CN105152685A - Matte metal glaze, matte metal glaze ceramic product prepared from same and preparation method of matte metal glaze ceramic product - Google Patents
Matte metal glaze, matte metal glaze ceramic product prepared from same and preparation method of matte metal glaze ceramic product Download PDFInfo
- Publication number
- CN105152685A CN105152685A CN201510674938.6A CN201510674938A CN105152685A CN 105152685 A CN105152685 A CN 105152685A CN 201510674938 A CN201510674938 A CN 201510674938A CN 105152685 A CN105152685 A CN 105152685A
- Authority
- CN
- China
- Prior art keywords
- parts
- metal glaze
- sub
- light metal
- glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to matte metal glaze, a matte metal glaze ceramic product prepared from the same and a preparation method of the matte metal glaze ceramic product, belonging to the technical field of ceramics. The matte metal glaze comprises the following components in parts by weight: 45-55 parts of nepheline orthoclase, 28-35 parts of clinkers, 4-7 parts of quartz, 2-8 parts of barium carbonate, 2-7 parts of disthene, 3-7 parts of kaolin, 22-27 parts of manganese oxide and 1-1.9 parts of copper oxide, wherein the clinkers comprise the following components in parts by weight: 38-42 parts of borax, 22-28 parts of quartz, 3-6 parts of kaolin, 12-17 parts of calcium carbonate, 8-13 parts of sodium nitrate and 2-7 parts of potassium carbonate. The matte metal glaze ceramic product is endowed with good texture and appearance by the matte metal glaze; and by integrating metal luster with low-pitched matte, the matte metal glaze ceramic product is low-pitched and luxurious.
Description
Technical field
The invention belongs to ceramic technology field, be specifically related to a kind of sub-light metal glaze and by its sub-light metal glaze ceramic prepared and preparation method.
Background technology
Glaze is generally for raw material with quartz, feldspar, clay etc.; through grinding, modulation, glazing, the step such as to burn till; at the protective membrane of one deck glassiness thin layer that ceramic surface is formed; the glaze layer of ceramic surface; not only can strengthen the physicals such as physical strength, thermostability of pottery; the outward appearance of beautifying ceramic can also be strengthened, and facilitate the clean of ceramic surface.
Metal glaze is a kind of special glaze having metal-like, Sub-shine glaze is a kind of opaque, glaze that glossiness is lower, and sub-light metal glaze is a kind of special glaze kind having had metal glaze and Sub-shine glaze advantage concurrently, because independent Sub-shine glaze color is dimer, and independent metal glaze is too dazzling under light, due to the batching of sub-light metal glaze and the control of condition more difficult grasp when burning till, therefore rarely relevant to sub-light metal glaze at present report, and very important to the research of sub-light metal glaze, there are larger researching value and market outlook.
Summary of the invention
The object of the invention is to solve the deficiencies in the prior art, and provide a kind of sub-light metal glaze and by its sub-light metal glaze ceramic prepared and preparation method, this sub-light metal glaze gives the good texture of ceramic and outward appearance, metalluster and the sub-light of low-key is combined together, low-key.
The present invention adopts following technical scheme:
Sub-light metal glaze, comprises the following component according to mass fraction meter: nepheline syenite 45-55 part, frit 28-35 part, quartzy 4-7 part, barium carbonate 2-8 part, kyanite 2-7 part, kaolin 3-7 part, manganese oxide 22-27 part, cupric oxide 1-1.9 part.
Further, described sub-light metal glaze, comprises the following component according to mass fraction meter: nepheline syenite 50 parts, frit 30 parts, 5 parts, quartz, barium carbonate 5 parts, kyanite 5 parts, kaolin 5 parts, manganese oxide 25 parts, cupric oxide 1.5 parts.
Further, described sub-light metal glaze, wherein said frit comprises the following component according to mass fraction meter: borax 38-42 part, quartzy 22-28 part, kaolin 3-6 part, calcium carbonate 12-17 part, SODIUMNITRATE 8-13 part, salt of wormwood 2-7 part.
Further, described sub-light metal glaze, wherein said frit comprises the following component according to mass fraction meter: borax 40 parts, 25 parts, quartz, kaolin 5 parts, 15 parts, calcium carbonate, SODIUMNITRATE 10 parts, 5 parts, salt of wormwood.
Prepare the method for sub-light metal glaze ceramic with described sub-light metal glaze, comprise the steps:
Step one, grinding: according to the proportioning of frit, each raw material is mixed, for subsequent use, according to described glaze weight proportion, after the mixing of each feed composition, ball milling 30-35h, after to go out slurry for subsequent use;
Step 2, glaze concentration adjustment: add water in step one gained slurry, regulates concentration to 44 °-47 ° of degree Beaume, obtains glaze slurry;
Step 3, glazing: immersed by the biscuit of ceramics baked in step 2 gained glaze slurry and carry out glazing, glazed thickness is 1.0-1.3mm, dry, obtains ceramic first product;
Step 4, oxidation is fired: fired under oxidation atmosphere by step 3 gained ceramic first product, kiln temperature is at the uniform velocity warming up to 600 DEG C in 20-30min, and rear constant temperature fires 35-40min, is more at the uniform velocity warming up in 40-50min and continues to 1270 DEG C, constant temperature fires 175-180min, after be at the uniform velocity warming up to 1310 DEG C in 10-20min, constant temperature fires 10-15min, rear leave standstill treat naturally cooling, kiln discharge is checked, and obtains described sub-light metal glaze ceramic.
