CN105195116B - 一种β‑环糊精修饰多孔葡聚糖凝胶吸附剂的制备方法 - Google Patents

一种β‑环糊精修饰多孔葡聚糖凝胶吸附剂的制备方法 Download PDF

Info

Publication number
CN105195116B
CN105195116B CN201510602165.0A CN201510602165A CN105195116B CN 105195116 B CN105195116 B CN 105195116B CN 201510602165 A CN201510602165 A CN 201510602165A CN 105195116 B CN105195116 B CN 105195116B
Authority
CN
China
Prior art keywords
porous
beta
sephadex
diethyllaminoethyl
adsorbent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201510602165.0A
Other languages
English (en)
Other versions
CN105195116A (zh
Inventor
李慧芝
李冬梅
赵淑英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
University of Jinan
Original Assignee
University of Jinan
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by University of Jinan filed Critical University of Jinan
Priority to CN201510602165.0A priority Critical patent/CN105195116B/zh
Publication of CN105195116A publication Critical patent/CN105195116A/zh
Application granted granted Critical
Publication of CN105195116B publication Critical patent/CN105195116B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种β‑环糊精修饰多孔葡聚糖凝胶吸附剂的制备方法,其特征在于,先将二乙氨基乙基葡聚糖凝胶于‑20℃迅速冷冻,再进行冷冻干燥,得到多孔二乙氨基乙基葡聚糖凝胶;按如下组成加入,N,N‑二甲基甲酰胺:50~60%,乙二醇二缩水甘油醚:8~15%,β‑环糊精:10~20%,搅拌溶解后,升温至50±2℃恒温、搅拌、回流反应2~4 h,再加入多孔二乙氨基乙基葡聚糖凝胶:15~25%,各组分之和为百分之百,于75~85℃恒温、搅拌、回流反应18~24 h,取出后放真空干燥箱中干燥,得到β‑环糊精修饰多孔葡聚糖凝胶吸附剂。该吸附剂对全氟辛酸具有很高的吸附容量,反复使用次数多,既成本低又绿色环保。

