CN104862056A - 冷旋压铜合金管润滑剂组合物 - Google Patents

冷旋压铜合金管润滑剂组合物 Download PDF

Info

Publication number
CN104862056A
CN104862056A CN201510304251.3A CN201510304251A CN104862056A CN 104862056 A CN104862056 A CN 104862056A CN 201510304251 A CN201510304251 A CN 201510304251A CN 104862056 A CN104862056 A CN 104862056A
Authority
CN
China
Prior art keywords
copper alloy
alloy tube
cold spinning
lubricant compositions
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510304251.3A
Other languages
English (en)
Other versions
CN104862056B (zh
Inventor
黄福川
李康春
卢朝霞
黄旖瑶
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangxi University
Original Assignee
Guangxi University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangxi University filed Critical Guangxi University
Priority to CN201510304251.3A priority Critical patent/CN104862056B/zh
Publication of CN104862056A publication Critical patent/CN104862056A/zh
Application granted granted Critical
Publication of CN104862056B publication Critical patent/CN104862056B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了冷旋压铜合金管润滑剂组合物，采用MVI 150基础油作为基础油，配合多种添加剂，包括：油性剂、极压剂、抗磨剂、抗氧剂、摩擦改进剂、补强剂、助剂。本发明的润滑剂组合物具有较强的浸润性、流动性，油膜强度大，抗磨性、抗剪切性、耐压性和粘温性好，极压性强、油膜厚度和强度的稳定性、压强分布均匀性和润滑性好，有较小的流动剪切应力，提高管材的表面光洁度和尺寸规格精度，较好的氧化安定性、冷却性和适当的闪点及着火点，保证使用与清理方便，有防止出现铜锈斑和防腐蚀的能力。

