8%~1.4%.
4. a kind of OK a karaoke club card tower textured man-made stone diamond stone sheet material according to claim 1, it is characterised in that：According to weight percent
Than the component and proportioning of the decorative pattern material B colors are：Inorganic pigment 100%；Or inorganic pigment 1%~30%, 0.045~
0.212mm silica flours 70%~99%.
5. a kind of OK a karaoke club card tower textured man-made stone diamond stone sheet material according to claim 1, it is characterised in that：According to weight percent
Than the component and proportioning of the decorative pattern material C colors are：0.005~0.045mm silica flours 75%~90%；Colored pigment 0.01%
~3%；Silane coupler 0.1%~1%；Unsaturated polyester resin 8%~14%；Curing agent 0.8%~1.4%.
6. a kind of OK a karaoke club card tower textured man-made stone diamond stone sheet material according to claim 1, it is characterised in that：According to weight percent
Than the component and proportioning of the decorative pattern material D colors are：Inorganic pigment 100%；Or inorganic pigment 1%~30%, 0.045~
0.212mm silica flours 70%~99%；Or colored pigment 0.01%~3%, silane coupler 0.1%~1%, unsaturation are poly-
Ester resin 94.6%~99.09% and curing agent 0.8%~1.4%.
7. a kind of OK a karaoke club card tower textured man-made stone diamond stone sheet material according to claim 1, it is characterised in that：It is described unsaturated poly-
Ester resin is the one or more in epoxy resin, phenolic resin, acrylic resin and polyurethane resin；The colored pigment is
The one or more of inorganic pigment or organic pigment or mill base；The curing agent is peroxidating (2 ethyl hexanoic acid) tert-butyl ester, mistake
One or more in MEKP, peroxidized t-butyl perbenzoate, dibenzoyl peroxide and fat polyamine.
8. a kind of OK a karaoke club card tower textured man-made stone diamond stone sheet material according to claim 7, it is characterised in that：The inorganic pigment
For titanium white, medium chrome yellow, iron oxide yellow, iron oxide red, barba hispanica, cadmium red, cadmium yellow, carbon black or iron oxide black, the organic pigment is pigment scarlet powder, azo
Yellow, dark green or phthalocyanine blue, the mill base are white slurry, black wash, bright red slurry, dark green slurry or phthalocyanine blue slurry.
9. a kind of OK a karaoke club card tower textured man-made stone diamond stone sheet material according to claim 1, it is characterised in that：It is described silane coupled
Agent is γ-methacryloxypropyl trimethoxy silane, γ-(2,3- the third oxygen of epoxy) propyl trimethoxy silicane, N- β
(aminoethyl)-γ-aminopropyltriethoxy dimethoxysilane, N- (β-aminoethyl)-gamma-aminopropyl-triethoxy-silane, N- β (ammonia
Ethyl)-γ-aminopropyltrimethoxysilane, anilinomethyl triethoxysilane, gamma-aminopropyl-triethoxy-silane, vinyl
One or more in triethoxysilane, vinyltrimethoxy silane and γ-chloropropyl triethoxysilane.
10. a kind of production technology of OK a karaoke club card tower textured man-made stone diamond stone sheet material, it is characterised in that：Comprise the following steps：
(1) each material is weighed according to formula；
(2) stir：1. the particulate materials of major ingredient A colors step (1) weighed, silane coupler are in double planetary agitator
Premixing；The curing agent mixed, colored pigment and unsaturated polyester resin are poured into and mixed in double planetary agitator
Close, then add 0.005~0.045mm silica flours and mixed, 15~55Hz of stirring frequency, 180~600s of mixing time；
2. decorative pattern material B colorants rub material by manually sieving uniformly；
3. inserts C colorants are stirred：Silane coupler, curing agent, colored pigment and the unsaturated polyester (UP) that step (1) is weighed
Resin is poured into be mixed in double planetary agitator, is then added 0.005~0.045mm silica flours and is mixed, stirring frequency
15~55Hz of rate, 180~600s of mixing time；
4. spray pattern material D colorants are stirred：1. the material that step (1) is weighed is pre-mixed standby in powder beater agitator；2. institute
The material resin that weighs, silane coupler, color, curing agent are scattered in homogenizer agitator high speed；Stirring frequency 15
~55Hz, 60~240s of mixing time；
(3) distributing mode and texture operation technique：
1. first ready OK a karaoke club card tower mould in advance is put into charge car；
2. major ingredient A colors are filled full whole charge car by artificial cloth again, OK a karaoke club card tower mould is flooded；
3. starting the preformer material good to cloth carries out precompressed；
Separated 4. an OK a karaoke club card tower mould lifts with major ingredient A colors；
5. ready spray pattern D colors, the requirement of OK a karaoke club card tower drawings marked is compareed to OK a karaoke club Ka Tamo by dry powder spray gun in advance
Tool carries out dry powder spray pattern；Or ready spray pattern D colors in advance, the requirement of OK a karaoke club card tower drawings marked is compareed by liquid spray gun
Slurry spray pattern is carried out to OK a karaoke club card tower mould；
6. an inserts C color being stirred in advance is placed on above ground quartz plate；
7. first layer completes filling C material, decorative pattern material B colors are sieved above inserts C colors completing；It is being sieved decorative pattern material B colors again
Material above spread inserts C colors；Sieve upper decorative pattern material B colors again again；Inserts C colors are finally then covered with, pass through multiple-layer stacked shape
Into folder line texture；
8. the shape that ready folder line texture is pressed into cuboid by preformer is stand-by；
9. the folder line texture cuboid that the folder line texture pressed in advance is cut into by thickness guiding ruler according to the sheet material of different-thickness
It is standby；
10. the OK a karaoke club card tower mould to pressing and foring OK a karaoke club card tower pattern in advance is required according to OK a karaoke club card tower drawing standard
White space is filled with folder line texture cuboid；
11. according to the difference of pattern, filling thickness, length, shape can be adjusted, all white spaces are filled up successively simultaneously
The good material of cloth is paved；
(4) suppress：After cloth is completed, repressed vibration equipment is compressing under -0.1Mpa vacuum condition, and pressure 50~
200t, 30~55Hz of vibration frequency, 60~600s of time；
(5) heat cure：After vibration compacting, into curing apparatus, solidify at a temperature of 80~130 DEG C, hardening time is 30
~180 minutes；
(6) after the completion of solidifying, the room temperature completely rear sheet material thicknessing machine that enters to be cooled determines thickness, then enters by water mill polissoir
Row polishing.