Description

一种β-环糊精修饰多孔葡聚糖凝胶吸附剂的制备方法
技术领域
本发明涉及一种生物吸附剂的制备方法的技术领域,特别涉及一种环糊精多孔葡聚糖凝胶吸附剂的制备方法及对全氟辛酸(PFOA)吸附的应用技术。
背景技术
β-环糊精是一系列以α-1,4-糖苷键合的环状低聚糖,呈截顶圆锥状花环结构,具有内疏水和外亲水性,对尺寸适宜的分子可进行包接。这一特殊的性质使其在药物载体、手性识别、化学分离、电化学传感等方面得到了广泛应用。近年来,许多学者开始关注β-环糊精及其衍生物在环境领域中的应用。孙琳琳等,研究了羧甲基-β-环糊精功能化四氧化三铁磁性纳米复合物对罗丹明B的吸附性能(孙琳琳等,羧甲基-β-环糊精功能化四氧化三铁磁性纳米复合物对罗丹明B的吸附性能,应用化学,2015,32(1):110-117);李伟等研究了β-环糊精修饰聚乙烯醇纳米纤维的制备及其吸附性能(李伟等,β-环糊精修饰聚乙烯醇纳米纤维的制备及其吸附性能研究,2013,20(4):21-24)。
全氟辛酸(PFOA),或者称为“C8”,为一种人工合成的化学品,通常是用于生产高效能氟聚合物时所不可或缺的加工助剂。这些高效能氟聚合物可被广泛应用于航空航天科技、运输、电子行业,以及厨具(如不粘锅)等民生用品。从20世纪80年代早期开始,这种非挥发性全氟有机化合物在工业及民用领域的应用增长迅速。该类产品的大量使用使得其以各种途径进入到全球范围内的各种环境介质如土壤、水体、大气中,通过食物链的传递放大,目前在许多动物组织和人体中发下了PFOA的存在。因此PFOA已经成为一种重要的全球性污染物,它对环境污染的广度和深度超出人们预想,目前对于该问题的研究已经成为环境科学的研究热点。
对于PFOA等全氟烷基类持久性污染物的治理技术目前研究甚少,因其极好的稳定性造成采用传统废水处理方法无法将其降解,还可能在处理过程中造成其前体的分解产生新的PFOA。处理含全氟类烷基化合物的有机废水,高级氧化技术也速手无策,强氧化性的羟基自由基也与PFOA等全氟类烷基化合物的反应速率极慢,另外,还有人采用光化学、活性炭吸附和纳滤膜等方法,处理效果都不是特别明显。赵德明等,研究了采用超声波降解全氟类烷基化合物(赵德明等,超声波降解全氟辛烷磺酸和全氟辛酸的动力学,化工学报,2011,62(2):829~832),超声降解适用于高浓度的全氟污染物,对于微量的全氟污染物处理达不到理想效果。吸附分离除去环境水中存在的有机、无机污染物,已被认为是一种十分有效和常用的处理方法,采用吸附分离法除去水中的PFOA成为本领域技术人员关注问题。采用吸附分离除去PFOA报道很少。
当进社会,水污染问题引起人们越来越多的关注。随着水污染问题的日益加重,制备针对性强、处理效果好、可重复利用的新材料已成为研究重点。其中,二乙氨基乙基葡聚糖凝胶是具有多孔性三度空间网状结构的高分子化合物,属于软性凝胶,其微孔能吸入大量溶剂,比表面积大,葡聚糖含有亲水性,还带有丰富的二乙氨基乙基、羟基等配位基、很容易进行化学改性,葡聚糖凝胶是由葡萄糖发酵、交联而制得的,属于天然高分子,可以生物降解,来源丰富绿色环保,可反复使用。本发明将二乙氨基乙基葡聚糖凝胶在水中充分浸泡活化、冷冻干燥获得多孔二乙氨基乙基葡聚糖凝胶,通过交联剂将β-环糊精与多孔二乙氨基乙基葡聚糖凝胶连接,由于多孔二乙氨基乙基葡聚糖凝胶连接的比表面积大,连接位点多,活性基团连接的数量就多。它即具有无机材料的机械性能好的优点,又具有有机材料的所有优点,目前未见β-环糊精修饰多孔葡聚糖凝胶制备吸附剂的报道。天然高分子材料被利用作为吸附剂具有可再生、可降解、环保友好、廉价等优点,是重要的生物资源。
发明内容
本发明的目的之一是提供一种β-环糊精修饰多孔葡聚糖凝胶吸附剂的制备方法,获取的一种β-环糊精修饰多孔葡聚糖凝胶吸附剂对水体系中PFOA的进行吸附分离。
本发明的目的通过以下技术方案实现。
一种β-环糊精修饰多孔葡聚糖凝胶吸附剂的制备方法,特征在于该方法具有以下工艺步骤:
(1)多孔二乙氨基乙基葡聚糖凝胶制备:在反应器中,将二乙氨基乙基葡聚糖凝胶用蒸馏水浸泡36h,用蒸馏水充分洗涤至中性,过滤,置于塑料容器中于-20℃迅速冷冻,取出后放入冷冻干燥箱内,冷冻干燥20 h,得到多孔二乙氨基乙基葡聚糖凝胶;
(2)β-环糊精修饰多孔葡聚糖凝胶吸附剂制备:在反应器中,按如下组成质量百分比加入,N,N-二甲基甲酰胺:50~60%,乙二醇二缩水甘油醚:8~15%,β-环糊精:10~20%,搅拌溶解后,升温至50±2℃恒温、搅拌、回流反应2~4 h,再加入多孔二乙氨基乙基葡聚糖凝胶:15~25%,各组分之和为百分之百,于75~85℃恒温、搅拌、回流反应18~24 h,反应完毕后用丙酮回流洗涤,取出后放真空干燥箱中干燥,得到β-环糊精修饰多孔葡聚糖凝胶吸附剂。
所述的二乙氨基乙基葡聚糖凝胶的粒径在40~120μm之间。
在步骤(2)中所述的β-环糊精与多孔二乙氨基乙基葡聚糖凝胶质量比在1:1.5~2.5范围内为最优。
本发明的另一目的是提供β-环糊精修饰多孔葡聚糖凝胶吸附剂对水体系中对PFOA的吸附,特点为:将制备好的β-环糊精修饰多孔葡聚糖凝胶吸附剂用去离子水浸泡4~6h,按静态法吸附。
将制备好的β-环糊精修饰多孔葡聚糖凝胶吸附剂用去离子水浸泡4~6h,按动态法吸附。
本发明与现有技术比较,具有如下优点及有益效果:
(1)本发明获得的β-环糊精修饰多孔葡聚糖凝胶吸附剂具有良好的物理化学稳定性和优异的机械强度,吸附容量大,最大吸附容量达156.21 mg/g,耐磨可反复使用次数可达10次以上,吸附的速度快,吸附选择好,解吸性能好,能够在较宽的酸碱范围内使用。
(2)本发明获得的β-环糊精修饰多孔葡聚糖凝胶吸附剂既具有固相载体材料的优点,也解决了活性基团β-环糊精应用到水环境中的流失问题。
