CN104762433A - 一种铸铁金属液清洁剂 - Google Patents
一种铸铁金属液清洁剂 Download PDFInfo
- Publication number
- CN104762433A CN104762433A CN201510160151.8A CN201510160151A CN104762433A CN 104762433 A CN104762433 A CN 104762433A CN 201510160151 A CN201510160151 A CN 201510160151A CN 104762433 A CN104762433 A CN 104762433A
- Authority
- CN
- China
- Prior art keywords
- metal liquid
- iron metal
- chemical index
- cast iron
- sio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种铸铁金属液清洁剂,其特征在于,由以下重量百分比的原料组成:40~80目的珍珠岩94%、粒度≤100目的粘土1%、20~80目的玻璃3%、20~80目的石灰石1%、粒度≤100目的磷酸二氢铝1%。与现有技术相比,本发明提供的铸铁金属液清洁剂粘度和温度匹配,铺展性能好,除渣次数少,用量小。
Description
技术领域
本发明涉及一种铸铁金属液清洁剂。
背景技术
导致铸件报废的原因有多个方面,综合起来有以下几种:析出气孔、侵入气孔、缩孔、疏松、砂眼、渣眼、化学成份偏析、化学成份不合、尺寸不合,不同缺陷形成的原因不同。渣眼缺陷严重影响到铸件的质量指标,申请的发明专利主要阐述解决铸件的渣眼问题。
铸件的渣眼主要是由炉衬材料、废铸铁料表面泥污造成。针对如何减少或避免铸件的渣眼缺陷这个问题,国内外铸造界、冶金材料生产行业采取了诸多措施,截至到2012年,没有找到一个良好的解决问题的措施。
冶金铸造行业为了克服这一问题,研究和生产了诸如金属液净化剂、除渣剂等冶金辅料产品,这些产品均呈现出高温粘度低、铺展性差等缺点。
例如:中国专利201210267374.0公开了一种除渣剂,具体涉及一种铸造用复合除渣剂,属金属加工除渣技术领域。它由粒度<0.3mm的珍珠岩细粉75-95重量%,活性SiO20.2-10重量%、活性Al2O30.1-5重量%和水玻璃2-15重量%混合均匀、干燥固化、破碎筛分制备而成。该复合除渣剂可以满足从小包至大包,从铸铁到铸钢的不同生产要求。生产出的除渣剂体轻,在金属液上安静,熔化后熔体粘度高,利于聚渣和扒渣。
发明内容
本发明要解决的技术问题是提供一种铸铁金属液清洁剂。
本发明是通过以下技术方案来实现:
一种铸铁金属液清洁剂,由以下重量百分比的原料组成:40~80目的珍珠岩94%、粒度≤100目的粘土1%、20~80目的玻璃3%、20~80目的石灰石1%、粒度≤100目的磷酸二氢铝1%。
进一步,珍珠岩的化学指标为:SiO2≥68%、FeO≤1.0%、H2O≤8%;粘土的化学指标为:SiO2≥65%、Al2O3≥28%、H2O≤1.0%;玻璃的化学指标为:SiO2≥70%、CaO≤20%、Na2O+K2O≤15%;石灰石的化学指标为:CaCO3≥60%、SiO2≤20%;磷酸二氢铝的化学指标为:Al(H2PO4)3≥98%。
与现有技术相比,本发明提供的铸铁金属液清洁剂粘度和温度匹配,铺展性能好,除渣次数少,用量小。
具体实施方式
下面结合实施例对本发明作进一步说明:
实施例1
一种铸铁金属液清洁剂,由以下重量百分比的原料组成:40~80目的珍珠岩94%、粒度≤100目的粘土1%、20~80目的玻璃3%、20~80目的石灰石1%、粒度≤100目的磷酸二氢铝1%。
进一步,珍珠岩的化学指标为:SiO2≥68%、FeO≤1.0%、H2O≤8%;粘土的化学指标为:SiO2≥65%、Al2O3≥28%、H2O≤1.0%;玻璃的化学指标为:SiO2≥70%、CaO≤20%、Na2O+K2O≤15%;石灰石的化学指标为:CaCO3≥60%、SiO2≤20%;磷酸二氢铝的化学指标为:Al(H2PO4)3≥98%。
实施例3
在铸铁料加入完毕之前,提前加入金属液洁净剂,使之得到充分熔化,便于冶炼大渣的去除。大渣去除以后,分2~3次向金属液表面加入金属洁净剂,待洁净剂变红后即可除渣,除渣2~3次即可。
Claims (2)
1.一种铸铁金属液清洁剂,其特征在于,由以下重量百分比的原料组成:40~80目的珍珠岩94%、粒度≤100目的粘土1%、20~80目的玻璃3%、20~80目的石灰石1%、粒度≤100目的磷酸二氢铝1%。
2.根据权利要求1所述的一种铸铁金属液清洁剂,其特征在于,珍珠岩的化学指标为:SiO2≥68%、FeO≤1.0%、H2O≤8%;粘土的化学指标为:SiO2≥65%、Al2O3≥28%、H2O≤1.0%;玻璃的化学指标为:SiO2≥70%、CaO≤20%、Na2O+K2O≤15%;石灰石的化学指标为:CaCO3≥60%、SiO2≤20%;磷酸二氢铝的化学指标为:Al(H2PO4)3≥98%。