CN106064889B - The noble metal glaze art pottery and its production method - Google Patents
The noble metal glaze art pottery and its production method Download PDFInfo
- Publication number
- CN106064889B CN106064889B CN201610372871.5A CN201610372871A CN106064889B CN 106064889 B CN106064889 B CN 106064889B CN 201610372871 A CN201610372871 A CN 201610372871A CN 106064889 B CN106064889 B CN 106064889B
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- noble metal
- art pottery
- metal glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to ceramic fabrication technique field, be specifically related to a kind of noble metal glaze art pottery and its production method.This kind of noble metal glaze art pottery, glaze uses lead free soldering, calcite, kaolin, quartz, iron oxide yellow, MnO2, NiO, Al2O3, CrO3, ZrSiO4, V2O5, CuO, TiO2, CMC is formed, pass through unique making, burning process, the produced noble metal glaze art pottery, glazing effect has very strong metallic luster, adjustable formula makes glaze at golden yellow, silver color, the metallochromes such as grey black, glaze is smooth, in mirror-reflection, gloss keeps lasting, it is with good stability, in addition lead is free of in this kind of noble metal glaze art pottery glaze, chromium, it is safe to use.
Description
Technical field
The present invention relates to ceramic fabrication technique field, be specifically related to a kind of noble metal glaze art pottery and its making
Method.
Background technology
The polished rear surface of the noble metals such as noble metal such as gold, silver, titanium is one layer of bright minute surface, this kind of mirror effect
It is combined with unique artistic effect, the side of the noble metal minute surface generally use plating of existing ceramic surface with ceramic material
Formula obtains, but the excessively bright deviation standard gold/silver color of the effect being electroplated, and gap is big compared with true noble metal minute surface;In addition,
Ceramic electroplating cost is high, and the product content of beary metal obtained after being electroplated is high, can not be used as domestic ceramics.
To solve the above problems, application publication number be 104496555 A of CN imitative cermet artistic glaze and its prepare and
Application method discloses a kind of imitative cermet artistic glaze, this kind of imitative cermet artistic glaze is using frit, wollastonite, Tuo Pa
Stone, mica, copper oxide, talcum, titanium dioxide, manganese dioxide, nickel oxide, aluminium oxide are made, the imitative metal art prepared
Ceramic product, for glaze in golden yellow, metallic luster is strong, is in mirror-reflection, and appearance can match in excellence or beauty metal product.This kind of imitative metal
Though ceramic artistic glaze glaze, at mirror effect, color is to be only capable of embodying golden yellow, and noble metal also has other than golden yellow
The multiple colors such as silver color, platinum color, Zijin, copper red color, this kind of imitative cermet artistic glaze glazing effect be single, production cost
It is high.
Invention content
In order to solve the deficiencies in the prior art, the present invention provides a kind of noble metal glaze art pottery and its making side
Method.
To achieve the above object, this noble metal glaze art pottery, which is characterized in that the noble metal glaze art pottery
Glaze component it is as follows:45-70 parts of lead free soldering, 5-10 parts of calcite, 5-10 parts of kaolin, 5-10 parts of quartz, iron oxide yellow 5-
10 parts, MnO25-10 parts, 1-10 parts of NiO, Al2O31-5 parts, CrO31-5 parts, ZrSiO41-5 parts, V2O51-5 parts, CuO
1-5 parts, TiO21-3 parts, 0.5-1 parts of CMC;The composition of wherein lead free soldering is as follows:30-45 parts of potassium feldspar, zinc oxide 10-20
Part, 5-10 parts of quartz, calcite 5-10,5-10 parts of barium carbonate, Al2O35-10 parts, WO35-10 parts, K21-5 parts of O, Na2O 1-
5 parts, Li21-5 parts of O.
Optimization, the glaze component of the noble metal glaze art pottery is as follows:49 parts of lead free soldering, 6 parts of calcite, kaolinite
6 parts of soil, 7 parts of quartz, 9 parts of iron oxide yellow, MnO26 parts, 2 parts of NiO, Al2O33 parts, CrO31 part, ZrSiO42 parts, V2O55 parts,
1 part of CuO, TiO22.5 parts, 0.5 part of CMC.
