CN104845504A - 一种金属防锈涂料 - Google Patents

一种金属防锈涂料 Download PDF

Info

Publication number
CN104845504A
CN104845504A CN201510287361.3A CN201510287361A CN104845504A CN 104845504 A CN104845504 A CN 104845504A CN 201510287361 A CN201510287361 A CN 201510287361A CN 104845504 A CN104845504 A CN 104845504A
Authority
CN
China
Prior art keywords
parts
egg
nanometer
shell meal
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510287361.3A
Other languages
English (en)
Other versions
CN104845504B (zh
Inventor
龚重勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Huzhou Great Zhou Macromolecular Material Co Ltd
Original Assignee
Huzhou Great Zhou Macromolecular Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Huzhou Great Zhou Macromolecular Material Co Ltd filed Critical Huzhou Great Zhou Macromolecular Material Co Ltd
Priority to CN201510287361.3A priority Critical patent/CN104845504B/zh
Publication of CN104845504A publication Critical patent/CN104845504A/zh
Application granted granted Critical
Publication of CN104845504B publication Critical patent/CN104845504B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种金属防锈涂料,属于涂料技术领域。由重量份数的以下物质制成:水性丙烯酸改性环氧树脂40-50份、苯并三氮唑5-10份、聚有机硅氧烷4-9份、铁氰酸盐5-12份、苯乙烯6-15份、铝粉8-15份、粒径为20-25nm的纳米银0.5-1.5份、粒径为30-40nm的纳米蛋壳粉30-40份、三聚磷酸铝6-9份、四氟硼酸四乙胺2-5份、滑石粉3-7份、氧化铁颜料浆5-10份、水20-30份。上述一种金属防锈涂料,各组分的配比合理,涂层质地紧密、耐低温、附着性好、防水效果好、耐腐蚀、防变色,还具有良好的耐磨、可冲压性能和抗菌效果。

