CN107915407A - A kind of black glazed tiles glaze - Google Patents

A kind of black glazed tiles glaze Download PDF

Info

Publication number
CN107915407A
CN107915407A CN201711239853.0A CN201711239853A CN107915407A CN 107915407 A CN107915407 A CN 107915407A CN 201711239853 A CN201711239853 A CN 201711239853A CN 107915407 A CN107915407 A CN 107915407A
Authority
CN
China
Prior art keywords
parts
glaze
glazed tiles
black glazed
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201711239853.0A
Other languages
Chinese (zh)
Inventor
符绩承
吴锡银
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanning Shengrun Technology Co Ltd
Original Assignee
Nanning Shengrun Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanning Shengrun Technology Co Ltd filed Critical Nanning Shengrun Technology Co Ltd
Priority to CN201711239853.0A priority Critical patent/CN107915407A/en
Publication of CN107915407A publication Critical patent/CN107915407A/en
Withdrawn legal-status Critical Current

Abstract

The present invention relates to a kind of black glazed tiles glaze, is made of potassium albite, white glass, quartz, kaolin, cobaltosic oxide, glaze fruit, green glass, tin frit, manganese oxide.Expansion coefficient difference between a kind of base glaze of black glazed tiles glaze of the present invention is small, and glaze paint is less prone to cracking, collapses phenomena such as stripping;A kind of black glazed tiles glaze performance of the present invention is stablized, and good water-proof effect, has good promotional value;A kind of black glazed tiles glaze preparation process of the present invention is simple, and color changeable effect is good, and performance is stablized, and the cost for preparing the black glazed tiles glaze is low.

