CN107698152A - A kind of golden glazed tiles glaze - Google Patents

A kind of golden glazed tiles glaze Download PDF

Info

Publication number
CN107698152A
CN107698152A CN201711239867.2A CN201711239867A CN107698152A CN 107698152 A CN107698152 A CN 107698152A CN 201711239867 A CN201711239867 A CN 201711239867A CN 107698152 A CN107698152 A CN 107698152A
Authority
CN
China
Prior art keywords
parts
golden
glaze
glazed tiles
raw material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201711239867.2A
Other languages
Chinese (zh)
Inventor
符绩承
吴锡银
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanning Shengrun Technology Co Ltd
Original Assignee
Nanning Shengrun Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanning Shengrun Technology Co Ltd filed Critical Nanning Shengrun Technology Co Ltd
Priority to CN201711239867.2A priority Critical patent/CN107698152A/en
Publication of CN107698152A publication Critical patent/CN107698152A/en
Withdrawn legal-status Critical Current

Abstract

The present invention relates to a kind of golden glazed tiles glaze, is made up of potassium albite, white glass, the bright material of pearl, dolomite, iron oxide, glaze fruit, green glass, tin frit, red lead.The present invention a kind of water resistance, the weatherability of golden glazed tiles glaze is good, high mechanical strength;A kind of golden glazed tiles glaze of the present invention is easily modulated, bright in luster, and manufacturing cost is low;A kind of golden waterproof thermal-insulated effect of glazed tiles glaze of the present invention is good, applied widely, has good promotional value.

