CN104844945A - 一种用于橡胶发泡的预分散母胶粒及其制备方法 - Google Patents
一种用于橡胶发泡的预分散母胶粒及其制备方法 Download PDFInfo
- Publication number
- CN104844945A CN104844945A CN201510225273.0A CN201510225273A CN104844945A CN 104844945 A CN104844945 A CN 104844945A CN 201510225273 A CN201510225273 A CN 201510225273A CN 104844945 A CN104844945 A CN 104844945A
- Authority
- CN
- China
- Prior art keywords
- parts
- dispersed
- rubber
- masterbatch particles
- coupling agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
发泡材料编号 | 密度(g/cm3) | 拉伸强度/MPa | 拉断伸长率/% |
I(实施例1) | 0.57 | 1.78 | 523.87 |
II(实施例2) | 0.56 | 1.76 | 524.65 |
III(实施例3) | 0.56 | 1.77 | 521.23 |
IV(实施例4) | 0.50 | 1.75 | 534.25 |
V(比较例1) | 0.57 | 1.79 | 512.34 |
VI(比较例2) | 0.58 | 1.80 | 519.67 |
VII(比较例3) | 0.59 | 1.81 | 514.89 |
0(发泡剂粉体) | 0.63 | 1.83 | 506.40 |
Claims (8)