Description

A kind of black glazed tiles glaze
Technical field
The present invention relates to glaze manufacturing technology field, more particularly to a kind of black glazed tiles glaze.
Background technology
Glaze is a kind of silicate, and the glaze applied on ware is generally using quartz, feldspar, clay as raw material, ground plus water After modulation, coated on billet surface, melted through the roasting of certain temperature, when the temperature drops, forming the nature of glass of ceramic surface Thin layer.It makes ware increase mechanical strength, heat endurance, dielectric strength and the erosion for preventing liquid, gas.Glaze also has increase Porcelain is beautiful and wipes easy to wash, the effect such as is not sticky with by dust.Glazed tiles are to use high-quality ore raw materials, are crushed by screening, High-pressure molding, high-temperature firing form.With intensity is high, flatness is good, water absorption rate is low, anti-folding, it is freeze proof, acidproof, alkaline-resisting, never take off Color, etc. remarkable advantage.The industry such as workshop, house, hotel, villa and civil buildings are widely used in, and with its various shapes, glaze Chromaticness is plain, colorful, environmentally friendly, durable, firmly gets the high praise of building great masters.At present can be due between the base glaze of poor quality glazed tiles glaze Expansion coefficient difference is larger, and glaze layer is thicker, and glaze layer internal stress is larger, causes product glaze paint cracking occur, collapse the defects of stripping. Using effect is poor, is unfavorable for promoting the use of for glazed tiles glaze.
The content of the invention
It is an object of the invention to:For above-mentioned problem, there is provided one kind is not easy to peel off, preparation process is simple, system Cause this low black glazed tiles glaze.
The present invention is achieved by the following technical solutions:
A kind of black glazed tiles glaze, is made of the component of following parts by weight:55~58 parts of potassium albite, white glass 10~15 Part, 20~25 parts of quartz, 20~25 parts of kaolin, 15~20 parts of cobaltosic oxide, 15~20 parts of glaze fruit, green glass 15~20 Part, 3~4 parts of tin frit, 1~3 part of manganese oxide;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added Enter pulverizer, be crushed to the mesh of 300 mesh~320, obtain hybrid particles;B, hybrid particles are stirred evenly, 1350 DEG C~1500 DEG C fusing, and keeps the temperature 2h~4h;C, it is put into quench in the water that temperature is 15 DEG C~18 DEG C and frit is made, then vibration of ultrasonic wave 5min~ 8min, up to the black glazed tiles glaze.
Preferably, a kind of black glazed tiles glaze, is made of the component of following parts by weight:55 parts of potassium albite, white glass 10 parts of glass, 20 parts of quartz, 20 parts of kaolin, 15 parts of cobaltosic oxide, 15 parts of glaze fruit, 15 parts of green glass, 3 parts of tin frit, oxidation 1 part of manganese;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, 300 mesh is crushed to, obtains To hybrid particles;B, hybrid particles are stirred evenly, in 1350 DEG C of fusings, and keeps the temperature 2h;C, it is put into the water that temperature is 15 DEG C Quench and frit is made, then vibration of ultrasonic wave 5min, up to the black glazed tiles glaze.
Preferably, a kind of black glazed tiles glaze, is made of the component of following parts by weight:58 parts of potassium albite, white glass 15 parts of glass, 25 parts of quartz, 25 parts of kaolin, 20 parts of cobaltosic oxide, 20 parts of glaze fruit, 20 parts of green glass, 4 parts of tin frit, oxidation 3 parts of manganese;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, 320 mesh is crushed to, obtains To hybrid particles;B, hybrid particles are stirred evenly, in 1500 DEG C of fusings, and keeps the temperature 4h;C, it is put into the water that temperature is 18 DEG C Quench and frit is made, then vibration of ultrasonic wave 8min, up to the black glazed tiles glaze.
Preferably, a kind of black glazed tiles glaze, is made of the component of following parts by weight:56 parts of potassium albite, white glass 12 parts of glass, 22 parts of quartz, 23 parts of kaolin, 18 parts of cobaltosic oxide, 18 parts of glaze fruit, 17 parts of green glass, 3.5 parts of tin frit, oxygen Change 2 parts of manganese;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, are crushed to 310 mesh, Obtain hybrid particles;B, hybrid particles are stirred evenly, in 1450 DEG C of fusings, and keeps the temperature 3h;C, it is put into the water that temperature is 16 DEG C In quench frit be made, then vibration of ultrasonic wave 6min, up to the black glazed tiles glaze.
The raw material being related in this application can be obtained in buying on the market.
The beneficial effects of the invention are as follows:
1. the expansion coefficient difference between a kind of base glaze of black glazed tiles glaze of the present invention is small, glaze paint is less prone to cracking, collapses Phenomena such as stripping.
2. a kind of black glazed tiles glaze performance of the present invention is stablized, good water-proof effect, has good promotional value.
3. a kind of black glazed tiles glaze preparation process of the present invention is simple, color changeable effect is good, and performance is stablized, and prepares and be somebody's turn to do The cost of black glazed tiles glaze is low.
Embodiment
This specification(Including any accessory claim, summary)Disclosed in any feature, unless specifically stated, Replaced by other equivalent or with similar purpose alternative features.I.e., unless specifically stated, each feature is a series of An example in equivalent or similar characteristics.
Embodiment 1:
A kind of black glazed tiles glaze, is made of the component of following parts by weight:55 parts of potassium albite, 10 parts of white glass, quartz 20 parts, 20 parts of kaolin, 15 parts of cobaltosic oxide, 15 parts of glaze fruit, 15 parts of green glass, 3 parts of tin frit, 1 part of manganese oxide;Prepare Step is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, are crushed to 300 mesh, obtain mixing Grain;B, hybrid particles are stirred evenly, in 1350 DEG C of fusings, and keeps the temperature 2h;C, be put into temperature be quench in 15 DEG C of water be made it is molten Block, then vibration of ultrasonic wave 5min, up to the black glazed tiles glaze.
Embodiment 2:
A kind of black glazed tiles glaze, is made of the component of following parts by weight:58 parts of potassium albite, 15 parts of white glass, quartz 25 parts, 25 parts of kaolin, 20 parts of cobaltosic oxide, 20 parts of glaze fruit, 20 parts of green glass, 4 parts of tin frit, 3 parts of manganese oxide;Prepare Step is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, are crushed to 320 mesh, obtain mixing Grain;B, hybrid particles are stirred evenly, in 1500 DEG C of fusings, and keeps the temperature 4h;C, be put into temperature be quench in 18 DEG C of water be made it is molten Block, then vibration of ultrasonic wave 8min, up to the black glazed tiles glaze.
Embodiment 3:
A kind of black glazed tiles glaze, is made of the component of following parts by weight:56 parts of potassium albite, 12 parts of white glass, quartz 22 parts, 23 parts of kaolin, 18 parts of cobaltosic oxide, 18 parts of glaze fruit, 17 parts of green glass, 3.5 parts of tin frit, 2 parts of manganese oxide;System Standby step is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, are crushed to 310 mesh, obtain mixing Grain;B, hybrid particles are stirred evenly, in 1450 DEG C of fusings, and keeps the temperature 3h;C, be put into temperature be quench in 16 DEG C of water be made it is molten Block, then vibration of ultrasonic wave 6min, up to the black glazed tiles glaze.
Although above the present invention is described in detail with a general description of the specific embodiments, On the basis of the present invention, it can be made some modifications or improvements, this will be apparent to those skilled in the art.Cause This, these modifications or improvements, belong to the scope of protection of present invention without departing from theon the basis of the spirit of the present invention.

