CN104892818A - 一种阴离子交换树脂的制备方法 - Google Patents
一种阴离子交换树脂的制备方法 Download PDFInfo
- Publication number
- CN104892818A CN104892818A CN201510295356.7A CN201510295356A CN104892818A CN 104892818 A CN104892818 A CN 104892818A CN 201510295356 A CN201510295356 A CN 201510295356A CN 104892818 A CN104892818 A CN 104892818A
- Authority
- CN
- China
- Prior art keywords
- preparation
- exchange resin
- polymerization
- white ball
- archon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种阴离子交换树脂的制备方法，涉及树脂技术领域，其特征在于：依次包括以下步骤，水相：将纯水，分散剂，亚甲基兰一起投入聚合釜，搅拌升温到50℃后待用；油相：把苯乙烯，二乙烯苯，引发剂在室温状态下，投进混料釜，待混匀后投入水相聚合釜，油相投入聚合釜后，在搅拌情况下分段升温，保持进行悬浮聚合到96～103℃后开始固化，得到聚合珠体反应物白球，然后抽去母液，把聚合白球放到过滤器90℃热纯水洗涤3次以上，洗净的白球进行沸腾床真空干燥，干燥后筛选后即可得成品。本发明聚合反应彻底，树脂的吸附能力强，吸附后体积变化较小，机械强度高，白球的粒径达，不容易结块。
Description
技术领域：
本发明涉及树脂技术领域，具体是一种阴离子交换树脂的制备方法。
背景技术：
吸附树脂是以吸附为特点，具有多孔立体结构的树脂吸附剂。它是最近几年高分子领域里新发展起来的一种多孔性树脂，通过悬浮共聚法制得的鱼籽样的小圆球。吸附树脂常常用于污水处理以及提取等领域。现有的用于吸附的树脂在制作后的，现有的工艺容易聚合反应不彻底，树脂的吸附能力不强，吸附后体积变化较大，机械强度低，白球的粒径小，容易结块。
发明内容：
本发明所要解决的技术问题在于提供一种聚合反应彻底，树脂的吸附能力强，吸附后体积变化较小，机械强度高，白球的粒径达，不容易结块的阴离子交换树脂的制备方法。
本发明所要解决的技术问题采用以下技术方案来实现。
一种阴离子交换树脂的制备方法，其特征在于：依次包括以下步骤，
(1)水相：将纯水，分散剂，亚甲基兰一起投入聚合釜，搅拌升温到50℃后待用；
(2)油相：把苯乙烯，二乙烯苯，引发剂在室温状态下，投进混料釜，
(3)待混匀后投入水相聚合釜，油相投入聚合釜后，在搅拌情况下分段升温，保持进行悬浮聚合到96～103℃后开始固化，得到聚合珠体反应物白球，然后抽去母液，把聚合白球放到过滤器90℃热纯水洗涤3次以上，洗净的白球进行沸腾床真空干燥，干燥后筛选后即可得成品。
所述的苯乙烯和二乙烯苯经纯化后的混合单体放置时间不能超过1小时。
所述的固化的末期进行保温5～6小时。
本发明的有益效果是：本发明聚合反应彻底，树脂的吸附能力强，吸附后体积变化较小，机械强度高，白球的粒径达，不容易结块。
具体实施方式：
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
一种阴离子交换树脂的制备方法，依次包括以下步骤，
(1)水相：将纯水，分散剂，亚甲基兰一起投入聚合釜，搅拌升温到50℃后待用；
(2)油相：把苯乙烯，二乙烯苯，引发剂在室温状态下，投进混料釜，
(3)待混匀后投入水相聚合釜，油相投入聚合釜后，在搅拌情况下分段升温，保持进行悬浮聚合到96～103℃后开始固化，得到聚合珠体反应物白球，然后抽去母液，把聚合白球放到过滤器90℃热纯水洗涤3次以上，洗净的白球进行沸腾床真空干燥，干燥后筛选后即可得成品。
苯乙烯和二乙烯苯经纯化后的混合单体放置时间不能超过1小时。
固化的末期进行保温5～6小时。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (3)
1.一种阴离子交换树脂的制备方法，其特征在于：依次包括以下步骤，
(1)水相：将纯水，分散剂，亚甲基兰一起投入聚合釜，搅拌升温到50℃后待用；
(2)油相：把苯乙烯，二乙烯苯，引发剂在室温状态下，投进混料釜，
(3)待混匀后投入水相聚合釜，油相投入聚合釜后，在搅拌情况下分段升温，保持进行悬浮聚合到96～103℃后开始固化，得到聚合珠体反应物白球，然后抽去母液，把聚合白球放到过滤器90℃热纯水洗涤3次以上，洗净的白球进行沸腾床真空干燥，干燥后筛选后即可得成品。
2.根据权利要求1所述的一种阴离子交换树脂的制备方法，其特征在于：所述的苯乙烯和二乙烯苯经纯化后的混合单体放置时间不能超过1小时。
3.根据权利要求1所述的一种阴离子交换树脂的制备方法，其特征在于：所述的固化的末期进行保温5～6小时。