Description

冷旋压铜合金管润滑剂组合物
技术领域
本发明属于金属加工润滑剂领域，特别是冷旋压铜合金管润滑剂组合物。
背景技术
铜是与人类关系非常密切的有色金属，被广泛地应用于电气、轻工、机械制造、建筑工业、国防工业等领域，在中国有色金属材料的消费中仅次于铝。铜在电气、电子工业中应用最广、用量最大，占总消费量一半以上。用于各种电缆和导线，电机和变压器，开关以及印刷线路板的制造中。在机械和运输车辆制造中，用于制造工业阀门和配件、仪表、滑动轴承、模具、热交换器和泵等。在化学工业中广泛应用于制造真空器、蒸馏锅、酿造锅等。在国防工业中用以制造子弹、炮弹、枪炮零件等。在建筑工业中，用做各种管道、管道配件、装饰器件等。
冷旋压技术是近年来研究较多的加工工艺。冷旋压技术的发展主要是开发高附加值的产品，其生产的管件质量高，能承受大的冲击力作用，其塑性、韧性等力学性能较好；在保证零件设计强度的前提下，减轻设备和装置自身重量；节约金属材料；降低生产成本，生产效率高。
发明内容
本发明要解决的技术问题是提供一种具有较强的浸润性、流动性，油膜强度大，抗磨性、抗剪切性、耐压性和粘温性好，极压性强、油膜厚度和强度的稳定性、压强分布均匀性和润滑性好，有较小的流动剪切应力，提高管材的表面光洁度和规格精度，较好的氧化安定性、冷却性和适当的闪点及着火点，保证使用与清理方便，有防止出现铜锈斑和防腐蚀的能力的冷旋压铜合金管润滑剂组合物。
本发明采用如下技术方案解决上述技术问题：
冷旋压铜合金管润滑剂组合物，采用MVI 150基础油为基础油，配合多种添加剂，其各组分及其质量百分数为：
组分 质量百分数含量
基础油 余量
油性剂 8.0％～10.0％
极压剂 3.0％～4.0％
抗磨剂 4.0％～6.0％
抗氧剂 0.2％～0.5％
摩擦改进剂 4.0％～5.0％
补强剂 0.5％～1.2％
助剂 0.3％～0.8％
油性剂是工业猪油。
极压剂是二聚酸乙二醇酯。
抗磨剂是亚磷酸二正丁酯T304。
抗氧剂是受阻酚混合物IrganoXL-134。
摩擦改进剂是膦酸酯T451。
补强剂是烷基磷酸酯胺盐Mobilad C-423。
助剂是苯三唑衍生物T551。
本发明的的显著优点有：具有较强的浸润性、流动性，油膜强度大，抗磨性、抗剪切性、耐压性和粘温性好，极压性强、油膜厚度和强度的稳定性、压强分布均匀性和润滑性好，有较小的流动剪切应力，提高管材的表面光洁度和规格精度，较好的氧化安定性、冷却性和适当的闪点及着火点，保证使用与清理方便，有防止出现铜锈斑和防腐蚀的能力。
具体实施方式
实施例1：
将下列质量百分数的各组分调和而成：
组分 质量百分数含量
MVI 150基础油 78.0％
工业猪油 8.0％
二聚酸乙二醇酯 3.0％
亚磷酸二正丁酯(T304) 5.0％
受阻酚混合物(IrganoXL-134) 0.3％
膦酸酯(T451) 4.5％
烷基磷酸酯胺盐(Mobilad C-423) 0.7％
苯三唑衍生物(T551) 0.5％
实施例2：
将下列质量百分数的各组分调和而成：
组分 质量百分数含量
MVI 150基础油 75.7％
工业猪油 8.5％
二聚酸乙二醇酯 4.0％
亚磷酸二正丁酯(T304) 5.5％
受阻酚混合物(IrganoXL-134) 0.4％
膦酸酯(T451) 4.5％
烷基磷酸酯胺盐(Mobilad C-423) 0.9％
苯三唑衍生物(T551) 0.5％
实施例3：
将下列质量百分数的各组分调和而成：
组分 质量百分数含量
MVI 150基础油 77.2％
工业猪油 9.0％
二聚酸乙二醇酯 3.5％
亚磷酸二正丁酯(T304) 4.5％
受阻酚混合物(IrganoXL-134) 0.4％
膦酸酯(T451) 4.0％
烷基磷酸酯胺盐(Mobilad C-423) 0.8％
苯三唑衍生物(T551) 0.6％
实施例3典型主要理化指标：
项目 质量指标
40℃运动粘度/(mm2﹒s-1) 29.3
粘度指数 92
倾点/℃ -14
闪点(开口)/℃ 255
最大无卡咬负荷(Pb)，Kg 97
酸值/mg KOH﹒g-1 0.063
水分，％ 痕迹
氧化安定性(旋转氧弹法，150℃)，min 233
腐蚀试验(铜片、100℃、3h)，级 1
机械杂质，％ 无

Claims (8)

1.冷旋压铜合金管润滑剂组合物，其特征在于：采用MVI 150基础油为基础油，配合多种添加剂，其各组分及其质量百分数为：
2.如权利要求1所述的冷旋压铜合金管润滑剂组合物，其特征在于，油性剂是工业猪油。
3.如权利要求1所述的冷旋压铜合金管润滑剂组合物，其特征在于，极压剂是二聚酸乙二醇酯。
4.如权利要求1所述的冷旋压铜合金管润滑剂组合物，其特征在于，抗磨剂是亚磷酸二正丁酯T304。
5.如权利要求1所述的冷旋压铜合金管润滑剂组合物，其特征在于，抗氧剂是受阻酚混合物IrganoXL-134。
6.如权利要求1所述的冷旋压铜合金管润滑剂组合物，其特征在于，摩擦改进剂是膦酸酯T451。
7.如权利要求1所述的冷旋压铜合金管润滑剂组合物，其特征在于，补强剂是烷基磷酸酯胺盐Mobilad C-423。
8.如权利要求1所述的冷旋压铜合金管润滑剂组合物，其特征在于，助剂是苯三唑衍生物T551。
CN201510304251.3A 2015-06-05 2015-06-05 冷旋压铜合金管润滑剂组合物 Active CN104862056B (zh)