Further, the method for sub-light metal glaze ceramic prepared by described use sub-light metal glaze, and wherein ball milling described in step one is that the water adding raw material gross weight 40-45% carries out ball milling, and rotating speed during ball milling is 300-350r/min.
The sub-light metal glaze ceramic that the method that the present invention also provides a kind of use sub-light metal glaze to prepare sub-light metal glaze ceramic is obtained.
Compared with prior art, its beneficial effect is in the present invention:
The sub-light metal glaze adopting glaze of the present invention and method to obtain both had metalluster, but can not be too dazzling under light, had again the sub-light quality sense of low-key, but was not intensely dark, enamel low-key, high-end and atmospheric; In addition, according to method of the present invention, by temperature when heat-up rate during conservative control gloss firing and gloss firing and firing time, not only give the physical strength of ceramic excellence, ceramic is also made to have excellent corrosion resistance and Nai Gao fire performance, seldom there will be the defect wares such as glaze bubble, contracting glaze and pin hole, yield rate can up to more than 95%.
Embodiment
Below in conjunction with embodiment, the present invention is described in further detail.
It will be understood to those of skill in the art that the following example only for illustration of the present invention, and should not be considered as limiting scope of the present invention.
embodiment 1
Sub-light metal glaze, comprises the following component according to mass fraction meter: nepheline syenite 50 parts, frit 30 parts, 5 parts, quartz, barium carbonate 5 parts, kyanite 5 parts, kaolin 5 parts, manganese oxide 25 parts, cupric oxide 1.5 parts; Wherein said frit comprises the following component according to mass fraction meter: borax 40 parts, 25 parts, quartz, kaolin 5 parts, 15 parts, calcium carbonate, SODIUMNITRATE 10 parts, 5 parts, salt of wormwood.
Prepare the method for sub-light metal glaze ceramic with described sub-light metal glaze, comprise the steps:
Step one, grinding: according to the proportioning of frit, each raw material is mixed, for subsequent use, according to described glaze weight proportion, after each feed composition mixing, the water adding raw material gross weight 42% carries out ball milling, rotating speed during ball milling is 320r/min, ball milling 32h, after to go out slurry for subsequent use;
Step 2, glaze concentration adjustment: add water in step one gained slurry, regulates concentration to 45 ° degree Beaume, obtains glaze slurry;
Step 3, glazing: immersed by the biscuit of ceramics baked in step 2 gained glaze slurry and carry out glazing, glazed thickness is 1.2mm, dry, obtains ceramic first product;
Step 4, oxidation is fired: fired under oxidation atmosphere by step 3 gained ceramic first product, kiln temperature is at the uniform velocity warming up to 600 DEG C in 25min, and rear constant temperature fires 38min, is more at the uniform velocity warming up in 45min and continues to 1270 DEG C, constant temperature fires 178min, after be at the uniform velocity warming up to 1310 DEG C in 15min, constant temperature fires 12min, rear leave standstill treat naturally cooling, kiln discharge is checked, and obtains described sub-light metal glaze ceramic.
embodiment 2
Sub-light metal glaze, comprises the following component according to mass fraction meter: nepheline syenite 45 parts, frit 28 parts, 4 parts, quartz, barium carbonate 2 parts, kyanite 2 parts, kaolin 3 parts, manganese oxide 22 parts, cupric oxide 1 part; Wherein said frit comprises the following component according to mass fraction meter: borax 38 parts, 22 parts, quartz, kaolin 3 parts, 12 parts, calcium carbonate, SODIUMNITRATE 8 parts, 2 parts, salt of wormwood.
Prepare the method for sub-light metal glaze ceramic with described sub-light metal glaze, comprise the steps:
Step one, grinding: according to the proportioning of frit, each raw material is mixed, for subsequent use, according to described glaze weight proportion, after each feed composition mixing, the water adding raw material gross weight 40% carries out ball milling, rotating speed during ball milling is 300r/min, ball milling 35h, after to go out slurry for subsequent use;
Step 2, glaze concentration adjustment: add water in step one gained slurry, regulates concentration to 44 ° degree Beaume, obtains glaze slurry;
Step 3, glazing: immersed by the biscuit of ceramics baked in step 2 gained glaze slurry and carry out glazing, glazed thickness is 1.0mm, dry, obtains ceramic first product;
Step 4, oxidation is fired: fired under oxidation atmosphere by step 3 gained ceramic first product, kiln temperature is at the uniform velocity warming up to 600 DEG C in 20min, and rear constant temperature fires 35min, is more at the uniform velocity warming up in 40min and continues to 1270 DEG C, constant temperature fires 175min, after be at the uniform velocity warming up to 1310 DEG C in 10min, constant temperature fires 10min, rear leave standstill treat naturally cooling, kiln discharge is checked, and obtains described sub-light metal glaze ceramic.
embodiment 3
Sub-light metal glaze, comprises the following component according to mass fraction meter: nepheline syenite 55 parts, frit 35 parts, 7 parts, quartz, barium carbonate 8 parts, kyanite 7 parts, kaolin 7 parts, manganese oxide 27 parts, cupric oxide 1.9 parts.