(3)稳定性好,是天然绿色产品,再生材料,废弃物可生物降解;
(4)合成的过程要求的条件容易控制,能耗低,操作简单,属于清洁生产工艺,易于工业化生产。
具体实施方式
实施例1
(1)多孔二乙氨基乙基葡聚糖凝胶制备:在反应器中,将二乙氨基乙基葡聚糖凝胶用蒸馏水浸泡36h,用蒸馏水充分洗涤至中性,过滤,置于塑料容器中于-20℃迅速冷冻,取出后放入冷冻干燥箱内,冷冻干燥20 h,得到多孔二乙氨基乙基葡聚糖凝胶;
(2)β-环糊精修饰多孔葡聚糖凝胶吸附剂制备:在反应器中,分别加入,N,N-二甲基甲酰胺:58 mL,乙二醇二缩水甘油醚:12g,β-环糊精:15g,搅拌溶解后,升温至50±2℃恒温、搅拌、回流反应3 h,再加入多孔二乙氨基乙基葡聚糖凝胶:18g,于80℃恒温、搅拌、回流反应20h,反应完毕后用丙酮回流洗涤,取出后放真空干燥箱中干燥,得到β-环糊精修饰多孔葡聚糖凝胶吸附剂。
实施例2
(1)多孔二乙氨基乙基葡聚糖凝胶制备:在反应器中,将二乙氨基乙基葡聚糖凝胶用蒸馏水浸泡36h,用蒸馏水充分洗涤至中性,过滤,置于塑料容器中于-20℃迅速冷冻,取出后放入冷冻干燥箱内,冷冻干燥20 h,得到多孔二乙氨基乙基葡聚糖凝胶;
(2)β-环糊精修饰多孔葡聚糖凝胶吸附剂制备:在反应器中,分别加入,N,N-二甲基甲酰胺:53 mL,乙二醇二缩水甘油醚:15g,β-环糊精:10g,搅拌溶解后,升温至50±2℃恒温、搅拌、回流反应2 h,再加入多孔二乙氨基乙基葡聚糖凝胶:25g,于75℃恒温、搅拌、回流反应24h,反应完毕后用丙酮回流洗涤,取出后放真空干燥箱中干燥,得到β-环糊精修饰多孔葡聚糖凝胶吸附剂。
实施例3
(1)多孔二乙氨基乙基葡聚糖凝胶制备:在反应器中,将二乙氨基乙基葡聚糖凝胶用蒸馏水浸泡36h,用蒸馏水充分洗涤至中性,过滤,置于塑料容器中于-20℃迅速冷冻,取出后放入冷冻干燥箱内,冷冻干燥20 h,得到多孔二乙氨基乙基葡聚糖凝胶;
(2)β-环糊精修饰多孔葡聚糖凝胶吸附剂制备:在反应器中,分别加入,N,N-二甲基甲酰胺:63 mL,乙二醇二缩水甘油醚:8g,β-环糊精:12g,搅拌溶解后,升温至50±2℃恒温、搅拌、回流反应4 h,再加入多孔二乙氨基乙基葡聚糖凝胶:20g,于85℃恒温、搅拌、回流反应18h,反应完毕后用丙酮回流洗涤,取出后放真空干燥箱中干燥,得到β-环糊精修饰多孔葡聚糖凝胶吸附剂。
实施例4
(1)多孔二乙氨基乙基葡聚糖凝胶制备:在反应器中,将二乙氨基乙基葡聚糖凝胶用蒸馏水浸泡36h,用蒸馏水充分洗涤至中性,过滤,置于塑料容器中于-20℃迅速冷冻,取出后放入冷冻干燥箱内,冷冻干燥20 h,得到多孔二乙氨基乙基葡聚糖凝胶;
(2)β-环糊精修饰多孔葡聚糖凝胶吸附剂制备:在反应器中,分别加入,N,N-二甲基甲酰胺:55 mL,乙二醇二缩水甘油醚:13g,β-环糊精:20g,搅拌溶解后,升温至50±2℃恒温、搅拌、回流反应2.5 h,再加入多孔二乙氨基乙基葡聚糖凝胶:15g,于78℃恒温、搅拌、回流反应19h,反应完毕后用丙酮回流洗涤,取出后放真空干燥箱中干燥,得到β-环糊精修饰多孔葡聚糖凝胶吸附剂。
实施例5
(1)多孔二乙氨基乙基葡聚糖凝胶制备:在反应器中,将二乙氨基乙基葡聚糖凝胶用蒸馏水浸泡36h,用蒸馏水充分洗涤至中性,过滤,置于塑料容器中于-20℃迅速冷冻,取出后放入冷冻干燥箱内,冷冻干燥20 h,得到多孔二乙氨基乙基葡聚糖凝胶;
(2)β-环糊精修饰多孔葡聚糖凝胶吸附剂制备:在反应器中,分别加入,N,N-二甲基甲酰胺:61mL,乙二醇二缩水甘油醚:10g,β-环糊精:18g,搅拌溶解后,升温至50±2℃恒温、搅拌、回流反应3.5 h,再加入多孔二乙氨基乙基葡聚糖凝胶:16g,于82℃恒温、搅拌、回流反应22h,反应完毕后用丙酮回流洗涤,取出后放真空干燥箱中干燥,得到β-环糊精修饰多孔葡聚糖凝胶吸附剂。
实施例6
(1)多孔二乙氨基乙基葡聚糖凝胶制备:在反应器中,将二乙氨基乙基葡聚糖凝胶用蒸馏水浸泡36h,用蒸馏水充分洗涤至中性,过滤,置于塑料容器中于-20℃迅速冷冻,取出后放入冷冻干燥箱内,冷冻干燥20 h,得到多孔二乙氨基乙基葡聚糖凝胶;
(2)β-环糊精修饰多孔葡聚糖凝胶吸附剂制备:在反应器中,分别加入,N,N-二甲基甲酰胺:28 mL,乙二醇二缩水甘油醚:6g,β-环糊精:8g,搅拌溶解后,升温至50±2℃恒温、搅拌、回流反应3 h,再加入多孔二乙氨基乙基葡聚糖凝胶:9g,于75℃恒温、搅拌、回流反应23h,反应完毕后用丙酮回流洗涤,取出后放真空干燥箱中干燥,得到β-环糊精修饰多孔葡聚糖凝胶吸附剂。
实施例7
称取0.20gβ-环糊精修饰多孔葡聚糖凝胶吸附剂置于250mL具塞锥形瓶中浸泡5h,过滤洗涤后,加入100mL浓度为400mg/LPFOA标准溶液中,以稀酸或碱调节体系的pH值为2.0~11.0范围内,在室温下震荡吸附10~12h,取上清液,用高效液相色谱法测定PFOA的浓度,根据吸附前后水中PFOA的浓度差,计算出β-环糊精修饰多孔葡聚糖凝胶吸附剂的吸附容量,本发明所制得的β-环糊精修饰多孔葡聚糖凝胶吸附剂对PFOA的吸附pH值在6.5~7.5范围内吸附剂对PFOA的吸附容量最大而且稳定,在室温下震荡吸附10h,PFOA基本吸附完全,PFOA的吸附容量可达156.21 mg/g。
实施例8
称取1.0gβ-环糊精修饰多孔葡聚糖凝胶吸附剂置于250mL具塞锥形瓶中,加入100mL浓度为200mg/LPFOA标准溶液中,以稀酸或碱调节体系的pH值为6.5~7.5范围内,在室温下震荡吸附10h,取上清液,用高效液相色谱法测定PFOA的浓度,根据吸附前后水中PFOA的浓度差,计算出β-环糊精修饰多孔葡聚糖凝胶吸附剂对PFOA的去除率,本发明所制得的β-环糊精修饰多孔葡聚糖凝胶吸附剂对PFOA的去除率都在95.12%以上,最高可达98.36%。