Description

A kind of golden glazed tiles glaze
Technical field
The present invention relates to glaze manufacturing technology field, more particularly to a kind of golden glazed tiles glaze.
Background technology
Glaze is a kind of silicate, and the glaze applied on ware is typically using quartz, feldspar, clay as raw material, ground plus water After modulation, coated on billet surface, melted through the roasting of certain temperature, when the temperature drops, forming the nature of glass of ceramic surface Thin layer.It makes ware increase mechanical strength, heat endurance, dielectric strength and the erosion for preventing liquid, gas.Glaze also has increase Porcelain is attractive in appearance and is easy to wash and wipes, the effect such as is not sticky with by dust.Glazed tiles are to use high-quality ore, are crushed by screening, High-pressure molding, high-temperature firing form.With intensity is high, flatness is good, water absorption rate is low, anti-folding, it is freeze proof, acidproof, alkaline-resisting, never take off Color, etc. remarkable advantage.The industry such as factory building, house, hotel, villa and civil buildings are widely used in, and with its various shapes, glaze Chromaticness is plain, colorful, environmentally friendly, durable, firmly gets the high praise of building great masters.Current golden glazed tiles glaze modulated process is more multiple Miscellaneous, cost is higher, and is easily modulated into khaki, and color is not bright-coloured enough.
The content of the invention
It is an object of the invention to:For above-mentioned problem, there is provided one kind modulation is simple, bright in luster, is manufactured into This low golden glazed tiles glaze.
The present invention is achieved by the following technical solutions:
A kind of golden glazed tiles glaze, is made up of the component of following parts by weight:58~60 parts of potassium albite, white glass 10~15 Part, 20~25 parts of the bright material of pearl, 20~25 parts of dolomite, 15~20 parts of iron oxide, 15~20 parts of glaze fruit, 15~20 parts of green glass, 3~4 parts of tin frit, 1~3 part of red lead;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into powder Broken machine, the mesh of 300 mesh~320 is crushed to, obtains hybrid particles;B, hybrid particles are stirred, it is molten at 1350 DEG C~1500 DEG C Change, and be incubated 2h~4h;C, it is put into quench in the water that temperature is 15 DEG C~18 DEG C and frit is made, then vibration of ultrasonic wave 5min~ 8min, produce the golden glazed tiles glaze.
Preferably, a kind of golden glazed tiles glaze, is made up of the component of following parts by weight:58 parts of potassium albite, white glass 20 parts of the bright material of 10 parts of glass, pearl, 20 parts of dolomite, 15 parts of iron oxide, 15 parts of glaze fruit, 15 parts of green glass, 3 parts of tin frit, red lead 1 Part;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, 300 mesh is crushed to, obtains Hybrid particles;B, hybrid particles are stirred, in 1350 DEG C of fusings, and is incubated 2h;C, it is put into the water that temperature is 15 DEG C and quenches Frit, then vibration of ultrasonic wave 5min is made, produces the golden glazed tiles glaze.
Preferably, a kind of golden glazed tiles glaze, is made up of the component of following parts by weight:60 parts of potassium albite, white glass 25 parts of the bright material of 15 parts of glass, pearl, 25 parts of dolomite, 20 parts of iron oxide, 20 parts of glaze fruit, 20 parts of green glass, 4 parts of tin frit, red lead 3 Part;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, 320 mesh is crushed to, obtains Hybrid particles;B, hybrid particles are stirred, in 1500 DEG C of fusings, and is incubated 4h;C, it is put into the water that temperature is 18 DEG C and quenches Frit, then vibration of ultrasonic wave 8min is made, produces the golden glazed tiles glaze.
Preferably, a kind of golden glazed tiles glaze, is made up of the component of following parts by weight:59 parts of potassium albite, white glass 22 parts of the bright material of 12 parts of glass, pearl, 23 parts of dolomite, 18 parts of iron oxide, 18 parts of glaze fruit, 17 parts of green glass, 3.5 parts of tin frit, red lead 2 parts;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, 310 mesh is crushed to, obtains Hybrid particles;B, hybrid particles are stirred, in 1450 DEG C of fusings, and is incubated 3h;C, it is put into the water that temperature is 16 DEG C and quenches Frit, then vibration of ultrasonic wave 6min is made, produces the golden glazed tiles glaze.
The raw material being related in this application can obtain in buying on the market.
The beneficial effects of the invention are as follows:
1. the present invention a kind of water resistance, the weatherability of golden glazed tiles glaze is good, high mechanical strength.
2. a kind of golden glazed tiles glaze of the present invention is easily modulated, bright in luster, and manufacturing cost is low.
3. a kind of golden waterproof thermal-insulated effect of glazed tiles glaze of the present invention is good, applied widely, there is good promotion price Value.
Embodiment
This specification(Including any accessory claim, summary)Disclosed in any feature, unless specifically stated otherwise, Replaced by other equivalent or with similar purpose alternative features.I.e., unless specifically stated otherwise, each feature is a series of An example in equivalent or similar characteristics.
Embodiment 1:
A kind of golden glazed tiles glaze, is made up of the component of following parts by weight:58 parts of potassium albite, 10 parts of white glass, pearl are bright 20 parts of material, 20 parts of dolomite, 15 parts of iron oxide, 15 parts of glaze fruit, 15 parts of green glass, 3 parts of tin frit, 1 part of red lead;Preparation process It is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, 300 mesh is crushed to, obtains hybrid particles;B、 Hybrid particles are stirred, in 1350 DEG C of fusings, and are incubated 2h;C, it is put into quench in the water that temperature is 15 DEG C and frit is made, then Vibration of ultrasonic wave 5min, produce the golden glazed tiles glaze.
Embodiment 2:
A kind of golden glazed tiles glaze, is made up of the component of following parts by weight:60 parts of potassium albite, 15 parts of white glass, pearl are bright 25 parts of material, 25 parts of dolomite, 20 parts of iron oxide, 20 parts of glaze fruit, 20 parts of green glass, 4 parts of tin frit, 3 parts of red lead;Preparation process It is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, 320 mesh is crushed to, obtains hybrid particles;B、 Hybrid particles are stirred, in 1500 DEG C of fusings, and are incubated 4h;C, it is put into quench in the water that temperature is 18 DEG C and frit is made, then Vibration of ultrasonic wave 8min, produce the golden glazed tiles glaze.
Embodiment 3:
A kind of golden glazed tiles glaze, is made up of the component of following parts by weight:59 parts of potassium albite, 12 parts of white glass, pearl are bright 22 parts of material, 23 parts of dolomite, 18 parts of iron oxide, 18 parts of glaze fruit, 17 parts of green glass, 3.5 parts of tin frit, 2 parts of red lead;Prepare step It is rapid as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, 310 mesh is crushed to, obtains hybrid particles; B, hybrid particles are stirred, in 1450 DEG C of fusings, and is incubated 3h;C, it is put into quench in the water that temperature is 16 DEG C and frit is made, Vibration of ultrasonic wave 6min again, produce the golden glazed tiles glaze.
Although above the present invention is described in detail with a general description of the specific embodiments, On the basis of the present invention, it can be made some modifications or improvements, this will be apparent to those skilled in the art.Cause This, these modifications or improvements, belong to the scope of protection of present invention without departing from theon the basis of the spirit of the present invention.

