CN105256402A - 一种高性能吊带及其生产工艺 - Google Patents
一种高性能吊带及其生产工艺 Download PDFInfo
- Publication number
- CN105256402A CN105256402A CN201510784018.XA CN201510784018A CN105256402A CN 105256402 A CN105256402 A CN 105256402A CN 201510784018 A CN201510784018 A CN 201510784018A CN 105256402 A CN105256402 A CN 105256402A
- Authority
- CN
- China
- Prior art keywords
- parts
- machine barrel
- suspender belt
- screw rod
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高性能吊带,所述吊带包括原材料组分及配比如下:聚丙烯粒100份、钙粉30-50份、石蜡4-5份、硬脂酸3-4份、偶联剂3.5-4.5份、聚乙烯5份;偶联剂0.8-1.2份、抗氧剂0.2-0.6份、纳米碳酸钙12-16份、聚氧化甲烯9-11份、高密度聚乙烯20-40份、聚乙烯蜡1.3-1.6份、乙烯-丙烯酸甲酯共聚物3.1-3.6份、柠檬酸三丁酯1.3-1.7份、松节油0.5-0.9份。本发明还公开了制备所述高性能吊带的工艺方法,通过该方法制备的吊带使同等单位质量的吊带,强度提高15%~30%。可以在1.5吨集装袋上使用,吊带实际强度可以达到26000N/m。
Description
技术领域
本发明属于集装带操作辅助设备领域,具体涉及一种高性能吊带及其生产工艺。
背景技术
我国集装袋生产始于上世纪80年代,晚于先进国家你,虽发展很快,但仍处于落后的状态。在集装袋生产中,吊带的质量对整袋的性能有着至关重要的作用,装载过程中吊带承载能力不足是导致事故的重要原因。因此吊带的性能是保证集装袋安全卸载的重要因素。装卸过程中,在起吊上升或紧急制动的瞬间,集装袋会受到一个瞬间的冲击力作用,这个外力在袋体、吊带或其他部件上得到分配,但是对吊带的影响最为显著。所以确定装卸时吊带所需达到的强度要求并合理选择材料,是至关重要的问题。
目前,有关集装袋吊带力学性能方面的研究较少,国内有通过拉伸试验对吊带的抗拉强度进行分析,研究了材料不同对吊带强度的影响,国外有关集装袋吊带的研究主要集中在材料的抗静电方面,而有关力学性能方面的研究较少。国标中规定了吊带需达到1:6的安全系数。在实际设计中要考虑缝制过程中对吊带强度的损耗,以及吊装方式来选择吊带。
现有技术中,如果提高吊带的强度,吊带的克重也随之增加,这样就增加了集装袋的重量。所以如何研发出一种质轻强度高的吊带对于集装带的装卸至关重要。
发明内容
有鉴于此,本发明的目的在于提供一种一种高性能吊带及其生产工艺。
为达到上述目的,本发明提供如下技术方案:
1、一种高性能吊带,按重量份比,所述吊带包括原材料组分及配比如下:聚丙烯粒100份、钙粉30-50份、石蜡4-5份、硬脂酸3-4份、偶联剂3.5-4.5份、聚乙烯5份;偶联剂0.8-1.2份、抗氧剂0.2-0.6份、纳米碳酸钙12-16份、聚氧化甲烯9-11份、高密度聚乙烯20-40份、聚乙烯蜡1.3-1.6份、乙烯-丙烯酸甲酯共聚物3.1-3.6份、柠檬酸三丁酯1.3-1.7份、松节油0.5-0.9份。
优选的,所述抗氧剂为硫代二丙酸双月桂酯。