Optimization, the composition of lead free soldering is as follows:42 parts of potassium feldspar, 18 parts of zinc oxide, 6 parts of quartz, calcite 7, carbonic acid
6 parts of barium, Al2O35 parts, WO36 parts, K23 parts of O, Na22 parts of O, Li25 parts of O.
Optimization, the glaze component of the noble metal glaze art pottery is as follows:53 parts of lead free soldering, 5 parts of calcite, kaolinite
8 parts of soil, 6 parts of quartz, 5 parts of iron oxide yellow, MnO25 parts, 1 part of NiO, Al2O33 parts, CrO34 parts, ZrSiO42 parts, V2O51 part,
5 parts of CuO, TiO21 part, 1 part of CMC.
Optimization, the composition of lead free soldering is as follows:36 parts of potassium feldspar, 16 parts of zinc oxide, 7 parts of quartz, calcite 8, carbonic acid
8 parts of barium, Al2O38 parts, WO37 parts, K23 parts of O, Na22 parts of O, Li25 parts of O.
Optimization, the glaze component of the noble metal glaze art pottery is as follows:62 parts of lead free soldering, 5 parts of calcite, kaolinite
5 parts of soil, 5 parts of quartz, 8 parts of iron oxide yellow, MnO25 parts, 2 parts of NiO, Al2O32 parts, CrO31 part, ZrSiO41 part, V2O51 part,
1 part of CuO, TiO21 part, 1 part of CMC.
Optimization, the composition of lead free soldering is as follows:40 parts of potassium feldspar, 16 parts of zinc oxide, 8 parts of quartz, calcite 7, carbonic acid
4 parts of barium, Al2O39 parts, WO37 parts, K23 parts of O, Na23 parts of O, Li23 parts of O.
A kind of production method with the noble metal glaze art pottery, prepares the noble metal glaze described in above-mentioned any one
The art pottery is as follows:
Step 1, the shraff during Production of Ceramics is collected, shraff is cleaned, crushes, 1100- after sieving
1200 DEG C of high-temperature calcinations, for use;
Step 2, according to traditional shaping method of ceramics, ceramic body is produced;
Step 3, it weighs, mix according to the glaze component of noble metal glaze art pottery progress raw material, by raw material wet bulb
It grinds, glaze crosses 200 mesh sieve after wet ball mill, obtains glaze;
Step 4, ceramic body is put into baking oven after glazing and toasts 5-20 in 45-50 DEG C by the glazing on ceramic body
Hour, removal is for use;
Step 5, the ceramic body after glazing is put into kiln, is formed by a firing, firing temperature is 1200-1260 DEG C, is protected
Natural cooling after 30-60 minutes warm.
Further, in step 3, when wet ball mill, expects:Ball:Water=1:2:1:1-0.8, ball milling 30-60 minutes, tails over 1%.
Further, in step 4, glaze thickness 0.3-0.5mm.
By the above-mentioned description of this invention it is found that the noble metal glaze art pottery provided by the invention, glazing effect have very
Strong metallic luster, adjustable formula make glaze at metallochromes such as golden yellow, silver color, grey blacks, and glaze is smooth, anti-in minute surface
It penetrates, gloss keeps lasting, with good stability, makes in addition without lead, chromium in this kind of noble metal glaze art pottery glaze
With safety.
Specific implementation mode
Below by way of specific implementation mode, the invention will be further described.
The glaze component of this noble metal glaze art pottery, the noble metal glaze art pottery is as follows:Lead free soldering
45-70 parts, 5-10 parts of calcite, 5-10 parts of kaolin, 5-10 parts of quartz, 5-10 parts of iron oxide yellow, MnO25-10 parts, NiO 1-10
Part, Al2O31-5 parts, CrO31-5 parts, ZrSiO41-5 parts, V2O51-5 parts, 1-5 parts of CuO, TiO21-3 parts, CMC 0.5-
1 part;
The composition of wherein lead free soldering is as follows:30-45 parts of potassium feldspar, 10-20 parts of zinc oxide, 5-10 parts of quartz, calcite
5-10,5-10 parts of barium carbonate, Al2O35-10 parts, WO35-10 parts, K21-5 parts of O, Na21-5 parts of O, Li21-5 parts of O.
