CN103332861A - Preparation method of metallic luster glaze - Google Patents
Preparation method of metallic luster glaze Download PDFInfo
- Publication number
- CN103332861A CN103332861A CN201310273810XA CN201310273810A CN103332861A CN 103332861 A CN103332861 A CN 103332861A CN 201310273810X A CN201310273810X A CN 201310273810XA CN 201310273810 A CN201310273810 A CN 201310273810A CN 103332861 A CN103332861 A CN 103332861A
- Authority
- CN
- China
- Prior art keywords
- glaze
- metal
- metallic luster
- preparation
- weighing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a preparation method of a metallic luster glaze, which comprises the following steps: (1) respectively weighing the following substances in percentage by weight: 5-30% of quartz, 20-50% of feldspar, 2-20% of limestone, 2-20% of dolomite, 2-20% of barium carbonate, 2-20% of zinc oxide and 2-10% of lead silicate, and then evenly mixing; (2) fusing the mixture prepared in the step (1) at 1200-1400 DEG C, and performing water quenching to obtain a basic glaze fused block; and (3) weighing the following substances in percentage by weight: 70-90% of basic glaze fused block, 1-10% of kaolin, 1-11% of MnO2, 1-10% of TiO2, 1-10% of CuO and 1-10% of NiO, then mixing, and integrally performing coarse crushing, fine crushing and ingredient grinding sequentially; and evenly mixing to obtain the metallic luster glaze. The metallic luster glaze provided by the invention is brilliant and bright in color; platinum and gold metallic luster can be obtained by changing the composition of the metal glaze; and the method and the process are simple and are very suitable for production and manufacturing of wall bricks.
Description
Technical field
The present invention relates to construction sanitary ceramic decoration technique field, especially relate to a kind of preparation method of metal-lustrous glaze.
Background technology
In the prior art, in nineteen ninety, professors Chen Xianqiu of Shanghai Inst. of Silicate, Chinese Academy of Sciences etc. studies show that its gloss derives from ferro-cobalt spinel crystallite at the reflectance signature that is parallel on the implements surface direction in the microstructure analysis of blue or green uranium pottery " imitative " literary composition.This mainly be veil density bigger 1,1,1} crystal face with the surface strict parallel, light is presented strong reflection.The grain size of these crystallites, distribution, integrated degree can both influence metalluster.The cardinal principle of metal-lustrous glaze is in the raw material of certain component, adds the coloring metal oxide compound, as
,
,
,
And
Deng, make it when burning till cooling, separate out crystal because of supersaturation, produce the metalluster of various different-effects.As the patent No.: 200710008547.6, patent name is a kind of metal glaze production method, and its technology is simple, only suitable metal glaze brick modelled after an antique, but similarly the tone of metal-lustrous glaze is bright-coloured inadequately, not too is fit to bright, the bright-coloured requirement of the desired tone of interior wall ornamental brick.
Summary of the invention
The objective of the invention is to solve the problems of the prior art, be colour-stable, bright in luster and provide a kind of, the preparation method of the simple metal-lustrous glaze of technology.
The technical solution adopted in the present invention is such: a kind of preparation method of metal-lustrous glaze may further comprise the steps:
(1), by weight percentage with 5%～30% quartz, 20%～50% feldspar, 2%～20% Wingdale, 2%～20% rhombspar, 2%～20% barium carbonate, 2%～20% zinc oxide and 2%～10% lead silicate, mix after taking by weighing each material;
(2), with the prepared mixture of step (1), carry out 1200 ℃-1400 ℃ found after, after shrend, obtain the parent glaze frit;
(3), by weight percentage with 70%～90% parent glaze frit, 1%～10% kaolin, 1%～11%
, 1%～10%
, 1%～10%
, 1%～10%
, each material takes by weighing the back to be mixed, and integral body is successively through coarse crushing, in small, broken bits, batching grinding; Mix and to make metal-lustrous glaze.
Preferably, the fineness of described metal-lustrous glaze is less than 2% through the 10000-hole sieve excess.