Claims (4)

  1. A kind of 1. golden glazed tiles glaze, it is characterised in that:It is made up of the component of following parts by weight:Potassium albite 58~60 Part, 10~15 parts of white glass, 20~25 parts of the bright material of pearl, 20~25 parts of dolomite, 15~20 parts of iron oxide, 15~20 parts of glaze fruit, 15~20 parts of green glass, 3~4 parts of tin frit, 1~3 part of red lead;Preparation process is as follows:A, raw material is measured according to parts by weight, will be upper State raw material and add pulverizer, be crushed to the mesh of 300 mesh~320, obtain hybrid particles;B, hybrid particles are stirred, 1350 DEG C~1500 DEG C fusings, and it is incubated 2h~4h;C, it is put into quench in the water that temperature is 15 DEG C~18 DEG C and frit is made, then ultrasound Ripple shakes 5min~8min, produces the golden glazed tiles glaze.
  2. A kind of 2. golden glazed tiles glaze according to claim 1, it is characterised in that:It is the component group by following parts by weight Into:58 parts of potassium albite, 10 parts of white glass, 20 parts of the bright material of pearl, 20 parts of dolomite, 15 parts of iron oxide, 15 parts of glaze fruit, green glass 15 parts, 3 parts of tin frit, 1 part of red lead;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added and crushed Machine, 300 mesh are crushed to, obtain hybrid particles;B, hybrid particles are stirred, in 1350 DEG C of fusings, and is incubated 2h;C, it is put into Temperature is to quench that frit is made in 15 DEG C of water, then vibration of ultrasonic wave 5min, produces the golden glazed tiles glaze.
  3. A kind of 3. golden glazed tiles glaze according to claim 1, it is characterised in that:It is the component group by following parts by weight Into:60 parts of potassium albite, 15 parts of white glass, 25 parts of the bright material of pearl, 25 parts of dolomite, 20 parts of iron oxide, 20 parts of glaze fruit, green glass 20 parts, 4 parts of tin frit, 3 parts of red lead;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added and crushed Machine, 320 mesh are crushed to, obtain hybrid particles;B, hybrid particles are stirred, in 1500 DEG C of fusings, and is incubated 4h;C, it is put into Temperature is to quench that frit is made in 18 DEG C of water, then vibration of ultrasonic wave 8min, produces the golden glazed tiles glaze.
  4. A kind of 4. golden glazed tiles glaze according to claim 1, it is characterised in that:It is the component group by following parts by weight Into:59 parts of potassium albite, 12 parts of white glass, 22 parts of the bright material of pearl, 23 parts of dolomite, 18 parts of iron oxide, 18 parts of glaze fruit, green glass 17 parts, 3.5 parts of tin frit, 2 parts of red lead;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into powder Broken machine, 310 mesh are crushed to, obtain hybrid particles;B, hybrid particles are stirred, in 1450 DEG C of fusings, and is incubated 3h;C, put Enter to quench in the water that temperature is 16 DEG C and frit is made, then vibration of ultrasonic wave 6min, produce the golden glazed tiles glaze.
CN201711239867.2A 2017-11-30 2017-11-30 A kind of golden glazed tiles glaze Withdrawn CN107698152A (en)