Specific embodiment one:
The glaze component of the noble metal glaze art pottery is as follows:49 parts of lead free soldering, 6 parts of calcite, 6 parts of kaolin,
7 parts of quartz, 9 parts of iron oxide yellow, MnO26 parts, 2 parts of NiO, Al2O33 parts, CrO31 part, ZrSiO42 parts, V2O55 parts, CuO 1
Part, TiO22.5 parts, 0.5 part of CMC;
The composition of lead free soldering is as follows:42 parts of potassium feldspar, 18 parts of zinc oxide, quartz 6 parts, calcite 7,6 parts of barium carbonate,
Al2O35 parts, WO36 parts, K23 parts of O, Na22 parts of O, Li25 parts of O.
The noble metal glaze art pottery background color being burnt into the present embodiment has very strong metal in golden yellow, glazing effect
Gloss, glaze is smooth, is in mirror-reflection, and gloss keeps lasting, with good stability, in addition this kind of noble metal glaze art
It is safe to use without lead, chromium in ceramic glaze.
Specific embodiment two:
The glaze component of the noble metal glaze art pottery is as follows:53 parts of lead free soldering, 5 parts of calcite, 8 parts of kaolin,
6 parts of quartz, 5 parts of iron oxide yellow, MnO25 parts, 1 part of NiO, Al2O33 parts, CrO34 parts, ZrSiO42 parts, V2O51 part, CuO 5
Part, TiO21 part, 1 part of CMC;
The composition of lead free soldering is as follows:36 parts of potassium feldspar, 16 parts of zinc oxide, quartz 7 parts, calcite 8,8 parts of barium carbonate,
Al2O38 parts, WO37 parts, K23 parts of O, Na22 parts of O, Li25 parts of O.
The noble metal glaze art pottery background color being burnt into the present embodiment is in gold and silver color, and glazing effect has very strong metal
Gloss, glaze is smooth, is in mirror-reflection, and gloss keeps lasting, with good stability, in addition this kind of noble metal glaze art
It is safe to use without lead, chromium in ceramic glaze.
Specific embodiment three:
The glaze component of the noble metal glaze art pottery is as follows:62 parts of lead free soldering, 5 parts of calcite, 5 parts of kaolin,
5 parts of quartz, 8 parts of iron oxide yellow, MnO25 parts, 2 parts of NiO, Al2O32 parts, CrO31 part, ZrSiO41 part, V2O51 part, CuO 1
Part, TiO21 part, 1 part of CMC;
The composition of lead free soldering is as follows:40 parts of potassium feldspar, 16 parts of zinc oxide, quartz 8 parts, calcite 7,4 parts of barium carbonate,
Al2O39 parts, WO37 parts, K23 parts of O, Na23 parts of O, Li23 parts of O.
The noble metal glaze art pottery background color being burnt into the present embodiment is in grey black, and glazing effect has very strong metal
Gloss, glaze is smooth, is in mirror-reflection, and gloss keeps lasting, with good stability, in addition this kind of noble metal glaze art
It is safe to use without lead, chromium in ceramic glaze.
A kind of production method with the noble metal glaze art pottery, prepares the arbitrary noble metal of specific embodiment one or three
The glaze art pottery, is as follows:
Step 1, the shraff during Production of Ceramics is collected, shraff is cleaned, crushes, 1100- after sieving
1200 DEG C of high-temperature calcinations, for use;
Step 2, according to traditional shaping method of ceramics, ceramic body is produced;
Step 3, it weighs, mix according to the glaze component of noble metal glaze art pottery progress raw material, by raw material wet bulb
Mill, glaze crosses 200 mesh sieve after wet ball mill, obtains glaze, and when wet ball mill expects:Ball:Water=1:2:1:1-0.8,30-60 points of ball milling
Clock tails over 1%;
Step 4, ceramic body, is put into baking oven by the glazing on ceramic body, glaze thickness 0.3-0.5mm after glazing
It is toasted 5-20 hours in 45-50 DEG C, removal is for use;
Step 5, the ceramic body after glazing is put into kiln, is formed by a firing, firing temperature is 1200-1260 DEG C, is protected
Natural cooling after 30-60 minutes warm.
