CN109264994A - Unglazed golden metallic glaze and preparation method thereof - Google Patents
Unglazed golden metallic glaze and preparation method thereof Download PDFInfo
- Publication number
- CN109264994A CN109264994A CN201811107779.1A CN201811107779A CN109264994A CN 109264994 A CN109264994 A CN 109264994A CN 201811107779 A CN201811107779 A CN 201811107779A CN 109264994 A CN109264994 A CN 109264994A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- unglazed
- component
- oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of unglazed golden metallic glaze and preparation method thereof, the component and each component mass parts that glaze used in unglazed golden metallic glaze contains are as follows: potassium feldspar: 15-20 parts, albite: and 10-15 parts, calcite: 5-10 parts, wollastonite: 7-10 parts, aluminium powder: 8-10 parts, zinc oxide: 3-6 parts, barium carbonate: 2-4 parts, copper oxide: 1-2 parts, bismuth oxide: 1-3 parts, nickel oxide: 1-2 parts, manganese carbonate: 5-10 parts.Glaze paint of the invention has extremely beautiful unglazed gold, and intensity is high, and wear-resisting, low cost is applicable in vast household china, and porcelain can allow client more safe to use.
Description
Technical field
The present invention relates to a kind of unglazed golden metallic glaze and preparation method thereof.
Background technique
Currently, the moulding of porcelain billet is the basis of quality product in porcelain industry, the allotment of glaze keeps porcelain more gorgeous
Colorful, the porcelain billet of same moulding often because of the difference of glaze paint, and generates different influences to the vision of consumer.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies of existing technologies, a kind of unglazed golden metallic glaze is provided,
Its glaze paint has extremely beautiful unglazed gold, and intensity is high, wear-resisting, low cost, is applicable in vast household china, porcelain,
Client can be allowed more safe to use.
In order to solve the above technical problems, the technical scheme is that a kind of unglazed golden metallic glaze, used in it
The component and each component mass parts that glaze contains are as follows:
Potassium feldspar: 15-20 parts,
Albite: 10-15 parts,
Calcite: 5-10 parts,
Wollastonite: 7-10 parts,
Aluminium powder: 8-10 parts,
Zinc oxide: 3-6 parts,
Barium carbonate: 2-4 parts,
Copper oxide: 1-2 parts,
Bismuth oxide: 1-3 parts,
Nickel oxide: 1-2 parts,
Manganese carbonate: 5-10 parts.
The present invention also provides a kind of preparation method of unglazed golden metallic glaze, the step of method in contain:
S1: it stocks up according to the component and each component mass parts of glaze；
S2: press glaze: ball: mass ratio=1:1:1.5 of water, wet ball grinding 15~18 hours, the glaze after ball milling crossed 325
Mesh, then it is tuned into the glaze slip of 40~45 Baume degrees；
S3: after the chinaware body for taking appearance bright and clean immerses the glaze slip, through being fired under 1290 DEG C -1330 DEG C of oxidizing atmospheres
Product.
After above-mentioned technical proposal, the glaze paint of unglazed golden metallic glaze of the invention has extremely beautiful matt gold
Color, intensity is high, and wear-resisting, low cost is applicable in vast household china, and porcelain can allow client more safe to use.
Specific embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, to the present invention make into
One step detailed description.
Embodiment one
A kind of unglazed golden metallic glaze, the component and each component mass parts that glaze used in it contains are as follows:
Potassium feldspar: 15 parts,
Albite: 10 parts,
Calcite: 5 parts,
Wollastonite: 7 parts,
Aluminium powder: 8 parts,
Zinc oxide: 3 parts,
Barium carbonate: 2 parts,
Copper oxide: 1 part,
Bismuth oxide: 1 part,
Nickel oxide: 1 part,
Manganese carbonate: 5 parts.
Contain in the step of preparation method of this is unglazed golden metallic glaze, method:
S1: it stocks up according to the component and each component mass parts of glaze；
S2: press glaze: ball: mass ratio=1:1:1.5 of water, wet ball grinding 15 hours, the glaze after ball milling crossed 325 mesh
Sieve, then it is tuned into the glaze slip of 40~45 Baume degrees；
S3: after the chinaware body for taking appearance bright and clean immerses the glaze slip, through being fired under 1290 DEG C -1330 DEG C of oxidizing atmospheres
Product.