Description

一种金属防锈涂料
技术领域
本发明属于涂料技术领域,具体为一种金属防锈涂料。
背景技术
金属涂料是具有金属质感的涂料,多数需要对金属表面进行某种形式的预处理,改善表面状况,以利于提高涂层的附着力、增强对金属基材的防腐保护作用。和传统涂料涂装相似,金属涂装之前,多数需要对金属表面进行某种形式的预处理,改善表面状况,以利于提高涂层的附着力、增强对金属基材的防腐保护作用。现有的金属材料,存在易腐蚀问题,表面容易污损,影响美观;需要进行涂装保护,现有的金属涂料的耐腐性一般,无法满足市场对金属涂料的使用需求。
发明内容
针对现有技术中存在的上述问题,本发明的内容在于设计提供一种金属防锈涂料的技术方案,各组分的配比合理,涂层质地紧密、耐低温、附着性好、防水效果好、耐腐蚀、防变色,还具有良好的耐磨、可冲压性能和抗菌效果。
所述的一种金属防锈涂料,其特征在于由重量份数的以下物质制成:水性丙烯酸改性环氧树脂40-50份、苯并三氮唑5-10份、聚有机硅氧烷4-9份、铁氰酸盐5-12份、苯乙烯6-15份、铝粉8-15份、粒径为20-25nm的纳米银0.5-1.5份、粒径为30-40nm的纳米蛋壳粉30-40份、三聚磷酸铝6-9份、四氟硼酸四乙胺2-5份、滑石粉3-7份、氧化铁颜料浆5-10份、水20-30份。
所述一种金属防锈涂料,其特征在于水性丙烯酸改性环氧树脂42-48份、苯并三氮唑6-9份、聚有机硅氧烷5-8份、铁氰酸盐6-10份、苯乙烯8-12份、铝粉10-14份、纳米银0.8-1.2份、纳米蛋壳粉32-38份、三聚磷酸铝7-8份、四氟硼酸四乙胺3-4份、滑石粉4-6份、氧化铁颜料浆6-8份、水22-28份。
所述一种金属防锈涂料,其特征在于水性丙烯酸改性环氧树脂44-46份、苯并三氮唑7-8份、聚有机硅氧烷6-7份、铁氰酸盐7-8份、苯乙烯9-10份、铝粉11-12份、纳米银0.9-1份、纳米蛋壳粉34-36份、三聚磷酸铝8份、四氟硼酸四乙胺4份、滑石粉5份、氧化铁颜料浆7份、水24-26份。
所述的水性丙烯酸改性环氧树脂具有较好的光泽度、耐候性、耐化学品性和稳定性高,且无污染、无毒性,是一种低VOC的绿色环保产品。
所述的苯并三氮唑主要作为水处理剂、金属防锈剂和缓蚀剂。广泛用于循环水处理剂,防锈油、脂类产品中,也应用于铜及铜合金的气相缓蚀剂、润滑油添加剂。在电镀中用以表面纯化银、铜、锌,有防变色作用。BTA与铜原子形成共价键和配位键,相互多替成链状聚合物,在铜加表面组成多层保护膜,使铜的表面不起氧化还原反应,不发生氢气,起防蚀作用。对铅、铸铁、镍、锌等金属材料也有同样效果。BTA可与多种缓蚀剂配合,提高缓蚀效果。也可与多种阻垢剂、杀菌灭藻剂配合使用,尤其对封闭用循环冷却水系统缓蚀效果甚佳,在汽车用防冻剂乙二醇和水中,涂料中添加BTA都能挥发保护材料的作用。BTA为良好的紫外光吸收剂,对紫外光敏感的制品可起到稳定的作用,例如防止重氮染料褪色,用BTA处理纸、编织物、胶片、金属硬币等薄片制品可以防止变色。
所述的聚有机硅氧烷,其表面张力低,表征压力低,高分子量时候具有液态性能,极低的粘温系数。
本发明通过加入苯乙烯成分,使得该涂料具有很好的防水效果。
本发明通过加入适量的四氟硼酸四乙胺,使得涂料具有良好的耐腐蚀性能。
所述的蛋壳是经过天然自然形成,经现代各种科学手段检测蛋壳中含碳酸钙83-85%,蛋白质15-17%,并含有多种微量元素锌、铜、锰、铁、硒等,其中对人体有害的重金属元素铅、砷的含量极其低,均小于1PPM。纳米碳酸钙在涂料中为颜料填充剂,起一种骨架作用,具有细腻、均匀、白度高、光学性能好等优点。纳米级超细碳酸钙具有空间位阻效应.在制漆中,能使配方中密度较大的立德粉悬浮,起防沉降作用.制漆后,漆膜白度增加,光泽度高,而遮盖力可作为颜料填充剂,具有细腻、均匀、白度高、光学性能好等优点;制漆后,漆膜白度增加,光泽高,而遮盖力却不下降。碳酸钙的粒径越小,则性能越好。纳米碳酸钙可以部分取代钛白粉,降低原料成本。纳米碳酸钙还具有一定的杀菌效果。
所述的纳米银材料具有稳定的物理化学性能,如高导热性、高导电性和优良的光学性能等,在电学、光学、催化、生物传感器、数据存储、磁性器件、医药抗菌、表面增强拉曼光谱等方面广泛应用;不同形貌的纳米银粉性能不同,如粒径较小、粒度分布窄的球形纳米银粉具有良好的抗菌性能。研究表明,纳米银的粒径越小,则抗菌性能越好。纳米银可以从市场上直接购得。
上述涂料中各组分、含量的不同,对涂料的性能有着显著的影响。
上述一种金属防锈涂料,各组分的配比合理,涂层质地紧密、耐低温、附着性好、防水效果好、耐腐蚀、防变色,还具有良好的耐磨、可冲压性能和抗菌效果。
具体实施方式
以下结合具体实施例对本发明作进一步说明。
实施例1
所述的一种金属防锈涂料,由重量份数的以下物质制成::水性丙烯酸改性环氧树脂40份、苯并三氮唑5份、聚有机硅氧烷4份、铁氰酸盐5份、苯乙烯6份、铝粉8份、粒径为20nm的纳米银0.5份、粒径为30nm的纳米蛋壳粉30份、三聚磷酸铝6份、四氟硼酸四乙胺2份、滑石粉3份、氧化铁颜料浆5份、水20份;将上述各组份按配比投入高速混料缸高速混合,然后在螺杆挤出机进行挤出,即得到抗菌性粉末涂料。
实施例2
所述的一种金属防锈涂料,由重量份数的以下物质制成:水性丙烯酸改性环氧树脂42份、苯并三氮唑6份、聚有机硅氧烷5份、铁氰酸盐6份、苯乙烯7份、铝粉9份、粒径为25nm的纳米银0.6份、粒径为40nm的纳米蛋壳粉32份、三聚磷酸铝7份、四氟硼酸四乙胺3份、滑石粉4份、氧化铁颜料浆6份、水22份;将上述各组份按配比投入高速混料缸高速混合,然后在螺杆挤出机进行挤出,即得到抗菌性粉末涂料。
实施例3
所述的一种金属防锈涂料,由重量份数的以下物质制成:水性丙烯酸改性环氧树脂45份、苯并三氮唑8份、聚有机硅氧烷7份、铁氰酸盐10份、苯乙烯12份、铝粉12份、粒径为20nm的纳米银1份、粒径为35nm的纳米蛋壳粉35份、三聚磷酸铝8份、四氟硼酸四乙胺4份、滑石粉6份、氧化铁颜料浆8份、水25份;将上述各组份按配比投入高速混料缸高速混合,然后在螺杆挤出机进行挤出,即得到抗菌性粉末涂料。
实施例4
所述的一种金属防锈涂料,由重量份数的以下物质制成:水性丙烯酸改性环氧树脂50份、苯并三氮唑10份、聚有机硅氧烷9份、铁氰酸盐12份、苯乙烯15份、铝粉15份、粒径为25nm的纳米银1.5份、粒径为40nm的纳米蛋壳粉40份、三聚磷酸铝9份、四氟硼酸四乙胺5份、滑石粉7份、氧化铁颜料浆10份、水30份;将上述各组份按配比投入高速混料缸高速混合,然后在螺杆挤出机进行挤出,即得到抗菌性粉末涂料。
上述实施例2的粉末涂料经性能检测,测试结果表明 :涂层干燥时间表干30min、实干1h;固化时间1-2天,涂层附着力3级、5mpa,涂层抗冲击强度强为50,涂层柔韧性2.5mm;涂层耐热试验,400℃、48小时无变化;VOC含量为每升25克,远远低于国家标准。以实施例1、实施例3、实施例4进行性能检测,也能达到本发明所述的有益效果。