A specific implementation mode of the present invention is above are only, but the design concept of the present invention is not limited thereto, all utilizations
This design carries out the present invention change of unsubstantiality, should all belong to the behavior for invading the scope of the present invention.
Claims (7)
1. the noble metal glaze art pottery, which is characterized in that the glaze component of the noble metal glaze art pottery is as follows:It is unleaded
45-70 parts of frit, 5-10 parts of calcite, 5-10 parts of kaolin, 5-10 parts of quartz, 5-10 parts of iron oxide yellow, MnO25-10 parts, NiO1-
10 parts, Al2O31-5 parts, CrO31-5 parts, ZrSiO41-5 parts, V2O51-5 parts, 1-5 parts of CuO, TiO21-3 parts, CMC 0.5-1
Part;
The composition of wherein lead free soldering is as follows:30-45 parts of potassium feldspar, 10-20 parts of zinc oxide, 5-10 parts of quartz, calcite 5-10
Part, 5-10 parts of barium carbonate, Al2O35-10 parts, WO35-10 parts, K21-5 parts of O, Na21-5 parts of O, Li21-5 parts of O.
2. the noble metal glaze art pottery according to claim 1, which is characterized in that the noble metal glaze art pottery
Glaze component it is as follows:49 parts of lead free soldering, 6 parts of calcite, 6 parts of kaolin, 7 parts of quartz, 9 parts of iron oxide yellow, MnO26 parts, NiO 2
Part, Al2O33 parts, CrO31 part, ZrSiO42 parts, V2O55 parts, 1 part of CuO, TiO22.5 parts, 0.5 part of CMC.
3. the noble metal glaze art pottery according to claim 1 or 2, which is characterized in that the composition of the lead free soldering
It is as follows:42 parts of potassium feldspar, 18 parts of zinc oxide, 6 parts of quartz, 7 parts of calcite, 6 parts of barium carbonate, Al2O35 parts, WO36 parts, K2O 3
Part, Na22 parts of O, Li25 parts of O.
4. the noble metal glaze art pottery according to claim 1 or 2, which is characterized in that the composition of the lead free soldering
It is as follows:36 parts of potassium feldspar, 16 parts of zinc oxide, 7 parts of quartz, 8 parts of calcite, 8 parts of barium carbonate, Al2O38 parts, WO37 parts, K2O 3
Part, Na22 parts of O, Li25 parts of O.
5. the noble metal glaze art pottery according to claim 1, which is characterized in that the noble metal glaze art pottery
Glaze component it is as follows:62 parts of lead free soldering, 5 parts of calcite, 5 parts of kaolin, 5 parts of quartz, 8 parts of iron oxide yellow, MnO25 parts, NiO 2
Part, Al2O32 parts, CrO31 part, ZrSiO41 part, V2O51 part, 1 part of CuO, TiO21 part, 1 part of CMC.
6. a kind of production method with the noble metal glaze art pottery prepares your gold described in claim 1-5 any one
Belong to the glaze art pottery, is as follows:
Step 1, the shraff during Production of Ceramics is collected, shraff is cleaned, crushes, 1100-1200 DEG C after sieving
High-temperature calcination, for use;
Step 2, according to traditional shaping method of ceramics, ceramic body is produced;
Step 3, it weighs, mix according to the glaze component of noble metal glaze art pottery progress raw material, by raw material wet ball mill, wet bulb
Glaze crosses 200 mesh sieve after mill, obtains glaze;
Step 4, ceramic body is put into baking oven after glazing and is toasted 5-20 hours in 45-50 DEG C, gone by the glazing on ceramic body
Except for use;
Step 5, the ceramic body after glazing is put into kiln, is formed by a firing, firing temperature is 1200-1260 DEG C, keeps the temperature 30-
Natural cooling after sixty minutes.
7. the production method of the noble metal glaze art pottery according to claim 6, it is characterised in that:In the step 4,
Glaze thickness is 0.3-0.5mm.