Embodiment two
A kind of unglazed golden metallic glaze, the component and each component mass parts that glaze used in it contains are as follows:
Potassium feldspar: 20 parts,
Albite: 15 parts,
Calcite: 10 parts,
Wollastonite: 10 parts,
Aluminium powder: 10 parts,
Zinc oxide: 6 parts,
Barium carbonate: 4 parts,
Copper oxide: 2 parts,
Bismuth oxide: 3 parts,
Nickel oxide: 2 parts,
Manganese carbonate: 10 parts.
Contain in the step of preparation method of this is unglazed golden metallic glaze, method:
S1: it stocks up according to the component and each component mass parts of glaze；
S2: press glaze: ball: mass ratio=1:1:1.5 of water, wet ball grinding 18 hours, the glaze after ball milling crossed 325 mesh
Sieve, then it is tuned into the glaze slip of 40~45 Baume degrees；
S3: after the chinaware body for taking appearance bright and clean immerses the glaze slip, through being fired under 1290 DEG C -1330 DEG C of oxidizing atmospheres
Product.
Embodiment three
A kind of unglazed golden metallic glaze, the component and each component mass parts that glaze used in it contains are as follows:
Potassium feldspar: 17 parts,
Albite: 12 parts,
Calcite: 8 parts,
Wollastonite: 8 parts,
Aluminium powder: 9 parts,
Zinc oxide: 5 parts,
Barium carbonate: 3 parts,
Copper oxide: 2 parts,
Bismuth oxide: 2 parts,
Nickel oxide: 1 part,
Manganese carbonate: 8 parts.
Contain in the step of preparation method of this is unglazed golden metallic glaze, method:
S1: it stocks up according to the component and each component mass parts of glaze；
S2: press glaze: ball: mass ratio=1:1:1.5 of water, wet ball grinding 17 hours, the glaze after ball milling crossed 325 mesh
Sieve, then it is tuned into the glaze slip of 40~45 Baume degrees；
S3: after the chinaware body for taking appearance bright and clean immerses the glaze slip, through being fired under 1290 DEG C -1330 DEG C of oxidizing atmospheres
Product.
The unglazed golden metallic glaze that three above embodiment is prepared, by it has been observed that its glaze paint all has extremely
Beautiful unglazed gold, meets design requirement.
Particular embodiments described above has carried out further in detail the purpose of the present invention, technical scheme and beneficial effects
It describes in detail bright, it should be understood that the above is only a specific embodiment of the present invention, is not intended to restrict the invention, it is all
Within the spirit and principles in the present invention, any modification, equivalent substitution, improvement and etc. done should be included in guarantor of the invention
Within the scope of shield.
Claims (2)
1. a kind of unglazed golden metallic glaze, it is characterised in that the component and each component mass parts that glaze used in it contains are such as
Under:
Potassium feldspar: 15-20 parts,
Albite: 10-15 parts,
Calcite: 5-10 parts,
Wollastonite: 7-10 parts,
Aluminium powder: 8-10 parts,
Zinc oxide: 3-6 parts,
Barium carbonate: 2-4 parts,
Copper oxide: 1-2 parts,
Bismuth oxide: 1-3 parts,
Nickel oxide: 1-2 parts,
Manganese carbonate: 5-10 parts.
2. a kind of preparation method of unglazed golden metallic glaze as described in claim 1, it is characterised in that contain in the step of method
Have:
S1: it stocks up according to the component and each component mass parts of glaze；
S2: press glaze: ball: mass ratio=1:1:1.5 of water, wet ball grinding 15~18 hours, the glaze after ball milling crossed 325 mesh
Sieve, then it is tuned into the glaze slip of 40~45 Baume degrees；
S3: after the chinaware body for taking appearance bright and clean immerses the glaze slip, through firing finished product under 1290 DEG C -1330 DEG C of oxidizing atmospheres.