By adopting the aforementioned techniques scheme, the invention has the beneficial effects as follows: this metal-lustrous glaze is can colour generation bright-coloured bright, and the composition that changes metal glaze can obtain the metalluster of platinum look and gold look.Ball milling is even in proportion with the metalluster glaze; And add 0.3% Xylo-Mucine, in glaze: the ratio of ball milling value: water=1:1.2:0.5 is made glaze slip, evenly imposes on the biscuit surface, thickness 0.2-1mm; Wherein the ball milling value is the diameter of the ball of zirconium white or aluminum oxide material, the fineness of the corresponding meeting of the diameter value of different ball milling ectocrine abrasive lapping.Dry by 1050-1200 ℃, firing time 1 hour is fired gold look and the platinum non-ferrous metal gloss glaze that can obtain the tone beauty respectively; Method technology is simple, is fit to very much the manufacturing of wall brick.
Embodiment
Describe the present invention particularly with embodiment below, scope of the present invention is not subjected to the restriction of embodiment.
Embodiment 1
(1), by weight percentage with 17% quartz, 46% feldspar, 14% Wingdale, 5% rhombspar, 4% barium carbonate, 6% zinc oxide and 8% lead silicate, mix after taking by weighing each material;
(2), with the prepared mixture of step (1), through 1350 ℃ found after, shrend obtains basic glaze frit;
(3), by weight percentage with 78% parent glaze frit, 5% kaolin, 10.5%
, 3%
, 1.7%
, 1.8%
, each material takes by weighing the back to be mixed, and integral body is successively through coarse crushing, in small, broken bits, batching grinding; Mix the metal-lustrous glaze that makes the gold look.
Embodiment 2
(1), by weight percentage with 17% quartz, 46% feldspar, 14% Wingdale, 5% rhombspar, 4% barium carbonate, 6% zinc oxide and 8% lead silicate, mix after taking by weighing each material;
(2), with the prepared mixture of step (1), through 1350 ℃ found after, shrend obtains basic glaze frit;
(3), by weight percentage with 78% parent glaze frit, 5% kaolin, 8.5%
, 5.8%
, 1.5%
, 1.2%
, each material takes by weighing the back to be mixed, and integral body is successively through coarse crushing, in small, broken bits, batching grinding; Mix the metal-lustrous glaze that makes the platinum look.
In proportion by the even mixed grinding of ball mill, fineness is less than 2% through the 10000-hole sieve excess with above-mentioned metal-lustrous glaze; With metal-lustrous glaze in conjunction with the Xylo-Mucine that adds 0.3%, in glaze: the ratio of ball: water=1:1.2:0.5 is made glaze slip; It is evenly imposed on the biscuit surface, guarantee that the thickness of glazing is 0.2-1mm; Wherein the ball milling value is the diameter of the ball of zirconium white or aluminum oxide material, the fineness of the corresponding meeting of the diameter value of different ball milling ectocrine abrasive lapping.Dry calcining by 1050 ℃-1200 ℃, firing time is 1 hour, can obtain the platinum non-ferrous metal gloss glaze of tone beauty.
Above-described, only be preferred embodiment of the present invention, can not limit scope of the invention process, every equalization of doing according to the present patent application claim changes and decorates, and all should still belong in the scope that the present invention contains.
Claims (2)
1. the preparation method of a metal-lustrous glaze is characterized in that: may further comprise the steps:
(1), by weight percentage with 5%～30% quartz, 20%～50% feldspar, 2%～20% Wingdale, 2%～20% rhombspar, 2%～20% barium carbonate, 2%～20% zinc oxide and 2%～10% lead silicate, mix after taking by weighing each material;
(2), with the prepared mixture of step (1), carry out 1200 ℃-1400 ℃ found after, after shrend, obtain the parent glaze frit;
(3), by weight percentage with 70%～90% parent glaze frit, 1%～10% kaolin, 1%～11%
, 1%～10%
, 1%～10%
, 1%～10%
, each material takes by weighing the back to be mixed, and integral body is successively through coarse crushing, in small, broken bits, batching grinding; Mix and to make metal-lustrous glaze.
2. the preparation method of a kind of metal-lustrous glaze according to claim 1 is characterized in that: the fineness of described metal-lustrous glaze for through the 10000-hole sieve excess less than 2%.