优选的,所述吊带包括原材料组分及配比如下:聚丙烯粒100份、钙粉50份、石蜡4份、硬脂酸3份、偶联剂3.5份、聚乙烯5份;偶联剂1份、抗氧剂0.4份、纳米碳酸钙12份、聚氧化甲烯10份、高密度聚乙烯20份、聚乙烯蜡1.3份、乙烯-丙烯酸甲酯共聚物3.3份、柠檬酸三丁酯1.4份、松节油0.7份。
2、所述的高性能吊带的制备工艺,步骤如下:
1)挤出机包括机筒、螺杆以及模头,机筒与螺杆配合工作,机筒包容螺杆,螺杆在机筒内转动,所述机筒有4个温度控制区,设置机筒第一、第二、第三、第四温度控制区温度分别为180±20℃、200±20℃、220±20℃、240±20℃,设置模头温度为220±20℃,控制螺杆转速为15-60r/min,取原材料混合并加入机筒,在螺杆与机筒的相互剪切下把原料全部塑化成熔融状,原料从机筒随着螺杆经过机筒第一、第二、第三、第四温度控制区,再经过机头模具至挤出机挤出成薄膜;
2)将步骤1)挤出成型的薄膜经过水冷却,水温控制在25~55℃,用刀片将薄膜切丝;
3)将经步骤2)切的丝通过牵伸一区,将牵伸一区速度控制为25-40r/min、再经过加热风箱进行扁丝拉伸,风箱温度为110±20℃,再经过牵伸二区,将牵伸二区速度控制为30-45r/min,然后经过第三牵伸区挤压冷却,由原来的圆柱形变为扁圆形的扁丝并收卷,控制牵引倍率为5-8倍,扁丝为宽度为1.55~1.60mm,厚度为35±2mm的半圆形纱线;
4)将收卷后的纱线放在吊带机上进行编织,最终织出宽度为80±5mm克重为65±5g的吊带。
本发明的有益效果在于:该技术使同等单位质量的吊带,强度提高15%~30%。可以在1.5吨集装袋上使用,吊带实际强度可以达到26000N/m。
具体实施方式
下面将对本发明的优选实施例进行详细的描述。
实施例1
高性能吊带的制备工艺如下:
1)取原材料并混合,按重量份比,原材料组分及配比如下:聚丙烯粒100份、钙粉50份、石蜡4份、硬脂酸3份、偶联剂3.5份、聚乙烯5份;偶联剂1份、硫代二丙酸双月桂酯0.4份、纳米碳酸钙12份、聚氧化甲烯10份、高密度聚乙烯20份、聚乙烯蜡1.3份、乙烯-丙烯酸甲酯共聚物3.3份、柠檬酸三丁酯1.4份、松节油0.7份。
/2、所述的高性能吊带的制备工艺,步骤如下:
2)挤出机包括机筒、螺杆以及模头,机筒与螺杆配合工作,机筒包容螺杆,螺杆在机筒内转动,所述机筒有4个温度控制区,设置机筒第一、第二、第三、第四温度控制区温度分别为180℃、200℃、220℃、240℃,设置模头温度为240℃,控制螺杆转速为30r/min,取原材料混合并加入机筒,在螺杆与机筒的相互剪切下把原料全部塑化成熔融状,原料从机筒随着螺杆经过机筒第一、第二、第三、第四温度控制区,再经过机头模具至挤出机挤出成薄膜;
3)将步骤2)挤出成型的薄膜经过水冷却,水温控制在30℃,用刀片将薄膜切丝;
4)将经步骤3)切的丝通过牵伸一区,将牵伸一区速度控制为30r/min、再经过加热风箱进行扁丝拉伸,风箱温度为90℃,再经过牵伸二区,将牵伸二区速度控制为35r/min,然后经过第三牵伸区挤压冷却,由原来的圆柱形变为扁圆形的扁丝并收卷,控制牵引倍率为6倍,扁丝为宽度为1.57mm,厚度为35mm的半圆形纱线;
5)将收卷后的纱线放在吊带机上进行编织,最终织出宽度为80mm克重为65g的吊带。
实施例2
高性能吊带的制备工艺如下:
1)取原材料并混合,按重量份比,原材料组分及配比如下:聚丙烯粒100份、钙粉30-50份、石蜡5份、硬脂酸4份、偶联剂4.5份、聚乙烯5份;偶联剂1.2份、硫代二丙酸双月桂酯0.6份、纳米碳酸钙16份、聚氧化甲烯11份、高密度聚乙烯40份、聚乙烯蜡1.6份、乙烯-丙烯酸甲酯共聚物3.6份、柠檬酸三丁酯1.7份、松节油0.9份。
