CN105199362A - 一种抗紫外线的遮阳用聚碳酸酯板材的制备方法 - Google Patents
一种抗紫外线的遮阳用聚碳酸酯板材的制备方法 Download PDFInfo
- Publication number
- CN105199362A CN105199362A CN201510730742.4A CN201510730742A CN105199362A CN 105199362 A CN105199362 A CN 105199362A CN 201510730742 A CN201510730742 A CN 201510730742A CN 105199362 A CN105199362 A CN 105199362A
- Authority
- CN
- China
- Prior art keywords
- parts
- azo
- ultraviolet
- mixture
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
弯曲强度(Mpa) | 冲击强度(缺口:KJ/m2) | 拉伸强度(Mpa) | |
实施例1 | 92.4 | 57 | 56.2 |
实施例2 | 91.5 | 57 | 55.6 |
实施例3 | 93.6 | 59 | 58.5 |
对照例1 | 87.4 | 56 | 52.9 |
对照例2 | 88.5 | 56 | 53.4 |
弯曲强度(Mpa) | 冲击强度(缺口:KJ/m2) | 拉伸强度(Mpa) | |
实施例1 | 91.2 | 55 | 54.5 |
实施例2 | 91.0 | 55 | 54.6 |
实施例3 | 92.1 | 56 | 56.5 |
对照例1 | 78.5 | 49 | 45.6 |
对照例2 | 77.6 | 48 | 44.7 |
Claims (7)