CN104962367A - 一种铌粗丝拉拔润滑剂组合物 - Google Patents
一种铌粗丝拉拔润滑剂组合物 Download PDFInfo
- Publication number
- CN104962367A CN104962367A CN201510428440.1A CN201510428440A CN104962367A CN 104962367 A CN104962367 A CN 104962367A CN 201510428440 A CN201510428440 A CN 201510428440A CN 104962367 A CN104962367 A CN 104962367A
- Authority
- CN
- China
- Prior art keywords
- favorable
- wire drawing
- lubricant composition
- niobium
- niobium wire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种铌粗丝拉拔润滑剂组合物,采用去离子水、阿拉伯树胶、瓜尔胶、250目石墨粉、司盘80、三嗪(Starcide BK)、烷氧基磷酸酯和2,2-硫代苯并噻唑复合构成。本发明的润滑剂组合物能直接用于铌粗丝拉拔的润滑过程当中,具有润滑性、抗磨、承载性能优良;分散性、浸润性、冷却性、清洗能力好;不易腐败变味,使用周期长,操作方便、价格低廉的优点。
Description
技术领域
本发明属于金属加工润滑剂领域,特别涉及一种铌粗丝拉拔润滑剂组合物。
背景技术
铌是灰白色金属,熔点2468℃,沸点4742℃,密度8.57g/cm3。室温下铌在空气中稳定,在氧气中红热时也不被完全氧化,高温下与硫、氮、碳直接化合,能与钛、锆、铪、钨形成合金。不与无机酸或碱作用,也不溶于王水,但可溶于氢氟酸。铌能吸收气体,用作除气剂,也是一种良好的超导体。用铌制造的合金,临界温度高达绝对温度十八点五到二十一度,是目前最重要的超导材料。在钢的各种微合金化元素中,铌是最有效的微合金化元素,铌的作用如此之大,以至于铁原子中含有丰富的铌原子,就能达到改善钢性能的目的。
实际上钢中加入0.001%~0.1%的铌,就足以改变钢的力学性能。铌还可以通过诱导析出和控制冷却速度,实现析出物弥散分布。在较宽的范围内调整钢的韧性水平。因此,加入铌不仅可以提高钢的强度,还可以提高钢的韧性、抗高温氧化性和耐蚀性,降低钢脆性转变温度,获得好的焊接性能和成型性能。
拉拔润滑剂的作用包括:润滑、冷却、清洗等作用。拉拔润滑剂种类:液体、半固体、固体润滑剂。拉拔过程中,润滑剂能减少金属拉拔时的摩擦,它不仅能降低拉拔温度,而且还能减缓拉模和和设备的损耗,提高拉拔速度和拉拔件表面质量。金属的拉拔是极为苛刻条件下使金属发生塑性变形,通常认为:存在流体摩擦,边界摩擦,干摩擦和半干摩擦等几种摩擦形式。
拉拔润滑剂应具备的性能:优良的润滑剂和冷却作用,减少拉模的磨损,能减少拉拔时的震纹、断头等不良现象,保证控制件的表面质量,提高生产率;不与控制材料和拉模材料反应,不引起金属变色和腐蚀,不产生难以消除的沉积物;良好的去垢性能,确保拉拔润滑剂的正常循环和设备的清洁;不易产生油斑,保证控制件的表面光洁度;防锈性好,不锈蚀设备和控制件;泡沫低,消泡性能好,使用寿命长;对操作者和环境无毒害。.
发明内容
本发明要解决的技术问题是提供一种润滑性、抗磨、承载性能优良;分散性、浸润性、冷却性、清洗能力好;不易腐败变味,使用周期长,操作方便、价格低廉的铌粗丝拉拔润滑剂组合物。
本发明采用如下技术方案解决上述技术问题:
一种铌粗丝拉拔润滑剂组合物,其各组分及其质量百分数为:
组分 | 质量百分数含量 |
去离子水 | 余量 |
阿拉伯树脂 | 8%~12% |
瓜尔胶 | 3%~6% |
石墨粉 | 18%~20% |
司盘80 | 3%~5% |
三嗪(Starcide BK) | 0.01%~1% |
烷氧基磷酸酯 | 0.5%~3% |
2,2-硫代苯并噻唑 | 1%~3% |
石墨粉为250目石墨粉。
本发明的显著优点在于:润滑性、抗磨、承载性能优良;分散性、浸润性、冷却性、清洗能力好;不易腐败变味,使用周期长,操作方便、价格低廉。
具体实施方式
实施例1:将各组分按下列质量百分比调和而成:
组分 | 质量百分数含量 |
去离子水 | 64.49% |
阿拉伯树脂 | 8% |
瓜尔胶 | 3% |
250目石墨粉 | 18% |
司盘80 | 3% |
三嗪(Starcide BK) | 0.01% |
烷氧基磷酸酯 | 0.5% |
2,2-硫代苯并噻唑 | 3% |
实施例2:
将各组分按下列质量百分比调和而成:
组分 | 质量百分数含量 |
去离子水 | 57% |
阿拉伯树脂 | 10% |
瓜尔胶 | 5% |
250目石墨粉 | 19% |
司盘80 | 4% |
三嗪(Starcide BK) | 1% |
烷氧基磷酸酯 | 3% |
2,2-硫代苯并噻唑 | 1% |
实施例3:
将各组分按下列质量百分比调和而成:
组分 | 质量百分数含量 |
去离子水 | 52.5% |
阿拉伯树脂 | 12% |
瓜尔胶 | 6% |
250目石墨粉 | 20% |
司盘80 | 5% |
三嗪(Starcide BK) | 0.5% |
烷氧基磷酸酯 | 2% |
2,2-硫代苯并噻唑 | 2% |
实施例3产品的主要理化指标:
项目 | 质量指标 |
外观(0~60℃) | 黒色均匀粘稠半流体 |
乳化液pH值 | 9 |
腐蚀试验(T3铜,40℃,45号钢,1h) | 合格 |
消泡性(40℃,5min)/mL | 2 |
10%乳化液PB值/N | 735 |
Claims (2)
1.一种铌粗丝拉拔润滑剂组合物,其特征在于:其各组分及其质量百分数为:
去离子水 余量,
阿拉伯树脂 8%~12%,
瓜尔胶 3%~6%,
石墨粉 18%~20%,
司盘80 3%~5%,
三嗪Starcide BK 0.01%~1%,
烷氧基磷酸酯 0.5%~3%,
2,2-硫代苯并噻唑 1%~3%。
2.如权利要求1所述的一种铌粗丝拉拔润滑剂组合物,其特征在于,石墨粉为250目石墨粉。