Claims (3)

1.一种β-环糊精修饰多孔葡聚糖凝胶吸附剂的制备方法,其特征在于,该方法具有以下工艺步骤:
(1)多孔二乙氨基乙基葡聚糖凝胶制备:在反应器中,将二乙氨基乙基葡聚糖凝胶用蒸馏水浸泡36h,用蒸馏水充分洗涤至中性,过滤,置于塑料容器中于-20℃迅速冷冻,取出后放入冷冻干燥箱内,冷冻干燥20h,得到多孔二乙氨基乙基葡聚糖凝胶;
(2)β-环糊精修饰多孔葡聚糖凝胶吸附剂制备:在反应器中,按如下组成质量百分比加入,N,N-二甲基甲酰胺:50~60%,乙二醇二缩水甘油醚:8~15%,β-环糊精:10~20%,搅拌溶解后,升温至50±2℃恒温、搅拌、回流反应2~4h,再加入多孔二乙氨基乙基葡聚糖凝胶:15~25%,各组分之和为百分之百,于75~85℃恒温、搅拌、回流反应18~24h,反应完毕后用丙酮回流洗涤,取出后放真空干燥箱中干燥,得到β-环糊精修饰多孔葡聚糖凝胶吸附剂。
2.根据权利要求1中所述的一种β-环糊精修饰多孔葡聚糖凝胶吸附剂的制备方法,特征在于,步骤(1)所述的二乙氨基乙基葡聚糖凝胶的粒径在40~120μm之间。
3.根据权利要求1中所述一种β-环糊精修饰多孔葡聚糖凝胶吸附剂的制备方法所制备一种β-环糊精修饰多孔葡聚糖凝胶吸附剂。
CN201510602165.0A 2015-09-21 2015-09-21 一种β‑环糊精修饰多孔葡聚糖凝胶吸附剂的制备方法 Expired - Fee Related CN105195116B (zh)