Claims (4)

1. 一种金属防锈涂料,其特征在于由重量份数的以下物质制成:水性丙烯酸改性环氧树脂40-50份、苯并三氮唑5-10份、聚有机硅氧烷4-9份、铁氰酸盐5-12份、苯乙烯6-15份、铝粉8-15份、粒径为20-25nm的纳米银0.5-1.5份、粒径为30-40nm的纳米蛋壳粉30-40份、三聚磷酸铝6-9份、四氟硼酸四乙胺2-5份、滑石粉3-7份、氧化铁颜料浆5-10份、水20-30份。
2. 如权利要求1所述一种金属防锈涂料,其特征在于水性丙烯酸改性环氧树脂42-48份、苯并三氮唑6-9份、聚有机硅氧烷5-8份、铁氰酸盐6-10份、苯乙烯8-12份、铝粉10-14份、纳米银0.8-1.2份、纳米蛋壳粉32-38份、三聚磷酸铝7-8份、四氟硼酸四乙胺3-4份、滑石粉4-6份、氧化铁颜料浆6-8份、水22-28份。
3. 如权利要求1所述一种金属防锈涂料,其特征在于水性丙烯酸改性环氧树脂44-46份、苯并三氮唑7-8份、聚有机硅氧烷6-7份、铁氰酸盐7-8份、苯乙烯9-10份、铝粉11-12份、纳米银0.9-1份、纳米蛋壳粉34-36份、三聚磷酸铝8份、四氟硼酸四乙胺4份、滑石粉5份、氧化铁颜料浆7份、水24-26份。
4. 如权利要求1所述一种金属防锈涂料,其特征在于其特征在于所述的纳米贝壳粉采用以下方法制备:将鸡蛋、鸭蛋的蛋壳清洗烘干后用粉碎机粉碎成细粉,然后将细蛋壳粉加入到碱性氧化剂水溶液中,以氧化锆珠为球磨介质,室温下湿法球磨5-10小时,将球磨后蛋壳粉分离、清洗、干燥,制得粒径为30-40nm的纳米蛋壳粉。
CN201510287361.3A 2015-05-29 2015-05-29 一种金属防锈涂料 Expired - Fee Related CN104845504B (zh)