Prepare the method for sub-light metal glaze ceramic with described sub-light metal glaze, comprise the steps:
Step one, grinding: according to the proportioning of frit, each raw material is mixed, for subsequent use, according to described glaze weight proportion, after each feed composition mixing, the water adding raw material gross weight 45% carries out ball milling, rotating speed during ball milling is 350r/min, ball milling 30h, after to go out slurry for subsequent use;
Step 2, glaze concentration adjustment: add water in step one gained slurry, regulates concentration to 47 ° degree Beaume, obtains glaze slurry;
Step 3, glazing: immersed by the biscuit of ceramics baked in step 2 gained glaze slurry and carry out glazing, glazed thickness is 1.3mm, dry, obtains ceramic first product;
Step 4, oxidation is fired: fired under oxidation atmosphere by step 3 gained ceramic first product, kiln temperature is at the uniform velocity warming up to 600 DEG C in 30min, and rear constant temperature fires 40min, is more at the uniform velocity warming up in 50min and continues to 1270 DEG C, constant temperature fires 180min, after be at the uniform velocity warming up to 1310 DEG C in 20min, constant temperature fires 15min, rear leave standstill treat naturally cooling, kiln discharge is checked, and obtains described sub-light metal glaze ceramic.
The sub-light metal glaze ceramic obtained according to glaze formula described in embodiment 1 to 3 and preparation method all has moist glaze paint, and yield rate all can reach more than 95%.
The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (7)
1. sub-light metal glaze, it is characterized in that, comprise the following component according to mass fraction meter: nepheline syenite 45-55 part, frit 28-35 part, quartzy 4-7 part, barium carbonate 2-8 part, kyanite 2-7 part, kaolin 3-7 part, manganese oxide 22-27 part, cupric oxide 1-1.9 part.
2. sub-light metal glaze according to claim 1, it is characterized in that, comprise the following component according to mass fraction meter: nepheline syenite 50 parts, frit 30 parts, 5 parts, quartz, barium carbonate 5 parts, kyanite 5 parts, kaolin 5 parts, manganese oxide 25 parts, cupric oxide 1.5 parts.
3. sub-light metal glaze according to claim 1, it is characterized in that, described frit comprises the following component according to mass fraction meter: borax 38-42 part, quartzy 22-28 part, kaolin 3-6 part, calcium carbonate 12-17 part, SODIUMNITRATE 8-13 part, salt of wormwood 2-7 part.
4. sub-light metal glaze according to claim 3, is characterized in that, described frit comprises the following component according to mass fraction meter: borax 40 parts, 25 parts, quartz, kaolin 5 parts, 15 parts, calcium carbonate, SODIUMNITRATE 10 parts, 5 parts, salt of wormwood.
5. prepare the method for sub-light metal glaze ceramic with light metal glaze sub-described in claim 1, it is characterized in that, comprise the steps:
Step one, grinding: according to the proportioning of frit, each raw material is mixed, for subsequent use, according to described glaze weight proportion, after the mixing of each feed composition, ball milling 30-35h, after to go out slurry for subsequent use;
Step 2, glaze concentration adjustment: add water in step one gained slurry, regulates concentration to 44 °-47 ° of degree Beaume, obtains glaze slurry;
Step 3, glazing: immersed by the biscuit of ceramics baked in step 2 gained glaze slurry and carry out glazing, glazed thickness is 1.0-1.3mm, dry, obtains ceramic first product;
Step 4, oxidation is fired: fired under oxidation atmosphere by step 3 gained ceramic first product, kiln temperature is at the uniform velocity warming up to 600 DEG C in 20-30min, and rear constant temperature fires 35-40min, is more at the uniform velocity warming up in 40-50min and continues to 1270 DEG C, constant temperature fires 175-180min, after be at the uniform velocity warming up to 1310 DEG C in 10-20min, constant temperature fires 10-15min, rear leave standstill treat naturally cooling, kiln discharge is checked, and obtains described sub-light metal glaze ceramic.
6. the method for sub-light metal glaze ceramic prepared by use according to claim 5 sub-light metal glaze, it is characterized in that, ball milling described in step one is that the water adding raw material gross weight 40-45% carries out ball milling, and rotating speed during ball milling is 300-350r/min.
7. the sub-light metal glaze ceramic that the method that sub-light metal glaze ceramic prepared by use according to claim 5 sub-light metal glaze obtains.