Claims (4)

  1. A kind of 1. black glazed tiles glaze, it is characterised in that:It is made of the component of following parts by weight:Potassium albite 55~58 Part, 10~15 parts of white glass, 20~25 parts of quartz, 20~25 parts of kaolin, 15~20 parts of cobaltosic oxide, glaze fruit 15~20 Part, 15~20 parts of green glass, 3~4 parts of tin frit, 1~3 part of manganese oxide;Preparation process is as follows:A, measured according to parts by weight former Above-mentioned raw material are added pulverizer, are crushed to the mesh of 300 mesh~320, obtain hybrid particles by material;B, hybrid particles are stirred equal It is even, in 1350 DEG C~1500 DEG C fusings, and keep the temperature 2h~4h;C, it is put into quench in the water that temperature is 15 DEG C~18 DEG C and frit is made, Vibration of ultrasonic wave 5min~8min again, up to the black glazed tiles glaze.
  2. A kind of 2. black glazed tiles glaze according to claim 1, it is characterised in that:It is the component group by following parts by weight Into:55 parts of potassium albite, 10 parts of white glass, 20 parts of quartz, 20 parts of kaolin, 15 parts of cobaltosic oxide, 15 parts of glaze fruit, green glass 15 parts of glass, 3 parts of tin frit, 1 part of manganese oxide;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added Pulverizer, is crushed to 300 mesh, obtains hybrid particles;B, hybrid particles are stirred evenly, in 1350 DEG C of fusings, and keeps the temperature 2h;C、 It is put into quench in the water that temperature is 15 DEG C and frit is made, then vibration of ultrasonic wave 5min, up to the black glazed tiles glaze.
  3. A kind of 3. black glazed tiles glaze according to claim 1, it is characterised in that:It is the component group by following parts by weight Into:58 parts of potassium albite, 15 parts of white glass, 25 parts of quartz, 25 parts of kaolin, 20 parts of cobaltosic oxide, 20 parts of glaze fruit, green glass 20 parts of glass, 4 parts of tin frit, 3 parts of manganese oxide;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added Pulverizer, is crushed to 320 mesh, obtains hybrid particles;B, hybrid particles are stirred evenly, in 1500 DEG C of fusings, and keeps the temperature 4h;C、 It is put into quench in the water that temperature is 18 DEG C and frit is made, then vibration of ultrasonic wave 8min, up to the black glazed tiles glaze.
  4. A kind of 4. black glazed tiles glaze according to claim 1, it is characterised in that:It is the component group by following parts by weight Into:56 parts of potassium albite, 12 parts of white glass, 22 parts of quartz, 23 parts of kaolin, 18 parts of cobaltosic oxide, 18 parts of glaze fruit, green glass 17 parts of glass, 3.5 parts of tin frit, 2 parts of manganese oxide;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added Enter pulverizer, be crushed to 310 mesh, obtain hybrid particles;B, hybrid particles are stirred evenly, in 1450 DEG C of fusings, and keeps the temperature 3h; C, it is put into quench in the water that temperature is 16 DEG C and frit is made, then vibration of ultrasonic wave 6min, up to the black glazed tiles glaze.
CN201711239853.0A 2017-11-30 2017-11-30 A kind of black glazed tiles glaze Withdrawn CN107915407A (en)