2)挤出机包括机筒、螺杆以及模头,机筒与螺杆配合工作,机筒包容螺杆,螺杆在机筒内转动,所述机筒有4个温度控制区,设置机筒第一、第二、第三、第四温度控制区温度分别为200℃、210℃、230℃、240℃,设置模头温度为225℃,控制螺杆转速为60r/min,取原材料混合并加入机筒,在螺杆与机筒的相互剪切下把原料全部塑化成熔融状,原料从机筒随着螺杆经过机筒第一、第二、第三、第四温度控制区,再经过机头模具至挤出机挤出成薄膜;
3)将步骤2)挤出成型的薄膜经过水冷却,水温控制在35℃,用刀片将薄膜切丝;
4)将经步骤3)切的丝通过牵伸一区,将牵伸一区速度控制为30r/min、再经过加热风箱进行扁丝拉伸,风箱温度为100℃,再经过牵伸二区,将牵伸二区速度控制为35r/min,然后经过第三牵伸区挤压冷却,由原来的圆柱形变为扁圆形的扁丝并收卷,控制牵引倍率为6倍,扁丝为宽度为1.60mm,厚度为37mm的半圆形纱线;
5)将收卷后的纱线放在吊带机上进行编织,最终织出宽度为78mm克重为63g的吊带。
将实施例1和实施例2制备的吊带进行力学性能测试,使同等单位质量的吊带,强度提高15%~30%。可以在1.5吨集装袋上使用,吊带实际强度可以达到26000N/m。
最后说明的是,以上优选实施例仅用以说明本发明的技术方案而非限制,尽管通过上述优选实施例已经对本发明进行了详细的描述,但本领域技术人员应当理解,可以在形式上和细节上对其作出各种各样的改变,而不偏离本发明权利要求书所限定的范围。
Claims (4)
1.一种高性能吊带,其特征在于,按重量份比,所述吊带包括原材料组分及配比如下:聚丙烯粒100份、钙粉30-50份、石蜡4-5份、硬脂酸3-4份、偶联剂3.5-4.5份、聚乙烯5份;偶联剂0.8-1.2份、抗氧剂0.2-0.6份、纳米碳酸钙12-16份、聚氧化甲烯9-11份、高密度聚乙烯20-40份、聚乙烯蜡1.3-1.6份、乙烯-丙烯酸甲酯共聚物3.1-3.6份、柠檬酸三丁酯1.3-1.7份、松节油0.5-0.9份。
2.根据权利要求1所述高性能吊带,其特征在于,所述抗氧剂为硫代二丙酸双月桂酯。
3.根据权利要求1所述高性能吊带,其特征在于,所述吊带包括原材料组分及配比如下:聚丙烯粒100份、钙粉50份、石蜡4份、硬脂酸3份、偶联剂3.5份、聚乙烯5份;偶联剂1份、抗氧剂0.4份、纳米碳酸钙12份、聚氧化甲烯10份、高密度聚乙烯20份、聚乙烯蜡1.3份、乙烯-丙烯酸甲酯共聚物3.3份、柠檬酸三丁酯1.4份、松节油0.7份。
4.权利要求1~3任一项所述高性能吊带的制备工艺,其特征在于,步骤如下:
1)挤出机包括机筒、螺杆以及模头,机筒与螺杆配合工作,机筒包容螺杆,螺杆在机筒内转动,所述机筒有4个温度控制区,设置机筒第一、第二、第三、第四温度控制区温度分别为180±20℃、200±20℃、220±20℃、240±20℃,设置模头温度为220±20℃,控制螺杆转速为15-60r/min,取原材料混合并加入机筒,在螺杆与机筒的相互剪切下把原料全部塑化成熔融状,原料从机筒随着螺杆经过机筒第一、第二、第三、第四温度控制区,再经过机头模具至挤出机挤出成薄膜;
2)将步骤1)挤出成型的薄膜经过水冷却,水温控制在25~55℃,用刀片将薄膜切丝;
3)将经步骤2)切的丝通过牵伸一区,将牵伸一区速度控制为25-40r/min、再经过加热风箱进行扁丝拉伸,风箱温度为110±20℃,再经过牵伸二区,将牵伸二区速度控制为30-45r/min,然后经过第三牵伸区挤压冷却,由原来的圆柱形变为扁圆形的扁丝并收卷,控制牵引倍率为5-8倍,扁丝为宽度为1.55~1.60mm,厚度为35±2mm的半圆形纱线;
4)将收卷后的纱线放在吊带机上进行编织,最终织出宽度为80±5mm克重为65±5g的吊带。